1、A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2407 1 of 6 November, 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO

2、 CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 1. MATERIAL This specification covers the performance requirements for two part urethane suitable for bonding moulded ABS to modified PPO. This material replaces HN 2186. 2. REFE

3、RENCES ASTM D3163 HN 0241 HN 1000 HN 2186 ASTM D2196 ASTM D1475 ASTM D2240 GM3629M 3. MATERIAL AND EQUIPMENT REQUIRED 3.1 ABS and PPO coupons approximately 25 x 100 x 2.5 mm. 3.2 Suitable bonding fixture. 3.3 Water soak chamber capable of maintaining 54 2 C. 3.4 Universal Tensile Testing Machine cap

4、able of measuring loads at an accuracy of 1%. 4. REQUIREMENTS 4.1 Physical Properties (uncured Adhesive System) 4.1.1 The adhesive and bonding method must be compatible with all production systems. Properties such as viscosity and open time must be satisfactory to the production system that operates

5、 at 35 C. 4.1.2 Slump Resistance Material mixed according to the manufactures recommended ratio and extruded to a 10 mm x 5 mm section 100 mm long on to a steel panel shall not slump more than 1 mm. The panel shall be in the vertical plane with the long edge horizontal. A.C.N. 006 893 232 Holden Lim

6、ited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2407 2 of 6 November, 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE D

7、ATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 4. REQUIREMENTS (continued) 4.1 Physical Properties (uncured Adhesive System) (continued) 4.1.3 Slump Resistance Working Life. Material mixed according to the manufactures recommended ratio stall have a work

8、ing life of a minimum of 20 minutes at 35 C Properties Requirement Test Method Appearance Tan Visual Brookfield Viscosity, cps 25C 7000-14000 ASTM D2196 Density (kg/m3) 1.23-1.27 ASTM D1475 % solids 98 - Mix ratio by volume 1:1 - Working time 24C 20-30 min Visual Handling Strength 24C 3 hours Visual

9、 Full Strength 24C 24 hours Visual Shore A Hardness 90 ASTM D2240 A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2407 3 of 6 November, 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN

10、 RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 4. REQUIREMENTS (continued) 4.2 Physical Properties/Requirement (Cure System) 4.2.1 Process Compatibility The cu

11、red adhesive system must meet all the performance criteria specified in this standard (See 4.5) after going through the production process for the intended application. 4.2.2 Cure Time The adhesive shall be fully cured after 48 hours at 23C. 4.3 Procedures 4.3.1 Specimen must be prepared and post cu

12、red according to the procedures outlined in HN 0241. 4.3.2 A sample set shall consist of minimum of 5 specimens. 4.3.3 Lap - shear specimens shall be tested according to the procedure outlined in ASTM D3163 except the cross head speed shall be between 10 to 12.7 mm/minute. 4.3.4 All samples must dem

13、onstrate cohesive failure of the adhesive or surface delamination of the ABS or PPO in all test conditions. 4.3.5 ABS/PPO fracture, below minimum performance requirements (4.5) is to be considered a no test condition and the test repeated or sample rejected. 4.4 Environmental Conditioning 4.4.1 Two

14、sample sets shall be maintained at room temperature (23 2 oC) and will be referred to as initial. 4.4.2 Two sample sets shall be maintained at - 30 C for four hours.A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2407 4 of 6 November

15、, 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 4. REQUIREMEN

16、TS (continued) 4.4 Environmental Conditioning (continued) 4.4.3 One sample set shall maintained at 82 C for 4 hours and tested within 5 minutes. 4.4.4 Two sample sets shall be exposed to water soak at 54 C for a period of 7 days. 4.4.5 Two sample sets shall be exposed to condensing humidity at 38 C

17、for 8 weeks. 4.4.6 Two sample sets shall be aged at 70 C for 8 weeks. 4.5 Performance Requirements 4.5.1 Lap - Shear Requirements (GM3629M) Environmental Test Condition Minimum MPa Initial Room Temperature 3.4 - 30 C - 30 C Tested within 5 minutes 3.4 82 C 82 C 1.4 54 C Water Soak Tested within 5 mi

18、nutes Wet 3.4 54 C Water Soak 24 hour recovery at Room Temperature 3.4 Condensing Humidity 24 hour recovery at Room Temperature 3.4 70 C Age 8 weeks 24 hour recovery at Room Temperature 3.4 A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION

19、: HN 2407 5 of 6 November, 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecification

20、Matspec.doc 4. REQUIREMENTS (continued) 4.5 Performance Requirements (continued) 4.5.2 All samples shall maintain a minimum of at least 75% of the initial strength regardless of the magnitude or failure made with the exception of the 82 C test which must maintain a minimum of 1.4 MPa. 5. MARKING Ref

21、er HN 1000, Clause D. Containers must carry the relevant HN specification number, a vendor batch number, the suppliers name, any other requirements as specified in the purchase order and any legal requirements. 6. APPROVAL, INSPECTION AND REJECTION Refer HN 1000, Clauses A and C. 7. HAZARDOUS MATERI

22、ALS Refer HN 1000, Clause H. 8. RESTRICTED CHEMICALS Refer HN 1000, Clause J. 9. APPROVED MATERIALS Approved Material Approved Supplier Lord 7542A/D Lord Adhesives A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2407 6 of 6 November,

23、 2002 June, 2003 NAME: ADHESIVE-URETHANE-TWO PART THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 10. REVISIONS June 2003 - Section 4.5.1 shear strength reduced from 5MPa to 3.4MPa in line with GM3629M - Approved material added. - Numbering correction. Section 4.4.6 was incorrectly numbered 4.5.6. Prepared by: Mark Franke