ANSI ASTM F2817-2013 Standard Specification for Poly (Vinyl Chloride) (PVC) Gas Pressure Pipe and Fittings For Maintenance or Repair《聚氯乙烯(PVC)气体压力管道及配件维护或维修规范》.pdf

《ANSI ASTM F2817-2013 Standard Specification for Poly (Vinyl Chloride) (PVC) Gas Pressure Pipe and Fittings For Maintenance or Repair《聚氯乙烯(PVC)气体压力管道及配件维护或维修规范》.pdf》由会员分享，可在线阅读，更多相关《ANSI ASTM F2817-2013 Standard Specification for Poly (Vinyl Chloride) (PVC) Gas Pressure Pipe and Fittings For Maintenance or Repair《聚氯乙烯(PVC)气体压力管道及配件维护或维修规范》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F2817 13 An American National StandardStandard Specification forPoly (Vinyl Chloride) (PVC) Gas Pressure Pipe and FittingsFor Maintenance or Repair1This standard is issued under the fixed designation F2817; the number immediately following the designation indicates the year oforiginal a

2、doption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers requirements for PVC pipe andtubing for us

3、e only to maintain or repair existing PVC gaspiping. This specification covers requirements for fittings foruse to maintain or repair existing PVC gas piping.1.1.1 In-plant quality control programs are specified inAnnex A1.1.2 The text of this specification references notes and,footnotes, and append

4、ixes which provide explanatory material.These notes and footnotes (excluding those in tables andfigures) shall not be considered as requirements of the speci-fication.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions

5、to SI units that are provided for information onlyand are not considered standard.1.4 The following is an index of the annexes in thisspecification:Annex SubjectAnnex A1 In-Plant Quality Control for PVCmaterialsup to 6 in.1.5 This standard does not purport to address all of thesafety concerns, if an

6、y, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D543 Practices for Evaluating the Resistance of Pl

7、astics toChemical ReagentsD618 Practice for Conditioning Plastics for TestingD638 Test Method for Tensile Properties of PlasticsD1598 Test Method for Time-to-Failure of Plastic PipeUnder Constant Internal PressureD1599 Test Method for Resistance to Short-Time HydraulicPressure of Plastic Pipe, Tubin

8、g, and FittingsD1600 Terminology forAbbreviated Terms Relating to Plas-ticsD1784 Specification for Rigid Poly(Vinyl Chloride) (PVC)Compounds and Chlorinated Poly(Vinyl Chloride)(CPVC) CompoundsD1898 Practice for Sampling of Plastics (Withdrawn 1998)3D2122 Test Method for Determining Dimensions of Th

9、er-moplastic Pipe and FittingsD2152 Test Method for Adequacy of Fusion of ExtrudedPoly(Vinyl Chloride) (PVC) Pipe and Molded Fittings byAcetone ImmersionD2290 Test Method for Apparent Hoop Tensile Strength ofPlastic or Reinforced Plastic PipeD2412 Test Method for Determination of External LoadingCha

10、racteristics of Plastic Pipe by Parallel-Plate LoadingD2444 Test Method for Determination of the Impact Resis-tance of Thermoplastic Pipe and Fittings by Means of aTup (Falling Weight)D2466 Specification for Poly(Vinyl Chloride) (PVC) PlasticPipe Fittings, Schedule 40D2564 Specification for Solvent

11、Cements for Poly(VinylChloride) (PVC) Plastic Piping SystemsD2837 Test Method for Obtaining Hydrostatic Design Basisfor Thermoplastic Pipe Materials or Pressure Design Basisfor Thermoplastic Pipe ProductsF412 Terminology Relating to Plastic Piping SystemsF402 Practice for Safe Handling of Solvent Ce

12、ments,Primers, and Cleaners Used for Joining ThermoplasticPipe and Fittings2.2 Plastic Pipe Institute:4PPI TR-4 Hydrostatic Design Bases and Maximum Recom-mended Hydrostatic Design Stresses for ThermoplasticPiping Materials1This specification is under the jurisdiction of ASTM Committee F17 on Plasti

13、cPiping Systems and is the direct responsibility of Subcommittee F17.60 on Gas.Current edition approved Aug. 1, 2013. Published August 2013. Originallyapproved in 2010. Last previous edition approved in 2010 as F281710. DOI:10.1520/F281713.2For referenced ASTM standards, visit the ASTM website, www.

14、astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from Plastics Pipe Institu

15、te (PPI), 105 Decker Court, Suite 825,Irving, TX 75062, http:/www.plasticpipe.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was develope

16、d in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1PPI TR-9 Recommended D

17、esign Factors and Design Coef-ficients for Thermoplastic Pressure Pipe2.3 Other Standards:ANSI B31.8 Gas Transmission and Distribution Piping Sys-tems5CFR Part 192 Transportation Of Natural And Other Gas ByPipeline: Minimum Federal Safety Standards6MIL-STD-1235 Single- and Multi-Level Continuous Sam

18、-pling Procedures and Tables for Inspection by Attributes63. Terminology3.1 DefinitionsDefinitions are in accordance with Termi-nology F412, and abbreviations are in accordance with Termi-nology D1600, unless otherwise specified.3.2 The gas industry terminology used in this specificationis in accord

19、ance with ANSI B31.8 or 49 CFR Part 192, unlessotherwise indicated.3.3 The term pipe used herein refers to both pipe and tubingunless specifically stated otherwise.3.4 pipe material designation codecode for thermoplasticpipe materials defined by the Plastics Pipe Institute in PPITR-4.3.5 category 1

20、mechanical fitting, nfitting for assemblingpipes, which includes a compression zone(s) to provide forpressure integrity, leak tightness, and resistance to end loadssufficient to cause no less than 25 % elongation of the PVCpiping as described in this specification.3.6 in-line fitting, nmechanical fi

21、tting used to make amechanical joint where the bore axis of the compression andsealing zones of the fitting is essentially the same as theconnected piping, for example, couplings, ells, and tees.3.7 mechanical saddle fitting, nmechanical fitting used tomake a mechanical joint that allows a lateral c

22、onnection to anexisting main in which a portion of the fitting is contoured tomatch the O.D. of the pipe to which it is attached.4. Materials4.1 GeneralThe plastic used to make PVC pipe and PVCfittings shall be virgin plastic or reworked plastic (see 4.2) andshall have a Plastics Pipe Institute (PPI

23、) long-term hydrostaticdesign stress and hydrostatic design basis rating.4.2 Rework MaterialClean rework material of the samecommercial designation, generated from the manufacturersown pipe and fitting production shall not be used unless thepipe and fitting produced meet all the requirements of this

24、specification.4.3 CompoundThe PVC compounds used for pipe andfittings shall equal or exceed the following classes described inSpecification D1784, PVC 12454, or 14333. The minimumHDB at 73F (23C) shall be 3150 psi.4.4 Elevated Temperature ServicePVC piping materialsintended for use at temperatures a

25、bove 73F (23C) shall havethe PPI hydrostatic design basis (HDB) determined at thespecific temperature in accordance with Test Method D2837.PVC piping materials intended for use at temperatures above73F (23C) shall use the PVC temperature derating factorsspecified in PPI TR-9.5. Requirements5.1 Gener

26、alPipe shall be supplied in straight lengths.5.2 WorkmanshipThe pipe and fittings shall be homoge-neous throughout and free of visible cracks, holes, foreigninclusion, blisters, and dents, or other injurious defects. Thepipe and fittings shall be as uniform as commercially practi-cable in color, opa

27、city, density, and other physical properties.5.3 Pipe and Tubing:5.3.1 Outside DiameterThe outside diameters and toler-ances shall be as shown in Table 1 when measured inaccordance with Test Method D2122. The tolerances forout-of-roundness shall apply only on pipe prior to shipment.5.3.2 Wall Thickn

28、essThe wall thicknesses and tolerancesshall be as shown in Table 2 when measured in accordancewith Test Method D2122.5.4 PVC Socket Cement Fitting Dimensions and Tolerances:5Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.

29、6Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/dodssp.daps.dla.mil.TABLE 1 IPS PVC PipeOutside Diameters and TolerancesNominal PipeSize (NPS)Average OutsideDiameter, in. (mm)Tolerances, in. (mm)For Average Maximum

30、 Out-of-Roundness (Maximum Minimum Diameter)SDR21 SDR17,SDR13.5,SDR1118 0.405 (10.29) 0.004 (0.10) . 0.016 (0.41)14 0.540 (13.72) 0.004 (0.10) . 0.016 (0.41)38 0.675 (17.14) 0.004 (0.10) . 0.016 (0.41)12 0.840 (21.34) 0.004 (0.10) . 0.016 (0.41)34 1.050 (26.67) 0.004 (0.10) . 0.020 (0.51)114 4 1.660

31、 (42.16) 0.005 (0.13) 0.030 (0.76) 0.024 (0.61)112 1.900 (48.26) 0.006 (0.15) 0.060 (1.52) 0.024 (0.61)2 2.375 (60.32) 0.006 (0.15) 0.060 (1.52) 0.024 (0.61)3 3.500 (88.90) 0.008 (0.20) 0.060 (1.52) 0.030 (0.76)4 4.500 (114.30) 0.009 (0.23) 0.100 (2.54) 0.030 (0.76)6 6.625 (168.28) 0.011 (0.28) 0.10

32、0 (2.54) 0.070 (1.78)F2817 1325.4.1 Fitting sockets inside diameters (waterways), mini-mum wall thicknesses, and dimensions shall be as shown inTable 3 when measured in accordance with Test MethodD2122.5.4.2 The minimum wall thickness of fittings shall be 125 %of the minimum wall thickness of the co

33、rresponding size ofSchedule 40 pipe for which they are designed to be used,except that for the socket, the wall thickness shall be at leastequal to the minimum wall thickness of the corresponding sizeof Schedule 40 pipe.5.4.3 The minimum inside diameter of the fittings shall benot less than the mini

34、mum specified inside diameter of thecorresponding size of Schedule 40 pipe.5.4.4 Minimum dimensions have zero negative tolerance.Tolerances on other dimensions are shown in Table 3.NOTE 1References to Schedule 40 pipes for socket dimensions usingPVC materials with an established HDB rating is based

35、on historicalprecedents and past references to socket dimensions under SpecificationD2466.TABLE 2 Wall Thicknesses and Tolerances for PVC Plastic Pipe with IPS Outside DiametersNominalPipe Size, in.Wall Thickness,Ain.BSDR21 SDR17 SDR13.5Minimum Tolerance Minimum Tolerance Minimum Tolerance18 . . . .

36、 0.060 +0.02014 . . . . 0.060 +0.02038 . . . . +0.020 +0.02012 . . . . 0.062 +0.02034 . . . . 0.078 +0.0201 0.063 +0.020 0.077 +0.020 0.097 +0.020114 0.079 +0.020 0.098 +0.020 0.123 +0.020112 0.090 +0.020 0.112 +0.020 0.141 +0.0202 0.113 +0.020 0.140 +0.020 0.176 +0.020212 0.137 +0.020 0.169 +0.020

37、0.213 +0.0263 0.167 +0.020 0.206 +0.025 0.259 +0.031312 0.190 +0.023 0.235 +0.028 0.296 +0.0364 0.214 +0.026 0.265 +0.032 0.333 +0.0405 0.265 +0.032 0.327 +0.039 0.412 +0.0496 0.316 +0.038 0.390 +0.047 0.491 +0.059AThe minimum is the lowest wall thickness of the pipe at any cross section. The maximu

38、m permitted wall thickness, at any cross section, is the minimum wall thicknessplus the stated tolerance. All tolerances are on the plus side of the minimum requirement.B1 in. = 25.4 mm (exact).TABLE 3 Tapered Sockets for PVC Pipe Fittings, Schedule 40, in.ANominalPipeSizeASocket Entrance DiameterBS

39、ocket Bottom DiameterCBSocketLength,minDCInsideDiameter,minWallThickness,minOutsideDiameterofHub,MEntrance,minDiameter ToleranceonDiameterMaxOut-of-RoundDiameter ToleranceonDiameterMaxOut-of-RoundE F EW EX,EZ18 0.417 0.004 0.016 (0.41) 0.401 0.004 0.016 (0.41) 0.500 0.225 0.068 0.085 0.52616416414 0

40、.552 0.004 0.016 (0.41) 0.536 0.004 0.016 (0.41) 0.500 0.320 0.088 0.110 0.67216416438 0.687 0.004 0.016 (0.41) 0.671 0.004 0.016 (0.41) 0.594 0.449 0.091 0.114 0.82113213212 0.848 0.004 0.016 (0.41) 0.836 0.004 0.016 (0.41) 0.688 0.578 0.109 0.136 0.99813213234 1.058 0.004 0.020 (0.51) 1.046 0.004

41、0.020 (0.51) 0.719 0.740 0.113 0.141 1.2211321321 1.325 0.005 0.020 (0.51) 1.310 0.005 0.020 (0.51) 0.875 0.990 0.133 0.166 1.504116116114 1.670 0.005 0.024 (0.61) 1.655 0.005 0.024 (0.61) 0.938 1.335 0.140 0.175 1.871116116112 1.912 0.006 0.024 (0.61) 1.894 0.006 0.024 (0.61) 1.094 1.564 0.145 0.18

42、1 2.1271161162 2.387 0.006 0.024 (0.61) 2.369 0.006 0.024 (0.61) 1.156 2.021 0.154 0.193 2.634116116212 2.889 0.007 0.030 (0.76) 2.868 0.007 0.030 (0.76) 1.750 2.414 0.203 0.254 3.170332183 3.516 0.008 0.030 (0.76) 3.492 0.008 0.030 (0.76) 1.875 3.008 0.216 0.270 3.84133218312 4.016 0.008 0.030 (0.7

43、6) 3.992 0.008 0.030 (0.76) 2.000 3.486 0.226 0.283 4.374332184 4.518 0.009 0.030 (0.76) 4.491 0.009 0.030 (0.76) 2.000 3.961 0.237 0.296 4.90733218AThe sketches and designs of fittings are illustrative only.BSocket depth, measured from socket entrance face to socket bottom face.CSee 5.4.4.F2817 133

44、5.5 FlatteningThere shall be no evidence of splitting,cracking, or breaking by the specimens subjected to this testand performed in accordance with Test Method D2412. Flattenthree specimens of the pipe, 2 in. (50.8 mm) long, betweenparallel plates in a suitable press until the distance between thepl

45、ates is 40 % of the outside diameter of the pipe or the wallsof pipe touch. The rate of loading shall be uniform and suchthat the compression is completed within 2 to 5 min. Onremoval of the load, examine the specimens for evidence ofsplitting, cracking, or breaking.5.6 Impact ResistanceThe impact r

46、esistance for PVC pipeshall fall within the range specified by the manufacturersdesignated Impact Classification Cell (IC). Table 4 lists impactclassification cell for SDR 17 and 21 pipe. The impactclassification rating for PVC pipe shall be determined inaccordance with Test Method D2444 using a fla

47、t plate holderand 20-lb tup B for sizes 2 in. and less and 30-lb tup B for alllarger sizes. The specimens shall be conditioned in a mixture ofice and water at 32 to 35F (0 to 2C) for1h(Note 2) andtested immediately on removal from this medium.NOTE 2Other conditioning media such as a refrigerated flu

48、id bath ofwater and ethylene glycol at 32 to 35F (0 to 2C) for1horarefrigeratedair chamber at 32 to 35F (0 to 2C) for 4 h may be used if it can bedemonstrated that equivalent results are obtained. However, in cases ofdisagreement, the ice water mixture shall be used.5.7 Impact Quality AssuranceThe i

49、mpact quality assur-ance is a “GO/NOGO” test. Five specimens shall be impactedin accordance with Test Method D2444 using the tup andholder specified in 5.5 from a height determined by the lowervalue of the designated Impact Classification (IC) cell. All fivespecimens shall pass. If one specimen fails, a second set of fivespecimens shall be tested. None of the second set shall fail. Ifnine out of the total ten specimens pass, the lot shall beconsidered to h