BS EN ISO 1924-2-2008 Paper and board - Determination of tensile properties - Constant rate of elongation method (20 mm min)《纸和纸板 拉伸性能的测定 恒速拉伸法(20mm min)》.pdf

《BS EN ISO 1924-2-2008 Paper and board - Determination of tensile properties - Constant rate of elongation method (20 mm min)《纸和纸板 拉伸性能的测定 恒速拉伸法(20mm min)》.pdf》由会员分享，可在线阅读，更多相关《BS EN ISO 1924-2-2008 Paper and board - Determination of tensile properties - Constant rate of elongation method (20 mm min)《纸和纸板 拉伸性能的测定 恒速拉伸法(20mm min)》.pdf（22页珍藏版）》请在麦多课文档分享上搜索。

1、BS EN ISO1924-2:2008ICS 85.060NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDPaper and board Determination oftensile propertiesPart 2: Constant rate of elongationmethod (20 mm/min) (ISO 1924-2:2008)Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/20

2、09 08:26, Uncontrolled Copy, (c) BSIThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 28 February2009 BSI 2009ISBN 978 0 580 58756 6Amendments/corrigenda issued since publicationDate CommentsBS EN ISO 1924-2:2008National forewordThis British Standa

3、rd is the UK implementation of EN ISO 1924-2:2008.It supersedes BS EN ISO 1924 :1995 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee PAI/11, Methods of test for paper, board and pulps.A list of organizations represented on this committee can be obtained

4、 onrequest to its secretary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.-2Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARD

5、S, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIEUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN ISO 1924-2December 2008ICS 85.060 Supersedes EN ISO 1924-2:1995 English VersionPaper and board - Determination of tensile properties - Part 2:Constant rate of elongation method (20 mm/min) (ISO 1924-2:20

6、08)Papier et carton - Dtermination des proprits de traction -Partie 2: Mthode gradient dallongement constant (20mm/min) (ISO 1924-2:2008)Papier und Pappe - Bestimmung von Eigenschaften beiZugbeanspruchung - Teil 2: Verfahren mit konstanterDehngeschwindigkeit (20 mm/min) (ISO 1924-2:2008)This Europea

7、n Standard was approved by CEN on 19 November 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references conce

8、rning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own l

9、anguage and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, L

10、uxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: Avenue Marnix 17, B-1000 Brussels 2008 CEN All right

11、s of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN ISO 1924-2:2008: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008EN ISO 1924-2:2008 (E) 3 Foreword This document (EN ISO 1924

12、-2:2008) has been prepared by Technical Committee ISO/TC 6 “Paper, board and pulps“ in collaboration with Technical Committee CEN/TC 172 “Pulp, paper and board“, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of

13、 an identical text or by endorsement, at the latest by June 2009, and conflicting national standards shall be withdrawn at the latest by June 2009. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be he

14、ld responsible for identifying any or all such patent rights. This document supersedes EN ISO 1924-2:1995. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyp

15、rus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 1

16、924-2:2008 has been approved by CEN as a EN ISO 1924-2:2008 without any modification. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008ISO 1924-2:2008(E) ISO 2008 All rights reserved iiiContents Page Foreword iv Introduction.v 1

17、Scope1 2 Normative references1 3 Terms and definitions .2 4 Principle2 5 Apparatus.3 6 Calibration and adjustment of apparatus .4 7 Sampling and preparation of test pieces4 7.1 Sampling.4 7.2 Conditioning 4 7.3 Preparation of test pieces.5 8 Procedure.5 9 Calculation and report 6 9.1 General .6 9.2

18、Tensile strength.6 9.3 Tensile index6 9.4 Strain at break6 9.5 Tensile energy absorption7 9.6 Tensile energy absorption index .7 9.7 Modulus of elasticity.7 10 Precision.8 10.1 General .8 10.2 Repeatability 8 10.3 Reproducibility 8 11 Test report10 Annex A (normative) Calibration of the tensile test

19、ing machine.11 Bibliography12 Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008ISO 1924-2:2008(E) iv ISO 2008 All rights reservedForeword ISO (the International Organization for Standardization) is a worldwide federation of natio

20、nal standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. Internati

21、onal organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rul

22、es given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at

23、least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 1924-2 was prepared by Technical Committee ISO/TC

24、 6, Paper, board and pulps, Subcommittee SC 2, Test methods and quality specifications for paper and board. This third edition cancels and replaces the second edition (ISO 1924-2:1994), which has been technically revised with respect to terms and definitions (in order to be in line with the terms an

25、d definitions used in ISO 1924-31). The numbering of clauses and their contents have been changed to be congruent with ISO 1924-3. ISO 1924 consists of the following parts, under the general title Paper and board Determination of tensile properties1): Part 2: Constant rate of elongation method (20 m

26、m/min) Part 3: Constant rate of elongation method (100 mm/min) 1) ISO 1924-1, Constant rate of loading method, was withdrawn in 2004 as it was considered obsolete. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008ISO 1924-2:2008(

27、E) ISO 2008 All rights reserved vIntroduction The method for determination of tensile properties specified in this part of ISO 1924 is the one most commonly used. It is related to the method specified in ISO 1924-3. In this part of ISO 1924 (ISO 1924-2), the constant rate of elongation applied is 20

28、 mm/min, whereas in ISO 1924-3, the constant rate of elongation applied is 100 mm/min. Since the results of a tensile test depend on the rate of elongation applied, this part of ISO 1924 and ISO 1924-3 will not give the same results. The rate dependence can vary according to paper grade and is diffe

29、rent for tensile strength, strain at break, tensile energy absorption and modulus of elasticity. NOTE 1 In most cases, the tensile properties can increase by 5 % to 15 % when the rate of elongation is increased from 20 mm/min (180 mm test span length) to 100 mm/min (100 mm test span length). NOTE 2

30、In this part of ISO 1924, the same terminology and symbols are used as in ISO 1924-3 and in general literature concerning materials physics and mechanics. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008Licensed Copy: Wang Bin,

31、ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008INTERNATIONAL STANDARD ISO 1924-2:2008(E) ISO 2008 All rights reserved 1Paper and board Determination of tensile properties Part 2: Constant rate of elongation method (20 mm/min) 1 Scope This part of ISO 1

32、924 specifies a method for measuring the tensile strength, strain at break and tensile energy absorption of paper and board, using a testing machine operating at a constant rate of elongation (20 mm/min). This part of ISO 1924 also specifies equations for calculating the tensile index, the tensile e

33、nergy absorption index and the modulus of elasticity. Testing in conformance with this part of ISO 1924 always includes the measurement of tensile strength. Measurement or calculation of other properties is subject to agreement between the parties concerned. This part of ISO 1924 is applicable to al

34、l papers and boards, including papers with a high strain at break if the results are within the capacity of the testing machine. It also applies to the components of corrugated board but not, however, to corrugated board itself. This part of ISO 1924 is not applicable to tissue paper and tissue prod

35、ucts for which ISO 12625-42is applicable. For the determination of tensile properties of laboratory sheets, ISO 52703is recommended. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies.

36、 For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 186, Paper and board Sampling to determine average quality ISO 187, Paper, board and pulps Standard atmosphere for conditioning and testing and procedure for monitoring the atmosphere and c

37、onditioning of samples ISO 534, Paper and board Determination of thickness, density and specific volume ISO 536, Paper and board Determination of grammage Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008ISO 1924-2:2008(E) 2 ISO

38、2008 All rights reserved3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 tensile strength maximum tensile force per unit width that paper and board will withstand before breaking under the conditions defined in this International Standard 3.2

39、tensile index tensile strength divided by the grammage 3.3 elongation increase in length of a test piece NOTE Elongation is expressed in millimetres. 3.4 strain ratio of the elongation of a test piece to the initial test length NOTE 1 Strain is expressed as a percentage of the initial test length. N

40、OTE 2 The initial test length of the test piece is the same as the initial span between the clamping lines. 3.5 strain at break ratio of the measured elongation at the moment of rupture of a test piece of paper, when extended under the conditions defined in the standard method of test, to the initia

41、l test length 3.6 tensile energy absorption amount of energy per unit surface area of a test piece when it is strained to the maximum tensile force NOTE Surface area is calculated as test length multiplied by width. 3.7 tensile energy absorption index tensile energy absorption divided by the grammag

42、e 3.8 modulus of elasticity maximum slope of the force-elongation curve multiplied by the initial length divided by the width and the thickness of the test piece NOTE See also Figure 2. 4 Principle A test piece of given dimensions is strained to break at a constant rate of elongation using a testing

43、 machine that records both the tensile force and, if required, the elongation. If the tensile force and elongation are continuously recorded, the strain at break, the tensile energy absorption and the modulus of elasticity may be determined. From the recorded data, and the knowledge of the grammage

44、of the sample, the tensile index and the tensile energy absorption index may be calculated. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2009 08:26, Uncontrolled Copy, (c) BSIBS EN ISO 1924-2:2008ISO 1924-2:2008(E) ISO 2008 All rights reserved 35 Apparatus 5.1 Tensile testing machine

45、, designed to extend a test piece of given dimensions at an appropriate constant rate of elongation (20 mm/min), and to measure the tensile force and, if required, the elongation produced. The tensile testing machine includes means of measuring and indicating the tensile force to an accuracy of 1 %

46、of the true force and, if required, the elongation to an accuracy of 0,1 % elongation. The tensile force may be recorded as a function of the elongation on an electronic integrator or an equivalent device. NOTE 1 The accuracy of measurement of elongation is very important. An appropriate extensomete

47、r, placed directly on the test piece, is recommended for accurate measurement of true elongation (see ISO 9513, class 1 or class 0,5). This is to avoid the possibility of including in the measurement any apparent elongation which can result from undetected slippage of the test piece in the clamps or

48、 from the take-up in the joints of the apparatus. The latter is dependent upon the load applied and the error can increase due to wear of the joints of an apparatus which has been in use for some time. It is advisable that means be applied to limit additional loads, which an extensometer would apply

49、 to the test piece, to the required accuracy of the tensile force. The tensile testing machine also includes two clamps, for holding a test piece of the required width (see 7.3). Each clamp shall be designed to grip the test piece firmly, but without damage or slippage, along a straight line across the full width of the test piece and have a means of adjusting the clamping force. The clamping surfaces of the clamps shall be in the same plane and so aligned that they hold the test piece in that plane throughout the test. NO