SAE AMS 5637H-2012 Steel Corrosion Resistant Bars and Wire 18Cr - 9 0Ni (SAE 30302) Solution Heat Treated Cold Drawn and Stress Relieved 125 ksi (862 MPa) Tensile Strength (UNS S30.pdf

《SAE AMS 5637H-2012 Steel Corrosion Resistant Bars and Wire 18Cr - 9 0Ni (SAE 30302) Solution Heat Treated Cold Drawn and Stress Relieved 125 ksi (862 MPa) Tensile Strength (UNS S30.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 5637H-2012 Steel Corrosion Resistant Bars and Wire 18Cr - 9 0Ni (SAE 30302) Solution Heat Treated Cold Drawn and Stress Relieved 125 ksi (862 MPa) Tensile Strength (UNS S30.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5637H AEROSPACE MATERIAL SPECIFICATION AMS5637 REV. H Issued 1949-03 Reaffirmed 2006-04 Re

5、vised 2012-07 Superseding AMS5637G Steel, Corrosion Resistant, Bars and Wire 18Cr - 9.0Ni (SAE 30302) Solution Heat Treated, Cold Drawn and Stress Relieved 125 ksi (862 MPa) Tensile Strength (Composition similar to S30200) RATIONALE AMS5637H revises the title to clarify product condition, removes th

6、e requirement for determining yield strength for wire under 0.125 inch (3.18mm) diameter (3.3.1) and results from a Five Year Review and update of this specification. 1. SCOPE 1.1 Form This specification covers a corrosion resistant steel in the form of bars and wire 0.75 inch (19 mm) and under in n

7、ominal diameter or distance between parallel sides. 1.2 Application These products have been used typically for small parts, such as bolts, screws, and clevis pins, requiring corrosion resistance up to 700 F (371 C) and which may be fabricated by heading or by machining from bars or wire and roll th

8、reading, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a sp

9、ecific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. SAE AMS5637H Page 2 of 4 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendal

10、e, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2241 Tolerances, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Bars and Wire AMS2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloy

11、s, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2806 Identification, Bars, Wire, Mechanical Tubing, and Extrusions, Carbon and Alloy Steels and Corrosion

12、 and Heat-Resistant Steels and Alloys 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM E 8/E 8M Tension Testing of Metallic Materials ASTM E 353 Chemical Analysis of Stainless, Heat-

13、Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 353, by spectrochemical methods, or by other analytical methods accep

14、table to purchaser. TABLE 1 - COMPOSITION Element min max Carbon - 0.15 Manganese - 2.00 Silicon - 1.00 Phosphorus - 0.040 Sulfur - 0.030 Chromium 17.00 19.00 Nickel 8.00 10.00 Molybdenum - 0.75 Copper - 0.75 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS22

15、48. 3.2 Condition Solution heat treated, cold drawn, heated to 700 F 25 (371 C 14), and descaled. SAE AMS5637H Page 3 of 4 3.3 Properties Product 0.75 inch (19 mm) and under in nominal diameter or least distance between parallel sides shall conform to the following requirements: 3.3.1 Tensile Proper

16、ties Shall be as shown in Table 2, determined in accordance with ASTM E 8/E 8M. Determination of yield strength is not required for wire under 0.125 inch (3.18 mm) diameter. TABLE 2 - MINIMUM TENSILE STRENGTH Property Value Tensile Strength 125 ksi (862 MPa) Yield Strength at 0.2% Offset 100 ksi (68

17、9 MPa) Elongation in 4D 17% Reduction of Area 45% 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. 3.5 Tolerances Shall conform to all applicable requiremen

18、ts of AMS2241. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing dee

19、med necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests Tests for all technical requirements are acceptance tests and shall be performed on each heat or lot as applicable. 4.3 Sampling and Testing Shall be in accordance with AMS2371. 4.4 Reports The v

20、endor of the product shall furnish with each shipment a report showing the results of tests for composition of each heat and for tensile properties of each lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lo

21、t numbers, AMS5637H, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. SAE AMS5637H Page 4 of 4 5. PREPARATION FOR DELIVERY 5.1 Sizes Except when exact lengths or multiples of exact lengths are ordered, straight bars and wire will be acceptable in mill lengths of

22、6 to 20 feet (1.8 to 6.1 m) but not more than 10% of any shipment shall be supplied in lengths shorter than 10 feet (3 m). 5.2 Identification Shall be in accordance with AMS2806. 5.3 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with ap

23、plicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders.

24、 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have

25、 been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Terms

26、used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information

27、. 8.4 Purchase documents should specify not less than the following: AMS5637H Product form and size of product desired Quantity of product desired. 8.5 Similar Specifications Federal QQ-S-763, Class 302, Condition B, is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met. PREPARED BY AMS COMMITTEE “F“