FORD FLTM BP 001-07-2000 DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER《硅弹性体的硬度和封闭空间耐热性》.pdf

《FORD FLTM BP 001-07-2000 DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER《硅弹性体的硬度和封闭空间耐热性》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BP 001-07-2000 DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER《硅弹性体的硬度和封闭空间耐热性》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BP 001-07 Date Action Revisions 2000 11 09 Revised Editorial no technical change A. Cockman 1992 07 29 Printed copies are uncontrolled Page 1 of 4 Copyright 2000, Ford Global Technologies, Inc. DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER Application This

2、 procedure is used for the determination of change in hardness and resistance of silicone elastomer when confined in a test fixture under heat. Apparatus Required Convection Oven Capable of maintaining 249 +/ - 2 C. Mold See Attached Figure 1. Mylar 8 inch x 8 inch x 0.003 thick, Type A electrical g

3、rade or equivalent. Source: Cadillac Plastic and Chemical Company 1502 Maumee Street Toledo, OH 42624 Hot Press Capable of m aintaining temperature of 177 +/ - 2 C. Pasadena Press Model B - 230 - H or equivalent. Source: Pasadena Hydraulics, Inc. 1433 Lidcombe Street El Monte, California 91731 Rever

4、sion Test Fixture See attached Figure 2. Durometer Shore A - 2 (ASTM D 676). Sour ce: Shore Instrument Company 90 - 35 Van Wyck Expressway Jamaica, New York 11435 Steel Plate 6 inches square x 0.250 inches thick. FORD LABORATORY TEST METHOD BP 001-07 Pa ge 2 of 4 Copyright 2000, Ford Global Technolo

5、gies, Inc. Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmos phere of 23 +/ - 2 C and 50 +/ - 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. Prepara

6、tion of Test Buttons 1. Place the mold on a piece of mylar and then place the mold and mylar on the 0.250 inch steel plate. 2. Fill the individual button molds with a sample of the silicone and place a piece of mylar on top of the filled mold. 3 Transfer the mold immediately to the press set at 177

7、C. 4. Cure for 25 minutes, remove the mold from the press and remove the test buttons from the mold. Allow the buttons to cool to 23 +/ - 2 C. 5. Measure the hardness. Type A durometer hardness limits shall be as specified on the engineering specification. Reversion Test 1. Clean the reve rsion test

8、 fixture and remove all solvent by heating in an oven. Cool fixture in a desiccator. 2. Record the original hardness of the cured test button. 3. Place button in cavity of test fixture and tighten cover bolt to 25 pounds inch using torque wren ch. 4. Put the test specimen and reversion fixture in ov

9、en for six hours at 249 C. 5. Remove the test fixture and allow it to cool for a minimum of 2 h. 6. Remove the button from the fixture, if possible. 7. Measure and record the following data on t he button. (a) Observe the physical state of the button. Note if button cannot be removed from fixture, c

10、annot be tested, is too firm, is too soft or is crumbly. Also, record any other unusual appearance features. (b) Determine hardness by use of durom eter Type A. 8. Loss in durometer shall be as shown in the engineering specification. Chemicals, materials, parts, and equipment referenced in this docu

11、ment must be used and handled properly. Each party is responsible for determining proper use and han dling in its facilities. FORD LABORATORY TEST METHOD BP 001-07 Pa ge 3 of 4 Copyright 2000, Ford Global Technologies, Inc. DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER Figure 1 FORD LABORATORY TEST METHOD BP 001-07 Pa ge 4 of 4 Copyright 2000, Ford Global Technologies, Inc. DUROMETER AND CONFINED HEAT RESISTANCE OF SILICONE ELASTOMER Figure 2