FORD WSS-M1H710-C1-2003 FABRIC DUNE II PATTERN WEFT KNITTED 3 MM TO BE USED WITH FORD WSS-M99P1111-A (Shown on WSS-M1H710-A)《DUNE II图案的3毫米厚纬编针织织物 与标准FORD WSS-M99P1111-A一起使用 列于标.pdf

《FORD WSS-M1H710-C1-2003 FABRIC DUNE II PATTERN WEFT KNITTED 3 MM TO BE USED WITH FORD WSS-M99P1111-A (Shown on WSS-M1H710-A)《DUNE II图案的3毫米厚纬编针织织物 与标准FORD WSS-M99P1111-A一起使用 列于标.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H710-C1-2003 FABRIC DUNE II PATTERN WEFT KNITTED 3 MM TO BE USED WITH FORD WSS-M99P1111-A (Shown on WSS-M1H710-A)《DUNE II图案的3毫米厚纬编针织织物 与标准FORD WSS-M99P1111-A一起使用 列于标.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 03 19 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.14, 3.15, 4 deleted 1998 04 28 Revised Revised para 3.2, 3.4, 3.6, 3.12 N.J. Komatsu 1996 04 22 Activated N.J. Komatsu Printed copies are uncontro

2、lled Page 1 of 4 Copyright 2003, Ford Global Technologies, Inc. FABRIC, DUNE II PATTERN, WEFT KNITTED, WSS-M1H710-A UNLAMINATED FABRIC, DUNE II PATTERN, WEFT KNITTED, 3 mm WSS-M1H710-B1 FABRIC, DUNE II PATTERN, WEFT KNITTED, 6 mm WSS-M1H710-B2 FABRIC, DUNE II PATTERN, WEFT KNITTED, 3 mm WSS-M1H710-C

3、1 FABRIC, DUNE II PATTERN, WEFT KNITTED, 6 mm WSS-M1H710-C2 FABRIC, DUNE II PATTERN, WEFT KNITTED, 6 mm WSS-M1H710-D2 1. SCOPE The material defined by these specifications is a weft knitted Jacquard 19 gage polyester velour fabric which can be flame laminated to polyester or polyether urethane foam

4、and backed with a knitted fabric. It can also be backed with an HFW weldable backcoating. 2 APPLICATION WSS-M1H710-A is used for modular headrests and also adhesive coated for use on inner door panels. WSS-M1H710-B1, B2, C1, C2, are used for seat wearing surfaces. WSS-M1H710-D2, is used adhesive for

5、 bonded door, quarter trim panel applications. DUNE PATTERN WSS-M1H710-A Unlaminated WSS-M1H710-B1 3.0 mm, flame laminated to polyether foam and knitted fabric WSS-M1H710-B2 6.0 mm , flame laminated to polyether foam and knitted fabric WSS-M1H710-C1 3.0 mm, flame laminated to polyester foam and knit

6、ted fabric WSS-M1H710-C2 6.0 mm , flame laminated to polyester foam and knitted fabric WSS-M1H710-D2 6.0 mm, flame laminated to polyether foam. ENGINEERING MATERIAL SPECIFICATION WSS-M1H710-A/B1/B2/C1/C2/D2 Page 2 of 4 Copyright 2003, Ford Global Technologies, Inc. 3. REQUIREMENTS In addition to the

7、 requirements listed herein, the fabric or laminate shall meet all requirements of WSB-M8P1-I. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTIO

8、N 3.4.1 Fabric Count, +/- 7 % tolerance (ASTM D 3887) (D2) Wales 106 wales/10 cm Courses 133 courses/10cm 3.4.2 Fabric Count, +/- 7 % tolerance (ASTM D 3887)(A, B1, B2, C1, C2) Wales 106 wales/10cm Courses 124 courses/10cm 3.4.3 Fabric Weight, range (D2) 335 - 385 g/m2(FLTM BN 106-01) (A, B1, B2, C1

9、, C2) 298 - 342 g/m23.4.4 Pile Height, min 1.7 mm (Microscope technique) 3.5 COMPOSITION (ASTM D 629) Fabric 100 % polyester 3.6 YARN CONSTRUCTION (ASTM D 1244) (D2) 3.6.1 Ground 240 dtex f48 (Polyester semi-dul dyed yarn) Pile 245 dtex f72 (Polyester, semi-dull, 2x110/36 comingled yarn) (A, B1, B2,

10、 C1, C2) 3.6.2 Ground 167 dtex f32 (Polyester semi-dul dyed yarn) ENGINEERING MATERIAL SPECIFICATION WSS-M1H710-A/B1/B2/C1/C2/D2 Page 3 of 4 Copyright 2003, Ford Global Technologies, Inc. Pile 245 dtex f72 (Polyester, semi-dul, 2x110/36 comingled yarn) *Ground construction based on a knitted jersey.

11、 3.7 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.8 FINISHING OPERATIONS As approved by Materials Engineering 3.9 REQUIREMENTS FOR POLYESTER FOAM As specified in WSD-M2D243-A4 3.10 REQUIREMENTS FOR POLYETHER FOAM As specified in WSD-M2D243-A2 3.11 REQUIREMENTS FOR THE BACKING

12、 As specified in FABRIC WSD-M9H134-B or an Engineering approved alternative 3.12 REQUIREMENTS FOR THE FLAME LAMINATED MATERIAL (WSD-M1H670-B1, B2, C1, C2, D2) 3.12.1 Thickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g force, 43 Pa pressure) WSS-M1H710-B1 3.0 +/- 1.0 mm WSS-M1H71

13、0-B2 6.0 +/- 1.0 mm WSS-M1H710-C1 3.0 +/- 1.0 mm WSS-M1H710-C2 6.0 +/- 1.0 mm WSS-M1H710-D2 6.0 +/- 1.0 mm 3.12.2 Weight, range WSS-M1H710-B1 480 +/- 30 g/m2WSS-M1H710-B2 590 +/- 40 g/m2WSS-M1H710-C1 450 +/- 30 g/m2WSS-M1H710-C2 535 +/- 40 g/m2WSS-M1H710-D2 540 +/- 40 g/m2ENGINEERING MATERIAL SPECIF

14、ICATION WSS-M1H710-A/B1/B2/C1/C2/D2 Page 4 of 4 Copyright 2003, Ford Global Technologies, Inc. 3.12.3 Stretch and Set, %, range (SAE J855) 3.12.3.1 Stretch Wales 17 +/- 7Cour 2Set Wales 0 -5 Cour 03.12.3.2 Modulus, max (WSS-M1H710-D2) Strain 6 %Wales 50 Cour 53.13 FLAMMABILITY (ISO 3795/SAE J369) Bu

15、rn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 Purchase departments will ensure that both materials defined in these specifications and shipped to any one assembly plant will be produced by one supplier only.