BS EN 611-2-1997 Tin and tin alloys - Pewter and pewterware - Pewterware《锡和锡合金 锡铅合金和锡铅合金器皿 第2部分 锡铅合金器皿》.pdf

《BS EN 611-2-1997 Tin and tin alloys - Pewter and pewterware - Pewterware《锡和锡合金 锡铅合金和锡铅合金器皿 第2部分 锡铅合金器皿》.pdf》由会员分享，可在线阅读，更多相关《BS EN 611-2-1997 Tin and tin alloys - Pewter and pewterware - Pewterware《锡和锡合金 锡铅合金和锡铅合金器皿 第2部分 锡铅合金器皿》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS EN 611-2 : 1997 The Eu

2、ropean Standard EN 611-2 : 1996 has the status of a British Standard ICS 77.120.60 ; 77.140.90 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Tin and tin alloys Pewter and pewterware Part 2. PewterwareThis British Standard, having been prepared under the direction of the Engi

3、neering Sector Board, was published under the authority of the Standards Board and comes into effect on 15 January 1997 BSI 1997 The following BSI references relate to the work on this standard: Committee reference NFE/27 Draft for comment 93/312327 DC ISBN 0 580 26261 8 BS EN 611-2 : 1997 Amendment

4、s issued since publication Amd. No. Date Text affected Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee NFE/27, Tin and tin alloys, upon which the following bodies were represented: Association of British Pewter Craftsmen

5、British Iron and Steel Producers Association Federation of the Electronics Industry ITRI Ltd. London Metal Exchange Metal Packaging Manufacturers Association Solder Makers AssociationBS EN 611-2 : 1997 BSI 1997 i Contents Page Committees responsible Inside front cover National foreword ii Foreword 2

6、 Text of EN 611-2 3ii BSI 1997 BS EN 611-2 : 1997 Foreword This British Standard has been prepared by Technical Committee NFE/27 and is the English language version of EN 611-2 : 1996, Tin and tin alloys Pewter and pewterware Part 2: Pewterware, published by the European Committee for Standardizatio

7、n (CEN). BS EN 611 : Part 2 : 1996, together with BS EN 611 : Part 1 : 1995, supersedes BS 5140 : 1974, which is withdrawn. Cross-references Publication referred to Corresponding British Standard EN 610 : 1995 BS EN 610 : 1996 Tin and tin alloys Ingot tin EN 611-1 : 1995 BS EN 611 Tin and tin alloys

8、 Pewter and pewterware Part 1 : 1995 Pewter EN 29453 : 1993 BS EN 29453 : 1994 Soft solder alloys Chemical compositions and forms Compliance with a British Standard does not of itself confer immunity from legal obligations.CEN European Committee for Standardization Comite Europe en de Normalisation

9、Europa isches Komitee fu r Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1996 Copyright reserved to CEN members Ref. No. EN 611-2 : 1996 E EUROPEAN STANDARD EN 611-2 NORME EUROPE ENNE EUROPA ISCHE NORM May 1996 ICS 77.120.60; 77.140.90 Descriptors: Metal products, tin, tin alloys,

10、 specifications, manufacturing, brazed and soldered joints, sampling, chemical analysis, components, chemical composition, food-container contact, marking English version Tin and tin alloys Pewter and pewterware Part 2 : Pewterware E tain et alliages detain E tain pour la fabrication dobjets en e ta

11、in et objets en e tain Partie 2: Objets en e tain Zinn und Zinnlegierungen Zinnlegierungen und Zinngera t Teil 2: Zinngera t This European Standard was approved by CEN on 1996-04-12. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving t

12、his European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exists in three official versions

13、(English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Denma

14、rk, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom.Page 2 EN 611-2 : 1996 BSI 1997 Foreword This European Standard has been prepared by CEN/TC 220, Tin and tin alloys, the secretariat of which is hel

15、d by BSI. This European Standard shall be given the status of a national standard, whether by publication of an identical text or by endorsement, at the latest by November 1996, and conflicting standards shall be withdrawn at the latest by November 1996. This standards consists of two Parts, of whic

16、h Part 2 specifies the requirements for pewterware. Part 1 gives the requirements for pewter alloys for use in the production of the pewterware in Part 2. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this Eu

17、ropean Standard: Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. Contents Page Foreword 2 1 Scope 3 2 Normative references 3 3 Materials of manufacture 3 4 Requirements

18、 3 5 Sampling and analysis 3 6 Marking 4 Annexes A (normative) Solders in EN 29453 referred to in 3.2 5Page 3 EN 611-2 : 1996 BSI 1997 1) In course of preparation. 1 Scope This Part of EN 611 specifies the requirements for the fabrication, sampling, analysis and marking of pewterware. It does not co

19、ver articles manufactured from materials other than pewter which have been coated or clad with pewter. NOTE. The requirements for pewter alloys are specified in EN 611-1. 2 Normative references This European Standard incorporates by dated or undated reference, provisions from other publications. The

20、se normative references are cited at the appropriate places in the text and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this Part of EN 611 only when incorporated in it by amendment or revision. For undated

21、references the latest edition of the publication referred to applies. EN 610 Tin and tin alloys Ingot tin EN 611-1 : 1995 Tin and tin alloys Pewter and pewterware Part 1: Pewter EN 29453 Soft solder alloys Chemical compositions and forms (ISO 9453 : 1990) 3 Materials of manufacture 3.1 Pewterware Th

22、e pewter part(s) of the pewterware can be fabricated from one or more pieces of pewter, each of which shall be an alloy conforming to EN 611-1. Materials used to simulate pewter alloys in the article, such as lead, zinc, aluminium or their alloys, shall not be used. Materials which do not simulate p

23、ewter alloys may be associated with the pewter in the article of pewterware for functional, decorative and/or structural purposes. NOTE. The finished pewterware may be surface treated, for example by painting or by patination. 3.2 Soldered joints For those cases where the soldered joint may reasonab

24、ly be expected to come into contact with foodstuffs, the solder used for joining the component parts of the pewterware shall contain not more than 0,25 % lead and 0,05 % cadmium. Examples of solders which meet this requirement are as follows: a) one of the alloys numbered 1 to 6 in table 1 of EN 611

25、-1 : 1995; or b) alloy 21 in EN 29453 (see table A.1); or c) tin complying with any of the grades specified in EN 610. NOTE. It is recommended that soldered joints which can reasonably be expected not to come into contact with foodstuffs should be made using solder which complies either with a), b)

26、or c) of this subclause, or with alloy 11 or alloy 12 in EN 29453 (see table A.1). 4 Requirements 4.1 Pewterware When sampled and analysed in accordance with a) of clause 5, the composition of each piece of pewter in the pewterware article (see 3.1) shall be found to conform to one of the alloys in

27、EN 611-1. 4.2 Soldered joints for contact with foodstuffs When sampled and analysed in accordance with b) of clause 5, the composition of the joint region of those joints which may reasonably be expected to come into contact with foodstuffs shall contain not more than 0,25 % lead (Pb) and 0,05 % cad

28、mium (Cd). 5 Sampling and analysis When analysis is required to be carried out to verify compliance of the pewterware article with this standard, the procedures given in a) and b) of this clause shall be followed. a) Sampling and analysis of the pewter component(s) of the pewterware article All surf

29、ace coatings on the pewter components to be sampled shall be removed before sampling. Analysis samples shall be taken, by drilling or cutting, to represent each pewter component part of the article. These samples shall be taken from zones furthest from any soldered joints. For routine control purpos

30、es each of the analysis samples so obtained shall be analysed by the use of recognized chemical, or instrumental, analytical procedures. In cases of dispute concerning the chemical composition of the pewterware, until the publication of European Standards 1) for the analysis of pewter, the methods o

31、f analysis to be used shall be subject to agreement between the disputing parties and any independent arbitrator. b) Sampling and analysis of soldered joints The joint shall be cut from the pewterware article. The sample for analysis shall be a length of the joint, taken so as to include not more th

32、an 2 mm of the pewter on each side of the joint. The mass of the sample taken for analysis shall be at least 0,1 g. Analysis shall be carried out on this sample to determine the lead and cadmium content (see 4.2). NOTE. It is not normally possible to determine the actual composition of the solder us

33、ed for the joint in the article. However, if one of the solders specified in 3.2 for joints in contact with foodstuffs has been used, then the composition of the sample of the joint will be found to contain less than 0,25 % Pb and 0,05 % Cd.Page 4 EN 611-2 : 1996 BSI 1997 6 Marking As a minimum requ

34、irement, each article of pewterware shall be permanently marked with: the name or mark of the producer and/or distributor; and the word PEWTER (or corresponding translation, for instance ETAIN in French, ZINN in German, etc.) In addition, the pewterware article or if this is not practicable, its lab

35、el or associated packaging shall be marked with the number of this Part of this European Standard (i.e. EN 611-2).Page 5 EN 611-2 : 1996 BSI 1997 Annex A (normative) Solders in EN 29453 referred to in 3.2 Table A.1 gives the chemical composition requirements for solders Nos 21, 11 and 12 referred to

36、 in 3.2 of this Part of EN 611. NOTE. The details have been extracted from EN 29453. BSI 1997 Page 6 EN 611-2 : 1996 Table A.1. Chemical compositions of EN 29453 solders Alloy number Alloy designation Melting, or solidus/liquidus temperature C Chemical composition %( m / m ) Element Sn Pb Sb Cd Zn A

37、1 Bi As Fe Cu Total excluding Sb, Bi, Cu 11 S-Sn63Pb37Sb 183 min. 62,5 Remainder 0,12 max. 63,5 0,50 0,002 0,001 0,001 0,10 0,03 0,02 0,05 0,08 12 S-Sn60Pb40Sb 183-190 min. 59,5 Remainder 0,12 max. 60,5 0,50 0,002 0,001 0,001 0,10 0,03 0,02 0,05 0,08 21 S-Bi57Sn43 138 min. 42,5 Remainder max. 43,5 0

38、,05 0,10 0,020 0,010 0,010 0,03 0,02 0,10 0,2 1) 2) 1) In alloy 21, the sum of all impurities (i.e. elements other than Bi and Sn) is 0,2 % maximum. 2) In alloy 21, the maximum indium (In) content is 0,05 % and the maximum silver (Ag) content is 0,05 %. BSI 1997 BS EN 611-2 : 1997 List of references

39、 (see national foreword)BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |

40、 | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendm

41、ent or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard wou

42、ld inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions

43、 of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that ha

44、ve been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are als

45、o available which give details on all its products and services. Contact the Information Centre. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of the

46、se and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, De

47、signs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard

48、, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel: 020 8996 7070.