DIN EN ISO 14273-2016 Resistance welding - Destructive testing of welds - Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds .pdf

《DIN EN ISO 14273-2016 Resistance welding - Destructive testing of welds - Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds .pdf》由会员分享，可在线阅读，更多相关《DIN EN ISO 14273-2016 Resistance welding - Destructive testing of welds - Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds .pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、November 2016 English price group 9No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 25.160.40!%u_“2588260www.din.deD

2、IN EN ISO 14273Resistance welding Destructive testing of welds Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds (ISO 14273:2016);English version EN ISO 14273:2016,English translation of DIN EN ISO 14273:2016-11Widerstandsschweien Zerstrende Pr

3、fung von Schweiverbindungen Probenmae und Verfahren fr die Scherzugprfung an Widerstandspunkt, Rollennaht und Buckelschweiungen mit geprgten Buckeln (ISO 14273:2016);Englische Fassung EN ISO 14273:2016,Englische bersetzung von DIN EN ISO 14273:2016-11Soudage par rsistance Essais destructifs des soud

4、ures Dimensions des prouvettes et mode opratoire pour lessai de tractioncisaillement des soudures par rsistance par points et par bossages (ISO 14273:2016);Version anglaise EN ISO 14273:2016,Traduction anglaise de DIN EN ISO 14273:2016-11SupersedesDIN EN ISO 14273:200203www.beuth.deDocument comprise

5、s 14 pagesDTranslation by DIN-Sprachendienst.In case of doubt, the German-language original shall be considered authoritative.11.16 DIN EN ISO 14273:2016-11 2 A comma is used as the decimal marker. National foreword This document (EN ISO 14273:2016) has been prepared by Technical Committee ISO/TC 44

6、 “Welding and allied processes” in collaboration with Technical Committee CEN/TC 121 “Welding and allied processes” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was DIN-Normenausschuss Schweien und verwandte Verfahren (DIN Standards Committee Welding and Allie

7、d Processes), Working Committee NA 092-00-12 AA Widerstandsschweien (DVS AG V 3). The DIN Standards corresponding to the International Standards referred to in this document are as follows: ISO 7500-1 DIN EN ISO 7500-1 ISO 14329 DIN EN ISO 14329 ISO 17677-1 DIN EN ISO 17677-1 Amendments This standar

8、d differs from DIN EN ISO 14273:2002-03 as follows: a) figures showing failure types, and procedures for tensile shear and cross tension testing in accordance with ISO 14329:2003 are no longer included; b) the standard has been adapted to DIN EN ISO 17667-1; c) the standard has been technically and

9、editorially revised. Previous editions DIN EN ISO 14273: 2002-03 National Annex NA (informative) Bibliography DIN EN ISO 7500-1, Metallic materials Calibration and verification of static uniaxial testing machines Part 1: Tension/compression testing machines Calibration and verification of the force-

10、measuring system DIN EN ISO 14329, Resistance welding Destructive tests of welds Failure types and geometric measurements for resistance spot, seam and projection welds DIN EN ISO 17677-1, Resistance welding Vocabulary Part 1: Spot, projection and seam welding EUROPEAN STANDARD NORME EUROPENNE EUROP

11、ISCHE NORM EN ISO 14273 March 2016 ICS 25.160.40 Supersedes EN ISO 14273:2001English Version Resistance welding - Destructive testing of welds - Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds (ISO 14273:2016) Soudage par rsistance - Essais d

12、estructifs des soudures - Dimensions des prouvettes et mode opratoire pour lessai de traction-cisaillement des soudures par rsistance par points et par bossages (ISO 14273:2016) Widerstandsschweien - Zerstrende Prfung von Schweiverbindungen - Probenmae und Verfahren fr die Scherzugprfung an Widersta

13、ndspunkt-, Rollennaht- und Buckelschweiungen mit geprgten Buckeln (ISO 14273:2016) This European Standard was approved by CEN on 13 December 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of

14、a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German).

15、 A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cy

16、prus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United K

17、ingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2016 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO

18、14273:2016 EEuropean foreword .3Introduction 51 Scope . 62 Normative references 63 Terms and definitions . 64 Test pieces and specimens . 65 Test equipment and testing procedure . 86 Test report 10Annex A (informative) Specimen size Saturated strength condition 11Bibliography . 12Contents PageDIN EN

19、 ISO 14273:2016-11 EN ISO 14273:2016 (E) 2Foreword .4European foreword This document (EN ISO 14273:2016) has been prepared by IIW International Institute of Welding in collaboration with Technical Committee CEN/TC 121 “Welding and allied processes” the secretariat of which is held by DIN. This Europ

20、ean Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2016, and conflicting national standards shall be withdrawn at the latest by September 2016. Attention is drawn to the possibility that some of the

21、elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 14273:2001. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the fo

22、llowing countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands

23、, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 14273:2016 has been approved by CEN as EN ISO 14273:2016 without any modification. DIN EN ISO 14273:2016-11 EN ISO 14273:2016 (E)3 ForewordISO (the I

24、nternational Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee

25、has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnica

26、l standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in a

27、ccordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. De

28、tails of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an

29、 endorsement.For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary informationThe committee r

30、esponsible for this document is ISO/IIW, International Institute of Welding, Commission III.This second edition cancels and replaces the first edition (ISO 14273:2000), which has been technically revised.Requests for official interpretations of any aspect of this International Standard should be dir

31、ected to the ISO Central Secretariat, who will forward them to the IIW Secretariat for an official response.DIN EN ISO 14273:2016-11 EN ISO 14273:2016 (E) 4 IntroductionThis edition of ISO 14273 no longer includes figures showing failure types and modes for tensile shear and cross tension testing in

32、 accordance with ISO 14329.ISO 14273 has been revised to align it with ISO 17677-1.DIN EN ISO 14273:2016-11 EN ISO 14273:2016 (E)5 1 ScopeThis International Standard specifies specimen dimensions and a testing procedure for tensile shear testing of spot and embossed projection welds, in overlapping

33、sheets, in any metallic material of thickness 0,5 mm to 10 mm, where the welds have a maximum diameter of 7t (where t is the sheet thickness in mm).The object of tensile shear testing is to determine the tensile shear force that the test specimen can sustain.2 Normative referencesThe following docum

34、ents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.ISO 7500-1, Metallic materi

35、als Verification of static uniaxial testing machines Part 1: Tension/compression testing machines Verification and calibration of the force-measuring systemISO 17677-1, Resistance welding Vocabulary Part 1: Spot, projection and seam welding3 Terms and definitionsFor the purposes of this document, th

36、e terms and definitions given in ISO 17677-1 and the following apply.3.1tensile shear strengthTSSmaximum (tensile shear) force obtained from this test3.2tensile shear forceforce applied on test specimen during tensile shear testing3.3saturated strength conditioncondition where beyond a certain speci

37、men width and overlap length, the weld strength does not increase4 Test pieces and specimensThe configuration of the test specimen is shown in Figure 1 and Table 1.The test specimen dimensions given in Table 1 are for testing in the saturated strength condition for weld diameters up to 5t.For weld d

38、iameters between 5t and 7t, tensile shear strength values can be underestimated when using the values given in Table 1 (see Annex A). When testing weld diameters over 5t in the saturated DIN EN ISO 14273:2016-11 EN ISO 14273:2016 (E) 6 strength condition, the minimum coupon width shall be 7 to 10 ti

39、mes of the weld diameter (see Figure A.1).Table 1 Tensile shear test specimen dimensions for weld diameter 5tThickness Overlap Specimen width aSpecimen lengthFree length be-tween clampsLength of individual test piecest a b lslfltmm mm mm mm mm mm0,5 t 1,5 35 45 (30) 175 95 1051,5 3 mm or where the r

40、atio of the thicknesses of the two sheets is 1,4, shim plates shall be used for clamping the test specimen in the grips of the tensile testing machine. The shim plate shall be as thick as the sheet of the test specimen as shown in Figure 3.Testing shall be carried out at room temperature.DIN EN ISO

41、14273:2016-11 EN ISO 14273:2016 (E) 8 11a) Profile without shim plates b) Profile with shim plates c) Front viewKey1 shim plateFigure 3 Tensile shear test configurationA load-displacement curve shall be plotted in order to give information on the deformation of the test specimen. Examples are shown

42、in Figure 4.The test results shall be recorded with values of the tensile shear strength in accordance with this test and type of failure mode and weld diameter of each weld in accordance with ISO 17677-1. Force measurement accuracy shall be equal or less than 1 %.DIN EN ISO 14273:2016-11 EN ISO 142

43、73:2016 (E)9 F0TSSTSSlKeyTSS tensile shear strengthF force (load)l crosshead displacementFigure 4 Examples of load-displacement curves for the tensile shear test (Not to scale)6 Test reportThe test report shall contain at least the following information:a) a reference to this International Standard,

44、 i.e. ISO 14273:2016;b) the welding process used;c) the welding conditions and equipment;d) the material and its condition;e) the dimensions of the test piece and of the test specimen;f) individual values, mean value and standard deviation of the tensile shear strength in kN;g) failure description (

45、symmetrical plug failure, asymmetrical plug failure, partial failure, plug failure, interfacial failure, etc.);h) individual values, mean value and standard deviation of the weld diameter;i) special remarks if any.DIN EN ISO 14273:2016-11 EN ISO 14273:2016 (E) 10 Annex A (informative) Specimen size

46、Saturated strength conditionThe test specimen dimensions specified in this standard are larger than normal test specimen sizes. This is in order to obtain the maximum measured strength of the welds in the saturated strength condition. Specimen width values, b, in parentheses given in Table 1 indicat

47、e around a 10 % reduction in test piece size.The relationship between the test piece size and measured weld strength (tensile shear strength) is shown in Figure A.1.a) TSS vs. test specimen width (Mild steel sheets, t = 0,8 3,2 mm, a = 100 mma)b) TSS vs. overlap length of test specimen (Mild steel sheets, t = 0,8 2,3 mm, b = 80 100 mmb)Key1 welddnnugget diametera/dnnon-dimensional overlap lengthb/dnnon-dimensional widthTSS(x)/TSS() non-dimensional weld