《FORD WSS-M1H709-A-2008 FABRIC DUETT JACQUARD WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《DUETT图案的提花机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H709-A-2008 FABRIC DUETT JACQUARD WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《DUETT图案的提花机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 02 06 N-STATUS No replacement named M. Dumitrescu 2003 03 19 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.18, 3.19, 4 deleted 1997 04 24 Activated N. Komatsu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, L

2、LC Page 1 of 2 FABRIC, DUETT, JACQUARD WOVEN WSS-M1H709-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 1998 M

3、Y. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS

4、-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 280 ends/10 cm Weft 102 picks/10 cm 3.4.2 Fabric Weight, range +/- 5% 360 - 410 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H709-A Printed

5、 copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 840 dtex resultant f136 (polyester, semi- dull, air texturized) Weft 18/2 Nm spun yarn (560 dtex) x2 (polyester, semi-dull). 3.7 METHOD OF DYEING Yarn dyed and spun or as appro

6、ved by Materials Engineering 3.8 FINISHED OPERATIONS As approved by Materials Engineering 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.