DIN EN 10028-4-2009 Flat products made of steels for pressure purposes - Part 4 Nickel alloy steels with specified low temperature properties English version of DIN EN 10028-4 2009.pdf

《DIN EN 10028-4-2009 Flat products made of steels for pressure purposes - Part 4 Nickel alloy steels with specified low temperature properties English version of DIN EN 10028-4 2009.pdf》由会员分享，可在线阅读，更多相关《DIN EN 10028-4-2009 Flat products made of steels for pressure purposes - Part 4 Nickel alloy steels with specified low temperature properties English version of DIN EN 10028-4 2009.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、September 2009DEUTSCHE NORM English price group 9No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77.140.30; 77.140.50!

2、$Y_k“1546072www.din.deDDIN EN 10028-4Flat products made of steels for pressure purposes Part 4: Nickel alloy steels with specified low temperature propertiesEnglish version of DIN EN 10028-4:2009-09Flacherzeugnisse aus Druckbehltersthlen Teil 4: Nickellegierte kaltzhe SthleEnglische Fassung DIN EN 1

3、0028-4:2009-09SupersedesDIN EN 10028-4:2003-09 andDIN EN 10028-4 Corrigendum1:2006-05www.beuth.deDocument comprises pages14DIN EN 10028-4:2009-09 National foreword This standard has been prepared by Technical Committee ECISS/TC 22 “Steels for pressure purposes Qualities” (Secretariat: DIN, Germany).

4、 The responsible German body involved in its preparation was the Normenausschuss Eisen und Stahl (Iron and Steel Standards Committee), Technical Committees NA 021-00-04-02 UA Sthle fr den Druckbehlterbau. This document specifies requirements for flat products for pressure equipment made of nickel al

5、loy steels with specified low temperature properties. Amendments This standard differs from DIN EN 10028-4:2003-09 and DIN EN 10028-4 Corrigendum 1:2006-05 as follows: a) Information regarding the harmonization with Directive 97/23/EC has been rendered more precise. b) The chemical composition has b

6、een modified (some maximum values for the sulfur content have been lowered). c) An option for a minimum impact energy of 40 J has been specified. d) Annex ZA has been revised. e) The standard has been editorially revised. Previous editions DIN 17280: 1985-07 DIN EN 10028-4: 1994-11, 2003-09 DIN EN 1

7、0028-4 Corrigendum 1: 2006-05 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10028-4 June 2009 ICS 77.140.30; 77.140.50 Supersedes EN 10028-4:2003 English Version Flat products made of steels for pressure purposes Part 4: Nickel alloy steels with specified low temperature properties Produits

8、 plats en aciers pour appareils pression Partie 4: Aciers allis au nickel avec caractristiques spcifies basse temprature Flacherzeugnisse aus Druckbehltersthlen Teil 4: Nickellegierte kaltzhe Sthle This European Standard was approved by CEN on 14 May 2009. CEN members are bound to comply with the CE

9、N/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or t

10、o any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versio

11、ns. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain

12、, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Mem

13、bers. Ref. No. EN 10028-4:2009: EEN 10028-4:2009 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions . 4 4 Dimensions and tolerances on dimensions . 4 5 Calculation of mass . 4 6 Classification and designation . 4 6.1 Classification 4 6.2 Designation 4 7 Informa

14、tion to be supplied by the purchaser . 4 7.1 Mandatory information 4 7.2 Options . 5 7.3 Example for ordering . 5 8 Requirements . 5 8.1 Steelmaking process . 5 8.2 Delivery condition 5 8.3 Chemical composition 5 8.4 Mechanical properties . 6 8.5 Surface condition. 9 8.6 Internal soundness 9 9 Inspe

15、ction . 9 9.1 Types of inspection and inspection documents 9 9.2 Tests to be carried out 9 9.3 Retests 9 10 Sampling . 9 11 Test methods 9 12 Marking . 9 Annex A (informative) Guidelines for heat treatment 10 Annex ZA (informative) Relationship between this European Standard and the Essential Requir

16、ements of EU Directive 97/23/EC . 11 Bibliography 12 DIN EN 10028-4:2009-09 EN 10028-4:2009 (E) 3 Foreword This document (EN 10028-4:2009) has been prepared by Technical Committee ECISS/TC 22 “Steels for pressure purposes - Qualities”, the secretariat of which is held by DIN. This European Standard

17、shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by December 2009, and conflicting national standards shall be withdrawn at the latest by December 2009. Attention is drawn to the possibility that some of the elements of thi

18、s document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10028-4:2003. This European Standard consists of the following parts, under the general title Flat products made of steels for p

19、ressure purposes: Part 1: General requirements Part 2: Non-alloy and alloy steels with specified elevated temperature properties Part 3: Weldable fine grain steels, normalized Part 4: Nickel alloy steels with specified low temperature properties Part 5: Weldable fine grain steels, thermomechanically

20、 rolled Part 6: Weldable fine grain steels, quenched and tempered Part 7: Stainless steels NOTE The clauses marked by two points () contain information relating to agreements that may be made at the time of enquiry and order. This document has been prepared under a mandate given to CEN by the Europe

21、an Commission and the European Free Trade Association, and supports essential requirements of EU Directive 97/23/EC. For relationship with EU Directive 97/23/EC, see informative Annex ZA, which is an integral part of this document. According to the CEN/CENELEC Internal Regulations, the national stan

22、dards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, P

23、ortugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. DIN EN 10028-4:2009-09 EN 10028-4:2009 (E) 4 1 Scope This European Standard specifies requirements for flat products for pressure equipment made of nickel alloy steels as specified in Table 1. The requirements a

24、nd definitions of EN 10028-1:2007 + A1:2009 also apply. NOTE Once this European Standard is published in the EU Official Journal (OJEU) under Directive 97/23/EC, presumption of conformity to the Essential Safety Requirements (ESRs) of Directive 97/23/EC is limited to technical data of materials in t

25、his European Standard (Part 1 and this Part 4 of the series) and does not presume adequacy of the material to a specific item of equipment. Consequently, the assessment of the technical data stated in this material standard against the design requirements of this specific item of equipment to verify

26、 that the ESRs of Directive 97/23/EC are satisfied, needs to be done. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced d

27、ocument (including any amendments) applies. EN 10028-1:2007 + A1:2009, Flat products made of steels for pressure purposes Part 1: General requirements EN 10204:2004, Metallic products Types of inspection documents 3 Terms and definitions For the purposes of this document, the terms and definitions g

28、iven in EN 10028-1:2007 + A1:2009 apply. 4 Dimensions and tolerances on dimensions See EN 10028-1:2007 + A1:2009. 5 Calculation of mass See EN 10028-1:2007 + A1:2009, 6 Classification and designation 6.1 Classification In accordance with EN 10020, all steel grades covered by this document are alloy

29、special steels. 6.2 Designation See EN 10028-1:2007 + A1:2009. 7 Information to be supplied by the purchaser 7.1 Mandatory information See EN 10028-1:2007 + A1:2009. DIN EN 10028-4:2009-09 EN 10028-4:2009 (E) 5 7.2 Options A number of options are specified in this European Standard and listed below.

30、 Additionally the relevant options of EN 10028-1:2007 + A1:2009 apply. If the purchaser does not indicate a wish to implement any of these options at the time of enquiry and order, the products shall be supplied in accordance with the basic specification (see also EN 10028-1:2007 + A1:2009). 1) deli

31、very condition other than that specified in Table 3 (see 8.2.2); 2) delivery of products in the untreated condition (see 8.2.3); 3) specification of a minimum impact energy of 40 J (see NOTE to 8.4 and Table 4); 4) mid thickness test pieces for the impact test (see Clause 10); 5) verification of imp

32、act energy for longitudinal test pieces (see Clause 11). 7.3 Example for ordering 10 plates with nominal dimensions, thickness = 50 mm, width = 2 000 mm, length = 10 000 mm, made of a steel grade with the name 15NiMn6 and the number 1.6228 as specified in EN 10028-4, to be delivered with inspection

33、document 3.1 as specified in EN 10204. 10 plates 50 x 2000 x 10 000 EN 10028-4 15NiMn6 Inspection document 3.1 or 10 plates 50 x 2000 x 10 000 EN 10028-4 1.6228 Inspection document 3.1. 8 Requirements 8.1 Steelmaking process See EN 10028-1:2007 + A1:2009. 8.2 Delivery condition 8.2.1 The delivery co

34、ndition shall be noted in the inspection document. 8.2.2 yy Unless otherwise agreed at the time of enquiry and order, the products covered by this document shall be supplied in the usual delivery conditions specified in Table 3. 8.2.3 yy If so agreed at the time of enquiry and order, the products ma

35、y be supplied in the untreated condition. In these cases, the specified tests shall be carried out on test pieces in the usual delivery condition as given in Table 3. NOTE Testing in a simulated heat treated condition does not discharge the processor from the obligation of providing proof of the spe

36、cified properties in the finished product. 8.3 Chemical composition 8.3.1 The requirements of Table 1 shall apply for the chemical composition according to the cast analysis. 8.3.2 The product analysis shall not deviate from the specified values for the cast analysis as specified in Table 1 by more

37、than the values given in Table 2. DIN EN 10028-4:2009-09 EN 10028-4:2009 (E) 6 Table 1 Chemical composition (cast analysis) a Steel grade % by mass Steel name Steel number C Si Mn P S AltotalMo Nb Ni V max. max. max. max. min. max. max. max. 11MnNi5-3 1.6212 0,14 0,50 0,70 to 1,50 0,025 0,010 0,020

38、0,05 0,30 bto 0,80 0,05 13MnNi6-3 1.6217 0,16 0,50 0,85 to 1,70 0,025 0,010 0,020 0,05 0,30 bto 0,85 0,05 15NiMn6 1.6228 0,18 0,35 0,80 to 1,50 0,025 0,010 1,30 to 1,70 0,05 12Ni14 1.5637 0,15 0,35 0,30 to 0,80 0,020 0,005 3,25 to 3,75 0,05 X12Ni5 1.5680 0,15 0,35 0,30 to 0,80 0,020 0,005 4,75 to 5,

39、25 0,05 X8Ni9 1.5662 0,10 0,35 0,30 to 0,80 0,020 0,005 0,10 8,5 to 10,0 0,05 X7Ni9 1.5663 0,10 0,35 0,30 to 0,80 0,015 0,005 0,10 8,5 to 10,0 0,01 aElements not listed in this Table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. A

40、ll appropriate measures shall be taken to prevent the addition from scrap or other materials used in steelmaking of these elements which may adversely affect the mechanical properties and usability. The content of Cr + Cu + Mo shall not exceed 0,50 %. bFor product thicknesses 40 mm, a minimum nickel

41、 content of 0,15 % is permitted. Table 2 Permissible product analysis tolerances on the limiting values given in Table 1 for the cast analysis Element Specified value in the cast analysis according to Table 1 % by mass Permissible deviationaof the product analysis % by mass C 0,18 + 0,02 Si 0,50 + 0

42、,05 Mn 1,00 0,05 1,00 to 1,70 0,10 P 0,015 + 0,003 0,015 to 0,025 + 0,005 S 0,010 + 0,003 Al 0,020 - 0,005 Mo 0,10 + 0,03 Nb 0,05 + 0,01 Ni 0,85 0,05 0,85 to 3,75 0,07 3,75 to 10,0 0,10 V 0,05 + 0,01 aIf several product analyses are carried out on one cast, and the contents of an individual element

43、determined lie outside the permission range of the chemical composition specified for the cast analysis, then it is only allowed to exceed the permissible maximum value or fall short of the permissible minimum value, but not both for one cast. 8.4 Mechanical properties The values given in Tables 3 a

44、nd 4 (see also EN 10028-1:2007 + A1:2009 and clause 10) shall apply. NOTE Optionally, for steel grades 11MnNi5-3, 13MnNi6-3, 15NiMn6, 12Ni14 and X12Ni5, a minimum impact energy value of 40 J may be specified for temperatures where lower minimum values are specified (see Table 4, footnote d). DIN EN

45、10028-4:2009-09 EN 10028-4:2009 (E) 7 Table 3 Mechanical properties at room temperature Steel grade Usual delivery conditiona,b (Heat treatment symbol) Product thickness t mm Yield strength ReH MPa min. Tensile strength RmMPa Elongation after fracture A % min. Steel name Steel number 11MnNi5-3 1.621

46、2 +N (+NT) 30 285 420 to 530 24 30 t 50 275 50 t 80 265 13MnNi6-3 1.6217 +N (+NT) 30 355 490 to 610 22 30 t 50 345 50 t 80 335 15NiMn6 1.6228 +N or +NT or +QT 30 355 490 to 640 22 30 t 50 345 50 t 80 335 12Ni14 1.5637 +N or +NT or +QT 30 355 490 to 640 22 30 t 50 345 50 t 80 335 X12Ni5 1.5680 +N or

47、+NT or +QT 30 390 530 to 710 20 30 t 50 380 X8Ni9 +NT640a 1.5662 +NT640 a+N plus +NT 30 490 640 to 840 18 30 t 50 480 X8Ni9 +QT640a 1.5662 +QT640a+QT 30 490 30 t 50 480 X8Ni9 +QT680 a1.5662 +QT680 a+QTc 30 585 680 to 820 18 30 t 50 575 X7Ni9 1.5663 +QTc 30 585 680 to 820 18 30 t 50 575 a+N: normaliz

48、ed; +NT: normalized and tempered; +QT: quenched and tempered; +NT640/+QT640/+QT680: Heat treatment variant with minimum tensile strength of 640 MPa or 680 MPa. bFor temperatures and cooling conditions, see Table A.1. cFor product thickness 15 mm, delivery conditions +N plus +NT are also applicable.

49、DIN EN 10028-4:2009-09 EN 10028-4:2009 (E) 8 Table 4 Minimum impact energy values Steel grade Heat treatment conditiona,b Product thickness mm Direction Minimum impact energy KV in J at a temperature in C of Steel name Steel number 20 0 -20 -40 -50 -60 -80 -100 -120 -150 -170 -196 11MnNi5-3 1.6212 +N (+NT) 80 longitudinal 70 60 55 50 45 40 13MnNi6-3 1.6217 transverse 50