AECMA PREN 4800-4-2001 Aerospace Series Titanium and Titanium Alloys Technical Specification Part 4 Wire Edition P1《航空航天系列.钛和钛合金 技术规范.第4部分 线材.P1版》.pdf

《AECMA PREN 4800-4-2001 Aerospace Series Titanium and Titanium Alloys Technical Specification Part 4 Wire Edition P1《航空航天系列.钛和钛合金 技术规范.第4部分 线材.P1版》.pdf》由会员分享，可在线阅读，更多相关《AECMA PREN 4800-4-2001 Aerospace Series Titanium and Titanium Alloys Technical Specification Part 4 Wire Edition P1《航空航天系列.钛和钛合金 技术规范.第4部分 线材.P1版》.pdf（20页珍藏版）》请在麦多课文档分享上搜索。

1、AECMA STANDARDNORME AECMAAECMA NORMprEN 4800-4Edition P 1April 2002PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES - STANDARDIZATION (AECMA-STAN)Gulledelle 94 B-1200 BRUXELLES Tel. (+32) 2 775 8110 Fax. (+32) 2 775 8111ENGLISH VERSIONAerospace seriesTitanium and titanium alloysTechnica

2、l specificationPart 4: WireSrie arospatialeTitane et alliages de titaneSpcification techniquePartie 4: FilsLuft- und RaumfahrtTitan und Titanlegierungen KneterzeugnisseTechnische LieferbedingungenTeil 4: DrhteThis “Aerospace Series“ Prestandard has been drawn up under the responsibility of AECMA-STA

3、N (TheEuropean Association of Aerospace Industries - Standardization). It is published on green paper for theneeds of the European Aerospace Industry. It has been technically approved by the experts of theconcerned Domain following member comments.Subsequent to the publication of this Prestandard, t

4、he technical content shall not be changed to anextent that interchangeability is affected, physically or functionally, without re-identification of thestandard.After examination and review by users and formal agreement of AECMA-STAN it will be submitted as adraft European Standard to CEN (European C

5、ommittee for Standardization) for formal vote.Nota - Extra copies can be supplied by B.N.A.E. Technopolis 54 - 199, rue Jean-Jacques Rousseau 92138 ISSY-LES-MOULINEAUX CEDEXEdition approved for publication2002-04-30Comments should be sent within six monthsafter the date of publication toAECMA-STANGu

6、lledelle 94B-1200 BRUXELLESMaterial DomainMr Evetts aecma 2002Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 2prEN 4800-4: 2002ContentsPage0 Intr

7、oduction. 31 Scope 32 Normative references. 33 Definitions. 44 Wording of order . 45 Health and safety 46 Technical requirements. 5Table 1 Technical requirements for lines 1 to 29, where appropriate. 7Table 2 Technical requirements for lines 30 onwards, where appropriate . 16Copyright Association Eu

8、ropeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 3prEN 4800-4: 20020 IntroductionThis standard is part of the series of EN metallic material standards for aerospace applic

9、ations. The generalorganization of this series is described in EN 4258.1 ScopeThis standard defines the requirements for the ordering, manufacture, testing, inspection and delivery oftitanium and titanium alloy bar and section. It shall be applied when referred to and in conjunction with theEN mater

10、ial standard unless otherwise specified on the drawing, order or inspection schedule.2 Normative referencesThis European Standard incorporates by dated or undated reference provisions from other publications.These normative references are cited at the appropriate places in the text and the publicati

11、ons are listedhereafter. For dated references, subsequent amendments to or revisions of any of these publications applyto this European Standard only when incorporated in it by amendment or revision. For undated referencesthe latest edition of the publication referred to applies.ISO 7800 Metallic ma

12、terials Wire Simple torsion testISO 7801 Metallic materials Wire Reverse bend testISO 7802 Metallic materials Wire Wrapping testISO 9649 Metallic materials Wire Reverse torsion testEN 2000 Aerospace series Quality assurance EN aerospace products Approval of the qualitysystem of manufacturersEN 2002-

13、1 Aerospace series Test methods for metallic materials Part 1: Tensile testing at ambienttemperature 1)EN 2002-2 Aerospace series Test methods for metallic materials Part 2: Tensile testing at elevatedtemperature 1)EN 2002-5 Aerospace series Test methods for metallic materials Part 5: Uninterrupted

14、creep andstress-rupture testing 1)EN 2002-8 Aerospace series Metallic materials Test methods Part 8: Micrographic determinationof grain size 1)EN 2002-16 Aerospace series Metallic materials Test methods Part 16: Non-destructive testing Penetrant testing 1)EN 2003-9 Aerospace series Test methods Tita

15、nium and titanium alloys Part 9 : Determination ofsurface contamination 1)EN 2032-1 Aerospace series Metallic materials Part 1: Conventional designationEN 2032-2 Aerospace series Metallic materials Part 2: Coding of metallurgical condition in deliveryconditionEN 2078 Aerospace series Metallic materi

16、als Manufacturing schedule, inspection schedule,inspection and test report Definition, general principles, preparation and approvalEN 2955 Aerospace series Recycling of titanium and titanium alloy scrapEN 3042 Aerospace series Quality assurance EN aerospace products Qualification procedureEN 3238 Ae

17、rospace series Test methods for metallic materials Shear test for rivet wires andrivets in metallic material except aluminium and aluminium alloys 2)Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or netw

18、orking permitted without license from IHS-,-,-Page 4prEN 4800-4: 2002EN 3114-1 Aerospace series Test method Microstructure of ( + ) titanium alloy wrought products Part 1: General requirements 1)EN 3114-2 Aerospace series Test method - Microstructure of ( + ) titanium alloy wrought products Part 2:

19、Microstructure of bars, sections, forging stock and forgings 1)EN 3683 Aerospace series Test methods Titanium alloy wrought products Determination ofprimary content Point count method and line intercept method 1)EN 3684 Aerospace series Test methods Titanium alloy wrought products Determination of t

20、ransus temperature Metallographic method 1)EN 3976 Aerospace series Titanium and titanium alloys Test method Chemical analysis for thedetermination of hydrogen content 1)EN 4258 Aerospace series Metallic materials General organization of standardization Linksbetween types of EN standards and their u

21、seEN 4259 Aerospace series Metallic materials Definition of general terms 1)EN 4268 Aerospace series Metallic materials Heat treatment facilities General requirements 2)TR 2410 Aerospace series Metallic materials Relationship between dimensional standards andmaterial standards 3)3 DefinitionsGeneral

22、 definition, see EN 4259.4 Wording of orderThe order shall clearly indicate: quantities to be supplied; dates of delivery; material standard number; delivery condition and metallurgical code of products; dimensions and tolerances or reference to an appropriate dimensional standard; product designati

23、on, when required; forwarding address; nature and type of packing, if required; definition and frequency of any special tests and their retest procedures, if required.5 Health and safetyProducts in the delivery condition shall fulfil the health and safety laws of the area of the country when andwher

24、e it is to be delivered.A product safety data sheet shall be available.1) Published as AECMA Prestandard at the date of publication of this standard2) In preparation at the date of publication of this standard3) Published as AECMA Technical Report at the date of publication of this standardCopyright

25、 Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 5prEN 4800-4: 20026 Technical requirements6.1 GeneralThe product shall be manufactured in accordance with t

26、he requirements of the relevant material standardand the applicable requirements of this specification. A manufacturing schedule shall be established andapplied in accordance with EN 2078.Product shall satisfy the requirements of the material standard and/or order and shall be free fromirregularitie

27、s prejudicial to the subsequent manufacture or use of this product.Not with standing previous acceptance complying with this material standard, any product that is found, at alater stage, to contain such defects shall be rejected.Unless otherwise specified, the requirements in tables 1 and 2 shall a

28、pply in conjunction with those of therelevant material standard. Table 1 relates to lines 1 to 29 (inclusive) of the material standard and table 2relates to lines 30 onwards in which the sub-line format is also used. Lines 2 to 98 may also be opened inline 100 if the material standard details specif

29、ic qualification requirements. If a specific line number is notshown in tables 1 and 2, the requirement is stated in the material standard and/or order.The requirements of the order and/or material standard shall over-ride the requirements of the technicalspecification.6.2 Qualification requirements

30、Qualification requirements when invoked by the material standard and/or order are detailed in tables 1 and 2.Unless otherwise agreed between the manufacturer and purchaser the qualification phase shall be run onthe first three batches, coming from three different ingots.6.3 Release requirements6.3.1

31、 Release testsRelease testing shall be the responsibility of the manufacturer.The purchaser reserves the right to perform any of the inspections and/or tests required by the materialstandard and/or order.The test samples shall be representative of the product.When required the manufacturer shall inf

32、orm the purchaser of the planned dates for extraction of samplesand release testing in order that these operations may be witnessed.Tables 1 and 2 detail the requirements for each line of the material standard. Unless otherwise specificallyrequested by the purchaser, a particular inspection and/or t

33、est for release shall be carried out ifcorresponding acceptance criteria and/or values are stated in the applicable material standard, but see also6.3.5 “Capability clause“.6.3.2 RetestsIf the test procedure or test piece preparation is faulty, testing shall be re-applied at the original frequencyaf

34、ter rectification of the original cause of failure.When failure cannot be attributed to faulty testing, or test piece preparation, further test samples shall beselected at twice the original frequency from the product, one of which shall be that on which the originalresults were obtained unless alre

35、ady withdrawn by the manufacturer after suitable identification of the causeof failure. If all retest results are satisfactory, the batch shall be accepted. If one or more tests areunsatisfactory, the batch shall be: rejected, or 100 % retested and the conforming products accepted, or partially or f

36、ully re-heat treated if heat treatment can rectify the cause of the failure and tested as acompletely new batch except for chemical composition, for which redetermination of hydrogen contentis required . No product or test sample shall be re-heat treated more than twice.Copyright Association Europee

37、ne des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 6prEN 4800-4: 20026.3.3 RejectionAny failure to meet the requirements of the material standard shall be cause for rejection.6.3

38、.4 Special testsSpecial tests may be required by the purchaser. In such cases, the nature of the test, method, frequency andtechnical requirements shall be specified on the order or inspection schedule and shall be mutually agreedby the manufacturer and purchaser.6.3.5 Capability clauseWhere capabil

39、ity clause is invoked and where sufficient statistical evidence exists, the test shall not becarried out (unless specifically requested by the purchaser). However, this in no way reduces the obligationsof the manufacturer to fulfil the requirements. If subsequent testing indicates that the product d

40、oes notcomply with the requirements, the batch shall be rejected.If sufficient statistical evidence does not exist, the test shall be carried out at a frequency agreed betweenthe manufacturer and the purchaser.6.3.6 Statistical process controlReduction in the extent of release testing, other than th

41、at defined in 6.3.5 above, may be negotiated with thepurchaser on the basis of appropriate statistical process control and/or statistical data.6.3.7 Inspection and test reportThe manufacturer shall furnish, with each delivery, a report conforming to the requirements of EN 2078stating the following:

42、manufacturers name and address and, if appropriate, identification of the plant; order number; material standard number; delivery condition and metallurgical code of the product; quantity and dimensions; manufacturing and inspection schedule reference; cast and batch number; batch and/or test sample

43、s heat treatment condition; results of the tests and retests if any.6.4 TraceabilityEach product shall be traceable to the cast, production batch and/or heat treatment batch at all stages ofmanufacture, testing and delivery.Copyright Association Europeene des Constructeurs de Materiel Aerospatial Pr

44、ovided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 7prEN 4800-4: 2002Table 1 Technical requirements for lines 1 to 29, where appropriateFrequency of testingMaterial standard linereferenceNo TitleRequirementsQualification Rele

45、ase1 Material designation See EN 2032-1. The test samples used for chemical analysis shall be representative of the product and shall be taken fromlocation corresponding to top and bottom of each ingot produced after the final melting stage. The methodof chemical analysis shall be at the discretion

46、of the manufacturer unless otherwise stated in the materialstandard or order. In cases of dispute, the method of chemical analysis shall be agreed between themanufacturer and purchaser preferably using existing chemical analysis standards. The measuredchemical composition shall be stated on the cert

47、ificate of conformance.2 per cast 2 per cast2 Chemical compositionSpecific requirements for hydrogen content:The hydrogen content shall be determined on each batch in the delivery condition in accordance withEN 3976.1 per batch 1 per batch3 Method of melting Method of melting consists of multiple me

48、lt using combination of non-consumable electrode, consumableelectrode and cold hearth (electron beam or plasma arc) melting practices. Some of the followingrequirements are dependent on the actual melting route.NOTE Non-consumable electrode melting should be used for consolidation purpose only.1 Raw material:Raw materials shall be purchased only from suppliers approved by the manufacturer and registered inhis list of approved suppliers.Approval of suppliers shall be made in accordance with written procedures contained within the qualityassurance system of the manufacture