GME QN 408300-2012 Wrought Copper-Zinc-Alloy (Revision 6 English German This standard may be applied only for current programs It is inactive for all future projects and without re.pdf

《GME QN 408300-2012 Wrought Copper-Zinc-Alloy (Revision 6 English German This standard may be applied only for current programs It is inactive for all future projects and without re.pdf》由会员分享，可在线阅读，更多相关《GME QN 408300-2012 Wrought Copper-Zinc-Alloy (Revision 6 English German This standard may be applied only for current programs It is inactive for all future projects and without re.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、MaterialSpecification QN 408300LIMITED USEWrought Copper-Zinc-Alloy Kupfer-Zink-KnetlegierungNOTE: This standard may be applied only forcurrent programs.It is inactive for all future projects and withoutreplacement.HINWEIS: Diese Spezifikation darf nur noch frlaufende Projekte angewendet werden und

2、ist fralle zuknftigen Projekte ohne Ersatz ungltig.1 Scope 1 ZweckNote: The material specified in this engineeringmaterial specification is protected by a patent ofChuetsu Metal Works Co. Ltd., Tokio/Tokyo, JP(patent letter DE 2830459 C3).Hinweis: Der in dieser Werkstoffvorschrift vorge-schriebene W

3、erkstoff ist durch die Fa. ChuetsuMetal Works Co. Ltd., Tokio/Tokyo, JP durch Patent(Patentschrift DE 2830459 C3) geschtzt.1.1 Material Description. Wrought copper-zinc-(aluminum-nickel)-cobalt-alloy (Special-brass).1.1 Werkstoffbeschreibung. Kupfer-Zink-(Alumi-nium-Nickel)-Kobalt-Knetlegierung (Son

4、dermessing).1.1.1 Material Identification. Rods, tubes, profilesand pressing parts, which can be supplied optionallyin cold or hot formed condition, see Table 1.1.1.1 Werkstoffkennzeichnung. Stangen, Rohre,Profile undPressteile, diewahlweise kalt- oder warm-geformt angeliefert werden knnen, siehe Ta

5、belle 1.Table 1: Form of Supply Tabelle 1: VerwendungsformDesignation /BezeichnungRods/Stangen QN 408300Tubes /Rohre QN 4083N0Pressing parts /Pressteile QN 4083F0Forgings /Schmiedeteile QN 4083S01.2 Cross-Reference of Replaced Specifications.Subparagraphs were not applicable.1.2 Cross-Referenz auf e

6、rsetzte Vorschriften.Unterabschnitte waren nicht anwendbar.1.3 Symbols. Not applicable. 1.3 Symbole. Nicht anwendbar.1.4 Typical Application. This alloy shall mainly beused for synchronizing rings and for such parts wherea very good wear resistance is required.1.4 Typische Anwendungen. Diese Legieru

7、ng wirdhauptschlich fr Synchronisierringe und solche Teileverwendet, von denen ein sehr gutes Verschleiver-halten verlangt wird. Copyright 2012 General Motors Company All Rights ReservedPublication Department: GME Specification CenterJuly 2012 Page 1 of 5PRD045 - VPRE ST 1 10/03 QN 408300 GM EUROPE

8、ENGINEERING STANDARDS1.5 Remarks. Deviations from the requirements ofthis specification or additional requirements are spec-ifiedintherespective componentdrawingsormaterialreleases.1.5 Bemerkungen. Abweichungen von den indieser Werkstoffvorschrift festgelegten Anforderun-gen oder zustzliche Anforder

9、ungen sind in denjeweiligen Teilezeichnungen oder Materialfreigabenvorgeschrieben.2 References 2 ReferenzenNote: Only the latest approved standards are appli-cable unless otherwise specified.Hinweis: Wenn nicht anders angegeben, ist jeweilsdieneuesteFassungder angegebenen Referenz gl-tig.2.1 Externa

10、l Standards/Specifications. 2.1 Externe Normen/Vorschriften.ISO 6506 DIN EN 10002-12.2 GM Standards/Specifications. 2.2 GM Normen/Vorschriften.GMW3001 GMW30592.3 Additional References. None. 2.3 Zustzliche Referenzen. Keine.3 Requirements 3 Anforderungen3.1 Requirements on Delivery. 3.1 Anforderunge

11、n bei Anlieferung.3.1.1 Chemical Requirements. 3.1.1 Chemische Anforderungen.3.1.1.1 ChemicalComposition (Product Analysis)in % by Mass. See Table 2.3.1.1.1 Chemische Zusammensetzung (Stck-analyse) in Massenanteile in %. Siehe Tabelle 2.Table 2: Alloying Elements Tabelle 2: LegierungsbestandteileEle

12、ment Unit /Einheit Value /WertZinc/Zink%bymass/Massenanteile in % 27.32Aluminum /Aluminium%bymass/Massenanteile in % 3.5.4.5Nickel %bymass/Massenanteile in % 2.5.4.0Cobalt /Kobalt%bymass/Massenanteile in % 1.5.2.0Silicon /Silizium%bymass/Massenanteile in % 0.5.1.5Iron/Eisen%bymass/Massenanteile in %

13、 0.5.1.3Copper /Kupfer%bymass/Massenanteile in %Remainder /Rest Copyright 2012 General Motors Company All Rights ReservedPage 2 of 5 July 2012PRD045 - VPRE ST G 10/03 GM EUROPE ENGINEERING STANDARDS QN 4083003.1.2 Mechanical Requirements. Mechanical prop-erties, see Table 3.3.1.2 Mechanische Anforde

14、rungen. MechanischeEigenschaften, siehe Tabelle 3.Table 3: Mechanical Properties Tabelle 3: Mechanische EigenschaftenProperties /EigenschaftUnits /EinheitValue /WertBrinell Hardness HB with F = 10 D2 /Brinellhrte mit F = 10 D2 HB 197.241Elongation at Break A5 transverse /Bruchdehnung A5 % 4 minTensi

15、le Strength Rm /Zugfestigkeit Rm N/mm2 635 min0.2 % Yield Strength Rp0.2 /0.2 % Streckgrenze Rp0.2 N/mm2 470 min3.1.3 Physical Requirements. Physical properties,see Table 4.3.1.3 Physikalische Anforderungen. Physikali-sche Eigenschaften, siehe Tabelle 4.Table 4: Physical Properties (Standard Values)

16、 Tabelle 4: Physikalische Eigenschaften(Richtwerte)Properties /EigenschaftUnits /UnitsValue /ValueModulus of Elasticity at +20 C/Elastizittsmodul bei +20 C kN/mm2 105Poissons Ratio /Poissonsche Zahl - 0.31Hot forming temperature /Warmarbeitstemperatur C +800.+850Melting Range /Schmelzbereich C +900.

17、+940Thermal Conductivity at (+20.+100) C/Wrmeleitfhigkeit bei (+20.+100) C W/cmK 0.84Linear Coefficient of Thermal Expansion at(+25.+100) C/Linearer Wrmeausdehnungskoeffizient bei(+25.+100) C10-6/ C 20.5Density/Dichte g/cm3 8.0 Copyright 2012 General Motors Company All Rights ReservedJuly 2012 Page

18、3 of 5PRD045 - VPRE ST U 10/03 QN 408300 GM EUROPE ENGINEERING STANDARDS3.1.4 Additional Requirements. 3.1.4 Zustzliche Anforderungen.3.1.4.1 Microstructure. The structure shall consistpredominantly of E-mixed-crystals. 30 % max. ofD-mixed crystals are permissible. The includedcobalt-precipitations

19、shall be in globulitic or compactshapes. Annealing may be necessary in order toachieve this specified structure.3.1.4.1 Mikrogefge. Das Gefge soll bewie-gend aus E-Mischkristallen bestehen. 30 % max.Anteile an D-Mischkristallen sind zulssig. Dieeingelagerten Kobaltausscheidungen mssen glo-bulitisch

20、oder kompakt ausgebildet sein. Um dieseGefgevorschrift zu gewhrleisten, ist evtl. eineGlhbehandlung erforderlich.3.1.4.2 The microstructure shall be free from oxideinclusions.3.1.4.2 Das Gefge soll frei sein von Oxideinschls-sen.3.1.4.3 For arbitration purposes the determination ofthe alloying eleme

21、nts shall be performed preferablyby wet analysis.3.1.4.3 Zur Ermittlung der Legierungsbestandteile istinSchiedsfllendienasschemische Bestimmung vor-zuziehen.3.2 Processing Requirements. Subparagraphswere not applicable.3.2 Prozessanforderungen. Unterabschnitte warennicht anwendbar.3.3 Performance Re

22、quirements. Subparagraphswere not applicable.3.3 Gebrauchsanforderungen. Unterabschnittewaren nicht anwendbar.3.4 Requirements on other Stages during LifeCycle. Subparagraphs were not applicable.3.4 Anforderungen an andere Zustnde whrenddes Lebenszyklus. Unterabschnitte waren nichtanwendbar.4 Manufa

23、cturing Process 4 Herstellungsprozess4.1 Post-treatments. Post-treatments(ifperformed)shall be free of hexavalent chromium.4.1 Nachbehandlungen. Falls Nachbehandlungendurchgefhrtwerden,mssendiesefreivonChromVIsein.4.2 Tests. 4.2 Prfungen.4.2.1 All tests shall be performed at (+23 5) C. 4.2.1 Alle Pr

24、fungen sind bei (+23 5) C durchzu-fhren.4.2.2 4.2.2Tensile test according to DIN EN 10002-1. Zugprfung nach DIN EN 10002-1.Brinell hardness shall be determined according toISO 6506.Ermittlung der Brinellhrte nach ISO 6506.5 Rules and Regulations 5 Gesetze und Vorschriften5.1 All materials supplied t

25、o this specification mustcomply with the requirements of GMW3001, Rulesand Regulations for Material Specifications.5.1 Alle Werkstoffe, die nach dieser Spezifikationgeliefert werden, mssen die Anforderungen derGMW3001, Gesetze und Vorschriften fr Werk-stoffvorschriften, erfllen.5.1.1 Language. Devia

26、ting from GMW3001, para-graph 5.2 (Language):5.1.1 Sprache. Abweichend von GMW3001,Abschnitt 5.2 (Sprache): Copyright 2012 General Motors Company All Rights ReservedPage 4 of 5 July 2012PRD045 - VPRE ST G 10/03 GM EUROPE ENGINEERING STANDARDS QN 408300In the event of any conflict between the English

27、 andGerman language regarding this document, the Ger-man language will take precedence.Im Falle von Unstimmigkeiten zwischen demeng-lischen und dem deutschen Text, ist der deut-sche Text ausschlaggebend.5.2 All materials supplied to this specificationmust comply with the requirements of GMW3059,Rest

28、ricted and Reportable Substances for Parts.5.2 Alle Werkstoffe, die nach dieser Spezifikationgeliefert werden, mssen die Anforderungen derGMW3059, Regelung ber die Zulssigkeit vongefhrlichen Stoffen, erfllen.6 Approved Sources 6 Zugelassene LieferantenNot applicable. Nicht anwendbar.7 Coding System

29、7 Angabe in DokumentenThis material specification shall be called up in otherdocuments, drawings, VTS, CTS etc. as follows:Diese Werkstoffvorschrift ist in anderen Doku-men-ten, Zeichnungen, VTS, CTS etc. wie folgt anzuge-ben:Example: Beispiel:“Requirements to QN 408300” “Anforderungen nach QN 40830

30、0”8 Release and Revisions 8 Freigabe und nderungen8.1 Release. This specification was first approvedand released in JUN 1986.8.1 Freigabe. Diese Vorschrift wurde erstmaliggenehmigt und freigegeben im JUN 1986.8.2 Revisions. 8.2 nderungen.Rev. Date /DatumDescription (Org.) /Beschreibung (Org.)4 OCT 1

31、989 Was Issue no. 3, Date of Issue 04/88 / completely new written with changes / Noteadded / permissible impurities deleted: Cobalt was 1.0.2.0 (TDC Central Laborato-ries)/war Ausfertigung Nr. 3, Datum 4/88 / Zulssige Beimengungen entfernt, Kobalt war1.0.2.0 / Hinweis zugefgt / neu geschrieben mit n

32、derungen (TEZ Zentrallabor)5 JAN 2002 Was Issue no. 4, Date of Issue 10/89 / reworked with new structure and layout / noteof hexavalent chromium absence added (ITDC Central Laboratories) /war Ausfertigung Nr. 4, Datum 10/89 / berarbeitet mit neuer Struktur und neuemLayout / Hinweis auf Chrom VI-Frei

33、heit zugefgt (ITEZ Zentrallabor)6 JUL 2012 Limited Use Status (GME Test Labs & Materials/Corrosion/Fastening Engineering) /Limited Use Status (GME Test Labs & Materials/Corrosion/Fastening Engineering) Copyright 2012 General Motors Company All Rights ReservedJuly 2012 Page 5 of 5PRD045 - VPRE ST U 10/03