1、Designation: A283/A283M 03 (Reapproved 2007) A283/A283M 12Standard Specification forLow and Intermediate Tensile Strength Carbon Steel Plates1This standard is issued under the fixed designation A283/A283M; the number immediately following the designation indicates the yearof original adoption or, in

2、 the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 T

3、his specification2 covers four grades (A, B, C, two grades (C and D) of carbon steel plates of structural quality for generalapplication.1.2 When the steel is to be welded, a welding procedure suitable for the grade of steel and intended use or service is to beutilized. See Appendix X3 of Specificat

4、ion A6/A6M for information on weldability.1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI unitsare shown in brackets. The values stated in each system are not exactly equivalents; therefore, each system is to be usedinde

5、pendently of the other, without combining values in any way.1.4 For plate produced from coil and furnished without heat treatment or with stress relieving only, the additional requirements,including additional testing requirements and the reporting of additional test results, of Specification A6/A6M

6、 apply.1.5 This specification contains notes or footnotes, or both, that provide explanatory material. Such notes and footnotes,excluding those in tables and figures, do not contain any mandatory requirements.2. Referenced Documents2.1 ASTM Standards:3A6/A6M Specification for General Requirements fo

7、r Rolled Structural Steel Bars, Plates, Shapes, and Sheet Piling3. General Requirements for Delivery3.1 Plates furnished under this specification shall con-form to the requirements of the current edition of Specification A6/A6M,for the specific date ordered, unless a conflict exists, in which case t

8、his specification shall prevail.3.2 Coils are excluded from qualification to this specification until they are processed into finished plates. Plates produced fromcoil means plates that have been cut to individual lengths from a coil. The processor directly controls, or is responsible for, theoperat

9、ions involved in the processing of a coil into finished plates. Such operations include decoiling, leveling, cutting to length,testing, inspection, conditioning, heat treatment (if applicable), packaging, marking, loading for shipment, and certification.NOTE 1For plates produced from coil and furnis

10、hed without heat treatment or with stress relieving only, two test results are to be reported for eachqualifying coil. Additional requirements regarding plate produced from coil are described in Specification A6/A6M.4. Process4.1 The steel shall be made by one or more of the following processes: ope

11、n-hearth, basic-oxygen, or electric-furnace.5. Chemical Requirements5.1 The heat analysis shall conform to the requirements prescribed in Table 1.5.2 The steel shall conform on product analysis to the requirements prescribed in Table 1, subject to the product analysistolerances in Specification A6/A

12、6M.1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.02on Structural Steel for Bridges, Buildings, Rolling Stock and Ships.Current edition approved Sept. 1, 2007Aug. 1, 2012. Publishe

13、d September 2007September 2012. Originally approved in 1946. Last previous edition approved in 20032007as A283/A283M 03.A283/A283M 03 (2007). DOI: 10.1520/A0283_A0283M-03R07.10.1520/A0283_A0283M-12.2 For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-283/SA 283M in S

14、ection II of that Code.3 For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standa

15、rd and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases

16、only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Tensile Require

17、mentsMechanical Properties6.1 Material as Tensile Properties:represented by the test specimens shall conform to the requirements as to tensile propertiesprescribed in Table 2.6.1.1 Material as represented by the test specimens shall conform to the requirements as to tensile properties prescribed in

18、Table2.7. Keywords7.1 carbon steel; plates; structural qualitySUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the order or contract. Standardizedsupplementary requirements for use at the option of the purchaser are listed in Specification A6/A6M.Those that ar

19、e considered suitable for use with this specification are listed by title:S2. Product Analysis,Analysis.S3. Simulated Post-Weld Heat Treatment of Mechanical Test Coupons,Coupons.S5. Charpy V-Notch Impact Test,Test.TABLE 1 Chemical RequirementsElements Heat Analysis,Grade A Grade B Grade C GradeCarbo

20、n, max 0.14 0.17 0.24 0.27Carbon, max 0.24 0.27Manganese, max 0.90 0.90 0.90 0.90Manganese, max 0.90 0.90Phosphorus, max 0.035 0.035 0.035 0.035Phosphorus, max 0.035 0.035Sulfur, max 0.04 0.04 0.04 0.04Sulfur, max 0.04 0.04SiliconPlates 112 in. 40 mm and under, max 0.40 0.40 0.40 0.40Plates 112 in.

21、40 mm and under, max 0.40 0.40Plates over 112 in. 40 mm 0.150.40 0.150.40 0.150.400.150.40Plates over 112 in. 40 mm 0.150.40 0.150.40Copper, min % when copper is specified 0.20 0.20 0.20 0.20Copper, min % when copper is specified 0.20 0.20TABLE 2 Tensile RequirementsAGrade A Grade B Grade CTensile s

22、trength, ksi MPa 4560 310415 5065 345450 5575 380515Yield point, min, ksi MPa 24 165 27 185 30 205Elongation in 8 in. 200 mm, min, %B 27 25 22Elongation in 2 in. 50 mm, min, %B 30 28 25TABLE 2 Tensile RequirementsAGrade C Grade DTensile strength, ksi MPa 5575 380515 6080 415550Yield point, min, ksi

23、MPa 30 205 33 230Elongation in 8 in. 200 mm, min, %B 22 20Elongation in 2 in. 50 mm, min, %B 25 23A See Specimen Orientation under the Tension Tests section of Specification A6/A6MB For plates wider than 24 in. 600 mm, the elongation requirement is reduced two percentage points. See elongation requi

24、rement adjustments in the Tension Tests sectionof Specification A6/A6M.A283/A283M 122S6. Drop Weight Test (for Material 0.625 in. 16 mm and over in Thickness),Thickness).S8. Ultrasonic Examination, andExamination.S15. Reduction of Area.S97. Limitation on Rimmed or Capped Steel:S97.1 The steel shall

25、be other than rimmed or capped.SUMMARY OF CHANGESCommittee A01 has identified the location of the following selected changes to this standard since the lastissue (A283/A283MA283/A283M 03 (2007)-00) that may impact the use of this standard. (Approved Aug. 1,2012.)(1) 1.4, 3.1, 3.1.1 (renumbered as 3.

26、2), and Note 1 have been revised to be consistent with the terminology and requirements ofSpecification A6/A6M.(1) Grades A and B removed from 1.1, Table 1 and Table 2.(2) Revised subject heading and numbering in Section 6.(3) Added Section 7.ASTM International takes no position respecting the valid

27、ity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subje

28、ct to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquart

29、ers. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard

30、 is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A283/A283M 123