GME QK 000135-2014 Polyamid 66 heat stabilized (Issue 5 English German This standard may be applied only for current programs It is inactive for all future projects and without rep n.pdf

《GME QK 000135-2014 Polyamid 66 heat stabilized (Issue 5 English German This standard may be applied only for current programs It is inactive for all future projects and without rep n.pdf》由会员分享，可在线阅读，更多相关《GME QK 000135-2014 Polyamid 66 heat stabilized (Issue 5 English German This standard may be applied only for current programs It is inactive for all future projects and without rep n.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、ADAM OPEL AGTDCCentral LaboratoriesTECHN. LIEFERBEDINGUNGENFR WERKSTOFFEENGINEERINGMATERIAL SPECIFICATIONLIMITED USEQK 000135Polyamid 66, wrmestabilisiertPolyamid 66, heat stabilizedWerkstoff: Polyamid 66 mit 35 Massenanteil in % Glasfasern verstrkt, wrmestabilisiertMaterial: Polyamid 66 reinforced

2、with 35 % by mass glass fibres, heat stabilizedKurzzeichen: PA66-GF35 Symbol:Verwendung: Spritzgietype zur Herstellung technischer Teile mit hoher Festigkeit und guterDimensionsstabilitt, auch unter dauernder Wrmeeinwirkung.Application: Injection moulding type for manufacturing technical parts, requ

3、iring very highstrength and good dimensional stability, also under continued heat influence.Handelsname: Ultramid A3WG7Trade Name:Lieferant: BASF AGSupplier: D - 67056 LudwigshafenLieferform: GranulatForm of Delivery: GranulesAusfertigungs-Nr.:Issue: 5Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehm

4、igt:Approved: MKSeite vonPage 1 of 4Unbeschadet etwaiger durch den Abnehmer erfolgenden Stichprobenprfungen trgt der Lieferant die Verantwortung dafr, da die gelieferteWare die Opel-Zeichnungsvorschriften erfllt. Ein Prfbericht mit zahlenmigen Ergebnissen aus Prfungen der Lieferung selbst ist bei je

5、derBemusterung, Erstbelieferung und Ausfhrungsnderung mitzugeben.Despite spot checks possibly performed by Opel, it is the suppliers responsibility that the delivered parts are in line with the Opel drawings.Deliveries of samples, first off-tool parts and parts, whose performance has been changed, m

6、ust be accompanied by a test report showing thetest results in terms of figures.LBSP TL WS 1 11/95Note: This standard may be applied only for current programs. It is inactive for all future projectsand without replacement.If this product should be used for a new project, a Re-Certification according

7、 to GMW15702 is re-quired.Hinweis: Diese Spezifikation darf nur noch fr laufende Projekte angewendet werden und ist fr allezuknftigen Projekte ohne Ersatz ungltig.Falls dieses Produkt fr ein neues Projekt zum Einsatz kommen soll, ist eine Neu-Zertifizierung nachGMW15702 erforderlich.LIMITED USE QK 0

8、00135Ausfertigungs-Nr.:Issue: 5Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 2 of 4Forderungen / Requirementsa) zu dokumentierende Eigenschaften / values for documentationEigenschaftenPropertiesMittelwertAverage ValueStandardab-weichungStandardDeviationEinheitUnitNorm

9、StandardDichteDensity 1,41 0,01 g/cm3ISO 1183GlhrckstandAsh 35 0,6Massenanteilin % /% by massISO 3451(bei/at +950C)ZugmodulTensile Modulus 11841 486 N/mm2ISO 527BruchspannungStress at Break 213 6,0 N/mm2ISO 527Charpy KerbschlagzhigkeitCharpy Notched Impact Strengthbei/at +23C 14,5 0,9 kJ/m2ISO 179 /

10、 1eAFormbestndigkeitstemperaturTemperature of Deflection underLoadVerfahren/Method A 248 3,0 CISO 75-2b) nur zur Information / only for informationEigenschaftenPropertiesMittelwertAverage ValueEinheitUnitNormStandardSchmelzevolumenrateMelt Volume Flow RateMVR 275/5 32 cm3/10 minISO 1133BruchdehnungS

11、train at Break 3,3 %ISO 527Charpy SchlagzhigkeitCharpy Impact Strengthbei/at +23C 99 kJ/m2ISO 179 / 1eUSchmelztemperaturMelting temperature 260 CISO 3146Koeffizient der linearen Wrmeaus-dehnungCoefficient of Linear Thermal Expan-sionlngs / longitudinal (+23 . +80C)quer / transverse (+23 . +80C)1,756

12、,5 10-5 1/K10-5 1/KDIN 53752DielektrizittszahlDielectric Number1 MHz 3,5DIN IEC 250Dielektrischer VerlustfaktorDielectric Dissapation Factor1 MHz 0,02DIN IEC 250Spez. DurchgangswiderstandVolume Resistivity 1015 :cmDIN IEC 93LIMITED USE QK 000135Ausfertigungs-Nr.:Issue: 5Datum:Date: 10/14Ausgefertigt

13、:Prepared: JKGenehmigt:Approved: MKSeite vonPage 3 of 4EigenschaftenPropertiesMittelwertAverage Va-lueEinheitUnitNormStandardSpez. OberflchenwiderstandSurface Resistivity 1012 :DIN IEC 93Vergleichszahl der KriechwegbildungComparative Tracking IndexCTI 450DIN IEC 112ViskosittszahlViscosity Number 136

14、 cm3/gISO 307Hinweis / ReferenceWeitere Informationen siehe QK 000000. /For further information refer to QK 000000.Bemerkung / NoteAlle Probekrper werden im Spritzgieverfahren hergestellt. Alle Werte werden an spritztrockenen Pro-bekrpern ermittelt (spritztrocken = Wassergehalt 0,2 Massenanteil in %

15、). Teile aus dieser Werkstoff-qualitt mssen bei Anlieferung einen Wassergehalt von mindestens 1,0 Massenanteil in % aufweisen(Prfung nach GMI 60270). Abweichungen hiervon werden auf der Teilzeichung besonders angegeben./All test pieces shall be manufactured by injection moulding. All values shall be

16、 determined on dry asmoulded test pieces (dry as moulded = water content 0,2 % by mass). Parts of this material qualitymust have a water content of at least 1,0 % by mass at delivery (test to GMI 60270). Deviations fromthis shall be specifically indicated in the part drawing.Abfallbeseitigung / Wast

17、e DisposalGruppe D, Opel-Betriebsrichtlinie Nr. 440 /Achtung! Bei unkontrollierter thermischer Zersetzung Bildung von giftigen Abbauprodukten. /Group D, Opel-Plant Directive No. 440Attention! Uncontrolled thermal decomposition gives poisonous decomposition products.LIMITED USE QK 000135LBSP TL 3 11/

18、9522.10.14 Limited Use Status08.09.98 War Ausfertigungs-Nr. 3, Datum 02/86Englische bersetzung zugefgtNach Herstellerangaben entsprechend QK 000000 berarbeitetWas Issue no. 3, date 02/86English translation addedReworked to suppliers information according to QK 00000006.02.86 War Ausfertigungs-Nr. 2,

19、 Datum 09/83Inhalt vollstndig berarbeitet, neu geschriebenWas Issue No. 2, date 09/83Content reworked, rewrittenDatumDateBeschreibung / Description GeprftCheckedGenehmigtAppd.nderungen / RevisionsAusfertigungs-Nr.:Issue: 5Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 4 of 4