EN 13733-2002 en Products and Systems for the Protection and Repair of Concrete Structures - Test Methods - Determination of the Durability of Structural Bonding Agents《混凝土结构保护和修缮用.pdf

《EN 13733-2002 en Products and Systems for the Protection and Repair of Concrete Structures - Test Methods - Determination of the Durability of Structural Bonding Agents《混凝土结构保护和修缮用.pdf》由会员分享，可在线阅读，更多相关《EN 13733-2002 en Products and Systems for the Protection and Repair of Concrete Structures - Test Methods - Determination of the Durability of Structural Bonding Agents《混凝土结构保护和修缮用.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD Products and systems for the protection and repair of concrete structure s Test methods Determination of the durability of structural bonding agents The European Standard EN 13733:2002 has the status ofa British Standard ICs 83.180; 91.080.40 BS EN 13733:2002 WkNb A%“ U- rn% E rn NO

2、 COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW $ present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate

3、them in the UK. - A list of organizations represented on this subcommittee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entit

4、led “International Standards Correspondence Index”, or by using the “Search”faci1ity ofthe BSI Electronic Catalogue or ofBritish Stan dards Online. This publication does not purport to include all the necessary provisions of a contract. Users of this publication are responsible for their correct app

5、lication. Compliance with a British Standard does not ofitself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 13 and a back cover. The BSI copyright date displayed in this document indicates when th

6、e document was last issued. Amendments issued since publication Amd.No. I Date I Comments O BSI 1 July 2002 ISBN O 580 39978 8 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13733 May 2002 ICs 83.180; 91.080.40 English version Products and systems for the protection and repair of concrete stru

7、ctures - Tests methods - Determination of the durability of structural bonding agents Produits et systmes pour la protection et la rparation des structures en bton - Mthodes dessai - Dtermination de la durabilit des produits de collage structural Produkte und Systeme fr den Schutz und die Instandset

8、zung von Betontragwerken - Prfverfahren - Bestimmung der Dauerhaftigkeit von Klebstoffen fr konstruktive Zwecke This European Standard was approved by CEN on 30 December 2001 CEN members are bound to comply with the CENKENELEC Internal Regulations which stipulate the conditions for giving this Europ

9、ean Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Management Centre or to any CEN member. This European Standard exists in three official versions (English, F

10、rench, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Czech Republic, De

11、nmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION EUROPISCHES KOMITEE FR NORMUNG COMIT EUROPEN DE NORMALISATION Management Centre: rue de Stassart,

12、36 B-1050 Brussels O 2002 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13733:2002 E EN 13733:2002 (E) Contents page Foreword 3 1 2 3 4 4.1 4.2 4.3 5 5.1 5.2 6 6.1 6.2 6.3 7 7.1 7.2 8 8.1 8.2 Scope 4 Normative references 4 Princi

13、ple 4 Equipment . 4 Concrete to concrete composites (see Figures la) and 1 b) 4 Steel to steel composite (see Figure 2) . 5 Environmental cabinets 5 Environmental regimes . 5 Thermal Cycle . 5 Warm-moist environment 5 Preparation of test specimens 5 General 5 Concrete to concrete composites 6 Produc

14、tion of steel-to-steel composite specimens 6 Test procedures . 6 Testing of the concrete-to-concrete specimens . 6 Testing of steel-to-steel specimens . 7 Test report 7 Concrete to concrete composite specimen 7 Steel-to-steel composite specimen 7 2 EN 13733:2002 (E) Foreword This document EN 13733:2

15、002 has been prepared by Technical Committee CEN/TC 104 “Concrete and related products“, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by November 2002, and

16、 conflicting national standards shall be withdrawn at the latest by December 2002. This standard does not supersede any other European Standard. It has been prepared by Sub-Committee 8 “Products and systems for the protection and repair of concrete structures“, the secretariat of which is held by AF

17、NOR. According to the CENKENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands,

18、Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. 3 EN 13733:2002 (E) 1 Scope The purpose of this European Standard is to define laboratory methods of testing to ascertain the durability of structural bonding agents in composite systems involving the bonding of hardened concrete t

19、o hardened concrete, fresh concrete to hardened concrete and steel-to-steel. 2 Normative references This European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text, and the publications

20、are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies (including amendments

21、). EN 1766, Products and systems for the protection and repair of concrete structures - Test methods - Reference concretes for testing. EN 12390-4, Testing hardened concrete - Part 4: Compressive strength - Specification for testing machines. IS0 8501-1, Preparation of steel substrates before applic

22、ation of paints and related products - Visual assessments of surface cleanliness - Part I: Rust grades and preparation grades of uncoated steel substrates and of steel substrates after overall removal of previous coatings. 3 Principle This standard describes a thermal cycling regime and a warm-moist

23、 environment, which are applied in turn to composite systems incorporating a structural bonding agent. For testing the structural bonding of concrete, the specimen consists of three concrete cubes bonded in line which are then exposed to an environmental regime prior to being subjected to a compress

24、ive shear force applied in the plane of the bond line. For testing the structural bonding of steel, two steel plates are bonded together and subjected to a cleavage force applied by the insertion of a wedge. The stressed specimen is then exposed to an environmental regime during which measurements a

25、re taken. 4 Equipment 4.1 Concrete to concrete composites (see Figures la) and lb) 4.1.1 Steel mould for casting 100 mm x 100 mm x 100 mm concrete cubes. 4.1.2 Jig to ensure accurate alignment when bonding the 100 mm x 100 mm x 100 mm cubes. 4.1.3 Steel mould 100 mm x 100 mm x 302 mm for casting fre

26、sh concrete to hardened concrete specimens. 4.1.4 conforming to 6.2.1 and 6.2.2 in compressive shear. Compression testing machine conforming to EN 12390-4 capable of testing the bonded specimens 4.1.5 Test rig support to align the bonded cube assembly securely in the testing machine whilst the compr

27、essive shearing force is applied parallel to the planes of the bonds and distributed evenly between them, as depicted in Figures la) and 1 b). 4 EN 13733:2002 (E) 4.2 Steel to steel composite (see Figure 2) 4.2.1 2 steel plates 150 mm x 25 mm x 3,O mm. 4.2.2 Steel wedge having dimensions depicted in

28、 Figure 2 4.2.3 PVC tape. 4.2.4 Travelling microscope of magnification 15, fitted with a rule graduated in mm. 4.3 Environmental cabinets 4.3.1 4.3.2 Temperature controlled conditioning cabinet adjustable to within 1 C. Programmable temperature cabinet capable of heating to (+ 55 12) OC and cooling

29、to (- 25 12) C. 4.3.3 Climatic chamber capable of heating to (+ 40 12) OC at (95 15) % relative humidity. 5 Environmental regimes 5.1 Thermal Cycle Thermal cycling takes place in a programmable temperature cabinet. The thermal cycling regime is depicted in Figure 3. After 15 min initial cooling from

30、 20 OC, the cycle starts from - 25 OC according to the detail given in Figure 3. Each thermal cycle consists of a cooling phase over 6 h in air at a temperature of (- 25 12) OC followed by a heatinq phase over 6 h in air at a temperature of (+ 55 12) C. The cooling and the heating shall take place a

31、t a rate of 3 C/min. One cycle lasts for 12 h and comprises the following stages : - 333 min air storage at T= (- 25 12) OC ; - 27 min heating in air to T= (+ 55 12) OC ; - 333 min air storage at T= (+ 55 I 2) OC ; - 27 min cooling in air to T= (- 25 12) C. During any interruption of the cycling the

32、 specimen shall be stored at standard climate conditions (21 12) C/(60 I IO) % relative humidity). The complete thermal cycling regime shall consist of 50 cycles. 5.2 Warm-moist environment The warm-moist environmental regime shall consist of six months exposure to an environment maintained at (+ 40

33、 12) OC, (95 15) % relative humidity). During any interruption to the regime the specimen shall be stored at standard climate conditions (21 12) C/(60 IIO) % relative humidity). 6 Preparation of test specimens 6.1 General For applications involving bonded plate reinforcement six specimens of hardene

34、d concrete to hardened concrete and six specimens of steel-to-steel shall be produced for testing associated with each environmental regime. 5 EN 13733:2002 (E) For applications involving bonded mortar or concrete six specimens of either hardened concrete to hardened concrete or fresh concrete to ha

35、rdened concrete shall be produced for testing associated with each environmental reg i m e. For each environmental regime three specimens shall be tested. A further three specimens shall be maintained at standard climate conditions (21 12) OC, (60 I IO) % relative humidity) for control purposes. 6.2

36、 Concrete to concrete composites 6.2.1 Production of the hardened concrete to hardened concrete specimens Concrete cubes of dimensions 100 mm x 100 mm x 100 mm shall be cast and cured in accordance with EN 1766. On one cube, two of the formed faces to be bonded and on two cubes, the formed face to b

37、e bonded, shall be gritblasted in accordance with the requirements of EN 1766. Immediately prior to bonding these gritblasted surfaces shall be vacuumed to remove any dust. Mix the components of the adhesive to be tested and apply an even layer approximately Imm thick to each of the prepared concret

38、e surfaces in accordance with the manufacturers instructions. Bond the three cubes together to produce a specimen with a bond line approximately 1 mm thick as shown in Figure 1. It is necessary to use a jig to ensure accurate alignment of adherents. Allow the adhesive to cure for at least 7 days at

39、(+ 21 12) OC, (60 I 1 O) % relative humidity. 6.2.2 Production of the fresh concrete to hardened concrete specimens Concrete cubes of dimensions 100 mm x 100 mm x 100 mm shall be cast and cured in accordance with EN 1766. On two of the cubes, the cast face to be bonded shall be gritblasted in accord

40、ance with the requirements of EN 1766. Immediately prior to bonding this gritblasted surface shall be vacuumed to remove any dust. The components of the adhesive shall be mixed and an even layer approximately 1 mm thick applied to the prepared concrete surfaces in accordance with the manufacturers i

41、nstructions. Place the two cubes at a separation of (102 I0,2) mm in the 100 mm x 100 mm x 302 mm mould. The concrete shall be poured into the central 100 mm x 100 mm x 100 mm volume and carefully compacted by hand in accordance with EN 1766. The complete assembly shall be cured for at least 28 days

42、 at (+ 21 12) OC, (60 I IO) % relative humidity. 6.3 Production of steel-to-steel composite specimens Degrease one side of each steel plate using a suitable degreasing agent and then gritblast to grade Sa 2.5 according to IS0 8501-1. The gritblasted surface shall then be vacuumed to remove any dust.

43、 Glue PVC tape (12,5 mm wide) on one end of the plate so that the wedge can be inserted there (see Figure 2). Mix the components of the adhesive and apply an even layer approximately 0,5 mm thick to each of the prepared steel surfaces in accordance with the manufacturers instructions. Bond the steel

44、 plates together in a suitable jig (for example, see Figure 4) in order to achieve a glueline thickness of (0,65 I0,05) mm. Allow the adhesive to cure for at least seven days at (+ 21 12) OC, (60 I IO) % relative humidity, before inserting the wedge at a rate of 50 mm/min to its full depth of 25 mm

45、in a suitable compression testing machine. 7 Test procedures 7.1 Testing of the concrete-to-concrete specimens After the specimens have undergone the appropriate environmental regime, they shall be conditioned for 24 h at (21 12) OC and (60 I IO) % relative humidity. The test and control specimens s

46、hall then be tested in shear as 6 EN 13733:2002 (E) shown in Figures la) and Ib). Load shall be applied at a rate of (60 120) kN/min. The load at failure in kN and the position of failure shall be noted in each case. 7.2 Testing of steel-to-steel specimens Immediately prior to commencement of the en

47、vironmental regime the crack length shall be measured on both sides of each test and control specimen to an accuracy of I0,l mm using, for example, a travelling microscope. The test specimens shall be placed immediately into the environmental chamber or cabinet, and measurements taken after 24 h, an

48、d then at 24 h intervals until the crack length has stabilised. Thereafter, measurements shall be taken at 7 day intervals until the end of the environmental regime. At each measurement the position of the crack (.e. within the adhesive or at an interface) shall be noted. 8 Testreport 8.1 Concrete t

49、o concrete composite specimen The report shall include the following information for each determination: a reference to this test method standard; name and address of the test laboratory; identification number and date of the test report; name and address of the manufacturer or supplier of the product; name and identification marks or batch number of the product; date of supply of the product; date of preparation of the test specimens and any deviation from the prescribed method of preparation; conditions of storage of prepared specimens prior t