EN 4708-104-2017 en Aerospace series - Sleeving heat-shrinkable for binding insulation and identification - Part 104 Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperatu.pdf

《EN 4708-104-2017 en Aerospace series - Sleeving heat-shrinkable for binding insulation and identification - Part 104 Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperatu.pdf》由会员分享，可在线阅读，更多相关《EN 4708-104-2017 en Aerospace series - Sleeving heat-shrinkable for binding insulation and identification - Part 104 Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperatu.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards PublicationWB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06Aerospace series - Sleeving, heat-shrinkable, for binding, insulation and identificationPart 104: Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperature - 55 C to 175 C - Product StandardBS EN 4708-104:2017EU

2、ROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 4708-104 November 2017 ICS 49.060 English Version Aerospace series - Sleeving, heat-shrinkable, for binding, insulation and identification - Part 104: Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperature - 55 C to 175 C - Product Standa

3、rd Srie arospatiale - Manchons thermortractables, de jonction, isolement et identification - Partie 104 : Semi-rigide polyvinylidene fluoride (PVDF) - Temprature dutilisation - 55 C 175 C - Norme de produit Luft- und Raumfahrt - Wrmeschrumpfender Schlauch zur Befestigung, Isolierung und Identifizier

4、ung - Teil 104: Halbsteif, Polyvinylidenfluorid (PVDF) - Betriebstemperatur - 55 C bis 175 C - ProduktnormThis European Standard was approved by CEN on 18 September 2017. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European

5、 Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (E

6、nglish, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgiu

7、m, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden,

8、Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN na

9、tional Members. Ref. No. EN 4708-104:2017 ENational forewordThis British Standard is the UK implementation of EN 4708104:2017.The UK participation in its preparation was entrusted to Technical Committee ACE/6, Aerospace avionic electrical and fibre optic technology.A list of organizations represente

10、d on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2017 Published by BSI Standards Limited 2017ISBN 978 0 580 987

11、12 0ICS 49.060Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 December 2017.Amendments/corrigenda issued since publicationDate Text affectedBRITISH STANDARDBS

12、 EN 4708104:2017EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 4708-104 November 2017 ICS 49.060 English Version Aerospace series - Sleeving, heat-shrinkable, for binding, insulation and identification - Part 104: Semi-rigid polyvinylidene fluoride (PDVF) - Operating temperature - 55 C to 175

13、C - Product Standard Srie arospatiale - Manchons thermortractables, de jonction, isolement et identification - Partie 104 : Semi-rigide polyvinylidene fluoride (PVDF) - Temprature dutilisation - 55 C 175 C - Norme de produit Luft- und Raumfahrt - Wrmeschrumpfender Schlauch zur Befestigung, Isolierun

14、g und Identifizierung - Teil 104: Halbsteif, Polyvinylidenfluorid (PVDF) - Betriebstemperatur - 55 C bis 175 C - ProduktnormThis European Standard was approved by CEN on 18 September 2017. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for gi

15、ving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three of

16、ficial versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies

17、of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Sloveni

18、a, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved wo

19、rldwide for CEN national Members. Ref. No. EN 4708-104:2017 EBS EN 4708104:2017EN 4708-104:2017 (E) 2 Contents Page European foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions . 4 4 Required characteristics 5 5 Quality assurance 9 6 Designation . 10 7 Labelling and packaging . 10

20、8 Technical specification . 10 BS EN 4708104:2017EN 4708-104:2017 (E) 3 European foreword This document (EN 4708-104:2017) has been prepared by the Aerospace and Defence Industries Association of Europe - Standardization (ASD-STAN). After enquiries and votes carried out in accordance with the rules

21、of this Association, this European Standard has received the approval of the National Associations and the Official Services of the member countries of ASD, prior to its presentation to CEN. This European Standard shall be given the status of a national standard, either by publication of an identica

22、l text or by endorsement, at the latest by May 2018, and conflicting national standards shall be withdrawn at the latest by May 2018. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN shall not be held responsible for identifyin

23、g any or all such patent rights. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav R

24、epublic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 4708104:2017EN 4708-104:2017 (E) 4 1 Sco

25、pe This European Standard specifies the required characteristics for a heat-shrinkable, semi-rigid polyvinylidene sleeving for use in aircraft electrical systems at operating temperatures between 55 C and 175 C. This sleeving is basically transparent, but may be tinted. It is semi-rigid, tough and a

26、brasion resistant, and is suitable for use where strain relief and mechanical protection are required, or where their transparent properties are desirable. These sleevings are normally supplied with internal diameters up to 25,4 mm for shrink ratios of 2:1. Sizes other than those specifically listed

27、 in this European Standard may be available. These items shall be considered to comply with this European Standard if they comply with the property requirements listed in Tables 2, 3 and 4 except for dimensions and mass. 2 Normative references The following documents, in whole or in part, are normat

28、ively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 3909, Aerospace series Test fluids and test methods for elec

29、trical and optical components and sub-assemblies EN 4708-001, Aerospace series Sleeving, heat-shrinkable, for binding, insulation and identification Part 001: Technical specification EN 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirement (IEC 60684-1:2003) EN 60684

30、-2:2011, Flexible insulating sleeving Part 2: Methods of test (IEC 60684-2:2011) EN ISO 846:1997, Plastics Evaluation of the action of microorganisms (ISO 846:1997) HD 457 S1:1985, Code for designation of colours (IEC 60757:1983) ISO 1817:2005, Rubber, vulcanized Determination of the effect of liqui

31、ds MIL-PRF-87937, Performance specification: cleaning compound, aerospace equipment 1)AMS 1476B:2004, Deodorant, Aircraft Toilet 2)3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 60684-1:2003 apply. 1) Published by: Department of Defense (DoD). http:/

32、www.defenselink.mil/ 2) Published by: SAE National (US) Society of Automotive Engineers. http:/www.sae.org/ BS EN 4708104:2017EN 4708-104:2017 (E) 5 4 Required characteristics 4.1 Dimension and mass See Table 1. Table 1 Dimensional and mass requirements Size code Internal diameter Recovered wall thi

33、ckness Mass per unit length max. mm mm g/m Expanded min. Recovered max. 1,2/0,6 1,2 0,6 0,25 0,05 1,5 1,6/0,8 1,6 0,8 0,25 0,05 1,9 2,4/1,2 2,4 1,2 0,25 0,05 2,5 3,2/1,6 3,2 1,6 0,25 0,05 3,2 4,8/2,4 4,8 2,4 0,25 0,05 4,6 6,4/3,2 6,4 3,2 0,30 0,10 8,1 9,5/4,8 9,5 4,8 0,30 0,10 11,8 12,7/6,4 12,7 6,4

34、 0,30 0,10 15,4 19,0/9,5 19,0 9,5 0,45 0,10 31,2 25,4/12,7 25,4 12,7 0,50 0,10 45,1 4.2 Conditions of test Unless otherwise specified, the sleeving shall be shrunk in a forced air circulation oven for (5 1) min. at 200 C 5 C prior to testing. 4.3 Tests See Table 2. BS EN 4708104:2017EN 4708-104:2017

35、 (E) 6 Table 2 Tests Designation of the test EN 60684-2:2011 Clause or subclause Requirements Remarks Dimensions 3 internal diameter 3.1.2 Table 1 wall thickness 3.3.2 Table 1 concentricity 3.3.3 expanded 65 % min. recovered 85 % min. Density 4 Not applicable See Clause 38. Heat shock 6 Heat at 250

36、C 5 C Tensile strength 19.1 and 19.2 15 MPa min. Elongation at break 19.1 and 19.2 75 % min. Longitudinal change 9 0 to 10 % max. Heat the expanded sleeving at 200 C 5 C for (5 1) min. Bending after heating 13 Not applicable See Clauses 6, 39 and 50. Bending at low temperature 14 No cracks shall be

37、visible. Condition at 55 C 3 C. For strips, the mandrel shall be no more than 10 times the wall thickness. Full section sleeving is tested unfilled and the mandrel shall be no more than 10 times the outer diameter. Dimensional stability during storage 16 The dimensions shall be as specified in Table

38、 1. Tensile strength 19.1 and 19.2 35 MPa min. Use a jaw separation rate of 100 mm/min. Below 6,5 mm diameter test as sleeving, at 6,5 mm diameter and above test as dumb-bells. Elongation at break 19.1 and 19.2 150 % min. Secant modulus at 2 % elongation 19.4 Between 250 MPa and 750 MPa Breakdown vo

39、ltage 21 Table 3 Volume resistivity 23 at ambient temperature 23.4.2 109 m min. after damp heat 23.4.4 108 m min. Flame propagation 26 Time of burning Method C 15 s max. Length burned 75 mm max. Oxygen index 27 Not applicable BS EN 4708104:2017EN 4708-104:2017 (E) 7 Designation of the test EN 60684-

40、2:2011 Clause or subclause Requirements Remarks Transparency 28 Print shall be eligible Transparent only Corrosion resistance (Tensile strengh and elongation) 32 Not applicable See Clause 33. Copper corrosion 33 None above the allowable 8 % max. Heat for (16 0,5) h at 175 C 3 C Colour fastness to li

41、ght 34 The colour contrast between the exposed and unexposed parts of the specimens shall be equal to or less than that of the fastness standard. Fastness standard No. 5 Resistance to selected fluids 36 Use the fluids and test temperatures specified in Table 4. Immersion time (24 1) h Tensile streng

42、th 19.1 and 19.2 25 MPa min. Elongation at break 19.1 and 19.2 50 % min. Thermal endurance 37 Not applicable See Clause 50. Mass per unit length 38 Table 1 Heat ageing 39 Heat at 200 C 5 C Tensile strength 19.1 and 19.2 15 MPa min. Elongation at break 19.1 and 19.2 75 % min. Water absorption 40 0,5

43、% max. Restricted shrinkage Visual 41 No cracking or splitting Heat at 225 C 5 C Perform the visual determination only Colour stability to heat 42 Not applicable See Clause 34. Smoke index 43 Not applicable Toxicity 44 Not applicable Halogen content 45 Not applicable Acid gas generatiion 46 Not appl

44、icable Long term ageing 50 100 % min. Ageing temperature shall be 175 C 3 C Elongation 19.1 and 19.2 Dynamic shear at ambient temperature 51 Not applicable Dynamic shear at elevated temperature 52 Not applicable Dynamic shear after heat shock and heat ageing 53 Not applicable Rolling drum peel to al

45、uminium 54 Not applicable Aluminium rod dynamic shear 55 Not applicable BS EN 4708104:2017EN 4708-104:2017 (E) 8 Designation of the test EN 60684-2:2011 Clause or subclause Requirements Remarks Sealing 56 Not applicable Adhesive T peel strength 57 Not applicable Fungus resistance The test method sha

46、ll be EN ISO 846:1997, method B. 56-day exposure Tensile strength 19.1 and 19.2 35 MPa min. Elongation at break 19.1 and 19.2 150 % min. Shelf life aEN 4708-001, 4.7 The dimensions shall be as specified in Table 1. Condition the sleeving for 60 months at ambient temperature prior to testing; interim

47、 measurements shall be made every 12 months. Artifical weathering EN 4708-001, Table 2 Tensile strength 24 MPa min. Elongation at break 105 % min. aDue to the duration of this test, lack of completion of this test shall not preclude certification of this sleeving. Additional evidence of compliance w

48、ith this requirement in the interim shall be as agreed between the supplier and/or the approval authority and/or the customer. 4.4 The breakdown voltage The breakdown voltage shall be determined by any of the methods described in EN 60684-2:2011, 21.2, 21.3 and 21.4. The central value shall comply w

49、ith the minimum value in Table 3. The rate of application of the voltage shall be 500 V/s. Table 3 Requirements for breakdown voltage Nominal recovered wall thickness a Breakdown voltage min. mm kV 0,25 5,0 0,30 6,0 0,45 9,0 0,50 10,0 aFor non-standard wall thicknesses, the electric strength shall be at least that of the next smaller standard wall thickness. For wall thicknesses sma