FORD WSS-M99C127-A1-2009 ADDITIVE CERIUM IRON BASED FOR USE WITH DIESEL PARTICULATE FILTERS 6 5% CERIUM IRON CONCENTRATION TO BE USED WITH FORD WSS-M99P1111-A 《柴油机微粒过滤器用铈 铁浓度6 5%.pdf

《FORD WSS-M99C127-A1-2009 ADDITIVE CERIUM IRON BASED FOR USE WITH DIESEL PARTICULATE FILTERS 6 5% CERIUM IRON CONCENTRATION TO BE USED WITH FORD WSS-M99P1111-A 《柴油机微粒过滤器用铈 铁浓度6 5%.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M99C127-A1-2009 ADDITIVE CERIUM IRON BASED FOR USE WITH DIESEL PARTICULATE FILTERS 6 5% CERIUM IRON CONCENTRATION TO BE USED WITH FORD WSS-M99P1111-A 《柴油机微粒过滤器用铈 铁浓度6 5%.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 11 18 N-STATUS No known use. No replacement named D. DiGregorio, NA 2004 10 28 Revised A3 added, para 3.2.5, 3.2.6 Ce/Fe ratio, water and particulate limits added; para 3.2.1, 3.2.2, 3.2.3 & 3.2.4 revised J.Bennett 2002 07 25 Activated J.

2、 Bennett Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 3 ADDITIVE, CERIUM/IRON BASED FOR USE WITH DIESEL PARTICULATE FILTERS 6.5% CERIUM/IRON CONCENTRATION WSS-M99C127-A1 8.0% CERIUM/IRON CONCENTRATION WSS-M99C127-A2 6.5% CERIUM/IRON CONCENTRATION WSS-M99C12

3、7-A3 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a cerium and iron based automotive diesel fuel additive to be used in association with the fitment of diesel particulate filter after treatment systems. 2. APPLICATION These specifications were released origi

4、nally for materials used for initial fill. This material is also suitable for service use. The material is intended for on-board vehicle dosing systems. 3. REQUIREMENTS 3.0 QUALITY SYSTEM REQUIREMENTS Material suppliers and part producers must conform to the Companys Standard Requirements for Produc

5、tion Materials (WSS-M99P1111-A). 3.2 PHYSICAL/CHEMICAL PROPERTIES 3.2.1 Density 20 C (ASTM D 1122) A1 847 kg/m3A2 867 kg/m3 A3 847 kg/m3 3.2.2 Viscosity 25 C (ASTM D 445) A1 2.8 mm2/s A2 3.1 mm2/s A3 2.6 mm2/s 3.2.3 Cerium/Iron Concentration A1 6.50 wt.% A2 8.00 wt.% A3 6.50 wt.% 3.2.4 Cerium/Iron r

6、atio 2.53 3.2.5 Flash Point, min 55 C (ASTM D 93) ENGINEERING MATERIAL SPECIFICATIONWSS-M99C127-A3 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 3 3.2.6 Water content, max (ASTM D 4377-00e1) A1 0.2000 wt.% A2 0.2500 wt.% A3 0.2500 wt.% 3.2.7 Particulate matt

7、er, max 6 (NF L 41 101/102) 3.3 COLOR The material may be dyed in accordance with supplier standard practice to a color agreed with Ford Motor Company. 3.4 VERIFICATION The affected Materials Engineering activity reserves the right to conduct verification testing. If the test results do not support

8、the originally submitted data, the supplier must re-test the product in coordination with the affected Materials Engineering activity. This re-test must be conducted and certified by a mutually agreed upon test facility. 3.5 CHEMICAL AND PHYSICAL PROPERTIES Supplier shall furnish appropriate chemica

9、l and physical properties as required on Supplement A along with the manufacturing limits that apply to the material upon which approval is requested. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications.

10、5.1 FLAMMABILITY This material represents a potential fire hazard. The Manufacturing Engineering Department or other responsible activity shall notify both the Security and Safety Units of its presence to assure that proper fire precautions are provided. The location in which it is used or stored sh

11、all be included in the notifications. 5.2 SAMPLING AND SUBMISSION OF SAMPLES (ISO 3170/3171, ASTM D 4057/D 4177) Quality Control records must be made available to Fuels and Lubricants Engineering upon request. Where applicable, the required tests shall be conducted in accordance with the most recent

12、ly approved procedures and the applicable ASTM Standards, Research Reports and Information. All tests under surveillance by ASTM must be conducted using test equipment monitored by and calibrated to the requirements of the ASTM Test Monitoring Center. ENGINEERING MATERIAL SPECIFICATIONWSS-M99C127-A3

13、 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 (Supplement A, p. 1 of 1) Manufacturer_ Date_ Product Name_ Blend Location _ Product Code_ Specification Test Mfg. Physical/Chemical Properties Requirements Results Limits Density at 20 C (ASTM D 1122), kg/m3A

14、1 (6.5% cerium/iron) 820 880 _ _ A2 (8.0% cerium/iron) 840 900 _ _ A3 (6.5% cerium/iron) 820 880 _ _ Viscosity at 25 C (ASTM D 445), mm2/s A1 (6.5% cerium/iron) 2.6 3.0 _ _ A2 (8.0% cerium/iron) 2.9 3.3 _ _ A3 (6.5% cerium/iron) 2.4 2.8 _ _ Cerium/Iron concn. (ISO 14596/ISO 24260), wt.% A1 (6.5% cer

15、ium/iron) 6.2 6.8 _ _ A2 (8.0% cerium/iron) 7.7 8.3 _ _ A3 (6.5% cerium/iron) 6.2 6.8 _ _ Cerium/Iron ratio (ISO 14596/ISO 24260), wt. 1.70 3.35 _ _ Flash Point (ASTM D 93-99c), C min 55 _ _ Water Content (ASTM D 4377-00e1), wt.%, max A1 (6.5% cerium/iron) 0.2000 max _ _ A2 (8.0% cerium/iron) 0.2000 max _ _ A3 (6.5% cerium/iron) 0.2500 max _ _ Particulate matter (NF L 41 101/102) 6 max _ _ Signature_ Title_