BS EN 13614-2011 Bitumen and bituminous binders Determination of adhesivity of bituminous emulsions by water immersion test《沥青和沥青结合料 水浸入试验测定沥青乳胶的粘度》.pdf

《BS EN 13614-2011 Bitumen and bituminous binders Determination of adhesivity of bituminous emulsions by water immersion test《沥青和沥青结合料 水浸入试验测定沥青乳胶的粘度》.pdf》由会员分享，可在线阅读，更多相关《BS EN 13614-2011 Bitumen and bituminous binders Determination of adhesivity of bituminous emulsions by water immersion test《沥青和沥青结合料 水浸入试验测定沥青乳胶的粘度》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 13614:2011BS 2000-521:2011Bitumen and bituminous binders Determination of adhesivity of bituminous emulsions by water immersion testLicensed Copy: Wang Bin, ISO/EXCHANGE CH

2、INA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 13614:2011. It supersedes BS EN 13614:2004, which is withdrawn.The UK participation in its preparation was entrusted to Technical Committe

3、e PTI/13, Petroleum Testing and Terminology.A list of organizations represented on this committee can be obtained on request to its secretary.Energy Institute, under the brand of IP, publishes and sells all Parts of BS 2000, and all BS EN petroleum test methods that would be Part of BS 2000, both in

4、 its annual publication “Standard methods for analysis and testing of petroleum and related products and British Standard 2000 Parts” and individually.Further information is available from:Energy Institute, 61 New Cavendish Street, London W1G 7AR.Tel: 020 7467 7100. Fax: 020 7255 1472.This publicati

5、on does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. BSI 2011 ISBN 978 0 580 69225 3 ICS 75.140; 91.100.50 Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published und

6、er the authority of the Standards Policy and Strategy Committee on 30 April 2011.Amendments issued since publicationDate T e x t a f f e c t e dLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EUROPEAN STANDARD NORME EUROPENNE EUROPIS

7、CHE NORM EN 13614 March 2011 ICS 75.140 Supersedes EN 13614:2004English Version Bitumen and bituminous binders - Determination of adhesivity of bituminous emulsions by water immersion test Bitumes et liants bitumineux - Dtermination de ladhsivit des mulsions de bitume par lessai dimmersion dans leau

8、Bitumen und bitumenhaltige Bindemittel - Bestimmung des Haftverhaltens von Bitumenemulsionen bei Wasserlagerung This European Standard was approved by CEN on 12 February 2011. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this Eur

9、opean Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versio

10、ns (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, B

11、elgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN C

12、OMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13614:2011: ELicensed Copy: Wang B

13、in, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EN 13614:2011 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions . 44 Principle 55 Reagents and materials 56 Apparatus . 57 Sampling . 58 Procedure . 69 Expression of res

14、ults 710 Precision . 711 Test report 7Annex A (informative) Guidance for the marking of coated surface area . 8Bibliography 9Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EN 13614:2011 (E) 3 Foreword This document (EN 13614:2011) h

15、as been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR/BNP. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2011, and conflict

16、ing national standards shall be withdrawn at the latest by September 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This docume

17、nt supersedes EN 13614:2004. This revised version (EN 13614:2011) makes a distinction between “immediate” adhesivity and water effect on binder adhesion. Compliance to the adhesivity requirements set by EN 13808 is verified according to the procedure defined for testing water effect on binder adhesi

18、on. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ire

19、land, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EN 13614:2011 (E) 4

20、 1 Scope This European Standard specifies a method for determining the adhesion of a bituminous emulsion coated onto aggregate when immersed in water. The method considers two different aspects of adhesivity, i.e. immediate adhesivity and water effect on binder adhesion. The method may be used with

21、a reference aggregate. In that case, it measures the intrinsic adhesion behaviour of a bituminous emulsion. The method may also be used with a specific aggregate as used on a job site. WARNING The use of this European Standard may involve hazardous materials, operations and equipment. This European

22、Standard does not purport to address all of the safety problems associated with its use. It is the responsibility of the user of this European Standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 2 Normative references

23、The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bi

24、tuminous binders EN 12594, Bitumen and bituminous binders Preparation of test samples EN 13808, Bitumen and bituminous binders Framework for specifying cationic bituminous emulsions EN ISO 3696, Water for analytical laboratory use Specification and test methods (ISO 3696:1987) 3 Terms and definition

25、s For the purposes of this document, the following terms and definitions apply. 3.1 adhesion ability of a binder to coat the surface of an aggregate and to remain bonded over time in the presence of water 3.2 adhesivity qualitative assessment of the measurement of the adhesion 3.3 immediate adhesivi

26、ty qualitative assessment of the ability of the binder from a bituminous emulsion to resist the action of water just after coating of the aggregate 3.4 water effect on binder adhesion qualitative assessment of the ability of the binder from a bituminous emulsion to resist the action of water after c

27、oating of the aggregate and a period of curing Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EN 13614:2011 (E) 5 4 Principle The bituminous emulsion is mixed thoroughly with the considered aggregate under specified conditions. When

28、 testing immediate adhesivity, the mixture is immediately washed under running water and the percentage of the aggregate surface covered with binder is assessed visually under specified conditions. When testing water effect on binder adhesion, the mixture is first left to cure and then immersed unde

29、r water under specified conditions. The percentage of the aggregate surface covered with binder is assessed visually under specified conditions. Conformity to the “adhesivity” requirement specified in EN 13808 is to be assessed while measuring the water effect on binder adhesion with a reference agg

30、regate. 5 Reagents and materials 5.1 Reference aggregate, as light in colour as possible, or aggregate from a specific job site, which either passes through a sieve having a mesh size of 10 mm and is retained on a sieve having a mesh size of 6,3 mm (sieve sizes belonging to the “basic set plus set 2

31、” sizes specified in EN 13043), or passes through a sieve having a mesh size of 11 mm and is retained on a sieve having a mesh size of 8 mm (sieve sizes belonging to the “basic set plus set 1” sizes specified in EN 13043). NOTE Each country should define petrographically its own reference aggregates

32、, for instance, in a national informative annex. 5.2 Water, distilled or deionised, conforming to EN ISO 3696. 5.3 Cleaning agents, conventionally used in a laboratory. 6 Apparatus 6.1 Ventilated oven, capable of maintaining a temperature of (60 3) C. 6.2 Spatula. 6.3 Two heat resistant dishes, diam

33、eter approximately 15 cm to 20 cm. 6.4 Timer, accurate to at least 1 s over 60 s. 6.5 Two beakers, approximately 500 ml capacity. 6.6 Set of five watch glasses, diameter of at least 15 cm. 6.7 Balance, of sufficient capacity, accurate to 1 g. 6.8 Measuring cylinder, 250 ml to 500 ml capacity. 6.9 Th

34、ermometer, of adequate range, allowing measuring the specified temperatures with an accuracy of 1 C. 6.10 Ventilated oven, capable of maintaining a temperature of (110 5) C. 7 Sampling Sample the test material in accordance with EN 58. Prepare the test samples in accordance with EN 12594. Licensed C

35、opy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSIBS EN 13614:2011EN 13614:2011 (E) 6 8 Procedure 8.1 General Carry out the procedure under normal laboratory conditions (23 5) C. If the intrinsic adhesivity of the emulsion is controlled, the procedure shall be

36、carried out with the reference aggregate(s). The reference aggregate(s) shall be washed with water (5.2) and dried in the ventilated oven (6.10) at (110 5) C for about 2 h. If the adhesivity behaviour of a specific emulsion/aggregate combination is controlled for a specific job site, the aggregate s

37、hall be used in its job site conditions (5.1). 8.2 Determination of immediate adhesivity 8.2.1 Weigh (100 5) g of aggregate (5.1) into a dish (6.3) and (150 5) g of emulsion into another dish (6.3). 8.2.2 Pour the aggregate into the emulsion and allow contacting for (60 5) s without stirring; the di

38、sh may be gently shaken to disperse any air bubbles which might prevent proper moistening of the aggregate. 8.2.3 Remove excess emulsion by carefully tilting the dish and wash the aggregate at room temperature, holding the dish tilted under a slow stream of water (5.2) until the water runs clear. 8.

39、2.4 Introduce the coated aggregate into a beaker (6.5) and cover with approximately 300 ml of water (5.2) at room temperature. 8.2.5 Immediately assess the surface coated with the film of binder and grade it according to the scheme indicated in Clause 9. 8.3 Water effect on binder adhesion 8.3.1 Gen

40、eral This procedure shall be used, with reference aggregate(s), to check conformity to the intrinsic “adhesivity” requirement specified in EN 13808. The reference aggregate(s) is (are) then washed with water (5.2) and dried in the ventilated oven (6.10) at (110 5) C for about 2 h. It may also be use

41、d to check water effect on binder adhesion for a specific emulsion/aggregate combination used on a specific job site. The aggregate shall then be used in its job site conditions (5.1). 8.3.2 Weigh (200 5) g of aggregate (5.1) into a dish (6.3) and an amount of emulsion corresponding to (10 1) g of b

42、ituminous binder into another dish (6.3). 8.3.3 Pour the aggregate into the emulsion and thoroughly mix by means of a spatula (6.2). 8.3.4 If full coating (100 % of coverage) is not achieved, restart the procedure as from 8.3.1 by increasing the amount of residual bitumen to (20 1) g. The amount of

43、residual bitumen actually used shall be mentioned in the test report (Clause 11 f). 8.3.5 Spread the mixture on a watch-glass (6.6) and place it in the ventilated oven (6.10) at (60 3) C for (24 1) h. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 18/07/2011 06:53, Uncontrolled Copy, (c) BSI

44、BS EN 13614:2011EN 13614:2011 (E) 7 8.3.6 Transfer the mixture in a beaker (6.5), pour approximately 300 ml of water (5.2), heated to (60 3) C onto the mixture and cover with a watch-glass (6.6). Place the beaker in the ventilated oven (6.10), at (60 3) C for (20 4) h. 8.3.7 Assess the surface coate

45、d with the film of binder and grade it according to the scheme indicated in Clause 9. 9 Expression of results The surface coated with the film of binder shall be graded according to the following scheme: 100: all the surface is coated; 90: more than approximately 90 % of the surface is coated; 75: a

46、pproximately 75 % to 90 % of the surface is coated; 50: approximately 50 % to 75 % of the surface is coated; 50: less than approximately 50 % of the surface is coated; 0: the binder is separate from the aggregates, except for some faint marks. The simple coloration of the aggregate surface by adsorb

47、ed light binder fractions shall not qualify this surface as a coated surface. NOTE 1 A guidance for the grading of the surface covered with binder is given, in the form of indicative sketches, in Annex A. NOTE 2 If necessary, to facilitate the assessment, it should be compared with an untreated and

48、immersed aggregate. 10 Precision The method is qualitative and it is not possible to quantify the precision. However, tests carried out by the same operator have shown that the same result is generally achieved for any given bitumen emulsion. 11 Test report The test report shall contain at least the

49、 following information: a) reference to this European Standard; b) type and complete identification of the emulsion sample under test; c) type and complete identification (reference aggregate or other aggregate) of the aggregate and fraction used (either 6/10 mm or 8/11 mm); d) test used : immediate adhesivity or water effect on binder adhesion; e) result of the test (see Clause 9); f) in case of a test performed according to 8.2, the correspond