BS 2L 169-2002 Ingots (as cast) and castings (solution treated and artificially aged) of aluminium-silicon-magnesium alloy (Si 7 Mg 0 6)《铝-硅-镁合金(Si 7、Mg 0 6)(溶解处理和人工老化的)铸锭和铸件》.pdf

《BS 2L 169-2002 Ingots (as cast) and castings (solution treated and artificially aged) of aluminium-silicon-magnesium alloy (Si 7 Mg 0 6)《铝-硅-镁合金(Si 7、Mg 0 6)(溶解处理和人工老化的)铸锭和铸件》.pdf》由会员分享，可在线阅读，更多相关《BS 2L 169-2002 Ingots (as cast) and castings (solution treated and artificially aged) of aluminium-silicon-magnesium alloy (Si 7 Mg 0 6)《铝-硅-镁合金(Si 7、Mg 0 6)(溶解处理和人工老化的)铸锭和铸件》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS 2L 169:2002 Ingots (as cast) and castings (solution treated and artificially aged) of aluminium- silicon-magnesium alloy (Si 7, Mg 0.6) ICS 49.025.20 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBS 2L 169:2002 This British Standard, havin

2、g been prepared under the direction of the Engineering Sector Policy and Strategy Committee, was published under the authority of the Standards Policy and Strategy Committee on 18 June 2002 BSI 18 June 2002 First published January 1986 Second edition June 2002 The following BSI references relate to

3、the work on this standard: Committee reference ACE/24 Draft for comment 82/79983 DC ISBN 0 580 39805 6 Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee ACE/24, Wrought and cast light alloys for aerospace, upon which the fo

4、llowing bodies were represented: Aluminium Federation Aluminium Stockholders Association Association of Light Alloy Refiners Limited BNF Metals Technology Centre British Forging Industry Association British Industrial Fasteners Federation British Investment Casting Trade Association Institute of Bri

5、tish Foundrymen Light Metal Founders Association Magnesium Industry Council Ministry of Defence Society of British Aerospace Companies Limited Amendments issued since publication Amd. No. Date of issue CommentsBS 2L 169:2002 BSI 18 June 2002 i Contents Page Committees responsible Inside front cover

6、Foreword ii 1S c o p e 1 2 Inspection and testing procedure 1 3 Chemical composition 1 4 Conditions of supply 1 5 Heat treatment 2 6 Mechanical properties of castings 2 Table 1 Chemical composition of ingots and castings 1 Table 2 Tensile properties of separately cast samples 2 Table 3 Tensile prope

7、rties of cut-up and integrally cast test samples 2 Bibliography 3BS 2L 169:2002 ii BSI 18 June 2002 Foreword This British Standard is a new edition of BS L 169:1986 and incorporates technical changes only. It does not reflect a full review or revision of the standard, which will be undertaken in due

8、 course. It has been prepared by Technical Committee ACE/24, Wrought and cast light alloys for aerospace, and supersedes BS L 169:1986, which is withdrawn. This new edition deletes beryllium from the chemical composition of ingots and castings and adjusts the requirements for grain refinement. This

9、publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front

10、 cover, pages i and ii, pages 1 to 3 and a back cover. The BSI copyright notice displayed in this document indicates when the document was last issued.BS 2L 169:2002 BSI 18 June 2002 1 1 Scope This British Standard specifies the inspection and testing procedure, chemical composition, heat treatment

11、and mechanical properties applicable to ingots and castings of aluminium-silicon-magnesium alloy. NOTE 1 The title of the publication referred to in this standard is given on the inside back cover. NOTE 2 The latest revision of an Aerospace Series standard is indicated by a prefix number. 2 Inspecti

12、on and testing procedure The inspection and testing procedure shall be as specified in the relevant sections of the latest edition of BS L 101. 3 Chemical composition 3.1 The chemical composition of ingots and castings shall be as given in Table 1. Table 1 Chemical composition of ingots and castings

13、 3.2 Grain refinement shall be carried out using titanium and/or boron. 3.3 The release documentation for ingots shall include a statement of grain refining elements used, if any. 4 Conditions of supply 4.1 Ingots shall be supplied as cast. 4.2 Castings shall be supplied fully heat treated in accord

14、ance with Clause 5 unless otherwise stated on the order. Element Composition by mass Min. % Max. % Copper 0.10 Magnesium 0.50 0.75 Silicon 6.5 7.5 Iron Ingots Castings 0 . 1 5 0 . 2 0 Manganese 0.10 Nickel 0.05 Zinc 0.10 Lead 0.05 Tin 0.05 Titanium 0.10 0.20 Others each 0.05 Others total 0.15 Alumin

15、ium Remainder NOTE 1 Specific modifying elements may be added in sufficient quantities to provide the necessary casting material quality. NOTE 2 Up to 0.07 % beryllium may be added to the melt by agreement with the purchaser. BS 2L 169:2002 2 BSI 18 June 2002 5 Heat treatment 5.1 The castings and te

16、st samples shall be heat treated together in accordance with a) to d) as follows. a) Solution treat at a temperature of 540 5 C for not less than 10 h. b) Quench in water or in a polymer quenchant at a temperature not greater than 30 C. NOTE The use of a polymer quenchant as an alternative to water

17、should be agreed by the purchaser. c) Artificially age at a temperature in the range 155 C to 165 C for not less than 2 h. The temperature selected shall be maintained within a tolerance of 5 C. d) Cool in air. 5.2 Where a polymer quenchant has been used in 5.1b), the nature of the quenchant shall b

18、e defined on the certificate of conformity for the castings. 6 Mechanical properties of castings 6.1 Tensile tests 6.1.1 The mechanical properties obtained from separately cast test samples, selected and prepared in accordance with the relevant requirements of the latest edition of BS L 101, shall b

19、e not less than those given in Table 2, when heat treated in accordance with Clause 5. Table 2 Tensile properties of separately cast samples 6.1.2 The mechanical properties obtained from cut-up and integrally cast test samples, heat treated in accordance with Clause 5, and selected and prepared in a

20、ccordance with the relevant requirements of the latest edition of BS L 101 shall be not less than those given in Table 3 or shall be as stated on the drawing for the casting or on the Inspection Schedule in accordance with the latest edition of BS L 101. 6.2 Hardness test The hardness of castings, h

21、eat treated in accordance with Clause 5 shall be not less than the following: Table 3 Tensile properties of cut-up and integrally cast test samples Test sample 0.2 % proof stress min. MPa Tensile strength min. MPa Elongation min. % Sand Investment cast Chill cast 240 240 240 290 300 320 3.0 3.5 4.0

22、a) sand and investment cast 80 HB, b) chill cast 85 HB. Casting thickness (t) mm Location of test samples 0.2 % proof stress min. MPa Tensile strength min. MPa Elongation % t 5 Designated locations 250 320 5 Other locations 230 300 3 5 t 20 Designated locations 240 300 3 Other locations 220 270 2 t

23、20 As stated on the drawing for the casting or on the Inspection ScheduleBS 2L 169:2002 BSI 18 June 2002 3 Bibliography Standards publication BS 4L 101, Procedure for inspection, testing and acceptance of aluminium-base and magnesium-base ingots and castings. 1) 1) Use the latest available edition o

24、f BS L 101.BS 2L 169:2002 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. R

25、evisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or

26、 ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400. BSI offers members an individual updating service called PLUS which ensure

27、s that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: ordersbsi-. Standards are also availab

28、le from the BSI website at http:/www.bsi-. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on nat

29、ional, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996 7111. Fax: +44 (0)20 89

30、96 7048. Email: infobsi-. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002. Fax: +44 (0)20 8996 7001. Em

31、ail: membershipbsi-. Information regarding online access to British Standards via British Standards Online can be found at http:/www.bsi- Further information about BSI is available on the BSI website at http:/www.bsi-. Copyright Copyright subsists in all BSI publications. BSI also holds the copyrigh

32、t, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise

33、without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: copyrightbsi-.