ASTM C724-1991(2010) Standard Test Method for Acid Resistance of Ceramic Decorations on Architectural-Type Glass《建筑装饰玻璃上陶瓷装璜耐酸性的标准试验方法》.pdf

《ASTM C724-1991(2010) Standard Test Method for Acid Resistance of Ceramic Decorations on Architectural-Type Glass《建筑装饰玻璃上陶瓷装璜耐酸性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM C724-1991(2010) Standard Test Method for Acid Resistance of Ceramic Decorations on Architectural-Type Glass《建筑装饰玻璃上陶瓷装璜耐酸性的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C724 91 (Reapproved 2010)Standard Test Method forAcid Resistance of Ceramic Decorations on Architectural-Type Glass1This standard is issued under the fixed designation C724; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revisi

2、on, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers qualitative determination of theacid resistance of the ceramic decoration on a

3、rchitectural glass.1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standar

4、d to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Terminology2.1 Definitions:2.1.1 architectural glassglass used in the building indus-try.3. Summary of Test Method3.1 This test method qualitatively determines, by visua

5、linspection, the degree of attack upon a ceramic decoration bya 10 % citric acid solution and a nominal 3.7 % hydrochloricacid solution.4. Significance and Use4.1 This test method evaluates the quality and serviceabilityof a ceramic decoration on architectural type glass. The degreeof attack is dete

6、rmined using an acidic solution both quantita-tively and qualitatively.4.2 This test method provides a convenient control testduring the manufacture of the ware.4.3 This test method is suitable for specification acceptance.5. Reagent5.1 Purity of ReagentsReagent grade chemicals shall beused in all t

7、ests. Unless otherwise indicated, it is intended thatall reagents shall conform to the specifications of the Commit-tee on Analytical Reagents of the American Chemical Society,where such specifications are available.2Other grades may beused, provided it is first ascertained that the reagent is ofsuf

8、ficiently high purity to permit its use without lessening theaccuracy of the determination.5.2 Citric Acid Solution (1 + 9)Add 10 parts by mass ofreagent grade citric acid to 90 parts by mass of distilled water.Prepare fresh for each determination.5.3 Hydrochloric Acid Solution (1 + 9)Add 10 parts b

9、ymass of reagent grade concentrated hydrochloric acid (HCl)(36 to 38 %) to 90 parts by mass of distilled water.6. Procedure6.1 Place four drops of each acid solution on a separatelocation on the surface of the ceramic decoration of thearchitectural glass to be tested. Cover each spot with awatchglas

10、s to retard evaporation and prevent contamination.Acid should remain on the surface of the test specimen for 15min at 20 62C.6.2 After 15 min of exposure, wash the acid solutions(1 + 9) from the test specimen with tap water and allow it to airdry.7. Report7.1 Report the following information:7.1.1 T

11、he degree of attack by visual observation by gradingas follows:Grade 1No attack apparentGrade 2Appearance of iridescence or visible stain on theexposed surface when viewed at a 45 angle but not apparentat angles less than 30Grade 3A definite stain which does not blur reflectedimages and is visible a

12、t angles less than 30Grade 4Definite stain with a gross color change orstrongly iridescent surface visible at angles less than 30 andwhich may blur reflected images1This test method is under the jurisdiction of ASTM Committee C14 on Glassand Glass Products and is the direct responsibility of Subcomm

13、ittee C14.10 onGlass Decoration.Current edition approved March 1, 2010. Published March 2010. Originallyapproved in 1974. Last previous edition approved in 2005 as C724 91(2005). DOI:10.1520/C0724-91R10.2Reagent Chemicals, American Chemical Society Specifications , AmericanChemical Society, Washingt

14、on, DC. For suggestions on the testing of reagents notlisted by the American Chemical Society, see Analar Standards for LaboratoryChemicals, BDH Ltd., Poole, Dorset, U.K., and the United States Pharmacopeiaand National Formulary, U.S. Pharmacopeial Convention, Inc. (USPC), Rockville,MD.1Copyright AS

15、TM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Grade 5Surface dull or matte with chalking possibleGrade 6Significant removal of enamel with pinholingevidentGrade 7Complete removal of enamel in exposed area8. Precision and Bias8.1 PrecisionIn rou

16、nd-robin testing and evaluation, thebetween-laboratory precision for citric-acid resistance determi-nation was found to be 61 grade (95 % students t). Thewithin-laboratory precision for citric-acid resistance determi-nation is estimated at no greater than 61 grade.8.2 BiasNo justifiable statement ca

17、n be made about thebias of this test method, because the subjective nature ofgrading may vary considerably among operators.9. Keywords9.1 acid resistance; architectural decorations; ceramicenamels; chemical durabilityASTM International takes no position respecting the validity of any patent rights a

18、sserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time

19、 by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will re

20、ceive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM In

21、ternational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C724 91 (2010)2