FORD FLTM BO 029-03-2001 WATER IMMERSION - WARP TEST OF ELASTOMERS AND PLASTICS《弹性体和塑料的水浸翘曲试验》.pdf

《FORD FLTM BO 029-03-2001 WATER IMMERSION - WARP TEST OF ELASTOMERS AND PLASTICS《弹性体和塑料的水浸翘曲试验》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BO 029-03-2001 WATER IMMERSION - WARP TEST OF ELASTOMERS AND PLASTICS《弹性体和塑料的水浸翘曲试验》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BO 029-03 Date Action Revisions 2001 03 27 Revised Editorial no technical change A. Cockman 1992 07 28 Printed copies are uncontrolled Page 1 of 4 Copyright 2001, Ford Global Technologies, Inc. WATER IMMERSION - WARP TEST OF ELASTOMERS AND PLASTICS Application This proce

2、dure is used to determine the amount of warp experienced by elastomer and/or plastic materials subjected to prolonged exposure to moisture. Apparatus Required Warp Test Fixture - see Figure 1 and 2. Drying Oven A mechanical convection oven maintained at a temperature of 121 +/- 2 C. Tank Size shall

3、be sufficient to totally submerge the sample and fixture in water. Desiccator Curtin Matheson Scientific Catalog No. 109-124 or equivalent to hold 305 mm test piece. Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +

4、/- 2 C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. Procedure 1. Prepare a sample test bar 305 x 25 mm x nominal part thickness. When the configuration and the size of the part permits, two samples should be

5、 prepared with the 305 mm dimension of one sample at a 90 orientation to that of the second sample. 2. Dry the sample in the oven for 16 h at 121 +/- 2 C unless otherwise specified in the material specification. 3. Remove the sample from the oven and immediately place in a desiccator for 1 h, allowi

6、ng the sample to cool to 23 +/- 2 C. COPYRIGHT Ford Motor CompanyLicensed by Information Handling ServicesFORD LABORATORY TEST METHOD BO 029-03 Page 2 of 4 Copyright 2001, Ford Global Technologies, Inc. 4. Remove the sample from the desiccator and place it on the test fixture (Figure 1 & 2) so that

7、one end of the sample contacts the fixed bracket. While holding the sample flat on the fixture, move the adjustable bracket until it contacts the other end of the sample. 5. Immerse the fixture and mounted sample under at least 50 mm of water in a bath conditioned at 23 +/- 2 C. 6. After immersion f

8、or the time required by the material specification, remove the fixture from the water and measure the maximum height the sample has risen from the base plate to the bottom surface of the sample and record to the nearest 0.8 mm. 7. Report the maximum height of warp and the time of immersion. Chemical

9、s, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities. COPYRIGHT Ford Motor CompanyLicensed by Information Handling ServicesFORD LABORATORY TEST METHOD BO 029-03 Page 3 of

10、4 Copyright 2001, Ford Global Technologies, Inc. APPARATUS FOR WARP TEST OF ELASTOMERS AND PLASTICS Figure 1 COPYRIGHT Ford Motor CompanyLicensed by Information Handling ServicesFORD LABORATORY TEST METHOD BO 029-03 Page 4 of 4 Copyright 2001, Ford Global Technologies, Inc. APPARATUS FOR WARP TEST OF ELASTOMERS AND PLASTICS Figure 2 COPYRIGHT Ford Motor CompanyLicensed by Information Handling Services