FORD WSS-M4D1005-B2-2018 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) HIGH MELT FLOW LOW DENSITY 17% MINERAL FILLED FULLY PAINTED ONLY MOLDING COMPOUND FASCIA THIN-WALLED EXTERIOR T.pdf

《FORD WSS-M4D1005-B2-2018 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) HIGH MELT FLOW LOW DENSITY 17% MINERAL FILLED FULLY PAINTED ONLY MOLDING COMPOUND FASCIA THIN-WALLED EXTERIOR T.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M4D1005-B2-2018 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) HIGH MELT FLOW LOW DENSITY 17% MINERAL FILLED FULLY PAINTED ONLY MOLDING COMPOUND FASCIA THIN-WALLED EXTERIOR T.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 2 2018 05 08 Editorial See Summary of Revisions G. Eaton, NA 2015 12 15 Editorial See Summary of Revisions K. Mueller, NA 2015 07 31 Released K.Mueller, FNA Controlled document at www.MATS Copyright 2018, Ford Global Technologies, LLC Pa

2、ge 1 of 11 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO), WSS-M4D1005-B1 HIGH MELT FLOW, LOW DENSITY, TPO-(PP+EPDM)-MD17 Table 1: Minimum Sample Size Initial Approval and/or Initial Approval in new region Additional Manufacturing Location for Previously Approved Material in Region Test Minimum Lots Speci

3、mens per lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1WSS-M99P1111-A, WSS-M98P13-E/latest or WSS-M2P181-C/Latest, Material retain for 6 months, Control Plan or CoA testing Reference Performance Specification 3.1.8 Thermoplastic Property Determination For CAE WSS-M99D68-A1

4、Reference WSS-M99D68-A1 3.3.1 Weathering Resistance (unpainted) 1 1 1 3.3.2 1 and 3 year Florida (unpainted) 1 1 1 3.3.3 Resistance to Scratch and Mar (unpainted) 1 3 3 3.3.4 Resistance to Water and Soap Spotting 1 3 3 3.4.1 Melt Flow Rate* 3 1 3 1 1 1 3.4.2 Filler Content* 3 1 3 1 1 1 3.4.3 Density

5、 1 3 3 3.4.4 Hardness, Durometer D 1 5 measurements 1 3.4.5 Tensile Strength at Yield* 3 5 15 1 5 5 3.4.6 Tensile Modulus 1 10 10 3.4.7 Impact Strength, Notched Charpy (per condition)* 3 10 30 1 10 10 3.4.8 Flexural Modulus* 3 10 30 1 10 10 3.4.9 Heat Deflection Temperature* 3 2 6 1 2 2 3.4.10 Heat

6、Aging Performance 3.4.10.1 Tensile Strength at Yield, Change 1 5 5 3.4.10.2 Impact Strength, Notched Izod, Change 1 10 10 3.4.11 Impact Strength, Multiaxial (per condition)* 3 10 30 1 10 10 3.4.12 Coefficient of Linear Thermal 1 3 3 ENGINEERING MATERIAL SPECIFICATION WSS-M4D1005-B1 WSS-M4D1005-B2 Co

7、ntrolled document at www.MATS Copyright 2018, Ford Global Technologies, LLC Page 11 of 11 Expansion (per condition) 3.4.13 Flammability 1 5 5 3.4.14.1 Mold Shrinkage 1 5 5 1 5 5 3.4.14.2 Post Shrinkage (per condition) 1 5 5 1 5 5 3.5.1 Paintability Test per WSS-M2P181-C/Latest Test per location 3.6.

8、1 SLIDO 1 3 3 1 3 3 3.6.2 Impact Strength Notched Izod (per condition) 1 10 10 3.6.3 Melt Temperature 3 1 3 3.6.4 Poissons Ratio 1 5 5 3.6.5 Curves - IR - TGA - DSC (first and second heat) - CLTE (3 flow and 3 cross flow) - Stress/Strain Curves 1 1 1 per test * For these requirements, the 3 Sigma va

9、lue from the raw data is used to meet the requirement. Table 2: Minimum Color Property Testing (WSS-M4D1005-B1 only) 5. SUMMARY OF REVISIONS 2018 05 08 Editorial - Corrected location of X-flow requirement in section 3.4.12 2015 12 15 Editorial Corrected typos in 3.4.10.2 and 4.5. Para. Test Method L

10、ots Specimens per Lot Total Test Specimens Color Test Direction 3.3.1 Weathering Resistance 1 1 1 Every color 3.3.3 Resistance to Scratch and Mar 1 3 3 As directed by Materials Engineering 3.4.5 Tensile Strength at Yield 1 5 5 As directed by Materials Engineering 3.4.7.1 Impact Strength, Notched Charpy at 23 +/- 2 C 1 10 10 As directed by Materials Engineering 3.4.8 Flexural Modulus 1 10 10 As directed by Materials Engineering