FORD WSS-M7G8-A-2011 LABEL INTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《标签的内部质量 与福特WSS-M99P1111-A 一起使用[使用 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P.pdf

《FORD WSS-M7G8-A-2011 LABEL INTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《标签的内部质量 与福特WSS-M99P1111-A 一起使用[使用 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M7G8-A-2011 LABEL INTERIOR QUALITY TO BE USED WITH FORD WSS-M99P1111-A 《标签的内部质量 与福特WSS-M99P1111-A 一起使用[使用 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P41-A10 福特WSS-M99P.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Changes 2011 09 08 N Status Replaced by WSS-M99P41-A10/A72 G. Eaton, NA 1996 08 26 Activated L. Koth WP 3948-a Page 1 of 7 LABEL, INTERIOR QUALITY WSS-M7G8-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined

2、 by this specification is a voluntary label that is not subject to governmental regulations regarding permanence or removability. 2. APPLICATION This specification was released originally for labels applied to instrument panel substrates to indicate that a rear facing child seat should not be used i

3、n the front seating position of the vehicle due to the presence of a passenger airbag. The label is appropriate for vehicles equipped with a passenger airbag and not equipped with a passenger airbag deactivation (PAD) switch. Peel-and-Stick labels and hot stamp labels comply with the specification.

4、Note: The peel-and-stick labels may be removed intact. 3. REQUIREMENTS 3.1 QUALITY SYSTEM REQUIREMENTS Material suppliers and part producers must conform to Quality System Requirements, QS-9000. Material specification requirements are to be used for initial qualification of materials. A Control Plan

5、 for ongoing production verification is required. This plan must be reviewed and approved by the relevant Ford Materials activity and/or Ford Supplier Technical Assistance (STA) prior to production parts submission. Appropriate statistical tools must be used to analyze process/product data and assur

6、e consistent processing of the materials. Part producers using this material in their products, must use Ford approved materials and must conform to a process control plan which has been approved by STA and/or the relevant Materials Activity. 3.2 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSIS Fo

7、rd Motor Company, at its option, may conduct infrared and/or thermal analysis of material/parts supplied to this specification. The IR spectra and thermograms established for initial approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All

8、 samples shall produce IR spectra and thermograms that correspond to the reference standard when tested under the same conditions. ENGINEERING MATERIAL SPECIFICATION WSS-M7G8-A WP 3948-b Page 2 of 7 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material condition

9、ed in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. For samples subjected to specified conditioning environments other than 23 C and 50 % R.H., tests shall be completed w

10、ithin 4 h after removal from the conditioning environment, unless otherwise noted. All tests shall be performed on labels bonded to the appropriate substrate, unless otherwise noted. 3.4 APPEARANCE The bonded labels shall be free of streaks, blisters, wrinkles, ragged edges and any other surface imp

11、erfections which will make them unsuitable for the intended usage. The design and color shall be specified on the engineering drawing. 3.5 PREPARATION OF TEST SPECIMENS 3.5.1 Substrate Typical substrates include A.B.S (WSB-M4D690-A), poly-carbonate (WSB-M4D627-A), polypropylene (WSB-M4D841-A), PVC c

12、ast skin (WSB-M98D22-B), and PVC laminate (WSB-M98D18-B2). All substrate/label combinations are approved separately. Use all substrates appropriate to the requested approval. 3.5.2 Substrate Preparation To ensure that all test specimens are free of mold release agents, fingerprints, oils, dirt and a

13、ny other detrimental surface contamination, substrates may be wiped with IPA (50 % v/v) prior to label application. 3.5.3 Application Process The application of the labels to all test specimens shall be accomplished in a production representative fashion. The application parameters shall be document

14、ed and submitted as part of the total data package. ENGINEERING MATERIAL SPECIFICATION WSS-M7G8-A WP 3948-b Page 3 of 7 3.6 RESISTANCE PROPERTIES (Label Bonded to Substrate) GENERAL REQUIREMENTS: After each of the resistance properties exposures, the label must not show evidence of delamination, los

15、s of printing or legibility, overall staining, loss of adhesion, curling of edges, blistering, checking, cracking, or any other effect which would detract from its proper function or appearance. Substrate degradation/distortion will be evaluated separately and is not cause for rejection of the label

16、 provided there is no label delamination or loss of legibility. Note: Legibility to be judged at a viewing distance of approximately 450 mm. 3.6.1 Humidity Resistance 7 days at 38 +/- 1 C and 95 - 100 % relative humidity. 3.6.2 Environmental Cycling Resistance 10 cycles, each cycle shall consist of

17、the following: . 4 h at 90 +/- 2 C . 4 h at 38 +/- 1 C and 95 - 100 % R.H. . 16 h at - 40 +/- 1 C 3.6.3 Resistance to Heat Aging, min Rating 4 (7 days at 100 +/- 2 C, AATCC Evaluation Procedure 1) 3.6.4 Heat Resistance (30 minutes at 120 +/- 2 C) Shall withstand a simulated paint repair bake. 3.6.5

18、Resistance to Fade, min 3.6.5.1 Xenon Arc Weatherometer (SAE J1885, AATCC Evaluation Procedure 1) 225.6 kJ/m2 Rating 4 488.8 kJ/m2 Rating 3 3.6.6 Crocking Rating 4 - 5 Wet and Dry, min (FLTM BN 107-01, using AATCC Evaluating Procedure 3) 3.6.7 Migration Staining None (FLTM BN 103-01) No evidence of

19、injurious exudation, adhesion (tackiness), separation or color transfer when placed face to face with the standard white vinyl test material (M1F Series.) ENGINEERING MATERIAL SPECIFICATION WSS-M7G8-A WP 3948-b Page 4 of 7 3.6.8 Abrasion Resistance, min 100 cycles (FLTM BN 108-02, CS-10 wheels, 1000

20、 g load) No visible substrate or loss of legibility. 3.6.9 Resistance to Scuffing 100 cycles (FLTM BN 108-04, 0.9 kg load, A head) No loss of legibility. No edge lifting. 3.6.10 Soiling, max 20 % (FLTM BN 112-01) Test method for rigid substrates: Cut a 57 mm diameter test specimen from the label/sub

21、strate area. Specimen should be stapled or adhesively bonded to the center of a flexible substrate* for mounting in the Stoll test machine. *Polyvinyl chloride (PVC) coated fabric or No. 10 cotton duck is recommended. 3.6.11 Removal Resistance No Removal Test Solutions: . Mild Soap and Water Solutio

22、n . Unleaded Fuel . Isopropyl Alcohol (50/50 mixture with deionized water) Test Method: Prepare a separate specimen for each fluid. Wipe test specimens 10 to 15 times with each test fluid. 3.6.12 Cold Flexibility (Flexible Substrates Only) (FLTM BN 102-01, for flexible materials) Original (As Receiv

23、ed) - 40 +/- 1 C After 7 days at 80 +/- 2C - 35 +/- 1 C Shall remain flexible and exhibit no delamination when bent around a 6.4 mm mandrel (label side up) after exposure. 3.7 FLAMMABILITY, max 100 mm/minute (SAE J369/ISO 3795) Tests shall be conducted with the label 100 % bonded to the substrate to

24、 form a material composite. 3.8 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 1 h) Fog Number, min 60 Formation of clear film, droplets or crystals is cause for rejection. Note: Test to be run on the film by itself. ENGINEERING MATERIAL SPECIFICATION WSS-M7G8-A

25、 WP 3948-b Page 5 of 7 3.9 ODOR, max Rating 2 (SAE J1351) Note: Test to be run on the film by itself. 3.10 LABEL ADHESION No label delamination or loss of (FLTM BI 106-01, Part “B“ legibility omit scribe lines) Test Method: Place a strip of 3M #898 25 mm wide tape along the entire bottom edge of the

26、 label with 16 +/- 2 mm of the tape width to be on the label. Apply the tape with moderate thumb pressure to the label and substrate. Remove the tape by pulling one end at a 90 degree angle with a quick snap. The label/substrate composites shall meet the label adhesion requirements as received and a

27、fter the environmental conditioning defined below. Samples must be tested between 1 and 4 hours after removal from exposure conditions unless otherwise noted. . Original . Heat Aging 7 days at 100 +/- 2 C 14 days at 100 +/- 2 C . Humidity 14 days at 38 +/- 1 C and 95 % relative humidity . Cycle Test

28、 (10 cycles) Each cycle shall consist of the following: . 4 h at 90 +/- 2 C . 4 h at 38 +/- 1 C and 95 - 100 % relative humidity . 16 h at - 40 +/- 1 C . Resistance to Fade, min 488.8 kJ/m2 (SAE J1885) 3.11 FINISHED PARTS 3.11.1 Quality The quality required is that obtainable with the best commercia

29、l practice. 3.11.1.1 Cleanliness All substrates to be covered by the film shall be clean in keeping with good commercial practice. Oil, grease, dust, and other foreign materials which would affect the adhesion of the film shall be removed prior to material application. ENGINEERING MATERIAL SPECIFICA

30、TION WSS-M7G8-A WP 3948-b Page 6 of 7 3.11.1.2 Appearance Parts shall match master samples approved by Design Center and initial samples approved by Quality Control for: . Color and Uniformity . Smoothness (absence of blisters) . Absence of scratches and tool marks 3.12 ADDITIONAL REQUIREMENTS Speci

31、fic requirements for material and/or manufactured parts shall be specified on the Engineering drawing, Engineering parts specification and/or performance specification. All critical areas with respect to these properties shall be clearly designated on the engineering drawing. 3.13 FUNCTIONAL APPROVA

32、L Materials being evaluated for approval to this specification shall be subjected to a production trial. Functional trial results must be approved by the affected assembly operation and Design Engineering. Results shall be made available to Materials Engineering prior to material approval and releas

33、e. 3.14 SUPPLIERS RESPONSIBILITY All materials supplied to this specification must be equivalent in all characteristics to the material upon which approval was originally granted. Prior to making any change in the properties, composition, construction, color, processing or labeling of the material o

34、riginally approved under this specification, whether or not such changes affect the materials ability to meet the specification requirements, the Supplier shall notify Purchasing, Toxicology and the affected Materials Engineering activity of the proposed changes and obtain the written approval of th

35、e Materials Engineering activity. Test data, test samples and a new code identification are to be submitted with the request. Substance restrictions imposed by law, regulations or Ford, apply to the materials addressed by this document. The restrictions are defined in Engineering Materials Specifica

36、tion WSS-M99P9999-A1. ENGINEERING MATERIAL SPECIFICATION WSS-M7G8-A WP 3948-b Page 7 of 7 4. APPROVAL OF MATERIALS Materials defined by this specification must have prior approval by the responsible Materials Engineering activity. Suppliers desiring approval of their materials shall first obtain an

37、expression of interest from the affected Purchasing, Design and Materials Engineering activity. Upon request, the Supplier shall submit to the affected Materials Engineering activity a completed copy of their laboratory test reports, signed by a qualified and authorized representative of the test fa

38、cility, demonstrating full compliance with all the requirements of this specification (test results, not nominal values), the material designation and code number, and test specimens for Ford evaluation. Fords engineering approval of a material will be based on its performance to this specification and on an assessment of suitability for intended processes and/or applications. Upon approval, the material will be added to the Engineering Material Approved Source List.