BS 7926-1998 Quantitative micrographic methods to determine the percentage content of non-metallic inclusions in cast steel《铸钢非金属夹杂物百分比含量测定的定量显微照相法》.pdf

《BS 7926-1998 Quantitative micrographic methods to determine the percentage content of non-metallic inclusions in cast steel《铸钢非金属夹杂物百分比含量测定的定量显微照相法》.pdf》由会员分享，可在线阅读，更多相关《BS 7926-1998 Quantitative micrographic methods to determine the percentage content of non-metallic inclusions in cast steel《铸钢非金属夹杂物百分比含量测定的定量显微照相法》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS 7926:1998 ICS 77.080.2

2、0 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Quantitative micrographic methods to determine the percentage content of non-metallic inclusions in cast steelThis British Standard, having been prepared under the direction of the Engineering Sector Board, was published under

3、the authority of the Standards Board and comes into effect on 15 August 1998 BSI 1998 The following BSI references relate to the work on this standard: Committee reference ISE/6 Draft for comment 97/709854 DC ISBN 0 580 29531 1 BS 7926:1998 Amendments issued since publication Amd. No. Date Text affe

4、cted Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee ISE/6, Steel castings, upon which the following bodies were represented: BEAMA Ltd. British Pump Manufacturers Association British Valve and Actuator Manufacturers Asso

5、ciation Castings Development Centre Hopkinsons Limited Institute of British Foundrymen Lloyds Register of Shipping Ministry of Defence Railway Industry AssociationBS 7926:1998 BSI 1998 i Contents Page Committees responsible Inside front cover Foreword ii Introduction 1 1 Scope 1 2 Normative referenc

6、es 1 3 Definitions 1 4 Information and items to be agreed and to be documented 1 5 Sampling 1 6 Preparation of specimens 2 7 Determination of the percentage inclusion content 2 8 Test report 2 Annex A (normative) 3 Figure 1 Test block 2 Table 1 Non-metallic inclusion content ranges from a variety of

7、 melting and refining processes 2ii BSI 1998 BS 7926:1998 Foreword This British Standard has been prepared by Technical Committee ISE/6. Annex A is normative. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for the

8、ir correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 to 3 and a back cover. BSI 1998 1 BS 7926:1998 Introduction Non-metallic inclus

9、ions are present in all metals and alloys and, for the most part, their presence is detrimental. One of the few beneficial effects is the enhancement of machinability. Not all non-metallic inclusions, however, are beneficial to machinability, notably hard oxides such as alumina which are present in

10、cast steels. Non-metallic inclusions can be divided into two discrete categories. Exogenous inclusions which originate from refractory materials used to contain molten metal during casting and/or entrapped slag, and indigenous inclusions which are natural products of melting and refining processes.

11、The oxide composition of both types of non-metallic inclusion can vary widely and is generally very complex. For this reason, this standard concentrates on determining the quantity of non-metallic inclusions contained in cast steel rather than discriminating between the various discrete oxide and/or

12、 sulfide phases that might be present. In most cases it is the quantity and shape of non-metallic inclusions that has the greatest effect on the mechanical properties of the cast steel and also the machinability. 1 Scope This British Standard specifies two micrographic methods for determining the no

13、n-metallic inclusion content of cast steels. Numerical values of the area fraction of non-metallic inclusions present in samples of cast steels is specified. The percentage content ranges of non-metallic inclusions are specified for four melting and refining methods in use in steel foundries through

14、out the UK. In addition to the definitive requirements, this standard also requires the items detailed in clause 4 to be documented. For compliance with this standard, both the definitive requirements and the documented items have to be satisfied. 2 Normative references The following normative docum

15、ents contain provisions which, through reference in this text, constitute provisions of this British Standard. For dated references, subsequent amendments to, or revisions of, any of these publications do not apply. For undated references, the latest edition of the publication referred to applies. B

16、S EN 1559-1, Founding Technical conditions of delivery Part 1: General. BS EN 1559-2, Founding Technical conditions of delivery Part 2: Additional requirements for steel castings. ISO 4990:1986, Steel Castings General technical delivery requirements. 3 Definitions For the purposes of this standard,

17、the following definitions apply. 3.1 inclusions non-metallic material, generally oxides and sulfides, present in cast steels 3.2 area fraction of inclusions surface area covered by inclusions as a percentage of total sample area under examination 4 Information and items to be agreed and to be docume

18、nted The following information to be supplied by the purchaser shall be fully documented. Both the definitive requirements specified throughout the standard and the following documented items shall be satisfied before a claim of compliance with the standard can be made and verified. a) The melting a

19、nd refining processes to be employed, see Table 1. b) The sampling technique and number of specimens to be examined, see clause 5. c) The number of counts per specimen, see clause 5. d) The acceptance category (see Table 1). 5 Sampling At least two specimens, from two different locations in the test

20、 block shall be taken and several counts shall be conducted on each. The degree of sampling and counting shall be agreed between the casting producer and purchaser, see clause 4. Specimens shall be at least 400 mm 2 (20 mm3 20 mm) and shall be cold-sawn from the bottom of a test block, after 20 mm o

21、f metal has been discarded (see Figure 1).2 BSI 1998 BS 7926:1998 Figure 1 Test block 6 Preparation of specimens The specimen shall be cut from the test block, ground and metallographically polished so as to obtain a smooth surface for examination. When polishing specimens, tearing-out or deformatio

22、n of the inclusions present, scratching and contamination of the polished surface shall be avoided. The surface shall be clean and the shape of the inclusions shall not be affected by polishing. 7 Determination of the percentage inclusion content 7.1 General 7.1.1 Determination of the percentage inc

23、lusion content shall be carried out in accordance with A.1 or A.2. NOTE Method 1 involves a simple manual count using a calibrated reference grid which facilitates the calculation of the area fraction of non-metallic inclusions. Method 2 utilizes a computer with appropriate software. 7.1.2 Method 1

24、Following preparation and examination in accordance with A.1 the area fraction of non-metallic inclusions shall conform to Table 1. 7.1.3 Method 2 Following preparation and examination in accordance with A.2 the area fraction of non-metallic inclusions shall conform to Table 1. 8 Test report The tes

25、t report shall contain the following information: a) the number and year of this British Standard, i.e. BS 7926:1998; b) melting and refining process and the cast number; c) location of specimen surface within test block; d) results of the examination; e) report number and date. Table 1 Non-metallic

26、 inclusion content ranges from a variety of melting and refining processes Category Melting and refining processes Area fraction, Area fraction, minimum maximum % 1 Induction or arc melting and argon oxygen decarburizing (AOD) or vacuum arc degassing (VAD) 0.01 0.08 2 Induction or arc melting and ga

27、s stirring in ladle 0.04 0.15 3 Induction melting 0.04 0.24 4 Arc melting 0.07 0.38 Wrought steel (for comparison only) 0.01 0.03BS 7926:1998 BSI 1998 3 Annex A (normative) A.1 Method 1 procedure A.1.1 Prepare the specimen in accordance with clause 6. A.1.2 View using an optical microscope at a magn

28、ification which enables the non-metallic inclusions to be readily identified and at a size approximately half that of the grid point spacing. NOTE In most cases the chosen magnification is3 100. A.1.3 Fix a test grid, 65 mm3 65 mm, with major squares at 10 mm intervals and minor grid markings in 1 m

29、m squares of clear plastic, to the microscope projection screen in a position which corresponds to the centre of the screen area. A.1.4 Choose the selected area randomly and mark with ink on the clear screen each of the non-metallic inclusions. Continue until a direct representation of the 65 mm3 65

30、 mm area has been made and a full replica of the non-metallic inclusion area is marked on the transparent screen. Take at least 10 readings see 4c) for each specimen and calculate the average reading. A.1.5 Remove the transparent screen and count the squares covered by the non-metallic inclusion are

31、a and determine the area fraction using the following equation. Area fraction (%) of inclusions = number of squares covered by inclusions3 100 4 225 NOTE The transparent screen may be retained as a permanent record for re-checking as necessary. A.2 Method 2 procedure A.2.1 Prepare the specimen in ac

32、cordance with clause 6. A.2.2 View the specimen using an optical microscope with lens configuration to facilitate a maximum magnification of3 100. A.2.3 Fit a black and white video camera to the microscope for the purpose of capturing a clear image of the field of view on a video monitor. Connect th

33、e monitor, in turn, to a computer loaded with software capable of point counting. A.2.4 Take at least 10 readings see 4c) for each specimen and calculate the average reading. A.2.5 Calculate the area fraction of inclusion as a percentage (%) from the following equation. Area fraction of inclusions3

34、100 Area of field of view NOTE The computer files may be retained as a permanent record for re-checking as necessary.BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |

35、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international

36、level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would b

37、e grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating

38、 service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders fo

39、r international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and

40、 its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developm

41、ents and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publicat

42、ions of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permiss

43、ion from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel: 020 8996 7070.