FORD ESB-M5G19-F1-1978 DEADENER FLOOR PAN MASTIC (Shown on ESB-M5G19-C1)《乳香脂制地板盘减声材料 列于标准ESB-M5G19-C1上》.pdf

《FORD ESB-M5G19-F1-1978 DEADENER FLOOR PAN MASTIC (Shown on ESB-M5G19-C1)《乳香脂制地板盘减声材料 列于标准ESB-M5G19-C1上》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M5G19-F1-1978 DEADENER FLOOR PAN MASTIC (Shown on ESB-M5G19-C1)《乳香脂制地板盘减声材料 列于标准ESB-M5G19-C1上》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Para No. Revisions1978 09 20 Metricated, Renumbered & Retyped CAHI-RD572066-1031976 11 03 Released AG1-6000-92Page 1 of 4DEADENER, FLOOR PAN - MASTIC ESB-M5G19-C1ESB-M5G19-C2 ESB-M5G19-F1INACTIVE ESB-M5G19-F21. SCOPE:The mater

2、ial defined by this specification is a 3 ply laminated deadener,composed of asphalt rubber mastic and an antiblocking agent on bothsurfaces to prevent blocking during shipping and storage. TheESB-M5G19-C1 and ESB-M5G19-F1 materials have polyethylene film onone side and kraft paper on one side. The E

3、SB-M5G19-C2 and ESB-M5G19-F2 have polyethylene or polyester film on both sides.2. APPLICATION:This specification was released originally for materials used as floorpan deadeners. The ESB-M5G19-C1 and ESB-M5G19-F1 are generallyused in thicknesses of 0.1 in (2.5 mm) and 0.08 in (2.0 mm), bothwith and

4、without fiber pads as a deadener and sound barrier.The ESB-M15G19-C2 and ESB-M5G19-F2 are more pliable and can be usedin thicknesses down to 0.06 in (1.5 mm) where lower weight orgreater flexibility is desired.3. REQUIREMENTS:ESB-M5G19-C1 and ESB-M5G19-F1 were originallydesignated ESB-M5G19-C and ES

5、B-M5G19-F, and where ESB-M5G19-C( ESB-M5G19-F) are indicated on engineering drawings, patterns, specifications, etc., ESB-M5G19-C1 ( ESB-M5G19-F1) will be understood.3.1 CONDITIONINGAll test values indicated herein are based on material conditionedin a controlled atmosphere of 23 +/- 2 C and 50 +/-

6、5% relativehumidity for 24 h prior to testing and tested under the samecontrolled conditions.3.2 THICKNESS As specified on engineering drawings(ASTM D 461, 1 lb (454 g)load, 1 in (25 mm) foot)3.3 DENSITY, min 86 lb/ft 3 (1378 kg/m 3 )(ASTM C 167)ENGINEERING MATERIAL SPECIFICATION ESB-M5G19-C1ESB-M5G

7、19-C2 ESB-M5G19-F1INACTIVE ESB-M5G19-F2Page 2 of 43.4 COMPOSITION(FLTM AV 1-1)ESB-M5G19-C1 & ESB-M5G19-F13.4.1 Asphalt Rubber mastic3.4.2 Creped kraft 0.01-0.02 lb/ft 2 (49-98 g/m 2 )3.4.3 Polyethylene film 0.002-0.005 lb/ft 2 (9.8-24.4 g/m 2 )ESB-M5G19-C2 & ESB-M5G19-F23.4.4 Asphalt rubber mastic3.

8、4.5 Polyethylene or polyester film 0.002-0.005 lb/ft 2(9.8-24.4 g/m 2 )Test Method: Polyethylene or polyester film is strippedfrom mastic, solvent wiped and weighed.3.5 BREAKING STRENGTH, min 0.01 in lb/mil thickness/inch width(ASTM D 461) (0.70 N/mm thickness/10 mm width)3.6 TEAR STRENGTH min 20 lb

9、 (89 N)(ASTM D 624, Die C“, any direction)3.7 FLEXIBILITY, At 23 +/- 2 C No crackingTest Method: Bend a 2 x 6 in (50 x 150 mm) sample 180 , slowly,around an 0.5 in (13 mm) mandrel with either surface up.3.8 PALLETIZING Shall be easily separatedTest Method: Ply up ten, 4 x 4 in (100 x 100 mm) samples

10、. Place a20 lb (9.1 kg) static load over the material and place ina mechanical convection oven maintained at 54 +/- 2 C for 72 h.Cool samples to 23 +/- 2 C and peel by hand.3.9 HEAT STABILITYNo dripping of mastic composition or fall-off of poly film.Test Method: Suspend samples of material in a vert

11、ical position for2 h at 88 +/- 2 C in a mechanical convection oven.ENGINEERING MATERIAL SPECIFICATION ESB-M5G19-C1ESB-M5G19-C2 ESB-M5G19-F1INACTIVE ESB-M5G19-F2Page 3 of 43.10 SOUND PROPERTIES3.10.1 Transmission, max 90.0 dB(FLTM BV 3-3)3.10.2 Vibrational Dampening(FLTM BV 3-4)3.11 ESB-M5G19-C1, & E

12、SB-M5G19-C2 FLAMMABILITY, max 4 in (101 mm/min(FLTM BN 24-2, without the lot sampling plan)sudden flaming on either surface in excess of the above maximumvalue. ESB-M5G19-F1 & ESB-M5G19-F2 FLAMMABILITY3.12.1 In order to comply with Federal Motor Vehicle SafetyStandard No. 302, the materials, portion

13、s of components,its surface, at a rate of more than 4 in (101 mm) per min.To demonstrate compliance, the sample size and method ofENGINEERING MATERIAL SPECIFICATION ESB-M5G19-C1ESB-M5G19-C2 ESB-M5G19-F1INACTIVE ESB-M5G19-F2Page 4 of 43.12.2 Performance - Environmental AgingAll materials, portions of

14、 components, and compositesdefined by this specification that have not been treated,modified or reformulated and exceed a max burn rate of 3.0in (76 mm) per min as specified by the Flammability LotSampling Plan of FLTM BN 24-2, must be evaluated forpermanency of the materials flame retardant propert

15、ies perESB-M25P3-A according to the accelerated environmentalaging requirements applicable to the basic materialcategory of this particular specification.Any material, portions of components, and compositesdefined by this specification that have been treated,modified or reformulated to conform to Fl

16、ammability LotSampling Plan of FLTM BN 24-2, regardless of max burn rate,must be evaluated for both permanency of materials flameretardant properties and changes in mechanical, chemicaland physical properties per ESB-M25P3-A applicable to thebasic materials category of this particular specification.

17、3.12.3 Flammability Test ProgramMaterials, portions of components, and composites governedby this specification must also comply with therequirements of ES-D3AB-11014-AA.3.13 SUPPLIERS RESPONSIBILITYMaterial supplied to this specification must be equivalent to thatoriginally approved. Changes in for

18、mulation or processing shallnot be made without prior approval as described in SupplierProcedure I-A.4. APPROVAL OF SUPPLIERS:Suppliers to this specification must be approved by the affected productengineering office. Procedure for gaining approval of a specificmaterial to a new/existing ES-M specification is contained in SupplierProcedure I-A. Approved new suppliers will be added to the EngineeringMaterials Approved Source List.