FORD FLTM AO 006-1-2001 HEIGHT OF FOAM RISE TEST.pdf

《FORD FLTM AO 006-1-2001 HEIGHT OF FOAM RISE TEST.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM AO 006-1-2001 HEIGHT OF FOAM RISE TEST.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD AO 006-01 Date Action Revisions 2001 01 30 Revised Editorial no technical change A. Cockman 2000 04 17 Editorial no technical change A. Cockman 1992 01 08 Printed copies are uncontrolled Page 1 of 2 Copyright 2001, Ford Global Technologies, Inc. HEIGHT OF FOAM RISE TEST

2、Application This procedure determines the height of rise of polyurethane foams prepared by mixing of polyols (Component A) and isocyanate (Component B). Apparatus Required Laboratory Oven Blue M POM 2066 (Matheson) or equivalent. Stirring Motor Capable of 3000 rpm, minimum. Stirring Motor Clamp Talb

3、oys Support Stand Stirring Rod 300 mm long, 51 mm diameter propeller. Band Saw Balance Scale 500 gm range accurate to 0.1 gm. Paper Cups Bottom diameter 60 mm, top diameter 79 mm, height 95 mm, 300 mL capacity. Conditioning and Test Conditions All test values indicated herein are based on material c

4、onditioned in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. FORD LABORATORY TEST METHOD AO 006-01 Page 2 of 2 Copyright 2001, Ford Global Technologies, Inc. Procedure 1.

5、Make suitable preparations to run three samples for each determination to be made. 2. Into clean dry paper cups, weigh out 65 g of the polyol resin (Component A). 3. Into the cups, one at a time (Steps 3 through 6) weigh 10 g of the isocyanate (Component B), being careful not to allow the material t

6、o deposit on the sides of the cup, and immediately proceed with Step 4. 4. With the stirrer motor running at 3000 rpm, place the sample under the spindle for 20 seconds while scraping the sides of the container with a wooden spatula. Note: Immerse mixer blade in methylene chloride. 5. Allow dwell ti

7、me of two minutes from the end of mix cycle. 6. After two minute dwell, put cup into oven for 8 minutes at 95 +/- 2 C. 7. Allow 30 minutes for material to cool to 23 +/- 2 C. 8. Using the band saw, slice the cup and cut sample into two equal portions. Calculations Measure the height of the three sam

8、ples from the bottom of the foam bun to the point of maximum rise. The three samples must agree on height of rise to within 10 %. Note: Any sample with large voids (i.e., 13 mm) from entrapped air must be discarded and a new sample made up. Report 1. Sample Identification 2. Temperature of Samples 3. Height of Rise 4. Observer and Date Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities.