BS ISO 12315-2010 Aluminium oxide primarily used for production of aluminium - Method for calculating the Al2O3 content of smelter-grade alumina《主要应用于铝制品的氧化铝 熔炼级氧化铝的Al2O3含量的计算方法》.pdf

《BS ISO 12315-2010 Aluminium oxide primarily used for production of aluminium - Method for calculating the Al2O3 content of smelter-grade alumina《主要应用于铝制品的氧化铝 熔炼级氧化铝的Al2O3含量的计算方法》.pdf》由会员分享，可在线阅读，更多相关《BS ISO 12315-2010 Aluminium oxide primarily used for production of aluminium - Method for calculating the Al2O3 content of smelter-grade alumina《主要应用于铝制品的氧化铝 熔炼级氧化铝的Al2O3含量的计算方法》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS ISO 12315:2010Aluminium oxide primarily used for production of aluminium Method for calculating the Al2O3content of smelter-grade aluminaBS ISO 12315:2010 BRITISH STANDARDNati

2、onal forewordThis British Standard is the UK implementation of ISO 12315:2010. The UK participation in its preparation was entrusted to TechnicalCommittee CII/24, Raw materials for the aluminium industry. A list of organizations represented on this committee can beobtained on request to its secretar

3、y.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. BSI 2010 ISBN 978 0 580 66356 7 ICS 71.100.10 Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was publishe

4、d under the authority of theStandards Policy and Strategy Committee on 31 July 2010 Amendments issued since publicationDate T e x t a f f e c t e dBS ISO 12315:2010Reference numberISO 12315:2010(E)ISO 2010INTERNATIONAL STANDARD ISO12315First edition2010-05-15Aluminium oxide primarily used for produc

5、tion of aluminium Method for calculating the Al2O3content of smelter-grade alumina Oxyde daluminium principalement utilis pour la production daluminium Mthode de calcul de la teneur en Al2O3de lalumine pour lectrolyse BS ISO 12315:2010ISO 12315:2010(E) PDF disclaimer This PDF file may contain embedd

6、ed typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of no

7、t infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters we

8、re optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2010 All rights rese

9、rved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the reques

10、ter. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2010 All rights reservedBS ISO 12315:2010ISO 12315:2010(E) ISO 2010 All rights reserved iiiForeword ISO (the International

11、Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been esta

12、blished has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardiza

13、tion. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for votin

14、g. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such

15、patent rights. ISO 12315 was prepared by Technical Committee ISO/TC 226, Materials for the production of primary aluminium. This International Standard is based on AS 2879.11, Alumina Guide to reporting Al2O3content of smelter-grade alumina, prepared by the Standards Australia Committee MN/9, Alumin

16、a and Materials Used in Aluminium Production. BS ISO 12315:2010BS ISO 12315:2010INTERNATIONAL STANDARD ISO 12315:2010(E) ISO 2010 All rights reserved 1Aluminium oxide primarily used for production of aluminium Method for calculating the Al2O3content of smelter-grade alumina 1 Scope This Internationa

17、l Standard describes methods for calculating and reporting the Al2O3content of smelter-grade alumina, on either a dry or ignited basis, from the results of the determinations in accordance with ISO 806 and AS 2879.7. NOTE Typical values of a smelter-grade alumina, if reported on a dry basis, would b

18、e in the range of 98,5 % to 98,9 % and, if reported on an ignited basis, would be in the range of 99,4 % to 99,7 % mass fraction. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. Fo

19、r undated references, the latest edition of the referenced document (including any amendments) applies. ISO 806, Aluminium oxide primarily used for the production of aluminium Determination of loss of mass at 300 C and 1 000 C AS 2879.7, Alumina Determination of trace elements Wavelength dispersive

20、X-ray fluorescence spectrometric method1)3 Principle From the determination of trace elements in accordance with AS 2879.7, where the elements are determined on an undried (“as-received” basis) by X-ray fluorescence spectrometry analysis, and the loss of mass at 300 C and 1 000 C is determined in ac

21、cordance with ISO 806, the proportion by mass is calculated and expressed as a percentage. The Al2O3content of alumina, expressed as a percentage (mass fraction), is calculated by subtracting the percentage of trace elements from the total, expressed as 100 %. The Al2O3content of alumina can be expr

22、essed on a dried basis or an ignited basis. The dried basis method eliminates the effect of loss of mass after heating to 300 C, under defined conditions. The ignited basis method eliminates the loss of mass after heating to 1 000 C, under defined conditions. Sulfur (S) shall be determined and inclu

23、ded as its oxide, SO2, in the sum of impurities term, I, if the alumina is derived from heavy-fuel-oil calcination. Sulfur from this source is largely present as adsorbed SO2. There is no standard method for determining sulfur in alumina. 1) To be replaced by ISO 23201, Aluminium oxide primarily use

24、d for production of aluminium Determination of trace elements Wavelength dispersive X-ray fluorescence spectrometric method (under preparation). BS ISO 12315:2010ISO 12315:2010(E) 2 ISO 2010 All rights reservedNOTE 1 By industry convention, these mass losses are often referred to as “moisture on ign

25、ition (MOI)” and “loss on ignition (LOI)”, respectively. NOTE 2 When sulfur is determined, it is traditionally reported as SO3, not SO2. 4 Procedures The determinations shall be as follows. a) Determine the impurities according to AS 2879.7. b) Determine the loss of mass at 300 C (moisture content,

26、MOI) and loss of mass on ignition at 1 000 C (LOI) (on a dry or “as-received” basis) in accordance with ISO 806. c) Determine the sulfur, reported as SO3, if the alumina is derived from heavy-fuel-oil calcination. 5 Calculations and expression of results Calculate and express the results as follows:

27、 a) Al2O3content determined on an ignited at 1 000 C basis: 1) for loss on ignition of alumina determined on a dried at 300 C basis, the Al2O3content, expressed as a percentage, is calculated using Equation (1). ()23Al O ,1000,d1000,d 300300 1000,d100100100100wIwwww= +(1) where wAl2O3, 1 000,dis the

28、 Al2O3content determined on an ignited at 1 000 C basis, expressed as a percentage; w300is the loss of mass at 300 C, expressed as a percentage; w1 000,dis the loss of mass on ignition (300 C to 1 000 C), expressed on a dried at 300 C basis; I is the sum of trace elements determined in accordance wi

29、th AS 2879.7. SO3shall be included in this sum, if required. 2) for loss on ignition of alumina determined on an “as-received” basis calculate the Al2O3content, expressed as a percentage, using Equation (2). ()()23Al O ,1000,ar300 1000,ar100100100wIww= (2) where wAl2O3, 1 000,aris the Al2O3content d

30、etermined on an ignited at 1 000 C basis, expressed as a percentage; w300is the loss of mass at 300 C, expressed as a percentage; BS ISO 12315:2010ISO 12315:2010(E) ISO 2010 All rights reserved 3w1 000,aris the loss of mass on ignition (300 C to 1 000 C) expressed on an “as-received” basis; I is the

31、 sum of the trace-element oxides determined in accordance with AS 2879.7. SO3shall be included in this sum, if required. b) Al2O3content determined on a dried at 300 C basis: 1) for loss on ignition of alumina determined on a dried at 300 C basis, the Al2O3content, expressed as a percentage, is calc

32、ulated using Equation (3). ()23Al O , 300,d 1000,d300100100100ww Iw= (3) where wAl2O3, 300,dis the Al2O3content determined on a dried at 300 C basis, expressed as a percentage, w300is the loss of mass at 300 C, expressed as a percentage; w1 000,dis the loss of mass on ignition (300 C to 1 000 C) on

33、a dried basis; I is the sum of the trace-element oxides determined in accordance with AS 2879.7. SO3shall be included in this sum, if required. 2) for loss on ignition of alumina determined on an “as-received” basis calculate the Al2O3content, expressed as a percentage, is calculated using Equation

34、(4). ()()23Al O , 300,ar 1000,ar300100100100wwIw= +(4) where wAl2O3, 300,aris the Al2O3content determined on a dried at 300 C basis, expressed as a percentage; w300is the loss of mass at 300 C, expressed as a percentage; w1 000,aris the loss of mass on ignition (300 C to 1 000 C), expressed on an “a

35、s-received” basis; I is the sum of the trace-element oxides determined in accordance with AS 2879.7. SO3shall be included in this sum, if required. 6 Test report The test report should include the following information: a) a reference to this International Standard; b) the date on which the sample w

36、as taken; c) the date of the determinations and calculations; d) details necessary for the complete identification of the material tested; BS ISO 12315:2010ISO 12315:2010(E) 4 ISO 2010 All rights reservede) whether the Al2O3content was determined and calculated on a dried at 300 C or ignited at 1 00

37、0 C basis; f) the Al2O3content, recorded to the nearest first decimal place. BS ISO 12315:2010BS ISO 12315:2010ISO 12315:2010(E) ICS 71.100.10 Price based on 4 pages ISO 2010 All rights reserved This page deliberately left blankBSI is the independent national body responsible for preparing British S

38、tandardsand other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Standards Institution (BSI)raising standards worldwideBSI Group Headquarters389 Chiswick High Road Lo

39、ndon W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards are updated by amendment or revision. Users of British Stan-dards should make sure that they possess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our products and serv-ices. We would be gr

40、ateful if anyone finding an inaccuracy or ambiguity whileusing this British Standard would inform the Secretary of the technical com-mittee responsible, the identity of which can be found on the inside frontcover.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001BSI offers Members an individual updat

41、ing service called PLUS which ensuresthat subscribers automatically receive the latest editions of standards.Tel: +44 (0)20 8996 7669 Fax: +44 (0)20 8996 7001Email: Buying standardsYou may buy PDF and hard copy versions of standards directly using acredit card from the BSI Shop on the website addit

42、ion all orders for BSI, international and foreign standards publicationscan be addressed to BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001Email: In response to orders for international standards, it is BSI policy tosupply the BSI implementation of those that have been publis

43、hedas British Standards, unless otherwise requested.Information on standardsBSI provides a wide range of information on national, Europeanand international standards through its Knowledge Centre.Tel: +44 (0)20 8996 7004 Fax: +44 (0)20 8996 7005Email: Various BSI electronic information services are a

44、lso available whichgive details on all its products and services. Tel: +44 (0)20 8996 7111 Fax: +44 (0)20 8996 7048Email: BSI Subscribing Members are kept up to date with standardsdevelopments and receive substantial discounts on the purchase priceof standards. For details of these and other benefit

45、s contact Membership Ad-ministration. Tel: +44 (0)20 8996 7002 Fax: +44 (0)20 8996 7001 Email: Information regarding online access to British Standards via BritishStandards Online can be found at information about BSI is available on the BSI website at www.bsi- subsists in all BSI publications. BS

46、I also holds the copyright,in the UK, of the publications of the international standardization bodies. Ex-cept as permitted under the Copyright, Designs and Patents Act 1988 no ex-tract may be reproduced, stored in a retrieval system or transmitted in anyform or by any means electronic, photocopying

47、, recording or otherwise without prior written permission from BSI. This does not preclude the freeuse, in the course of implementing the standard of necessary details such assymbols, and size, type or grade designations. If these details are to be usedfor any other purpose than implementation then the prior written permissionof BSI must be obtained. Details and advice can be obtained from the Copy-right & Licensing Manager.Tel: +44 (0)20 8996 7070Email: