SAE AMS 1659-1991 Coating Soil Barrier Semi-Permanent《土壤阻挡物半永久覆层》.pdf

《SAE AMS 1659-1991 Coating Soil Barrier Semi-Permanent《土壤阻挡物半永久覆层》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 1659-1991 Coating Soil Barrier Semi-Permanent《土壤阻挡物半永久覆层》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、SAESAECOATING, SOIL BARRIERSemi-PermanentAMS 1659Issued 1 APR 1991AEROSPACEMATERIALSPECIFICATIONSAESAEThe Engineering SocietyFor Advancing MobilityLand Sea Air and Space400 Commonwealth Drive, Warrendale, PA 15096-0001INTERNATIONALAn American National Standard1. SCOPE:1.1 Form: This specification co

2、vers a barrier coating in the form of aready-to-be applied liquid with a consistency suitable for brush, spray, ordip application to exterior surfaces of aircraft.1.2 Application: Primarily as a temporary protective coating for painted andunpainted exterior surfaces of aircraft to ease soil removal

3、fromdifficult-to-clean areas and to increase paint durability.1.3 Safety - Hazardous Materials: While the materials, methods, applications,and processes described or referenced in this specification may involve theuse of hazardous materials, this specification does not address the hazardswhich may b

4、e involved in such use. It is the sole responsibility of theuser to ensure familiarity with the safe and proper use of any hazardousmaterials and to take necessary precautionary measures to ensure the healthand safety of all personnel involved.2. APPLICABLE DOCUMENTS: The following publications form

5、 a part of thisspecification to the extent specified herein. The latest issue of SAEpublications shall apply. The applicable issue of other publications shallbe the issue in effect on the date of the purchase order.2.1 SAE Publications: Available from SAE, 400 Commonwealth Drive, Warrendale,PA 15096

6、-0001.SAE Technical Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences.The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringementarising therefrom, is

7、 the sole responsibility of the user.“SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites yourwritten comments and suggestions.Copyright 1991 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.S.A.SAE

8、AMS 1659AMS 16592.1.1 Aerospace Material Specifications:AMS 2470 - Anodic Treatment of Aluminum Alloys, Chromic Acid ProcessAMS 2475 - Protective Treatments, Magnesium AlloysAMS 2825 - Material Safety Data SheetsAMS 4037 - Aluminum Alloy Sheet and Plate, 4.4Cu 1.5Mg - 0.60Mn (2024;-T3 Flat Sheet, -T

9、351 Plate), Solution Heat TreatedAMS 4041 - Aluminum Alloy Sheet and Plate, Alclad, 4.4Cu - 1.5Mg - 0.60Mn(Alclad 2024 and 1-1/2% Alclad 2024, -T3 Flat Sheet; 1-1/2%Alclad 2024-T351 Plate)AMS 4049 - Aluminum Alloy Sheet and Plate, Alclad, 5.6Zn - 2.5Mg - 1.6Cu -0.23Cr (Alclad 7075; -T6 Sheet, -T651

10、Plate), Solution andPrecipitation Heat TreatedAMS 4376 - Magnesium Alloy Plate, 3.OAl - 1.OZn (AZ31B-H26), Cold Rolledand Partially AnnealedAMS 4911 - Titanium Alloy Sheet, Strip, and Plate, 6A1 - 4V, AnnealedMAM 4911 - Titanium Alloy Sheet, Strip, and Plate, 6AI - 4V, AnnealedAMS 5045 - Sheet and S

11、trip, 0.25 Carbon, maximum, Hard Temper2.2 ASTM Publications: Available from ASTM, 1916 Race Street, Philadelphia, PA19103-1187.ASTM B 117 - Salt Spray (Fog) TestingASTM D 56 - Flash Point by Tag Closed TesterASTM D 445 - Kinematic Viscosity of Transparent and Opaque Liquids (and theCalculation of D

12、ynamic Viscosity)ASTM D 1193 - Reagent WaterASTM D 1640 - Drying, Curing, or Film Formation of Organic Coatings at RoomTemperatureASTM D 1655 - Aviation Turbine FuelsASTM D 3359 - Measuring Adhesion by Tape TestASTM D 4141 - Conducting Accelerated Outdoor Exposure Tests of CoatingsASTM F 483 - Total

13、 Immersion Corrosion Test for Aircraft MaintenanceChemicalsASTM F 484 - Stress Crazing of Acrylic Plastics in Contact with Liquid orSemi-Liquid CompoundsASTM F 485 - Effects of Cleaners on Unpainted Aircraft SurfacesASTM F 519 - Mechanical Hydrogen Embrittlement Testing of Plating Processesand Aircr

14、aft Maintenance ChemicalsASTM F 1110 - Sandwich Corrosion TestASTM F 1111 - Corrosion of Low-Embrittling Cadmium Plate by AircraftMaintenance Chemicals2.3 U.S. Government Publications: Available from Standardization DocumentsOrder Desk, Building 4D, 700 Robbins Avenue, Philadelphia, PA 19111-5094.2.

15、3.1 Federal Specifications:PPP-P-1892 - Paint, Varnish, Lacquer; and Related Materials, Packaging,Packing, and Marking of- 2 -SAE AMS 1659AMS 16592.3.2 Federal Standards:FED-STD-141 - Paint, Varnish, Lacquer, and Related Materials, Methods ofInspection, Sampling and Testing2.3.3 Military Specificati

16、ons:MIL-P-23377 - Primer, Coating, Epoxy Polyamide, Chemical and SolventResistantMIL-P-25690 - Plastic, Sheets and Parts, Modified Acrylic Base, Monolithic,Crack Propagation ResistantMIL-C-83286 - Coating Urethane, Aliphatic Isocyanate, for AerospaceApplications3. TECHNICAL REQUIREMENTS:3.1 Material

17、: Shall be a water-base coating material containing no polyvinylchloride (PVC) or silicones and meeting the requirements of 3.2.3.2 Properties: Coating material shall conform to the following requirements:3.2.1 As Supplied:3.2.1.1 Viscosity: Shall be 1 to 10 centipoises (0.001 - 0.010 Pa.s) at25C 1

18、(77F 2), determined in accordance with ASTM D 445.3.2.1.2 Storage Life: Coating material shall show no abnormal change with agein sealed containers; it shall meet all other technical requirements ofthis specification at any time up to one year from date of shipment whenstored, under normal warehouse

19、 conditions, at 5 to 30C (41 to 86F).3.2.1.3 Corrosion of Metal Surfaces:3.2.1.3.1 Sandwich Corrosion: Test panels shall show a rating no worse than 2,determined in accordance with ASTM F 1110. Any dried coating shall beremoved from test panels with the remover solution described in 4.5.2.3.2.1.3.2

20、Total Immersion Corrosion: No test panel shall show evidence ofcorrosion nor a weight change greater than the following, determinedin accordance with ASTM F 483. The coating shall not be allowed todry on the panels prior to rinsing.PanelWeight Changemg/cm2 per 24 hoursAMS 4037 Aluminum Alloy, anodiz

21、ed as in AMS 2470 0.3AMS 4041 Aluminum Alloy 0.3AMS 4049 Aluminum Alloy 0.3AMS 4376 Magnesium Alloy, dichromate treated asin AMS 2475 0.2AMS 4911 or MAM 4911 Titanium Alloy 0.1AMS 5045 Carbon Steel 0.8- 3 -SAE AMS 1659AMS 16593.2.1.3.3 Low-Embrittling Cadmium Plate: Panels, coated with low-embrittli

22、ngcadmium plate, shall not show a weight change greater than 0.3mg/cm2per 24 hours, determined in accordance with ASTM F 1111. Thecoating shall not be allowed to dry on the panels prior to rinsing.3.2.1.4 Hydrogen Embrittlement: The coating material shall be non-embrittling,determined in accordance

23、with ASTM F 519, Type 1a, 1c, or 2a, exceptthat the coating material shall be applied to the specimens and allowedto dry for the duration of the test.3.2.1.5 Flash Point: Shall be not lower than 60C (140F), determined inaccordance with ASTM D 56.3.2.1.6 Effect on Transparent Acrylic Plastics: There

24、shall be no crazing orstaining of stretched, MIL-P-25690 plastic, determined in accordancewith ASTM F 484. Any coating residue shall be removed with remover(4.5.2.1) in place of the normal rinse procedure.3.2.1.7 Effect on Unpainted Surfaces: The coating material, tested inaccordance with ASTM F 485

25、, shall neither produce streaking nor leaveany stains requiring polishing to remove. The remover (4.5.2.1) shallbe used in place of water during the rinse procedure.3.2.2 Applied Films: Shall be as specified in 3.2.2.1 through 3.2.2.4,determined on both painted and unpainted panels prepared as in 4.

26、5.1.3.2.2.1 Odor: Shall be mild, determined on contents of freshly-opened containerduring coating application and during curing.3.2.2.2 Color: Colorless, unless otherwise ordered by purchaser.3.2.2.3 Appearance: Coating shall form a homogenous film, free from craters,pin holes, and other imperfectio

27、ns causing discontinuity of the appliedcoating.3.2.2.4 Air Drying: Coating, air dried at 25C 3 (77 5), shall exhibit aset-to-touch condition in not more than 20 minutes and a dry-hardcondition in not more than 30 minutes, determined in accordance withASTM D 1640.3.2.3 Cured Films: Shall conform to 3

28、.2.3.1 through 3.2.3.7, determined on bothpainted and unpainted panels.3.2.3.1 Adhesion:- 4 -SAE AMS 1659AMS 16593.2.3.1.1 To Unpainted Surfaces: Coating, when applied as in 4.5.1, shall notchip, crack, or peel before or after bending a test panel rapidly atroom temperature through an angle of 180 d

29、egrees around a diameterequal to 18 times the nominal thickness of the panel; slight crackingon the bend portion is acceptable. Scraping the surface with a knifeblade or thin metal object in accordance with FED-STD-141, Method6304, shall produce a fine, powdery residue; flaking or peeling of thecoat

30、ing is not acceptable. Sand blasting of the film shall result infilm wear by abrasion and not by chipping or peeling.3.2.3.1.2 To Painted Surfaces: Two parallel scratches, approximately 1 inch(25 mm) apart, shall be made by a sharp stylus on the coated surfaceof a panel prepared as in 4.5.1. The scr

31、atches shall penetrate onlythe coating and not the paint. Place a piece of pressure-sensitivetape across the two scratches, apply sufficient pressure to ensureadhesion, and test in accordance with ASTM D 3359, Method A. Removalof the tape, using an abrupt motion, shall cause no separation of thecoat

32、ing from the painted surface.3.2.3.2 Removability: Coating on panels, prepared as in 4.5.1, shall becompletely removed when tested as in 4.5.2.3.2.3.3 Heat Resistance: Coating shall show no evidence of chalking orblistering and shall meet the adhesion (3.2.3.1) and removability(3.2.3.2) requirements

33、 after being heated to 120C 3 (248F 5) for100 hours 1.3.2.3.4 Fluid Resistance: Coating shall show no apparent deterioration andshall meet the adhesion (3.2.3.1) and removability (3.2.3.2)requirements after exposure to ASTM D 1655, Jet A-1, aviation turbinefuel as in 4.5.3 and ethylene glycol as in

34、4.5.4.3.2.3.5 Salt Spray Resistance: Coating, applied as in 4.5.1, shall meet therequirements of 3.2.3.5.1, 3.2.3.5.2, and 3.2.3.5.3 after exposure tocontinuous salt spray testing in accordance with ASTM B 117 as follows:3.2.3.5.1 There shall be no pitting or other evidence of corrosion on thesurfac

35、e of unpainted panels after exposure for 8 hours 0.25.3.2.3.5.2 There shall be no peeling or blistering of the coating on paintedpanel surfaces after exposure for 8 hours 0.25.3.2.3.5.3 Coating on both unpainted and painted panels shall meet therequirements for adhesion (3.2.3.1) and removability (3

36、.2.3.2) afterexposure for 8 hours 0.25.3.2.3.6 Resistance to Ultraviolet Light: Coating on a painted panel, preparedas in 4.5.1.4, shall not discolor more than an uncoated painted panel,prepared as in 4.5.1.3, when tested in accordance with ASTM D 4141,Procedure A, after exposure for 60 days and sha

37、ll meet the requirementsfor removability (3.2.3.2).- 5 -SAE AMS 1659AMS 16593.3 Quality:3.3.1 The coating material, as received by purchaser, shall be homogeneous, freefrom grit and rough particles, and free from ingredients of respiratorytoxicity under normal conditions of use.3.3.2 When applied by

38、 dipping, brushing, or spraying, the resultant film shallbe free-working and shall produce a cured coating that is smooth, uniform,free from tackiness, craters, pin holes, sags, runs, bubbles, and heavyedges, and shall have leveling properties acceptable to purchaser.4. QUALITY ASSURANCE PROVISIONS:

39、4.1 Responsibility for Inspection: The vendor of coating material shall supplyall samples for vendors tests and shall be responsible for performing allrequired tests. Purchaser reserves the right to sample and to perform anyconfirmatory testing deemed necessary to ensure that the coating materialcon

40、forms to the requirements of this specification.4.2 Classification of Tests:4.2.1 Acceptance Tests: Tests for viscosity (3.2.1.1), odor (3.2.2.1), color(3.2.2.2), appearance (3.2.2.3), air drying (3.2.2.4), adhesion (3.2.3.1),and removability (3.2.3.2) are acceptance tests and shall be performed one

41、ach lot.4.2.2 Periodic Tests: Tests for heat resistance (3.2.3.3), fuel resistance(3.2.3.4), and salt spray resistance (3.2.3.5) are periodic tests andshall be performed at a frequency selected by the vendor unless frequencyof testing is specified by purchaser.4.2.3 Preproduction Tests: Tests for al

42、l technical requirements of thisspecification, except storage life (3.2.1.2), are preproduction tests andshall be performed prior to or on the initial shipment of coating materialto a purchaser, when a change in ingredients and/or processing requiresreapproval as in 4.4.2, and when purchaser deems c

43、onfirmatory testing tobe required.4.2.3.1 For direct U.S. Military procurement, substantiating test data and, whenrequested, preproduction test material shall be submitted to thecognizant agency as directed by the procuring activity, contractingofficer, or request for procurement.4.3 Sampling and Te

44、sting: Shall be as follows; a lot shall be all coatingmaterial produced in one continuous manufacturing operation from the samebatches of raw material under the same fixed conditions and presented forvendors inspection at one time.4.3.1 For Acceptance Tests: Sufficient coating material shall be take

45、n atrandom from each lot to perform all required tests. The number ofdeterminations for each requirement shall be as specified in theapplicable test procedure or, if not specified therein, not less than two.- 6 -SAE AMS 1659AMS 16594.3.2 For Periodic Tests and for Preproduction Tests: As agreed upon

46、 bypurchaser and vendor.4.4 Approval:4.4.1 Coating material shall be approved by purchaser before coating materialfor production use is supplied, unless such approval be waived bypurchaser. Results of tests on production coating material shall beessentially equivalent to those on the approved sample

47、.4.4.2 Vendor shall use ingredients and manufacturing processes on productioncoating material which are essentially the same as those used on theapproved sample coating material. If necessary to make any change iningredients or processing, vendor shall submit for reapproval a statementof the propose

48、d changes in ingredients and/or processing and, whenrequested by purchaser, sample coating material. Production coatingmaterial made by the revised procedure shall not be shipped prior toreceipt of reapproval.4.5 Test Methods:4.5.1 Test Panels:4.5.1.1 For all tests, panels shall be fabricated from A

49、MS 4041 aluminum alloy,approximately 0.032 x 4 x 9 inches (0.81 x 102 x 229 mm), and shall haverounded corners and smooth edges.4.5.1.2 Panels shall be cleaned free of water breaks, using a solutionconsisting of 4 parts n-butyl alcohol, 3 parts isopropyl alcohol, 1 part85% orthophosphoric acid, and 2 parts water. After cleaning, panelsshall be rinsed thoroughly with ASTM D 1193, Type IV, water at 20C 5(68F 9).4.5.1.3 Panels to be tested unpainted shall, after rinsing but without drying,be coated with coating material by brushing, spraying, or dipping t