DIN EN 12592-2015 Bitumen and bituminous binders - Determination of solubility German version EN 12592 2014《沥青和沥青粘合剂 溶解度的测定 德文版本EN 12592-2014》.pdf

《DIN EN 12592-2015 Bitumen and bituminous binders - Determination of solubility German version EN 12592 2014《沥青和沥青粘合剂 溶解度的测定 德文版本EN 12592-2014》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 12592-2015 Bitumen and bituminous binders - Determination of solubility German version EN 12592 2014《沥青和沥青粘合剂 溶解度的测定 德文版本EN 12592-2014》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、January 2015 Translation by DIN-Sprachendienst.English price group 8No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS

2、 75.140; 91.100.50!%?DD“2283333www.din.deDDIN EN 12592Bitumen and bituminous binders Determination of solubility;English version EN 12592:2014,English translation of DIN EN 12592:2015-01Bitumen und bitumenhaltige Bindemittel Bestimmung der Lslichkeit;Englische Fassung EN 12592:2014,Englische bersetz

3、ung von DIN EN 12592:2015-01Bitumes et liants bitumineux Dtermination de la solubilit;Version anglaise EN 12592:2014,Traduction anglaise de DIN EN 12592:2015-01SupersedesDIN EN 12592:2007-06www.beuth.deDocument comprises 11 pagesIn case of doubt, the German-language original shall be considered auth

4、oritative.12.14DIN EN 12592:2015-01 2 A comma is used as the decimal marker. National foreword This document (EN 12592:2014) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders” (Secretariat: AFNOR, France). The responsible German bodies involved in its preparation were the DIN-N

5、ormenausschuss Materialprfung (DIN Standards Committee Materials Testing) and the DIN-Normenausschuss Bauwesen (DIN Standards Committee Building and Civil Engineering), Joint Committee NA 062-03-32 GA Bitumen; Prfverfahren und Anforderungen fr die Bindemittel. Amendments This standard differs from D

6、IN EN 12592:2007-06 as follows: a) the function of the powdered glass has been clarified; b) the preparation of the test sample according to EN 12594 has been added to the test method; c) the standard has been editorially revised. Previous editions DIN EN 12592: 2000-04, 2007-06 EUROPEAN STANDARD NO

7、RME EUROPENNE EUROPISCHE NORM EN 12592 November 2014 ICS 75.140; 91.100.50 Supersedes EN 12592:2007English Version Bitumen and bituminous binders - Determination of solubility Bitumes et liants bitumineux - Dtermination de la solubilit Bitumen und bitumenhaltige Bindemittel - Bestimmung der Lslichke

8、it This European Standard was approved by CEN on 16 August 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical r

9、eferences concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a

10、 CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Maced

11、onia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EURO

12、PISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 12592:2014 EEN 12592:2014 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative referen

13、ces 4 3 Terms and definitions .4 4 Principle 4 5 Reagents and materials 4 6 Apparatus .5 7 Sampling .5 8 Procedure .5 8.1 Test conditions 5 8.2 Preparation of crucible 6 8.3 Test method 6 9 Calculation 6 10 Expression of results 7 11 Precision .7 11.1 Repeatability .7 11.2 Reproducibility .7 12 Test

14、 report 7 Bibliography 9 DIN EN 12592:2015-01 EN 12592:2014 (E) 3 Foreword This document (EN 12592:2014) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, eithe

15、r by publication of an identical text or by endorsement, at the latest by May 2015 and conflicting national standards shall be withdrawn at the latest by May 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC

16、 shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 12592:2007. In comparison with EN 12592:2007, the following significant changes have been made: changed/added wording of the Warning in the Scope; the function of the powdered glass (subclause 6

17、.1.2) as filter aid has been highlighted in the standard; preparation of the test sample according to EN 12594 in subclause 8.3 has been added. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Stan

18、dard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Sp

19、ain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 12592:2015-01 EN 12592:2014 (E) 4 1 Scope This European Standard specifies a method for determining the degree of solubility of bituminous binders having little or no mineral matter other than recovered bituminous binders from asphalt m

20、ixes, in a specific solvent. Toluene is used as the solvent for reference tests. NOTE Bituminous binders will have varying solubility in different solvents. WARNING Use of this European Standard can involve hazardous materials, operations and equipment. This European Standard does not purport to add

21、ress all of the safety problems associated with its use. It is the responsibility of the user of this European Standard to identify the hazards and assess the risks involved in performing this test method and to implement sufficient control measures to protect individual operators (and the environme

22、nt). This includes appropriate safety and health practices and determination of the applicability of regulatory limitations prior to use. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For da

23、ted references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bituminous binders EN 1425, Bitumen and bituminous binders Characterization of perceptible properti

24、es EN 12594, Bitumen and bituminous binders Preparation of test samples ISO 4793, Laboratory sintered (fritted) filters Porosity grading, classification and designation ISO 5272, Toluene for industrial use Specifications ISO 5280, Xylene for industrial use Specification 3 Terms and definitions For t

25、he purposes of this document, the following term and definition apply. 3.1 solubility portion of material that is soluble in a specific solvent 4 Principle A sample of bituminous binder is dissolved in a solvent. The solution is filtered through a layer of powdered glass in a sintered crucible. The

26、insoluble material is then washed, dried, and weighed. 5 Reagents and materials Examples of specific solvents are given in 5.1 and 5.2. 5.1 Toluene, conforming to ISO 5272. DIN EN 12592:2015-01 EN 12592:2014 (E) 5 5.2 Xylene, conforming to ISO 5280. 6 Apparatus Usual laboratory apparatus and glasswa

27、re, together with the following: 6.1 Filtering apparatus NOTE Assembled as illustrated in Figure 1. Details of the component parts are as given in 6.1.1 to 6.1.5. 6.1.1 Sintered glass crucible, porosity P4 (see ISO 4793), effective diameter approximately 30 mm. 6.1.2 Powdered glass, borosilicate gla

28、ss powder, particle diameter approximately between 50 m and 80 m. The powdered glass functions as filter aid. The granulometry of powdered glass may evolve over time. It is recommended to check the granulometry prior to using the powdered glass, if used. Instead of powdered glass, glass fibre or Wha

29、tman filter grade 934 or equivalent may also be used. However, the use of powdered glass is the reference method. When using glass wool or filter as filter aid, a Gooch crucible may also be used. 6.1.3 Filter flask, 250 ml or 500 ml, heavy-wall, with a side tube. 6.1.4 Filter tube, 40 mm to 42 mm in

30、side diameter. 6.1.5 Rubber tubing or adaptor, for holding the crucible on the filter tube. Other suitable assemblies permitting vacuum filtration with a crucible can be used. 6.2 Oven, capable of maintaining a temperature, T, of 15 C to 25 C above the boiling temperature of the selected solvent. 6.

31、3 Balance, accurate to 0,2 mg and readable to 0,1 mg. 7 Sampling Take the test sample in accordance with EN 58, taking all necessary safety precautions and ensuring that the test sample is representative of the laboratory sample from which it is taken. Ensure that the laboratory sample is homogenous

32、 and not contaminated (see EN 1425). If the sample contains water, heat a representative portion of between 100 g and 200 g at a temperature not exceeding 130 C stirring constantly until the binder ceases to foam. 8 Procedure 8.1 Test conditions Normally the temperature at which the test is run is n

33、ot critical and may be performed at the laboratory air temperature. For reference tests, the flask with the sample in solution shall be placed in a water bath maintained at (25 2) C for 1 h before filtering. Crystallized paraffins may disturb the analysis of the samples with high wax content. To avo

34、id this, use the higher test temperature of 40 C. DIN EN 12592:2015-01 EN 12592:2014 (E) 6 8.2 Preparation of crucible Weigh (3,0 0,1) g of clean dried powdered glass into the crucible. Place the crucible in the filter tube (6.1.4). Wash the powdered glass (6.1.2) with a small portion of the selecte

35、d solvent (see Clause 5) and filter carefully into the flask with or without vacuum, as necessary. Repeat the washing process several times. Place the crucible on a heater or steam bath for 30 min before placing in the oven (6.2) at the temperature T (see 6.2) for at least 20 min. Remove the crucibl

36、e from the filter tube and cool in a desiccator for 25 min to 35 min and determine the mass to the nearest 0,1 mg. Repeat the drying and weighing until constant mass is obtained, i.e. the difference between the two weights shall not exceed 0,5 mg. 8.3 Test method Prepare the test sample according to

37、 EN 12594 in order to homogenize it and transfer (2 1) g of the dry sample, if necessary, using a warmed knife, into a suitable weighed container, e.g. Erlenmeyer flask. Determine the mass of the container and sample to the nearest 1 mg. Add 100 ml of the selected solvent to the container in small p

38、ortions with continuous agitation until all lumps disappear and no undissolved sample adheres to the container. For reference testing stopper or cover the container and set aside for at least 15 min (see 8.1). Place the previously prepared and weighed crucible in the filter tube (6.1.4). Wet the pow

39、dered glass with a small portion of solvent and filter the solution carefully into the flask through the powdered glass of the crucible with or without vacuum as necessary. If the insoluble matter is appreciable, retain as much of it as possible in the container until the solution has drained throug

40、h the filter aid. Wash the container with a small amount of solvent and, using a stream of solvent from a wash bottle, transfer all insoluble matter to the crucible. If necessary use a glass rod to remove any insoluble matter adhering to the container and transfer it into the crucible. Thoroughly ri

41、nse the glass rod and container and transfer it with the crucible. Wash the insoluble matter in the crucible with solvent until the filtrate flows substantially colourless, then apply strong vacuum to remove the remaining solvent or place the crucible into a vacuum desiccator. Remove the crucible fr

42、om the tube or desiccator, wash the bottom free of any dissolved matter, and place the crucible on a heater or a steam bath for 30 min. Place in an oven at the temperature T (see 6.2) for at least 20 min. Remove the crucible from the filter tube and cool in a desiccator for 25 min to 35 min and dete

43、rmine the mass to the nearest 0,1 mg. Repeat the drying and weighing until constant mass is obtained, i.e. the difference between the two weights is not more than 0,5 mg. Repeat the determinations, making at least two valid determinations. Two solubility determinations shall be considered valid if t

44、hey do not differ by more than 0,2 % mass. 9 Calculation Calculate either the total mass percentage of insoluble matter (xi) or the mass percentage of soluble matter (xs), of the sample in the solvent as follows: 100BAi=mmx (1) = 100100BAsmmx (2) where xiis the percentage of insoluble matter, in per

45、cent; DIN EN 12592:2015-01 EN 12592:2014 (E) 7 xsis the percentage of soluble matter, in percent; mAis the mass of insoluble material, in grams; mBis the mass of the dry sample, in grams. 10 Expression of results Express the solubility as the percentage of mass of soluble material xs, to the nearest

46、 0,05 %, as the mean of the two valid determinations. 11 Precision 11.1 Repeatability The difference between two test results, obtained by the same operator with the same apparatus under constant operating conditions on identical test material would, in the long run, in the normal and correct operat

47、ion of the test method, exceed 0,10 % absolute in only one case in twenty. 11.2 Reproducibility The difference between two single and independent results obtained by different operators working in different laboratories on identical test material would, in the long run, in the normal and correct ope

48、ration of the test method, exceed 0,15 % absolute in only one case in twenty. These precision data are not automatically applicable to modified bitumen, and for modified bitumen, they should only be used for guidance until criteria data are available. 12 Test report The test report shall contain at

49、least the following information: a) type and complete identification of the sample under test; b) reference to this European Standard; c) solvent used; d) results obtained (see Clause 10); e) any deviation, by agreement or otherwise, from the procedure specified; f) date of the test; g) type of filtrating medium (glass powder, glass fibre, filter) used. DIN EN 12592:2015-01 EN 12592:2014 (E) 8 Key 1 sintered glass crucible 2 rubber tubing 3 filter tube 4 polychloroprene stopper 5 filter flask Figure 1 Filtering a