FORD FLTM BQ 005-06-2000 TERNE COAT POROSITY TEST《镀铅锡铁板的镀层孔隙度试验》.pdf

《FORD FLTM BQ 005-06-2000 TERNE COAT POROSITY TEST《镀铅锡铁板的镀层孔隙度试验》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BQ 005-06-2000 TERNE COAT POROSITY TEST《镀铅锡铁板的镀层孔隙度试验》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BQ 005-06 Date Action Revisions 2000 08 10 Editorial no technical change A. Cockman 1992 08 04 Printed copies are uncontrolled Page 1 of 2 Copyright 2000, Ford Global Technologies, Inc. TERNE COAT POROSITY TEST Application This test method describes the procedure for pre

2、paring and testing terne coated steel to determine coating porosity. Equipment Required Vapor Degreaser Detrex Model 20500, Size B62E or equivalent. Source: Detrex C hemical Company P.O. Box 501 Detroit, MI 48232 Tape Scotch Brand Acetate Fiber Tape 710 - 2, 25 mm wide. Water Bath Lab - Line Instrum

3、ents, Inc., Catalog No. 3088, Serial No. 0572 - 150 Watts. Source: Lab - Line Instruments, Inc. Melrose Park, IL Pyrex Jar Cy lindrical, plain, VWR Catalog #36360 - 187 (12“ O.D. x 12“) or 36360 - 245(16“ O.D. x 12“). Alternate: 2000 mL beaker, Pyrex. Source: VWR Scientific P.O. Box 855 Columbus, OH

4、 43216 Glass Stirring Rod 6 mm diameter, length as required to suspend samples in water bath jar. Plastic Template Approximately 75 x 125 mm with a 1 x 1 inch cutout to use for final evaluation to specification. Inhibited Methyl Chloroform M5B58A - 1 - 1 - 1 Trichloroethane. Note: This material must

5、 be used in a well ventilated area. FORD LABORATORY TEST METHOD BQ 005-06 Page 2 of 2 Copyright 2000, Ford Global Technologies, Inc. Distilled Water pH 6 to 6.5. Alligator (Battery) Clip Mueller Clip #27M (2 3/8 x 1/2 inches). Source: Mueller Electric Company Cleveland, OH Conditioning and Test Cond

6、itions All test values indicated herein are based on material conditioned in a control led atmosphere of 23 +/ - 2 C and 50 +/ - 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. Test Panel Preparation 1. Cut or shear test

7、panels 150 x 150 mm from the as - received c oil. Samples are to be taken from a location equally distant from the coil edges and a sufficient distance from the coil end to ensure a scratch -free surface. 2. Clean test panels as follows: a. Immerse panels into the boiling (70 - 77 C) chamber of th e

8、 degreaser containing 1 - 1 - 1 trichloroethane for 15 - 20 s. b. Transfer to rinse zone (52 - 57 C) for 10 - 15 s. This zone is to be continuously replenished with clean solvent distillate. 3. Tape cut edges of panels with acetate fiber tape. Double tape in areas of battery clip gripping. Procedure

9、 1. Fill rectangular Pyrex jars with distilled water and adjust pH (6 - 6.5) by the addition of hydrochloric acid. Place Pyrex jars into the temperature controller containing tap water regulated to a temperat ure of 90 - 98 C. 2. Suspend panels into distilled water using glass rods and Mueller Clips

10、. Allow panels to hang undisturbed with approximately 25 mm separation between panels. 3. At the end of 6 h immersion at 90 - 98 C, remove test panels. Blot dr y with paper towels. 4. Using the 1 inch square template and the unaided eye count the number of rust spots in 3 areas showing the greatest

11、indication of rust and obtain an average count. Edge spots are counted as half a spot. 5. Report as required in t he Engineering Material Specification. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities.