FORD ES2-M2A64-A-2003 BRASS WROUGHT GENERAL PURPOSE TO BE USED WITH FORD WSS-M99P1111-A 《通用锻造黄铜 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ES2-M2A64-A-2003 BRASS WROUGHT GENERAL PURPOSE TO BE USED WITH FORD WSS-M99P1111-A 《通用锻造黄铜 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ES2-M2A64-A-2003 BRASS WROUGHT GENERAL PURPOSE TO BE USED WITH FORD WSS-M99P1111-A 《通用锻造黄铜 与标准FORD WSS-M99P1111-A一起使用 》.pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 09 11 Revised Para 3.0 inserted; para 3.3 and 4 deleted 1978 06 12 Metricated and Retyped CF4H-RD 567168-21 1963 04 19 Released Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 1 BRASS, WROUGHT GENE

2、RAL PURPOSE ES2-M2A64-A 1. SCOPE This specification lists brass alloys that are suitable for the fabrication of parts requiring the particular properties of brass, such as corrosion resistance, thermal conductivity or electrical conductivity; but which do not require the properties of a specific typ

3、e. 2. APPLICATION This specification was released to obtain part print stability by allowing latitude in alloy selection for manufacturing, consistent with engineering drawing requirements. It is recognized that a given part may be produced by any one of several methods and that a single brass is no

4、t suitable for all methods. The brass alloys listed, are considered as optional for the part to which this specification is applied. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Product

5、ion Materials (WSS-M99P1111-A). 3.1 CHEMICAL COMPOSITION (Nominal) Copper Alloy No. Copper Zinc Lead Commercial Spec. CA 260 70 30 SAE, ASTM B 36, ASTM B 134 CA 268 66 34 SAE, ASTM B 36 CA 270 65 35 SAE, ASTM B 134 CA 360 61.5 35.5 3 SAE, ASTM B 16 CA 377 59 39 2 SAE, ASTM B 124 CA 464 60 40 SAE, AS

6、TM B 21 These listed brass alloys may be used providing they produce a part suitable for the intended purpose. It is not intended that a vendor use a large number of different alloys in producing a part, but to confine himself to a minimum variety for a particular run. 3.2 MECHANICAL PROPERTIES Specific mechanical properties shall be as shown on the engineering drawing.