BS HC 202-1973 Specification for precipitation hardening nickel base chromium-niobium-molybdenum-iron-tungsten alloy castings (Cr 20 0 Nb 6 6 Mo 6 0 Fe 3 0 W 2 5)《沉淀硬化镍基铬-铌-钼-铁-钨合金.pdf

《BS HC 202-1973 Specification for precipitation hardening nickel base chromium-niobium-molybdenum-iron-tungsten alloy castings (Cr 20 0 Nb 6 6 Mo 6 0 Fe 3 0 W 2 5)《沉淀硬化镍基铬-铌-钼-铁-钨合金.pdf》由会员分享，可在线阅读，更多相关《BS HC 202-1973 Specification for precipitation hardening nickel base chromium-niobium-molybdenum-iron-tungsten alloy castings (Cr 20 0 Nb 6 6 Mo 6 0 Fe 3 0 W 2 5)《沉淀硬化镍基铬-铌-钼-铁-钨合金.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS HC 202:1973 Incorporating Amendment No.1 Specification for Precipitation hardening nickel base chromium-niobium- molybdenum-iron- tungsten alloy castings (Cr 20.0, Nb 6.6, Mo 6.0, Fe 3.0, W 2.5) UDC 629.7:669.24526242812714:669.245.018.298BSHC202:1973 This Britis

2、h Standard, having been approved by the AerospaceIndustry Standards Committee, was published underthe authority of the Executive Board on 2 February 1973 BSI 01-2000 The following BSI references relate to the work on this standard: Committee reference ACE/60 Draft for comment 71/35555 ISBN 0 580 071

3、78 2 A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document compr

4、ises a front cover, an inside front cover, pages i and ii, page 1 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication Amd. No. Date

5、 Comments 3884 April 1982 Indicated by a sideline in the marginBSHC202:1973 BSI 01-2000 i Contents Page 1 Inspection and testing procedure 1 2 Chemical composition 1 3 Condition 1 4 Heat treatment 1 5 Mechanical properties 1 6 Rectification of defects 1ii blankBSHC202:1973 BSI 01-2000 1 NOTEThis spe

6、cification complies with AICMA Recommendation Ni-C103-HT with the exception of the tensile elongation requirement. 1 Inspection and testing procedure This British Standard shall be used in conjunction with the relevant sections of the latest issue of BSHC100 as follows: 2 Chemical composition The re

7、-melting stock and the castings shall contain: 3 Condition Castings shall be supplied in the fully heat treated condition unless otherwise agreed between the purchaser and the founder, in which case the condition required shall be stated on the drawing or order. 4 Heat treatment 4.1 Solution treatme

8、nt. Heat uniformly at a temperature between1080 C and1100 C for8h and cool in air to room temperature. 4.2 Precipitation treatment. Heat at a temperature of750 10 C for16h and cool in air to room temperature. 5 Mechanical properties 5.1 Unless otherwise stated on the order the room temperature tensi

9、le properties obtained from test pieces representing re-melting stock and castings, selected, prepared and tested in accordance with the relevant requirements of BSHC 100, shall be: 5.2 If the order requires a hardness determination to be carried out, it shall be not less than270HB, 280 HV or 28 HRC

10、. 6 Rectification of defects 6.1 Correction of distortion. When permitted in accordance with BS HC 100, distortion shall be corrected after solution treatment and castings shall subsequently be precipitation treated. 6.2 Repair of castings by welding. When repair by welding is permitted in accordanc

11、e with BS HC 100, this shall be carried out after solution treatment and castings shall subsequently be precipitation treated. Re-melting stock Sections 1 and 2 Precision castings Sections 1 and 3 Element % min. max. Carbon 0.04 Silicon 0.10 0.4 Manganese 0.10 0.5 Sulphur 0.015 Cobalt 2.0 Copper 0.2

12、 Chromium 19.0 21.0 Iron 2.0 4.0 Lead 0.0020 Molybdenum 5.5 6.5 Niobium + Tantalum 6.2 7.0 Nitrogen 0.06 Silver 0.0005 Tungsten 2.0 3.0 Nickel Remainder 0.2 % proof stress Tensile strength Elongation N/mm 2 N/mm 2 % min. min. min. 480 650 5 NOTE1 N/mm 2= 1 MN/m 2= 1 MPa. Information on SI units is g

13、iven in BS 3763, “The International System of units (SI)”; seealso BS 350, “Conversion factors and tables”.BS HC 202:1973 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view o

14、n standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the qua

15、lity of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI

16、 offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089

17、967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international st

18、andards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to dat

19、e with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the

20、UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without pr

21、ior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.