EN 485-2-2013 9145 Aluminium and aluminium alloys - Sheet strip and plate - Part 2 Mechanical properties《铝和铝合金 片材 带材和板材 第2部分 机械特性》.pdf

《EN 485-2-2013 9145 Aluminium and aluminium alloys - Sheet strip and plate - Part 2 Mechanical properties《铝和铝合金 片材 带材和板材 第2部分 机械特性》.pdf》由会员分享，可在线阅读，更多相关《EN 485-2-2013 9145 Aluminium and aluminium alloys - Sheet strip and plate - Part 2 Mechanical properties《铝和铝合金 片材 带材和板材 第2部分 机械特性》.pdf（92页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards PublicationBS EN 485-2:2013Aluminium and aluminiumalloys Sheet, strip and platePart 2: Mechanical propertiesCopyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 48

2、5-2:2013 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 485-2:2013. Itsupersedes BS EN 485-2:2008 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee NFE/35, Light metals and their alloys.A list of organizations repres

3、ented on this committee can beobtained on request to its secretary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. The British Standards Institution 2013. Published by BSI StandardsLimited 2013ISBN 978 0 580 82

4、479 1ICS 77.150.10Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 31 October 2013.Amendments issued since publicationDate Text affectedCopyright European Committee

5、 for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 485-2 October 2013 ICS 77.150.10 Supersedes EN 485-2:2008English Version Aluminium and al

6、uminium alloys - Sheet, strip and plate - Part 2: Mechanical properties Aluminium et alliages daluminium - Tles, bandes et tles paisses - Partie 2: Caractristiques mcaniques Aluminium und Aluminiumlegierungen - Bnder, Bleche und Platten - Teil 2: Mechanische Eigenschaften This European Standard was

7、approved by CEN on 22 August 2013. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nati

8、onal standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own langu

9、age and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece,

10、 Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN

11、-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2013 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 485-2:2013: ECopyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo

12、 reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Requirements .4 4 List of alloys with mechanical property limits 4 4.1 General 4 4.2 Elongation 5 4.3 List of alloys and their mechanic

13、al properties .5 Annex A (normative) Rules for rounding . 84 Annex B (informative) Explanation of temper designations used in Tables 1 to 5 based on definitions of EN 515 85 Bibliography . 87 Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo repr

14、oduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 3 Foreword This document (EN 485-2:2013) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be gi

15、ven the status of a national standard, either by publication of an identical text or by endorsement, at the latest by April 2014, and conflicting national standards shall be withdrawn at the latest by April 2014. Attention is drawn to the possibility that some of the elements of this document may be

16、 the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. CEN/TC 132 affirms its policy that if a patentee refuses to grant licences on standardized products under reasonable and not discriminatory conditions, this product will be

17、removed from the corresponding document. This document supersedes EN 485-2:2008. CEN/TC 132 decided to revise EN 485-2:2008 as follows: addition of the alloy EN AW-1350 in a new Table 18; addition of the alloy EN AW-4115 in a new Table 18; addition of the alloy EN AW-5449A in a new Table 36; additio

18、n of the alloy EN AW-5456 in a new Table 38; EN 10002-1 was replaced by EN ISO 6892-1. EN 485 comprises the following parts under the general title, “Aluminium and aluminium alloys Sheet, strip and plate“: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3:

19、 Tolerances on dimensions and form for hot-rolled products Part 4: Tolerances on shape and dimensions for cold-rolled products According to the CEN-CENELEC Internal Regulations, the national standards organisations of the following countries are bound to implement this European Standard: Austria, Be

20、lgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Swit

21、zerland, Turkey and the United Kingdom. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 4 1 Scope This European Standard specifies the mechanica

22、l properties of wrought aluminium and wrought aluminium alloy sheet, strip and plate for general engineering applications. It does not apply to semi-finished rolled products in coiled form to be subjected to further rolling (reroll stock) or to special products such as corrugated, embossed, painted,

23、 sheets and strips or to special applications such as aerospace, can stock, finstock, for which mechanical properties are specified in separate European Standards. The chemical composition limits of the alloys are specified in EN 573-3. Temper designations are defined in Annex B, in compliance with

24、the provisions of EN 515. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced doc

25、ument (including any amendments) applies. EN 485-1, Aluminium and aluminium alloys Sheet, strip and plate Part 1: Technical conditions for inspection and delivery EN ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature (ISO 6892-1) ASTM G66, Standard Test Method

26、for Visual Assessment of Exfoliation Corrosion Susceptibility of 5xxx Series Aluminium Alloys (ASSET Test) ASTM G67, Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5xxx Series Aluminium Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test) 3 Requiremen

27、ts The mechanical properties shall be in conformity with those specified in Clause 4 or those agreed upon between purchaser and manufacturer and stated on the order document. 4 List of alloys with mechanical property limits 4.1 General Table 1 to Table 50 contain mechanical property limits values ob

28、tained by tensile testing according to EN ISO 6892-1 after sampling and after sample preparation according to EN 485-1. They also contain values of bend radius and hardness following sampling and test methods as described in EN 485-1. These values are for information only. For some alloys they conta

29、in provisions related to intergranular corrosion, exfoliation corrosion or stress corrosion testing, see also EN 485-1. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-

30、2:2013EN 485-2:2013 (E) 5 4.2 Elongation The A50mmvalue is the elongation measured over a gauge length of 50 mm and expressed in percent. The A value for elongation is the elongation measured over a gauge length of 5,65 oS (where Sois the initial cross-sectional area of the test-piece), and expresse

31、d in percent. 4.3 List of alloys and their mechanical properties Page Table 1 Aluminium EN AW-1050A Al 99,5 7 Table 2 Aluminium EN AW-1070A Al 99,7 9 Table 3 Aluminium EN AW-1080A Al 99,8(A) 11 Table 4 Aluminium EN AW-1200 Al 99,0 13 Table 5 Aluminium EN AW-1350 Al 99,5 15 Table 6 Alloy EN AW-2014 A

32、l Cu4SiMg 17 Table 7 Alloy EN AW-2014A Al Cu4SiMg(A) 19 Table 8 Alloy EN AW-2017A Al Cu4MgSi(A) 21 Table 9 Alloy EN AW-2024 Al Cu4Mg1 22 Table 10 Alloy EN AW-2618A Al Cu2Mg1,5Ni 24 Table 11 Alloy EN AW-3003 Al Mn1Cu 25 Table 12 Alloy EN AW-3004 Al Mn1Mg1 27 Table 13 Alloy EN AW-3005 Al Mn1Mg0,5 29 T

33、able 14 Alloy EN AW-3103 Al Mn1 31 Table 15 Alloy EN AW-3105 Al Mn0,5Mg0,5 33 Table 16 Alloy EN AW-4006 Al Si1Fe 34 Table 17 Alloy EN AW-4007 Al Si1,5Mn 35 Table 18 Alloy EN AW-4015 Al Si2Mn 36 Table 19 Alloy EN AW-4115 Al Si2MnMgCu 36 Table 20 Alloy EN AW-5005 Al Mg1(B), alloy EN AW-5005A Al Mg1(C)

34、 37 Table 21 Alloy EN AW-5010 AlMg 0,5Mn 39 Table 22 Alloy EN AW-5026 AI Mg4,5 MnSiFe 40 Table 23 Alloy EN AW-5040 Al Mg1,5Mn 40 Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-B

35、S EN 485-2:2013EN 485-2:2013 (E) 6 Table 24 Alloy EN AW-5049 Al Mg2Mn0,8 41 Table 25 Alloy EN AW-5050 Al Mg1,5(C) 43 Table 26 Alloy EN AW-5052 Al Mg2,5 45 Table 27 Alloy EN AW-5059 Al Mg5,5MnZnZr 47 Table 28 Alloy EN AW-5070 Al Mg4MnZn 48 Table 29 Alloy EN AW-5083 Al Mg4,5Mn0,7 49 Table 30 Alloy EN

36、AW-5086 Al Mg4 52 Table 31 Alloy EN AW-5088 AlMg5Mn0,4 54 Table 32 Alloy EN AW-5154A Al Mg3,5(A) 55 Table 33 Alloy EN AW-5182 Al Mg4,5Mn0,4 57 Table 34 Alloy EN AW-5251 Al Mg2Mn0,3 58 Table 35 Alloy EN AW-5383 Al Mg4,5Mn0,9 61 Table 36 Alloy EN AW-5449 Al Mg2Mn0,8(B) 63 Table 37 Alloy EN AW-5449A Al

37、 Mg2Mn0,8(C) 63 Table 38 Alloy EN AW-5454 Al Mg3Mn 64 Table 39 Alloy EN AW-5456 Al Mg5Mn1 66 Table 40 Alloy EN AW-5754 Al Mg3 67 Table 41 Alloy EN AW-6016 Al Si1,2Mg0,4 69 Table 42 Alloy EN AW-6025 Al Mg2,5SiMnCu 69 Table 43 Alloy EN AW-6061 Al Mg1SiCu 70 Table 44 Alloy EN AW-6082 Al Si1MgMn 72 Tabl

38、e 45 Alloy EN AW-7010 Al Zn6MgCu 74 Table 46 Alloy EN AW-7020 Al Zn4,5Mg1 77 Table 47 Alloy EN AW-7021 Al Zn5,5Mg1,5 78 Table 48 Alloy EN AW-7022 Al Zn5Mg3Cu 79 Table 49 Alloy EN AW-7075 Al Zn5,5MgCu 80 Table 50 Alloy EN AW-8011A Al FeSi(A) 83 Copyright European Committee for Standardization Provide

39、d by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 7 Table 1 Aluminium EN AW-1050A Al 99,5 Temper Specified thickness Tensile strength Yield strength Elongation min. Bend radiusaHardness RmRp0,2mm MPa MP

40、a % HBWaover up to min. max. min. max. A50 mm A 180 90 Fa 2,5 150,0 60 O 0,2 0,5 65 95 20 20 0 t 0 t 20 0,5 1,5 65 95 20 22 0 t 0 t 20 1,5 3,0 65 95 20 26 0 t 0 t 20 3,0 6,0 65 95 20 29 0,5 t 0,5 t 20 6,0 12,5 65 95 20 35 1,0 t 1,0 t 20 12,5 80,0 65 95 20 32 20 H111 0,2 0,5 65 95 20 20 0 t 0 t 20 0,

41、5 1,5 65 95 20 22 0 t 0 t 20 1,5 3,0 65 95 20 26 0 t 0 t 20 3,0 6,0 65 95 20 29 0,5 t 0,5 t 20 6,0 12,5 65 95 20 35 1,0 t 1,0 t 20 12,5 80,0 65 95 20 32 20 H112 6,0 12,5 75 30 20 23 12,5 80,0 70 25 20 22 H12 0,2 0,5 85 125 65 2 0,5 t 0 t 28 0,5 1,5 85 125 65 4 0,5 t 0 t 28 1,5 3,0 85 125 65 5 0,5 t

42、0,5 t 28 3,0 6,0 85 125 65 7 1,0 t 1,0 t 28 6,0 12,5 85 125 65 9 2,0 t 28 12,5 40,0 85 125 65 9 28 H14 0,2 0,5 105 145 85 2 1,0 t 0 t 34 0,5 1,5 105 145 85 2 1,0 t 0,5 t 34 1,5 3,0 105 145 85 4 1,0 t 1,0 t 34 3,0 6,0 105 145 85 5 1,5 t 34 6,0 12,5 105 145 85 6 2,5 t 34 12,5 25,0 105 145 85 6 34 H16

43、0,2 0,5 120 160 100 1 0,5 t 39 0,5 1,5 120 160 100 2 1,0 t 39 1,5 4,0 120 160 100 3 1,5 t 39 H18 0,2 0,5 135 120 1 1,0 t 42 0,5 1,5 140 120 2 2,0 t 42 1,5 3,0 140 120 2 3,0 t 42 H19 0,2 0,5 155 140 1 45 0,5 1,5 150 130 1 45 1,5 3,0 150 130 1 45 Copyright European Committee for Standardization Provid

44、ed by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 8 Table 1 (continued) Temper Specified thickness Tensile strength Yield strength Elongation min. Bend radiusaHardness RmRp0,2mm MPa MPa % HBWaover up t

45、o min. max. min. max. A50 mm A 180 90 H22 0,2 0,5 85 125 55 4 0,5 t 0 t 27 0,5 1,5 85 125 55 5 0,5 t 0 t 27 1,5 3,0 85 125 55 6 0,5 t 0,5 t 27 3,0 6,0 85 125 55 11 1,0 t 1,0 t 27 6,0 12,5 85 125 55 12 2,0 t 27 H24 0,2 0,5 105 145 75 3 1,0 t 0 t 33 0,5 1,5 105 145 75 4 1,0 t 0,5 t 33 1,5 3,0 105 145

46、75 5 1,0 t 1,0 t 33 3,0 6,0 105 145 75 8 1,5 t 1,5 t 33 6,0 12,5 105 145 75 8 2,5 t 33 H26 0,2 0,5 120 160 90 2 0,5 t 38 0,5 1,5 120 160 90 3 1,0 t 38 1,5 4,0 120 160 90 4 1,5 t 38 H28 0,2 0,5 140 110 2 1,0 t 41 0,5 1,5 140 110 2 2,0 t 41 1,5 3,0 140 110 3 3,0 t 41 aFor information only. Copyright E

47、uropean Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 485-2:2013EN 485-2:2013 (E) 9 Table 2 Aluminium EN AW-1070A Al 99,7 Temper Specified thickness Tensile strength Yield strength Elongation min. Bend radiusaHardness RmRp0,2mm MPa MPa % HBWaover up to min. max. min. max. A50 mmA 180 90 Fa 2,5 25,0 60 O 0,2 0,5 60 90 15 23 0 t 0 t 18 0,5 1,5 60 90 15 25 0 t 0 t 18 1,5 3,0 60 90 15 29 0 t 0 t 18 3,0 6,0 60 90 15 32 0,5 t 0,5 t 18 6,0 12,5 60 90 15 35 0,5 t 0,5 t 18 12,5 25,0 60 90 15