BS ISO 6362-7-2014 en_1328 Wrought aluminium and aluminium alloys Extruded rods bars tubes and profiles Chemical composition《锻铝和铝合金.挤压棒 条材 管材和型材.化学成分》.pdf

《BS ISO 6362-7-2014 en_1328 Wrought aluminium and aluminium alloys Extruded rods bars tubes and profiles Chemical composition《锻铝和铝合金.挤压棒 条材 管材和型材.化学成分》.pdf》由会员分享，可在线阅读，更多相关《BS ISO 6362-7-2014 en_1328 Wrought aluminium and aluminium alloys Extruded rods bars tubes and profiles Chemical composition《锻铝和铝合金.挤压棒 条材 管材和型材.化学成分》.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards Publication BS ISO 6362-7:2014 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 7: Chemical compositionBS ISO 6362-7:2014 BRITISH STANDARD National foreword This British Standard is the UK implementation of ISO 6362-7:2014. It supersedes BS ISO 6362-7:

2、2012 which is withdrawn. The UK participation in its preparation was entrusted to Technical Committee NFE/35, Light metals and their alloys. A list of organizations represented on this committee can be obtained on request to its secretary. This publication does not purport to include all the necessa

3、ry provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2014. Published by BSI Standards Limited 2014 ISBN 978 0 580 84689 2 ICS 77.150.10 Compliance with a British Standard cannot confer immunity from legal obligations. This British Standard

4、 was published under the authority of the Standards Policy and Strategy Committee on 30 September 2014. Amendments issued since publication Date Text affectedBS ISO 6362-7:2014 ISO 2014 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 7: Chemical composition Alumini

5、um et alliages daluminium corroys Barres, tubes et profils fils Partie 7: Composition chimique INTERNATIONAL STANDARD ISO 6362-7 Second edition 2014-09-15 Reference number ISO 6362-7:2014(E)BS ISO 6362-7:2014ISO 6362-7:2014(E)ii ISO 2014 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2014 All

6、rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can be requested fro

7、m either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in SwitzerlandBS ISO 6362-7:2014ISO 6362-7:2014(E) ISO 2014 All

8、 rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative references 1 3 Terms and definitions . 1 4 Chemical composition . 1 Annex A (normative) Rules for rounding for determination of compliance .6BS ISO 6362-7:2014ISO 6362-7:2014(E) Foreword ISO (the International Organization for St

9、andardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the rig

10、ht to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. The procedure

11、s used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial ru

12、les of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights iden

13、tified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement. For an explanatio

14、n on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information The committee responsible for this document

15、is ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This second edition cancels and replaces the first edition (ISO 6362-7:2012), which has been technically revised. ISO 6362 consists of the following parts, under the general title Wrought aluminiu

16、m and aluminium alloys Extruded rods/bars, tubes and profiles: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Extruded rectangular bars Tolerances on shape and dimensions Part 4: Profiles Tolerances on shape and dimensions Part 5: Round, square and hex

17、agonal bars Tolerances on shape and dimensions Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and dimensions Part 7: Chemical compositioniv ISO 2014 All rights reservedBS ISO 6362-7:2014INTERNATIONAL ST ANDARD ISO 6362-7:2014(E) Wrought aluminium and aluminium alloys Extr

18、uded rods/bars, tubes and profiles Part 7: Chemical composition 1 Scope This part of ISO 6362 specifies the chemical composition of wrought aluminium and aluminium alloys. The chemical composition limits of aluminium and aluminium alloys specified herein are completely identical with those registere

19、d with the Aluminium Association, 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209, USA (known as the “Teal Sheets”), for the corresponding alloys. NOTE In the case of a discrepancy in the values listed in Table 1 with those listed in the “Registration Record Series Teal Sheets, International A

20、lloy Destinations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys”, the composition limits registered with the Aluminium Association and published in the “Teal Sheets” can be considered for controlling the composition. 2 Normative references The following documents,

21、in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 209, Aluminium and aluminium

22、 alloys Chemical composition ISO 6362-1, Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 1: Technical conditions for inspection and delivery 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 6362-1 apply. 4 Chemical c

23、omposition The chemical designations are specified in ISO 209. The chemical composition of the aluminium and aluminium alloys is given in percentage by mass in Table 1. For the purpose of determining conformance to these limits, an observed value or a calculated value obtained from analysis is round

24、ed off, in accordance with the rules for rounding given in Annex A. The conformance does not preclude the possible presence of other elements that are not specified. If the purchasers requirements necessitate limits for any other element not specified, these shall be agreed upon between the supplier

25、 and purchaser. “The remainder” is the difference between 100 % and the sum of all other metallic elements present in amounts of 0,010 % or more each, expressed to the second decimal place before determining the sum. ISO 2014 All rights reserved 1BS ISO 6362-7:2014ISO 6362-7:2014(E) Table 1 Chemical

26、 composition (% by mass) Alloy Limit Si Fe Cu Mn Mg Cr Zn Ti Remarks Others Aluminium Each Tot al 1070 min. max. 0,20 0,25 0,04 0,03 0,03 0,04 0,03 V 0,05 max. 0,03 99,70 1070A min. max. 0,20 0,25 0,03 0,03 0,03 0,07 0,03 0,03 99,70 1060 min. max. 0,25 0,35 0,05 0,03 0,03 0,05 0,03 0,03 99,60 1050 m

27、in. max. 0,25 0,40 0,05 0,05 0,05 0,05 0,03 V 0,05 max. 0,03 99,50 1050A min. max. 0,25 0,40 0,05 0,05 0,05 0,07 0,05 0,03 99,50 1350 min. max. 0,10 0,40 0,05 0,01 0,01 0,05 B 0,05 max. Ga 0,03 max. V+Ti 0,02 max. 0,03 0,10 99,50 1100 min. max. Si+Fe:0,95 0,05 0,20 0,05 0,10 a 0,05 0,15 99,00 1200 m

28、in. max. Si+Fe:1,00 0,05 0,05 0,10 0,05 0,05 0,15 99.00 2007 min. max. 0,8 0,8 3,3 4,6 0,50 1,0 0,40 1,8 0,10 0,8 0,20 Ni 0,20 max. Bi 0,20 max. Pb 0,8 to 1,5 Sn 0,20 max. 0,10 0,30 Remainder 2011 min. max. 0,40 0,7 5,0 6,0 0,30 Bi 0,20 to 0,6 Pb 0,20 to 0,6 0,05 0,15 Remainder 2011A min. max. 0,40

29、0,50 4,5 6,0 0,30 Bi 0,20 to 0,6 Pb 0,20 to 0,6 0,05 0,15 Remainder 2014 min. max. 0,50 1,2 0,7 3,9 5,0 0,40 1,2 0,20 0,8 0,10 0,25 0,15 b 0,05 0,15 Remainder 2014A min. max. 0,50 0,9 0,50 3,9 5,0 0,40 1,2 0,20 0,8 0,10 0,25 0,15 Zr+Ti 0,25 max. Ni 0,10 max. 0,05 0,15 Remainder 2017 min. max. 0,20 0

30、,8 0,7 3,5 4,5 0,40 1,0 0,40 0,8 0,10 0,25 0,15 b 0,05 0,15 Remainder 2017A min. max. 0,20 0,8 0,7 3,5 4,5 0,40 1,0 0,40 1,0 0,10 0,25 Zr+Ti 0,20 max. 0,05 0,15 Remainder 2024 min. max 0,50 0,50 3,8 4,9 0,30 0,9 1,2 1,8 0,10 0,25 0,15 b 0,05 0,15 Remainder 2030 min. max. 0,8 0,7 3,3 4,5 0,20 1,0 0,5

31、0 1,3 0,10 0,50 0,20 Bi 0,20 max. Pb 0,8 to 1,5 0,10 0,30 Remainder 3102 min. max. 0,40 0,7 0,10 0,05 0,40 0,30 0,10 0,05 0,15 Remainder aBe 0,000 3 % max. when used for welding rods and welding wires. bWith agreement between the purchaser and supplier, Zr+Ti can be 0,20 % max. cWith agreement betwe

32、en the purchaser and supplier, Zr+Ti can be 0,25 % max.2 ISO 2014 All rights reservedBS ISO 6362-7:2014ISO 6362-7:2014(E) Alloy Limit Si Fe Cu Mn Mg Cr Zn Ti Remarks Others Aluminium Each Tot al 3003 min. max. 0,6 0,7 0,05 0,20 1,0 1,5 0,10 0,05 0,15 Remainder 3103 min. max. 0,50 0,7 0,10 0,9 1,5 0,

33、30 0,10 0,20 Zr+Ti 0,10 max. 0,05 0,15 Remainder 3203 min. max. 0,6 0,7 0,05 1,0 1,5 0,10 0,05 0,15 Remainder 5005 min. max 0,30 0,7 0,20 0,20 0,50 1,1 0,10 0,25 0,05 0,15 Remainder 5005A min. max. 0,30 0,45 0,05 0,15 0,7 1,1 0,10 0,20 0,05 0,15 Remainder 5019 min. max. 0,40 0,50 0,10 0,10 0,6 4,5 5

34、,6 0,20 0,20 0,20 Mn+Cr 0,02max. 0,05 0,15 Remainder 5049 min. max. 0,40 0,50 0,10 0,50 1,1 1,6 2,5 0,30 0,20 0,10 0,05 0,15 Remainder 5051A min. max. 0,30 0,45 0,05 0,25 1,4 2,1 0,30 0,20 0,10 0,05 0,15 Remainder 5251 min. max. 0,40 0,50 0,15 0,10 0,50 1,7 2,4 0,15 0,15 0,15 0,05 0,15 Remainder 505

35、2 min. max. 0,25 0,40 0,10 0,10 2,2 2,8 0,15 0,35 0,10 0,05 0,15 Remainder 5154 min. max. 0,25 0,40 0,10 0,10 3,1 3,9 0,15 0,35 0,20 0,20 a 0,05 0,15 Remainder 5154A min. max 0,50 0,50 0,10 0,50 3,1 3,9 0,25 0,20 0,20 Mn+Cr 0,10 to 0,50 0,05 0,15 Remainder 5454 min. max. 0,25 0,40 0,10 0,50 1,0 2,4

36、3,0 0,05 0,20 0,25 0,20 0,05 0,15 Remainder 5754 min. max. 0,40 0,40 0,10 0,50 2,6 3,6 0,30 0,20 0,15 Mn+Cr 0,10 to 0,6 0,05 0,15 Remainder 5056 min. max. 0,30 0,40 0,10 0,05 0,20 4,5 5,6 0,05 0,20 0,10 0,05 0,15 Remainder 5083 min. max. 0,40 0,40 0,10 0,40 1,0 4,0 4,9 0,05 0,25 0,25 0,15 0,05 0,15

37、Remainder 5086 min. max. 0,40 0,50 0,10 0,20 0,7 3,5 4,5 0,05 0,25 0,25 0,15 0,05 0,15 Remainder 6101A min. max. 0,30 0,7 0,40 0,05 0,40 0,9 0,03 0,10 Remainder 6101B min. max 0,30 0,6 0,10 0,30 0,05 0,05 0,35 0,6 0,10 0,03 0,10 Remainder aBe 0,000 3 % max. when used for welding rods and welding wir

38、es. bWith agreement between the purchaser and supplier, Zr+Ti can be 0,20 % max. cWith agreement between the purchaser and supplier, Zr+Ti can be 0,25 % max.Table 1 (continued) ISO 2014 All rights reserved 3BS ISO 6362-7:2014ISO 6362-7:2014(E) Alloy Limit Si Fe Cu Mn Mg Cr Zn Ti Remarks Others Alumi

39、nium Each Tot al 6005 min. max. 0,6 0,9 0,35 0,10 0,10 0,40 0,6 0,10 0,10 0,10 0,05 0,15 Remainder 6005A min. max 0,50 0,9 0,35 0,30 0,50 0,40 0,7 0,30 0,20 0,10 Mn+Cr 0,12 to 0,50 0,05 0,15 Remainder 6005C min. max. 0,40 0,9 0,35 0,35 0,5 0,40 0,8 0,30 0,25 0,10 Mn+Cr 0,50 max. 0,05 0,15 Remainder

40、6106 min. max 0,30 0,6 0,35 0,25 0,05 0,20 0,40 0,8 0,20 0,10 0,05 0,10 Remainder 6008 min. max. 0,50 0,9 0,35 0,30 0,30 0,40 0,7 0,30 0,20 0,10 V 0,05 to 0,20 0,05 0,15 Remainder 6110A min. max. 0,7 1,1 0,50 0,30 0,8 0,30 0,9 0,7 1,1 0,05 0,25 0,20 Zr+Ti 0,20 max. 0,05 0,15 Remainder 6012 min. max

41、0,6 1,4 0,50 0,10 0,40 1,0 0,6 1,2 0,30 0,30 0,20 Bi 0,7 max. Pb 0,40 to 2,0 0,05 0,15 Remainder 6014 min. max. 0,30 0,6 0,35 0,25 0,05 0,20 0,40 0,8 0,20 0,10 0,10 V 0,05 to 0,20 0,05 0,15 Remainder 6018 min. max 0,50 1,2 0,7 0,15 0,40 0,30 0,8 0,6 1,2 0,10 0,30 0,20 Bi 0,40 to 0,7 Pb 0,40 to 1,2 0

42、,05 0,15 Remainder 6023 min. max 0,6 1,4 0,50 0,20 0,50 0,20 0,6 0,40 0,9 Bi 0,30 to 0,8 Sn 0,6 to 1,2 0,05 0,15 Remainder 6351 min. max. 0,7 1,3 0,50 0,10 0,40 0,8 0,40 0,8 - 0,20 0,20 0,05 0,15 Remainder 6060 min. max. 0,30 0,6 0,10 0,30 0,10 0,10 0,35 0,6 0,05 0,15 0,10 0,05 0,15 Remainder 6360 m

43、in. max. 0,35 0,8 0,10 0,30 0,15 0,02 0,15 0,25 0,45 0,05 0,10 0,10 0,05 0,15 Remainder 6061 min. max. 0,40 0,8 0,7 0,15 0,40 0,15 0,8 1,2 0,04 0,35 0,25 0,15 0,05 0,15 Remainder 6261 min. max. 0,40 0,7 0,40 0,15 0,40 0,20 0,35 0,7 1,0 0,10 0,20 0,10 0,05 0,15 Remainder 6262 min. max. 0,40 0,8 0,7 0

44、,15 0,40 0,15 0,8 1,2 0,04 0,14 0,25 0,15 Bi 0,40 to 0,7 Pb 0,40 to 0,7 0,05 0,15 Remainder 6262A min. max. 0,40 0,8 0,7 0,15 0,40 0,15 0,8 1,2 0,04 0,14 0,25 0,10 Bi 0,40 to 0,9 Sn 0,40 to 1,0 0,05 0,15 Remainder 6063 min. max. 0,20 0,6 0,35 0,10 0,10 0,45 0,9 0,10 0,10 0,10 0,05 0,15 Remainder 606

45、3A min. max. 0,30 0,6 0,15 0,35 0,10 0,15 0,6 0,9 0,05 0,15 0,10 0,05 0,15 Remainder aBe 0,000 3 % max. when used for welding rods and welding wires. bWith agreement between the purchaser and supplier, Zr+Ti can be 0,20 % max. cWith agreement between the purchaser and supplier, Zr+Ti can be 0,25 % m

46、ax.Table 1 (continued) 4 ISO 2014 All rights reservedBS ISO 6362-7:2014ISO 6362-7:2014(E) Alloy Limit Si Fe Cu Mn Mg Cr Zn Ti Remarks Others Aluminium Each Tot al 6463 min. max. 0,20 0,6 0,15 0,20 0,05 0,45 0,9 0,05 0,05 0,15 Remainder 6065 min. max. 0,40 0,8 0,7 0,15 0,40 0,15 0,8 1,2 0,15 0,25 0.10 Bi 0,50 to 1,5 Pb 0,05 max. Zr 0,15 max. 0,05 0,15 Rema