1、Designation: F 1913 04Standard Specification forVinyl Sheet Floor Covering Without Backing1This standard is issued under the fixed designation F 1913; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A num

2、ber in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers sheet floor covering having avinyl wear layer without backing. Products also may contain aclear specialty perfo

3、rmance top layer(s).1.2 This type of floor covering is intended for use incommercial and light commercial buildings. General informa-tion and performance characteristics, which determine service-ability and recommended use, are included in this specification.1.3 The values stated in inch-pound units

4、 are to be regardedas the standard. The values given in parentheses are forinformation only.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health pract

5、ices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2F 137 Test Method for Flexibility of Resilient FlooringMaterials With Cylindrical Mandrel ApparatusF 141 Terminology Relating to Resilient Floor CoveringsF 386 Test Method for Thic

6、kness of Resilient FlooringMaterials Having Flat SurfacesF 410 Test Method for Wear Layer Thickness of ResilientFloor Coverings by Optical MeasurementF 925 Test Method for Resistance to Chemicals of ResilientSheet FlooringF 970 Test Method for Static Load LimitF 1514 Test Method for Measuring Heat S

7、tability of Resil-ient Vinyl Flooring by Color ChangeF 1515 Test Method for Measuring Light Stability of Resil-ient Vinyl Flooring by Color ChangeF 1914 Test Method for Short-Term Indentation and Re-sidual Indentation of Resilient Floor Covering2.2 ANSI/ASQC Standard:ANS/ASQC Z1.4 Sampling Procedure

8、s and Tables for In-spection by Attributes33. Terminology3.1 Definitions Terms used in this specification are de-fined in accordance with Terminology F 141.3.2 Definitions of Terms Specific to This Standard:3.2.1 wear layer, nthe portion of a resilient floor coveringthat contains the pattern effect.

9、3.2.1.1 DiscussionThe wear layer thickness and totalthickness of through pattern unbacked sheet vinyl flooring arethe same. A clear specialty performance top layer may be usedto enhance specific properties and to protect the pattern effectand shall be counted as part of the wear layer. The wear laye

10、rdoes not include temporary finishes or maintenance coatings.4. Significance and Use4.1 The information in this specification is for use byspecifiers as a reference when selecting unbacked resilientsheet vinyl flooring for areas within commercial and lightcommercial buildings.5. Classification5.1 Sh

11、eet Vinyl floor covering shall conform to the follow-ing.5.1.1 The binder content of the PVC-pattern portion of thewear layer (vinyl resins, plasticizers, and stabilizers) shall be aminimum of 50 %. A clear specialty performance layer(s) usedas the top layer is not described by binder limits.PVC Bin

12、der ContentMinimum % PVC Wear Layer Description50 % The material shall be a vinyl compound consistingof a blended composition of pigments stabilizedagainst heat and light deterioration. The design,color and pattern extends throughout the thicknessof the wear layer.5.1.1.1 All flooring may have a cle

13、ar specialty performancetop layer(s) with an average minimum total thickness of 0.0004in. The specialty performance top layer(s) may consist of a1This specification is under the jurisdiction of ASTM Committee F06 onResilient Floor Coverings and is the direct responsibility of Subcommittee F06.80on S

14、pecifications.Current edition approved March 1, 2004. Published April 2004. Originallyapproved in 1998. Last previous edition approved in 2002 as F 1913-02.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of AST

15、MStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute, 25 W. 43rd St., 4thFloor, New York, NY 10036.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Unit

16、ed States.single layer or multiple layers, which do not delaminate undernormal use. Top layer(s) thinner than 0.0004 in. may be usedbut cannot be counted as part of the clear specialty perfor-mance top layer.5.1.2 The total thickness is the sum of the PVC wear layerand the clear specialty top layer(

17、s). The total thickness averageminimum is 0.075 in. (1.9 mm).6. Ordering Information6.1 Sheet vinyl floor covering without backing shall beordered according to characteristics important to the purchaserfor the intended use as indicated by Table 1.6.2 Intended Use The following is a partial list prov

18、idinggeneric guidance on typical applications of product use. Forspecific applications, refer to the manufacturers product rec-ommendations.6.2.1 LC (Light Commercial):6.2.1.1 Multi-family DwellingCommon Areas.6.2.1.2 Hotel/Motel Guest Rooms.6.2.2 C (Commercial):6.2.2.1 Educational/Institutional.6.2

19、.2.2 Hospital/Health Care.6.2.2.3 Retail/Mercantile.6.2.2.4 Office6.2.2.5 Hospitality.6.3 The purchaser may wish to specify the following items:6.3.1 Manufacturer,6.3.2 Style name and number,6.3.3 Minimum roll width (see 9.1),6.3.4 Surface texture (see 7.1.3), and6.3.5 Variation in list of chemicals

20、 used to demonstratechemical resistance (see 12.7).7. Material7.1 Wear Layer:7.1.1 The wear layer shall have a vinyl plastic binder andmay include pigments, fillers, extenders, and other ingredients;and shall be stabilized against heat and light deterioration (see12.8 and 12.9).7.1.2 The binder of t

21、he wear layer shall consist of one ormore vinyl resins, platicizers, and stabilizers. Each resin shallbe polyvinyl chloride or a copolymer of vinyl chloride not lessthan 85 % of which is vinyl chloride. The vinyl resin(s) shall benot less than 60 % by weight of the binder.7.1.3 The composition shall

22、 be uniform and extend through-out the full thickness of the pattern portion of the wear layer.7.2 Specialty Performance Top LayerA clear specialtyperformance top layer(s) of a product can be a PVC or nonPVC layer(s), which may constitute part of the total thicknessup to a maximum 0.005 in. and is n

23、ot removable by normalmaintenance procedures.8. Physical Requirements8.1 Sheet vinyl floor covering shall meet the requirements inTable 2.9. Dimensions9.1 Common roll widths are 49-in. (1.25-m), 59-in. (1.5-m),72-in. (1.83-m), and 78-in. (2-m) widths (minus 0 in.). Otherwidths may be available.9.2 T

24、he floor covering shall be furnished in a minimumaverage overall thickness of 0.075 in. (1.9 mm).10. Workmanship, Finish and Appearance10.1 Materials furnished under this specification shall be anacceptable match to an approved sample(s) in pattern, color,and surface appearance. The product shall be

25、 free of defects,which would adversely affect performance or appearance.11. Sampling11.1 Sampling for testing physical characteristics listed inTable 2 shall be done in accordance with the provisions setforth in ANSI/ASQC Z1.4. The inspection level shall bespecial inspection level S-1 as noted in Ta

26、ble 1 and theacceptable quality level (AQL) shall be 6.5 defects/100 units asnoted in Table II-A or as otherwise specified in 11.3. The lotsize shall be expressed in units. A unit represents a single,manufactured, inventoried, finished roll.11.2 Samples shall be obtained in the required length fromt

27、he outside end of the roll and shall encompass the total widthof the material.11.3 Sampling for testing physical characteristics listed inTable 2 shall be agreed upon by the purchaser and themanufacturer as part of the procurement documents.12. Test Methods12.1 Wear Layer Binder ContentThe wear laye

28、r bindercontent shall be determined by statement of formula (manu-facturers certificate of compliance).12.2 Clear Specialty Performance Top Layer ThicknessThe specialty performance top layer thickness shall be deter-mined in accordance with Test Method F 410 except thethickness of the sample shall b

29、e the average of the measure-ments on three specimens taken 12 in. (305 mm) in from eachedge and the center of the sample.12.3 Overall ThicknessThe overall thickness shall bedetermined in accordance with Test Method F 386 except thatthe presser foot shall exert a total force of 1 6 0.1 oz (28.3 62.8

30、 g) on the specimen. The thickness of the sample should bethe average of the measurements on three specimens taken 12in. (305 mm) in from each edge and the center of the sample.12.4 Residual IndentationResidual indentation shall bedetermined in accordance with Test Method F 1914 as follows:1 h after

31、 75-lb load/0.250 in. diameter flat tip/15 min (34-kgload/6.4 mm diameter flat tip/15 min.).12.5 Static Load ResistanceThe static load resistanceshall be determined in accordance with Test Method F 970using an applied load of 250 lb (113.4 kg).12.6 Flexibility The flexibility shall be determined ina

32、ccordance with Test Method F 137. The flexibility shall besuch that the wear surface will not crack or break when bentface out and face in over a 112 in. (3.81 cm) diameter mandrel.12.7 Resistance to ChemicalsThe chemical resistance ofsheet flooring shall be determined in accordance with TestMethod

33、F 925 when exposed to the following chemicals.TABLE 1 Total ThicknessAverage Minimum in. (mm) Intended Use0.075 (1.9) LC/CF191304212.7.1 White Vinegar, (5 % acetic acid).12.7.2 Rubbing Alcohol, (70 % isopropyl alcohol).12.7.3 White Mineral Oil, (medicinal grade).12.7.4 Sodium Hydroxide Solution, 5 %

34、 NaOH.12.7.5 Hydrochloric Acid Solution, 5 % HCl.12.7.6 Sulfuric Acid Solution,5%H2SO4.12.7.7 Household Ammonia Solution,5%NH4OH.12.7.8 Household Bleach Solution, 5.25 % NaOCl.12.7.9 Olive Oil, light.12.7.10 Kerosene (Kl).12.7.11 Unleaded Gasoline, regular grade.NOTE 1These chemicals are representat

35、ive of those likely to be foundin domestic, commercial, and institutional use. Many proprietary com-pounds contain one or more of these chemicals. Should the flooring for anunusual application need to be resistant to a specific chemical, thisfollowing requirement should become part of the procuremen

36、t document.12.8 Resistance to HeatThe resistance of the sheet vinylfloor covering to color change from exposure to elevatedtemperature, 158F (70C), over a specified time, seven days,shall be determined in accordance with Test Method F 1514.12.9 Resistance to LightThe resistance of sheet vinylfloor c

37、overing to color change from exposure to light, simu-lated by a properly fitted xenon-arc radiant energy source, overtime, 300 h, shall be determined in accordance with TestMethod F 1515.13. Inspection13.1 Inspection of the sheet vinyl floor covering for defectsthat would adversely affect performanc

38、e (see 10.1) shall bedone in accordance with the provisions set forth in ANS/ASQCZ1.4. The inspection level shall be Level I as noted in Table 1and the acceptable quality level (AQL) of 6.5 defects/100 unitsas noted in Table IIA or as otherwise specified in 13.2. The lotsize shall be expressed in un

39、its, one of which is represented asa single, manufactured, inventoried, finished roll.13.2 For alternate AQL, the inspection of sheet vinyl floorcovering for defects shall be done as agreed upon by thepurchaser and the manufacturer, as part of the procurementdocuments.14. Certification14.1 When spec

40、ified in the purchase order or contract, amanufacturers certification shall be furnished to the purchaserthat the material was manufactured, sampled, tested, inspected,and packaged in accordance with this specification and hasbeen found to meet the requirements.15. Product Marking15.1 Unless otherwi

41、se specified in the purchase order orcontract, shipping containers shall be marked with the name ofthe material, the size, the thickness (when the material isavailable in more than one thickness), the pattern number, thequantity contained therein and the name of the manufacturer.15.2 When product sa

42、mple sets, sample set cover cards,marketing and technical literature reference this specification,the complete product classification relative to this specificationshall be included.16. Packaging and Package Marking16.1 The sheet vinyl floor covering shall be packaged andmarked in accordance with no

43、rmal commercial practice andpacked to ensure acceptance by common carrier and to provideproduct protection against damage during normal shipping,handling, and storage. Rolls shall be stored upright (on end) atall times prior to installation.17. Keywords17.1 resilient; sheet; vinyl; without backingTA

44、BLE 2 Testing Physical CharacteristicsCharacteristics Requirement Test Method SectionComposition 50 % minimum binder content Manufacturers certificate of compliance 12.1Clear specialty top layer 0.0004 in. (0.01 mm) min Test Method F 410 12.20.005 in. (0.137 mm) maxTotal thickness min 0.075 in. (1.9

45、 mm) Test Method F 386 12.3Residual indentation #0.007 in. (0.18 mm) Test Method F 1914 12.4Static load resistance #0.005 in. (0.13 mm) at 250 lb (113.4 kg) Test Method F 970 12.5Flexibility Mandrel diameter 1 1/2 in. (38 mm) no crack/breakTest Method F 137 12.6Resistance to chemicals No more than a

46、 slight change in surface dulling,surface attack, or stainingTest Method F 925 12.7Resistance to heat DE #8 Test Method F 1514 12.8Resistance to light DE #8 Test Method F 1515 12.9F1913043APPENDIX(Nonmandatory Information)X1. ADDITIONAL INFORMATIONX1.1 The following sources can be consulted for addi

47、tionalinformation.X1.1.1 ASTM Standards:F 693 Practice for Sealing Seams of Resilient SheetFlooring Products by Use of Liquid Seam Sealers2F 710 Practice for Preparing Concrete Floors and OtherMonolithic Floors to Receive Resilient Flooring2F 1482 Guide to Wood Underlayment Products Availablefor Use

48、 Under Resilient Flooring2F 1516 Practice for Sealing Seams of Resilient FlooringProducts by the Heat-Weld Method (When Recommended)2X1.1.2 Other Sources:Recommended Work Practices for the Removal of ResilientFloor Coverings4ASTM International takes no position respecting the validity of any patent

49、rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Internation