BS EN ISO 9073-7-1998 Textiles Test methods for nonwovens Determination of bending length《纺织品 无纺织物的试验方法 弯曲长度的测定》.pdf

《BS EN ISO 9073-7-1998 Textiles Test methods for nonwovens Determination of bending length《纺织品 无纺织物的试验方法 弯曲长度的测定》.pdf》由会员分享，可在线阅读，更多相关《BS EN ISO 9073-7-1998 Textiles Test methods for nonwovens Determination of bending length《纺织品 无纺织物的试验方法 弯曲长度的测定》.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BSENISO 9073-7:1998 Textiles Test methods for nonwovens Part 7: Determination of bending length The European Standard EN ISO 9073-7:1998 has the status of a British Standard ICS 59.080.30BSEN ISO 9073-7:1998 This British Standard, having been prepared under the directionof the Secto

2、r Board forMaterials and Chemicals, waspublished under the authorityof the Standards Boardand comes into effect on 15November1998 BSI 05-1999 ISBN 0 580 30632 1 National foreword This British Standard is the English language version of EN ISO9073-7:1998. It is identical with ISO9073-7:1995. The UK p

3、articipation in its preparation was entrusted to Technical Committee TCI/24, Physical testing of textiles, which has the responsibility to: aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change,

4、and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references Attention is drawn to the fact that CEN and CENELEC standards

5、 normally include an annex which lists normative references to international publications with their corresponding European publications. The British Standards which implement international or European publications referred to in this document may be found in the BSI Standards Catalogue under the se

6、ction entitled “International Standards Correspondence Index”, or by using the “Find” facility of the BSI Standards Electronic Catalogue. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct applicatio

7、n. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, the EN ISO titlepage, page 2, the ISO title page, pages ii to iv, pages 1 to 4, aninside back cover and abac

8、k cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication Amd. No. Date CommentsBSENISO9073-7:1998 BSI 05-1999 i Contents Page National foreword I

9、nside front cover Foreword 2 Foreword iii Text of ISO 9073-7 1ii blankEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 9073-7 July 1998 ICS 59.080.30 Descriptors: See ISO document English version Textiles Test methods for nonwovens Part7: Determination of bending length (ISO9073-7:1995) Text

10、iles Mthodes dessai pour nontisss Partie7: Dtermination de la longueur de flexion (ISO9073-7:1995) Textilien Prfverfahren fr Vliesstoffe Teil7: Bestimmung der Biegelnge (ISO9073-7:1995) This European Standard was approved by CEN on 1 July 1998. CEN members are bound to comply with the CEN/CENELEC In

11、ternal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN mem

12、ber. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN member

13、s are the national standards bodies of Austria, Belgium, CzechRepublic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and UnitedKingdom. CEN European Committee for Standardization Comit Europen de Normalisati

14、on Europisches Komitee fr Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1998 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 9073-7:1998 EENISO9073-7:1998 BSI 05-1999 2 Foreword The text of the International

15、Standard from Technical Committee ISO/TC38 “Textiles” of the International Organization for Standardization (ISO) has been taken over as an European Standard by Technical Committee CEN/TC248 “Textiles and textile products”, the secretariat of which is held by BSI. This European Standard shall be giv

16、en the status of a national standard, either by publication of an identical text or by endorsement, at the latest by January1999, and conflicting national standards shall be withdrawn at the latest by January1999. According to the CEN/CENELEC Internal Regulations, the national standards organization

17、s of the following countries are bound to implement this European Standard: Austria, Belgium, CzechRepublic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the UnitedKingdom. Endorsement notice The text of

18、 the International Standard ISO9073-7:1998 has been approved by CEN as a European Standard without any modification. NOTENormative references to International Standards are listed inAnnex ZA (normative).ENISO9073-7:1998 ii BSI 05-1999 Contents Page Foreword iii 1 Scope 1 2 Normative references 1 3 D

19、efinitions 1 4 Principle 1 5 Apparatus 1 6 Sampling 1 7 Preparation and conditioning of test pieces 1 8 Procedure 2 9 Expression of results 3 10 Test report 3 Annex A (informative) Flexural rigidity, bending length and overhanging length 4 Annex ZA (normative) Normative references to international p

20、ublicationswiththeir relevant European publications Inside back cover Figure 1 Apparatus for measuring bending length 2ENISO9073-7:1998 BSI 05-1999 iii Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The wo

21、rk of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governm

22、ental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. Draft International Standards adopted by the technical committees are circulated to the member bodies for voti

23、ng. Publication as an International Standard requires approval by at least75% of the member bodies casting a vote. International Standard ISO9073-7 was prepared by Technical Committee ISO/TC38, Textiles. ISO 9073 consists of the following parts, under the general title Textiles Testmethods for nonwo

24、vens: Part 1: Determination of mass per unit area; Part 2: Determination of thickness; Part 3: Determination of tensile strength and elongation; Part 4: Determination of tear resistance; Part 7: Determination of bending length; Part 8: Determination of liquid strike-through time (simulated urine); P

25、art 9: Determination of drape coefficient. Annex A of this part of ISO9073 is for information only. Descriptors: Textiles, fabrics, non-woven fabrics, tests, bend tests, determination, length.iv blankEN ISO 9073-7:1998 BSI 05-1999 1 1 Scope This part of ISO9073 specifies a method for determining the

26、 bending length of a nonwoven fabric. An equation is given for calculating the flexural rigidity of the fabric from the bending length. The method is not applicable to combination-type materials (composites or laminates) in which there can be a natural twist. NOTE 1This International Standard descri

27、bes a test method specific to nonwovens. Other International Standards applicable to textile, paper, plastics, rubber or other materials can also be applied to test certain nonwoven characteristics. 2 Normative references The following standards contain provisions which, through reference in this te

28、xt, constitute provisions of this part of ISO9073. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part of ISO9073 are encouraged to investigate the possibility of applying the most recent editions of the s

29、tandards indicated below. Members of IEC and ISO maintain registers of currently valid International Standards. ISO 139:1973, Textiles Standard atmospheres for conditioning and testing. ISO 186:1994, Paper and board Sampling to determine average quality. ISO 9073-1:1989, Textiles Test methods for no

30、nwovens Part1: Determination of mass per unit area. 3 Definitions For the purposes of this part of ISO9073, the following definitions apply. 3.1 bending length length of a rectangular strip of fabric, fixed at one end and free at the other, that will bend under its own weight to an angle of7,1 3.2 f

31、lexural rigidity ratio of small changes in bending moment per unit width of the material to corresponding small changes in curvature NOTE 2Flexural rigidity can be calculated from the bending length. 4 Principle A rectangular strip of fabric is supported on a horizontal platform with the long axis o

32、f the strip parallel to the long axis of the platform. The strip is advanced in the direction of its length so that an increasing part overhangs the platform and bends down under its own weight. The overhang is free at one end, and fixed at the other from the pressure applied by a slide on the part

33、of the test piece still on the platform. When the leading edge of the test piece has reached a plane passing through the edge of the platform and inclined at an angle of41,5 below the horizontal, the overhanging length will equal twice the bending length of the test piece (seeAnnex A), and thus the

34、bending length can be calculated. 5 Apparatus A suitable apparatus is shown inFigure 1. 5.1 Level table. 5.2 Platform, of width(40 2)mm and length(200 2)mm, supported at a height of at least150mm above the surface of the table(5.1). Each side of the platform support shall be transparent and marked w

35、ith a line (L 1and L 2respectively; seeFigure 1) running from the end of the platform at an angle of41,5 below the horizontal. A mark (D) shall be made on the platform at(10 1)mm from the front edge (seeFigure 1). NOTE 3To avoid adherence of the test piece, the platform should be coated or covered w

36、ith polytetrafluoroethylene (PTFE). 5.3 Steel rule, (25 1)mm, length(350 1)mm of width and mass(250 10)g, accurately graduated in millimetres, and with a rubber-covered underside. NOTE 4A rule made of steel plate3,5mm thick will have the correct mass. 6 Sampling Carry out sampling in accordance with

37、 ISO186. 7 Preparation and conditioning of test pieces 7.1 Cut out six test pieces (25 1) mm (250 1) mm with their long edges parallel to the textile manufacturing machine direction (MD) and an equal number of test pieces with their long edges in the perpendicular, or cross-machine, direction (CD).

38、The test pieces shall be taken at least50mm from the edge of the fabric and the test pieces shall be handled as little as possible.EN ISO 9073-7:1998 2 BSI 05-1999 NOTE 5Fabrics which tend to curl or twist should be conditioned before cutting out the test pieces. If the test pieces curl or twist ser

39、iously, they can often be made to lie flat long enough for testing by pressing lightly between flat surfaces for several hours. NOTE 6Additional samples may be taken at an angle of45 to the machine direction. NOTE 7For production control, the number of test pieces may be limited to three in each dir

40、ection (MD and CD). 7.2 Condition the test pieces and carry out the test in one of the standard atmospheres specified in ISO139. 8 Procedure 8.1 Weigh the test piece and calculate the mass per unit area in grams per square metre in accordance with ISO9073-1. 8.2 Place the apparatus on the level tabl

41、e(5.1). Place the test piece on the platform with one end coinciding with the front edge of the platform. Place the steel rule(5.3) on the test piece with the zero of the scale in line with the markD on the platform. Push the steel rule forward so that the test piece projects over the front edge of

42、the platform and bends down under its own weight. Move the rule forward at a constant speed (this can be facilitated by using an apparatus fitted with a motorized drive, see note7) until the overhanging end of the test piece reaches the two lines on the platform support L 1andL 2 . After an interval

43、 of(8 2)s, read on the scale on the steel rule the overhanging length of the test piece. NOTE 8Information on a suitable apparatus fitted with a motorized drive can be provided by the following associations in the nonwovens industry: INDA, 1001Winstead Drive, Suite460, Cary, NC27513, USA; EDANA, 157

44、 av. Eugne Plasky, B-1040 Brussels. 8.3 Repeat the operation in8.2 with the other face of the test piece up, and again at the other end of the test piece, first with the original face up and then with the test piece turned over. Figure 1 Apparatus for measuring bending lengthEN ISO 9073-7:1998 BSI 0

45、5-1999 3 NOTE 9It may be helpful to place the apparatus so that the zero of the scale on the rule lies towards the observer and at a level that enables the scale to be read with comfort. The position of the end of the test piece relative to L 1and L 2may be observed in a mirror suitably placed or at

46、tached to one side of the apparatus. 9 Expression of results 9.1 Taking the bending length to be half the length of the overhang, record the four values of the bending length for each test piece and from these calculate the mean bending length for each test piece. 9.2 Then calculate the overall mean

47、 bending length, C, in centimetres, for the six test pieces cut in the machine direction. Calculate the same parameter separately for the six test pieces cut in the cross-machine direction. 9.3 Calculate the mean flexural rigidity, G, per unit width, in millinewton centimetres, separately for the ma

48、chine direction and the cross-machine direction test pieces, using the following equation: G = m C 3 10 3 where NOTE 10In determining this equation, the acceleration due to gravity,9,81m/s 2 , has been rounded to10m/s 2 . 9.4 Calculate the coefficient of variation (ratio of the standard deviation to

49、 the average) for C and G in both machine direction and cross-machine direction. 10 Test report The test report shall include the following information: a) a reference to this part of ISO9073; b) all details necessary for the identification of the material; c) number of measurements taken; d) number of MD test pieces tested; e) number of CD test pieces tested; f) overall mean bending length and coefficient of variation of the test material for the machine direction; g) overall mean bending leng