FORD FLTM BV 153-2-2001 AGING OF SEALERS AND HEAVY MASTIC ADHESIVES (Replaces FLTM EU-BV 053-02).pdf

《FORD FLTM BV 153-2-2001 AGING OF SEALERS AND HEAVY MASTIC ADHESIVES (Replaces FLTM EU-BV 053-02).pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BV 153-2-2001 AGING OF SEALERS AND HEAVY MASTIC ADHESIVES (Replaces FLTM EU-BV 053-02).pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BV 153-02 Date Action Revisions 2001 04 10 Revised Editorial no technical change A. Cockman 1992 03 26 Printed copies are uncontrolled Page 1 of 6 Copyright 2001, Ford Global Technologies, Inc. AGING OF SEALERS AND HEAVY MASTIC ADHESIVES Application This method is used t

2、o determine the aging resistance of sealers and heavy mastic adhesives. Method A: Non-curing sealers Method B: Air drying sealers Method C: Heat curing sealers Method D: Heat curing heavy mastic adhesives Apparatus Required Laboratory Forced Air Circulation Oven Capable of maintaining temperatures u

3、p to 250 +/- 2 C. Test Apparatus Refer to Figure 2 and 3 (painted or plated steel). Template Refer to Figure 1 (may be made using steel, aluminum, or suitable plastic). Materials Required Test Panels Steel body skin panels. Dimensions: 60 x 300 mm surface finish 0.9 - 1.8 mm CLA Prepare according to

4、 the following Ford Laboratory Test Methods as required by the applicable Engineering Material Specification. 1. Oiled surfaces according to FLTM BZ 150-11, Normal Grade. 2. Primed surfaces according to FLTM BI 120-01. 3. Electrocoated and spray-primed surfaces according to FLTM BI 120-01 and BI 103

5、-02, Method E. FORD LABORATORY TEST METHOD BV 153-02 Page 2 of 6 Copyright 2001, Ford Global Technologies, Inc. Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less t

6、han 24 h prior to testing and tested under the same conditions unless otherwise specified. Procedure Method A 1. Apply to 3 test panels, prepared according to the applicable Engineering Material Specification, either a bead of sealer 200 mm in length using the template as shown in Figure 1, or a bea

7、d of premolded sealer 200 mm in length. The profiles of the premolded sealer must be pressed down to give a uniform thickness of 3 mm. 2. Place the specimens in the oven maintained at a temperature of 85 +/- 2 C for 670 h. Remove the specimens from the oven and cool to 23 +/- 2 C. 3. Test and examin

8、e the specimens as described under Evaluation. Method B 1. Apply to 3 test panels, prepare according to the applicable Engineering Material Specification, a bead of sealer 200 mm in length using the template. 2. Condition the specimens for 4 h at 23 +/- 2 C. 3. Place the specimens in the oven mainta

9、ined at a temperature of 85 +/- 2 C for 670 h. Remove the specimens from the oven and cool to 23 +/- 2 C. 4. Test and examine the specimens as described under Evaluation. Method C 1. Apply to 6 test panels, prepared according to applicable Engineering Material Specification, a bead of sealer 200 mm

10、in length using the template. 2. Condition the specimens at 23 +/- 2 C for an “open time“ of 10 minutes. 3. Cure 3 specimens in accordance with the minimum curing cycle and the other 3 specimens in accordance with the maximum curing cycle outlined in FLTM BV 150-05 (Table 2 or 3 as specified in the

11、applicable Engineering Material Specification). FORD LABORATORY TEST METHOD BV 153-02 Page 3 of 6 Copyright 2001, Ford Global Technologies, Inc. 4. Remove the specimens from the oven and condition for 2 h at 23 +/- 2 C. 5. Place the specimens in the oven at 85 +/- 2 C for 335 h. Remove the specimens

12、 from the oven and cool to 23 +/- 2 C. 6. Test and examine the specimens as described under Evaluation. Method D 1. Apply to 6 test panels, prepared according to the applicable Engineering Material Specification, a bead of sealer 200 mm in length using the template. 2. Condition the specimens at 23

13、+/- 2 C for an open time of: a. 4 h for solvent release materials or b. 10 minutes for solvent free materials 3. Cure 3 specimens in accordance with the minimum curing cycle and the other 3 specimens in accordance with the maximum curing cycle outlined in FLTM BV 150-05, Table 1. 4. Remove the speci

14、mens from the oven and condition for 2 h at 23 +/- 2 C. 5. Place the specimens in the oven at 85 +/- 2 C for 335 h. Remove the specimens from the oven and cool to 23 +/- 2 C. 6. Test and examine as described uder Evaluation. Evaluation After conditioning the specimens for 2 h at 23 +/- 2 C, bend eac

15、h specimen through an angle of 90 in 2 s around the mandrel using a bending fixture as shown in Figure 3. Examine and determine loss of adhesion, cracking and chipping as required by the applicable Engineering Material Specification. Chemicals, materials, parts, and equipment referenced in this docu

16、ment must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities. FORD LABORATORY TEST METHOD BV 153-02 Page 4 of 6 Copyright 2001, Ford Global Technologies, Inc. AGING OF SEALERS AND HEAVY MASTIC ADHESIVES FIGURE 1 FORD LABORATORY TEST METHOD BV 153-02 Page 5 of 6 Copyright 2001, Ford Global Technologies, Inc. AGING OF SEALERS AND HEAVY MASTIC ADHESIVES FIGURE 2 FORD LABORATORY TEST METHOD BV 153-02 Page 6 of 6 Copyright 2001, Ford Global Technologies, Inc. AGING OF SEALERS AND HEAVY MASTIC ADHESIVES Figure 3