1、September 1985 UDC 621.646-036.742.2:628.1:620.1 DEUTSCHE NORM Test temperature “c High-density polyethylene (HDPE) valves Tapping valves Requirements and test Duration of test service life), in hours Test pressure, in bar, when welded to an HDPE pipe I Part 1 20 1 Armaturen aus Polyethylen hoher Di

2、chte (HDPE); Anforderungen und Prfung von Anbohrarmaturen 2.4 X PN-) Supersedes July 1979 edition. In keeping with current practice in standards published by the International Organization for Standardization (so), a comma has been used throughout as the decimal marker. 1 Field of application This s

3、tandard applies to high-density polyethylene (HDPE) tapping valves. Tapping valves covered by this standard are intended for welding to HDPE pipes as specified in DIN 8075 “1, with dimensions in accordance with DIN 8074 Part 1 or Part 2. The specifications of DIN 16 963 Part 5, July 1977 edition, ta

4、ble 3 are applicable to the permissible working pressures in the case of liquid flow media, and the specifications of D VGW-Arbeitsblatt (Data sheet) G 477 are applicable to the permissible working pressures in the case of combustible gases. 2 Requirements 2.1 Material In the case of potable water p

5、iping systems, only materials shall be used that are not likely to impart either taste, odour or colour to the drinking water, or any substances injurious to health in amounts which could be prejudicial to hygiene. The formation of algae and the growth of bacteria shall not be fostered. The stipulat

6、ions made in the Mitteilungen aus dem Bundesgesundheitsamt (Federal Board of Health Bulletin) on the “Hygienic evaluation of plastic materials within the framework of the Foodstuffs Act“ shall be regarded as authoritative in this respect. 2.1.1 Valves Valves shall be made of highdensity stabilized p

7、oly- ethylene (as a general rule, stabilized with carbon black and suitable antioxidants). Moulding materials of uncontrolled composition shall not be used. The choice of stabilizer and of other auxiliary materials is left to the discretion of the manufacturer of the tapping valve. 2.1.2 Seals The m

8、aterials shall be selected according to the nature of the flow medium. DIN 3535 Part 3 shall be applicable to valves in gas installations. 2.2 Condition on supply Tapping valves shall be free from any shrink holes, inhomogeneities, bubbles and burr which might impair proper functioning. 2.3 Strength

9、 properties Tapping valves shall meet the strength requirements given in table 1 during the long-term hydrostatic pressure test in accordance with subclause 3.2. Table 1. Strength requirements for tapping valves during the long-term hydrostatic pressure test Pressure-bearing valve parts shall neithe

10、r leak nor suffer any fracture during the prescribed duration of the test. Rubber-sealed connections shall be safeguarded against deformations which might result in premature leakage. 2.4 Surface finish Tapping valves shall exhibit a smooth surface appropriate to the manufacturing process at the tim

11、e of the inspec- tion in accordance with subclause 3.3. There shall be no signs of burnt patches due to overheating during manufacture. 2.5 Dimensions DIN 3543 Part4 shall apply to the dimensions of tapping valves. Any dimensions which are not specified in the above-mentioned standard shall be selec

12、ted by the manufacturer in such a way that, apart from the strength requirements laid down in subclause 2.3, the additional stresses likely to occur in practical use can be absorbed by the tapping valves. 3 Testing 3.1 Point in time for performance of tests All tests shall not be performed any earli

13、er than 15 hours after completion of manufacture of the tapping valves. 3.2 Long-term hydrostatic presuie test 3.2.1 Three tapping valves shall be tested for each of the test conditions described in table 1. 3.2.2 The tests shall be carried out on complete tapping valves including their connections,

14、 using HDPE pips of the appropriate pressure rating in accordance with DIN 8075 *),with dimensions in accordance with “) At present at the stage of draft. Continued on page 2 Eeuth Verlag OrnbH, Berlin 30, has exclusive sale rights for German Standards (DIN-Normen) DIN 3544 Part 1 Engl. Price group

15、05.86 Sales No. 0105 Page 2 DIN 3544 Part 1 External pipe diameter, in mm Up to 63 Over 63 up to 225 Table 2. Lengths of piping to be welded Length of pipe between seals, in mm 300 600 DIN 8074 Part 1 or Part 2. The length of the welded pipes shall be selected in accordance with table 2, and the tap

16、ping valve shall be welded on centrically. The piping shall be fitted with seals on both ends in such a way that the axial forces arising from the internal pres- sure are transmitted to the welded joints. The specimen shall be capable of moving without hindrance in all directions. The pipe with tapp

17、ing valve welded onto it shall then be drilled with the maximum drilling diameter correlated to the valve concerned. 3.2.3 The specimens arranged in accordance with sub- clause 3.2.2 shall then be filled with water at the test temperature specified in table 1 (permissible deviations: f 5 K) through

18、an orifice in one of the seals capable of being closed subsequently, and placed in a water bath containing water maintained at test temperature (permissible deviations: f 1 K) and left in the bath for one hour to allow temperature equilibrium to be reached. 3.2.4 Then the test pressure in accordance

19、 with table 1 shall be applied to the specimens inside the bath within a time not exceeding 10 to 15 seconds, and maintained during the test period specified in table 1, with a permis- sible deviation of I2,5%. 3.2.5 It shall be checked whether the tapping valve subjected to the test has developed a

20、 leak or fractures during the specified test period. Tests in which leaks or fractures in the welded piping or in the clamping device have occured during the specified test period shall not be evaluated and shall be repeated. 3.3 Surface finish The external surface, and also the internal surface as

21、far as possible, shall be examined visually, using a suitable light source. 3.4 Dimensions The dimensions shall be checked with the aid of suitable measuring instruments. 3.5 Certificate If agreed, a certificate in accordance with DIN 50 O49 shall be issued in respect of the tests carried out at the

22、 manufacturers works. Standards referred to and other documents DIN 3535 Part 3 DIN 3543 Part 4 DIN 8074 Part 1 DIN 8074 Part 2 DIN 8075 DIN 16 963 Part 5 DIN 50 O49 D VGW-Arbeitsblatt G 477 Sealants for gas supplies; elastomeric sealants for gas supply mains and pipelines; safety requirements and t

23、esting of materials Highdensity polyethylene (HDPE) tapping valves for HDPE pipes; dimensions Type 1 high-density polyethylene (PE) pipes; dimensions Type 2 high-density polyethylene (HDPE) pipes; dimensions (at present at the stage of draft) Highdensity polyethylene (HDPE) pipes; general quality re

24、quirements, testing Pipe joints and fittings for high pressure pipelines of (type 1) high-density polyethylene (PE); general quality requirements, testing Documents on materials testing Manufacture, quality assurance and testing of unplasticized PVC (polyvinyl chloride) pipes and of HDPE (low-densit

25、y polyethylene) pipes for gas mains and requirements relating to pipe joints and fittings (obtainable from ZFGW-Verlag, P. O. Box 90 10 80, D-6000 Frankfurt 90) ( Recommendation) Kunststoffe und andere nichtmetallische Werkstoffe fr den Trinkwaserbereich Plastics and other nonmetallic materials for

26、the potable water field) (obtainable from Carl Heymanns Verlag KG, Gereonstrae 18-32, D-5000 Kln 1) KTW-Empfehlung Other relevant standards DIN 19 533 Previous editions DIN 3544 Part 1 : 07.79 Amendments The following amendmends have been made in comparison with the July 1979 edition: a) The designa

27、tion “type 1 rigid PE“ has been superseded by “highdensity polyethylene (HDPE)“ in the title, in the b) In table 1, the two columns relating to the test pressure have been amended. c) The standard has been editorially revised. International Patent Classification G O1 M 19/00 High-density PE (polyethylene) and low-density PE (polyethylene) pipelines for potable water supply systems; pipes, pipe joints, fittings field of application and in the remaining text of this standard. F 16 L 41/04