FORD ESB-M1C35-C-2008 GREASE CALCIUM COMPLEX HIGH TEMPERATURE RESISTANT ANTISQUEAK NLGI #2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI型减声、耐高温钙复合物润滑脂》.pdf

《FORD ESB-M1C35-C-2008 GREASE CALCIUM COMPLEX HIGH TEMPERATURE RESISTANT ANTISQUEAK NLGI #2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI型减声、耐高温钙复合物润滑脂》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1C35-C-2008 GREASE CALCIUM COMPLEX HIGH TEMPERATURE RESISTANT ANTISQUEAK NLGI #2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI型减声、耐高温钙复合物润滑脂》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 09 N-STATUS Replaced by WSS-M13P12-A L. Schmalz, FNA 2003 10 20 Revised Updated format 1965 09 17 Released AV1-268 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 2 GREASE, CALCIUM COMPLEX, HIGH

2、 TEMPERATURE ESB-M1C35-C RESISTANT, ANTI-SQUEAK, NLGI #2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a long life, high temperature resistant, anti-squeak lubricant. 2. APPLICATION This specification was released originally for material used as an anti-squeak

3、lubricant on elements of seat spring assemblies which are subjected to 260 C processing temperatures. It is not recommended for applications on or near painted interior or exterior automotive finishes. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part pro

4、ducers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION The material shall be composed of calcium complex soap, mineral oil, and suitable additives and fillers to give the required properties. 3.3 COLOR Light Tan 3.4 PENETRATION 265 - 295

5、(ASTM D 217, worked 60 strokes) 3.5 DROPPING POINT, min 260 C (ASTM D 566 or D 2265) 3.6 OXIDATION STABILITY, PRESSURE DROP, max 69 kPa (ASTM D 942, 100 h) ENGINEERING MATERIAL SPECIFICATIONESB-M1C35-C Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 2 of 2 3.7 PEN

6、ETRATION AFTER OXIDATION 310 - 340 (ASTM D 217, worked 60 strokes) 3.8 CONSISTENCY STABILITY INCREASE, max 10% (ASTM D 217 except 1.6 mm dia hole, worked 105cycles) 3.9 WATER WASHOUT, max 7% (ASTM D 1264, at 80 C) 3.10 HEAT RESISTANCE No loss of adhesion or evidence of a brittle or crisp texture. Te

7、st Method: Apply 0.76 mm thick x 50 mm x 150 mm and 3.2 mm thick x 50 mm x 150 mm films of grease to clean steel panels of convenient size. Scribe a line 6.4 mm below the grease films parallel to the 50 mm dimension. Place the panels with the 150 mm dimension vertical, in a mechanical convection ove

8、n for 30 minutes at 260 C. Allow the samples to cool and examine the grease films. Any loss of adhesion, flow beyond the scribe line, or evidence of brittleness shall be cause for rejection. 3.12 QUALITY Material shall be a smooth homogeneous product free from abrasive particles, it shall be consist

9、ent in color and texture, and free from objectionable odors during normal storage. It shall be suit-able for the intended application. 5. GENERAL INFOMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 The following parameters are recommended for the Quality Certification Requirements of para 3.1: 5.1.1 Infrared Analysis, para 3.2 of WSS-M99P1111-A. 5.1.2 Penetration, para 3.4. 5.1.3 Dropping Point, para 3.5.