DIN EN 15681-1-2016 Glass in building - Basic alumino silicate glass products - Part 1 Definitions and general physical and mechanical properties German version EN 15681-1 2016《建筑用.pdf

《DIN EN 15681-1-2016 Glass in building - Basic alumino silicate glass products - Part 1 Definitions and general physical and mechanical properties German version EN 15681-1 2016《建筑用.pdf》由会员分享，可在线阅读，更多相关《DIN EN 15681-1-2016 Glass in building - Basic alumino silicate glass products - Part 1 Definitions and general physical and mechanical properties German version EN 15681-1 2016《建筑用.pdf（19页珍藏版）》请在麦多课文档分享上搜索。

1、June 2016 English price group 12No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 81.040.20!%VpT“2517749www.din.deDIN

2、 EN 15681-1Glass in building Basic alumino silicate glass products Part 1: Definitions and general physical and mechanical properties;English version EN 15681-1:2016,English translation of DIN EN 15681-1:2016-06Glas im Bauwesen Basiserzeugnisse aus Alumo-Silicatglas Teil 1: Definitionen und allgemei

3、ne physikalische und mechanische Eigenschaften;Englische Fassung EN 15681-1:2016,Englische bersetzung von DIN EN 15681-1:2016-06Verre dans la construction Produits de base: verre aluminosilicate Partie 1: Dfinitions et proprits physiques et mcaniques gnrales;Version anglaise EN 15681-1:2016,Traducti

4、on anglaise de DIN EN 15681-1:2016-06www.beuth.deDTranslation by DIN-Sprachendienst.In case of doubt, the German-language original shall be considered authoritative.Document comprises 19 pages 06.16 2 A comma is used as the decimal marker. National foreword This document (EN 15681-1:2016) has been p

5、repared by Technical Committee CEN/TC 129 “Glass in building” (Secretariat: NBN, Belgium). The responsible German body involved in its preparation was DIN-Normenausschuss Bauwesen (DIN Standards Committee Building and Civil Engineering), Working Committee NA 005-09-29 AA Glas im Bauwesen (SpA zu CEN

6、/TC 129 und ISO/TC 160; SpA zu CEN/TC 129/WG 1, CEN/TC 129/WG 2, CEN/TC 129/WG 3, CEN/TC 129/WG 5, CEN/TC 129/WG 6, CEN/TC 129/WG 7, CEN/TC 129/WG 8, CEN/TC 129/WG 9, CEN/TC 129/WG 10, CEN/TC 129/WG 12, CEN/TC 129/WG 13, CEN/TC 129/WG 14, CEN/TC 129/WG 15, CEN/TC 129/WG 17, CEN/TC 129/WG 18, CEN/TC

7、129/WG 19, ISO/TC 160/SC 1, ISO/TC 160/SC 1/WG 1, ISO/TC 160/SC 1/WG 2, ISO/TC 160/SC 1/WG 3, ISO/TC 160/SC 1/WG 5, ISO/TC 160/SC 1/WG 6, ISO/TC 160/SC 1/WG 7, ISO/TC 160/SC 1/WG 8, ISO/TC 160/SC 1/WG 9, ISO/TC 160/SC 2, ISO/TC 160/SC 2/WG 1, ISO/TC 160/SC 2/WG 2, ISO/TC 160/SC 2/WG 3, ISO/TC 160/SC

8、 2/WG 5, ISO/TC 160/SC 2/WG 6, ISO/TC 160/SC 2/WG 7). DIN EN 15681-1:2016-06 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 15681-1 January 2016 ICS 81.040.20 English Version Glass in building - Basic alumino silicate glass products - Part 1: Definitions and general physical and mechanical pro

9、perties Verre dans la construction - Produits de base : verre aluminosilicate - Partie 1 : Dfinitions et proprits physiques et mcaniques gnrales Glas im Bauwesen - Basiserzeugnisse aus Alumo-Silicatglas - Teil 1: Definitionen und allgemeine physikalische und mechanische Eigenschaften This European S

10、tandard was approved by CEN on 30 November 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concer

11、ning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into

12、 its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Ge

13、rmany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey andUnited Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE F

14、R NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2016 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 15681-1:2016 EEN 15681-1:2016 (E) 2 Contents Page European foreword . 3 1 Scope 4 2 Normative reference

15、s 4 3 Terms and definitions . 4 4 Chemical composition . 6 4.1 General 6 4.2 Tint . 6 5 Physical and mechanical characteristics 6 5.1 General characteristics . 6 5.2 Characteristic bending strength 7 5.3 Designation of clear alumino silicate glass 7 5.3.1 General 7 5.3.2 Clear transparent alumino si

16、licate glass 8 5.3.3 Clear translucent alumino silicate glass . 8 5.4 Stability of physical and chemical characteristics 9 6 Dimensional requirements 9 6.1 Manufacturing dimensions 9 6.1.1 Stock sizes 9 6.1.2 Supplied and final cut sizes . 9 6.2 Thickness and thickness tolerances . 9 6.3 Length, wid

17、th and squareness . 10 7 Quality requirements . 10 7.1 General . 10 7.2 Methods of observation and measurement 11 7.2.1 Optical faults 11 7.2.2 Visual faults (spot faults, linear/extended faults), all types of basic alumino silicate glass . 12 7.3 Acceptance levels . 13 7.3.1 Optical faults 13 7.3.2

18、 Visual faults (spot faults, linear/extended faults), all types of basic alumino silicate glass . 13 7.4 Edge defects for final cut sizes . 14 7.4.1 Entrant and emergent faults 14 7.4.2 Bevel . 14 7.4.3 Limitations on edge defects 14 8 Designation. 15 Annex A (informative) Complementary information

19、related to REACH . 16 Bibliography . 17 DIN EN 15681-1:2016-06 EN 15681-1:2016 (E) 3 European foreword This document (EN 15681-1:2016) has been prepared by Technical Committee CEN/TC 129 “Glass in building”, the secretariat of which is held by NBN. This European Standard shall be given the status of

20、 a national standard, either by publication of an identical text or by endorsement, at the latest by July 2016, and conflicting national standards shall be withdrawn at the latest by July 2016. Attention is drawn to the possibility that some of the elements of this document may be the subject of pat

21、ent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document has been prepared under a mandate given to CEN by the European Commission and the European Free Trade Association. This European Standard consists of the following parts: EN 1568

22、1-1 Glass in Building Basic alumino silicate glass products Part 1: Definitions and general physical and mechanical properties; EN 15681-2 Glass in Building Basic alumino silicate glass products Part 2: Evaluation of conformity / Product standard1. According to the CEN-CENELEC Internal Regulations,

23、the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Lat

24、via, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. 1Standard under development. DIN EN 15681-1:2016-06 EN 15681-1:2016 (E) 4 1 Scope This Part of this European Standard specifies and classi

25、fies basic alumino silicate glass products, indicates their chemical composition, their main physical and mechanical characteristics, their dimensional and their minimum quality requirements (in respect of optical and visual faults). This European Standard applies to basic alumino silicate glasses s

26、upplied in stock sizes, supplied sizes or in cut sizes for final end use. This European Standard does not apply to final cut sizes having a dimension less than 100 mm or a surface area less than 0,05 m2. 2 Normative references The following documents, in whole or in part, are normatively referenced

27、in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 410, Glass in building - Determination of luminous and solar characteristics

28、of glazing ISO 9385, Glass and glass-ceramics Knoop hardness test 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 alumino silicate glass silicate glass containing between 5,8 % to 16,2 % aluminium and with a chemical composition according to

29、4.1 of this standard 3.2 alumino silicate float glass flat, transparent, clear or tinted alumino silicate glass having parallel and polished faces obtained by continuous casting and floatation on a metal bath Note 1 to entry: In French called glace and in German Floatglas. 3.3 alumino silicate drawn

30、 sheet glass flat, transparent or translucent, clear or tinted basic alumino silicate glass obtained by continuous drawing of a regular thickness and with the two surfaces fire polished 3.4 alumino silicate rolled glass flat, transparent or translucent, clear or tinted basic alumino silicate glass o

31、btained by rolling 3.5 length, H and width, B defined with reference to the direction of draw of the glass ribbon as shown in Figure 1 DIN EN 15681-1:2016-06 EN 15681-1:2016 (E) 5 Key I direction of draw H length B width Figure 1 Relationship between length, width and direction of draw 3.6 stock siz

32、es glass delivered in manufacturers standard stock sizes 3.7 supplied size pane of glass that has been supplied either as raw material for further processing and/or cutting down to a size for installation Note 1 to entry: This is a size that is outside the stock size. 3.8 final cut size pane of glas

33、s that has been cut down to the dimensions being required either for installation or processing into a final product Note 1 to entry: Examples of processed final products are insulating glass units and thermally toughened safety glass of those dimensions. 3.9 optical fault fault which leads to disto

34、rtions in the appearance of objects observed through the glass 3.10 visual fault fault which alters the visual quality of the glass Note 1 to entry: Visual faults include spot faults and linear / extended faults. 3.11 spot fault spherical or quasi spherical fault which is produced by differing mecha

35、nisms, e.g. gaseous inclusion, solid inclusion, mark or deposit of small size 3.12 linear / extended faults fault which can be on or in the glass, in the form of deposits, reams, marks or scratches that occupy an extended length or area DIN EN 15681-1:2016-06 EN 15681-1:2016 (E) 6 3.13 edge defect d

36、efect which can occur on the edge of a cut size piece in the form of entrant and emergent fault and/or bevel 3.14 concentration sum of the lengths of gaseous inclusions greater than 1,0 mm in any circle of 400 mm diameter 4 Chemical composition 4.1 General The basic glass products covered by this Eu

37、ropean Standard are all manufactured from alumino silicate glass. The magnitude of the proportions by mass of the constituents of alumino silicate glass covered by this standard is given in Table 1, see also Annex A Table 1 Magnitude of the proportions by mass of the constituents of alumino silicate

38、 glass Constituents Proportion by mass of element Silicon (Si) 25,3 % to 35,1 % Aluminium (Al) 5,8 % to 16,2 % Si + Al 32,1 % to 51,3 % Lithium (Li) 0 % to 3,7 % Sodium (Na) 0 % to 10,5 % Calcium (Ca) 0 % to 2,1 % Magnesium (Mg) 0 % to 5 % Zinc (Zn) 0 % to 2,4 % Potassium (K) 0 % to 7 % Zirconium (Z

39、r) 0 % to 3,0 % Strontium (Sr) 0 % to 2,5 % Barium (Ba) 0 % to 3,6 % Other componentsa0 % to 5 % aProperties other than photometric characteristics shall not be significantly altered by these other components 4.2 Tint Body tinted glass is obtained by the addition of suitable materials. 5 Physical an

40、d mechanical characteristics 5.1 General characteristics Conventional numerical values for the physical and mechanical characteristics of basic alumino silicate glass products excluding Characteristic bending strength (fg;k) are given in Table 2. These values, for DIN EN 15681-1:2016-06 EN 15681-1:2

41、016 (E) 7 normal annealed glass without any further toughening, are not precise requirements with which the glass shall strictly comply, but are the generally accepted figures for use in calculations where a high degree of accuracy is not required. Table 2 General characteristic values of basic alum

42、ino silicate glass Characteristic Symbol Value and unit Density (at 18 C) 2300 to 2600 kg/m3Hardness (Knoop) HK0,1/20 400 to 700 aYoungs modulus (modulus of elasticity) E 70 to 90 x GPa Poissons ratio 0,2 to 0,25 Specific heat capacity Cp 0,7 to 0,9 103J/(kg*K) Nominal value of average coefficient o

43、f linear expansion between 20 C and 300 C 3,5 to 9,8 106/K Resistance against temperature differential and sudden temperature change 60 K bThermal conductivity 0,8 to 1,7 W/(m*K) Mean refractive index to visible radiation (at 589,3 nm) n 1,5 to 1,55 Emissivity (corrected) 0,837 aKnoop Hardness in ac

44、cordance with ISO 9385 bGenerally accepted value that is influenced by edge quality and glass type 5.2 Characteristic bending strength The characteristic bending strength value applies to quasi-static loading over a short time, e.g. wind loading, and relate to a 5 % probability of breakage at the lo

45、wer limit of the 95 % confidence interval. The value of the characteristic bending strength, fg;k, for alumino silicate float glass is 45 MPa, for drawn sheet and rolled glass 25 MPa. NOTE Methods of determination of the bending strength of glass are given in EN 12881, EN 12882, EN 12883, EN 12884 a

46、nd EN 12885 (see 1, 2, 3, 4, 5). Design of glass panes is covered by prEN 16612 (see 6). 5.3 Designation of clear alumino silicate glass 5.3.1 General An alumino silicate glass product is designated as clear alumino silicate glass when it is not tinted and when the light transmittance of the glass m

47、aterial, unmodified by the possible presence of a coating or surface roughness complies with 5.3.2 and 5.3.3. In order to measure the light transmittance characteristics of glass, to determine whether it can be designated as a clear glass, it is necessary, in some cases, to carry out a pre-treatment

48、: coatings on smooth surfaces have to be eliminated, without modifying the thickness of the glass substrate; rough surfaces, with or without coatings, have to be eliminated by smoothing and polishing. The thickness of the glass will be modified by this process. The light transmittance of the glass s

49、ubstrate shall be measured with its surfaces in a polished condition. DIN EN 15681-1:2016-06 EN 15681-1:2016 (E) 8 NOTE The light transmittance values given in 5.3.2 and 5.3.3 are not suitable for design. They are values used only for the designation of clear glass and exclude the effects of coatings and of surface roughness. The values of light transmittance used for design can be obtained from the glass manufacture