FORD WSD-M96D15-A1-2010 DRIVE BELT TOOTHED HYDROGENATED NITRILE RUBBER (HNBR) GLASS TENSION CORDS EXTENDED LIFE SINGLE FACING FABRIC TO BE USED WITH FORD WSS-M99P1111-A 《单面织物背衬的含.pdf

《FORD WSD-M96D15-A1-2010 DRIVE BELT TOOTHED HYDROGENATED NITRILE RUBBER (HNBR) GLASS TENSION CORDS EXTENDED LIFE SINGLE FACING FABRIC TO BE USED WITH FORD WSS-M99P1111-A 《单面织物背衬的含.pdf》由会员分享，可在线阅读，更多相关《FORD WSD-M96D15-A1-2010 DRIVE BELT TOOTHED HYDROGENATED NITRILE RUBBER (HNBR) GLASS TENSION CORDS EXTENDED LIFE SINGLE FACING FABRIC TO BE USED WITH FORD WSS-M99P1111-A 《单面织物背衬的含.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 06 24 N-STATUS No replacement named C. Mracna, NA 2006 08 17 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.13 & 4 1990 06 29 Released C10068389 B. Hennessey Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Pa

2、ge 1 of 4 DRIVE BELT, TOOTHED, HYDROGENATED NITRILE WSD-M96D15-A1 RUBBER (HNBR), GLASS TENSION CORDS, EXTENDED LIFE, SINGLE FACING FABRIC NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a toothed drive belt based on Hydrogenated Nitrile Rubber (HNBR) with a singl

3、e layer of polyamide facing fabric and glass fiber tension cords. The belt is suitable for use where average service temperatures up to 110 C and peak service temperatures up to 135 C are experienced. The belt is oil and water resistant and remains flexible down to -40 C. 2. APPLICATION This specifi

4、cation was released originally for materials used as toothed belts used to drive components such as camshaft, injector pump and/or auxiliary engine parts. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Re

5、quirements For Production Materials (WSS-M99P1111-A). 3.4 BELT CONSTRUCTION The belt shall consist of a Hydrogenated Nitrile Rubber (HNBR) compound molded to the required tooth profile, covered on the contact face by a single layer of woven polyamide 6 or 66 fabric. There shall be no more than one j

6、oin in the fabric except on belts with lengths greater than 925 mm when two joins are permissible. The belt shall be reinforced by multifilament glass fiber tensioning cords in S and Z twist pairs. The pairs of cords shall be evenly spaced across the width of the belt. The cords shall be covered by

7、a layer of rubber the same as that used for the teeth. There shall be no ends or loops of tensioning cords protruding from the cut sides of the belt. 3.5 MATERIAL TESTING, Rubber The following tests shall be performed on finished belts and/or test specimens cut from them. The test specimens shall be

8、 die-cut from the finished parts and buffed or slit to the required thickness where necessary. When not feasible, specimens cut from molded test slabs manufactured from the same material with an equivalent state of cure shall be used. The test specimens shall have the following dimensions: 150 x 150

9、 mm, min x 2.0 +/- 0.2 mm 3.6 ORIGINAL PROPERTIES 3.6.1 Hardness, International Type A 65 - 73 (ASTM D 1415) Type B 73 - 83 ENGINEERING MATERIAL SPECIFICATIONWSD-M96D15-A1 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 4 3.6.2 Hardness, Durometer A Type A 63

10、- 71 (ISO 868/ASTM D 2240, instantaneous, Type B 71 - 81 plied-up specimens. Hand held durometers shall not be used) 3.6.3 Tensile Strength, min 18 MPa (ISO 37/ASTM D 412, Die C) 3.6.4 Elongation at Break, min 375% (Test according to para 3.6.3) 3.6.5 Modulus at 100% Elongation Type A 2.3 - 4.0 (Tes

11、t according to para 3.6.3) Type B 3.5 5.5 3.6.6 Compression Set, max 80% (ISO 815/ASTM D 395, Method B, except 25% compression, plied-up specimens, 70 h at 125 C) 3.7 HEAT AGED (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 110 +/- 2 C) 3.7.1 Hardness Change, max +20 3.7.2 Tensile Strength

12、 Change, max -20% 3.7.3 Elongation at Break Change, max -75% 3.8 HEAT AGED (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 168 h at 135 +/- 2 C) 3.8.1 Hardness Change, max +15 3.8.2 Tensile Strength Change, max -30% 3.8.3 Elongation at Break Change, max -75% 3.9 IMMERSION IN ASTM OIL No.1 (ISO 1817/A

13、STM D 471, 168 h at 135 +/- 2 C) 3.9.1 Hardness Change -5 to +8 3.9.2 Tensile Strength Change, max -30% 3.9.3 Elongation at Break Change, max -50% 3.9.4 Volume Change, max -15 to +5% 3.10 TENSION CORDS Glass fiber, multifilament spun with S twist and Z twist alternated. ENGINEERING MATERIAL SPECIFIC

14、ATIONWSD-M96D15-A1 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 3 of 4 3.11 FACING FABRIC A single layer of woven polyamide 6 or 66 fabric. The facing fabric construction shall be such that the requirements of this Material Specification and any Engineering Comp

15、onent Specification relating to the toothed belt are met. 3.12 FINISHED PART 3.12.1 Hardness, International (ASTM D 1415 Micro Method) Tooth 64 - 74 (Cut top of tooth horizontally to leave a flat rubber surface for measurement of hardness) Back 64 - 74 3.12.2 Breaking Load Test Method: Tests to be c

16、onducted on complete belts by pulling at 25 mm/minute between two 114 mm cylinders mounted with teeth facing outwards. One of the cylinders shall turn freely to equalize stress in the belt. The belt width shall be as stated on the Engineering Drawing. Original, min 20 kN/20 mm width Heat Aged, min 2

17、0 kN/20 mm (Test Method per 3.7) width Heat Aged, min 20 kN/20 mm (Test Method per 3.8) width After Immersion in ASTM Oil No. 1, min 20 kN/20 mm (Test Method per 3.9) width After Immersion in 5% Sodium Chloride 16 kN/20 mm Solution, min width (168 h at 60 +/- 2 C) 3.12.3 Face Fabric Adhesion to Rubb

18、er Test Method: The face fabric shall be separated from the rubber at 50 mm/minute on a tensile testing machine giving a continuous autographic load record. From the load record calculate the mean minimum peak force in the valley section of at least 6 consecutive teeth. In some cases it may be found

19、 that the fabric breaks instead of peeling from the rubber. This shall be noted in the results and be deemed acceptable providing the value at which breakage occurs exceeds the specified land section requirement. Original, min Valley 20 N/cm Heat Aged, min Valley 15 N/cm (Test Method per para 3.7) E

20、NGINEERING MATERIAL SPECIFICATIONWSD-M96D15-A1 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 4 of 4 Heat Aged, min Valley 12 N/cm (Test Method per para 3.8) After Immersion in ASTM Oil No. 1, min Valley 15 N/cm (Test Method per para 3.9) 3.12.4 Heat Aged No crack

21、s (Test Method per para 3.7) Test Method: After aging the belt shall be bent around a 25 mm diameter mandrel, the teeth facing inwards and outwards respectively (separate samples required). 3.12.5 Ozone Resistance, max Rating 0 (FLTM BP 101-01, belt to be bent around a 50 mm diameter mandrel with th

22、e teeth facing inwards)3.12.6 Low Temperature Flexibility (48 h at -40 +/- 2 C) Test Method: After conditioning, the belt shall be bent within 1 second around a temperature conditioned 25 mm diameter mandrel. Separate samples of belt shall be tested with the teeth facing inwards and outwards respect

23、ively. The belts shall be examined at 2X magnification. Original No Cracks Heat Aged per para 3.7 No Cracks Heat Aged per para 3.8 No Cracks 3.12.7 Oil Resistance No splitting, (Test Method per para 3.9) cracking or delamination Test Method: After conditioning, separate samples of belt shall be bent

24、 around a 25 mm diameter mandrel with the teeth facing inwards and outwards respectively. 3.12.8 Tooth Shear Resistance (FLTM BP 111-01, Procedure A) Original, min 0.9 kN/cm width Heat Aged, min 0.9 kN/cm width (Test Method per para 3.7) Heat Aged, min 0.9 kN/cm width (Test Method per para 3.8) After Immersion in ASTM Oil No.1, min 0.8 kN/cm width (Test Method per para 3.9, belt to be wiped dry with a cloth before fixing to jig).