FORD ESF-M91J3-A-2005 PAINT ALUMINUM HEAT RESISTANT TO BE USED WITH FORD WSS-M99P1111-A 《耐热铝漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESF-M91J3-A-2005 PAINT ALUMINUM HEAT RESISTANT TO BE USED WITH FORD WSS-M99P1111-A 《耐热铝漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESF-M91J3-A-2005 PAINT ALUMINUM HEAT RESISTANT TO BE USED WITH FORD WSS-M99P1111-A 《耐热铝漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 12 Revised Inserted 3.0; Deleted 3.9 and 4 1985 06 14 Revised CE3P-RD863100-E162 F. O. Swanson 1963 07 17 Released F6-1082 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 1 PAINT, ALUMINUM, HEAT

2、RESISTANT ESF-M91J3-A 1. SCOPE The material defined by this specification is a medium heat resistant paint (260 C maximum). 2. APPLICATION This material was released originally for coating shielded spark plugs. 3. REQUIREMENTS 3.1 COLOR Aluminum 3.2 NON-VOLATILE, min 35% (FLTM BI 102-01) 3.3 PIGMENT

3、, min Leafing aluminum, 86 g/L 3.4 VEHICLE Vegetable oil modified resin 3.5 VISCOSITY #4 FORD CUP AT 27 C 20 - 25 s (FLTM BI 111-01) 3.6 FILM THICKNESS As specified on the engineering drawing. 3.7 RESISTANCE TO HEAT After 24 h at 246 - 260 C, there shall be no blistering or peeling of paint film. 3.8 SHELF STABILITY This material must not jell, liver or hard set after aging for 30 days at 27 C. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 BAKING TIME at 121 C 20 minutes