BS EN 4700-006-2010 Aerospace series Steel nand heat resisting alloys nWrought products Technical nspecification nPart 006 Pre-production and production nforgings《航空航天系列 耐热合金钢 锻轧.pdf

《BS EN 4700-006-2010 Aerospace series Steel nand heat resisting alloys nWrought products Technical nspecification nPart 006 Pre-production and production nforgings《航空航天系列 耐热合金钢 锻轧.pdf》由会员分享，可在线阅读，更多相关《BS EN 4700-006-2010 Aerospace series Steel nand heat resisting alloys nWrought products Technical nspecification nPart 006 Pre-production and production nforgings《航空航天系列 耐热合金钢 锻轧.pdf（32页珍藏版）》请在麦多课文档分享上搜索。

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 4700-006:2010Aerospace series Steeland heat resisting alloys Wrought products TechnicalspecificationPart 006: Pre-production and productionforgingsBS EN 4700-006:2010 BRITI

2、SH STANDARDNational forewordThis British Standard is the UK implementation of EN 4700-006:2010.The UK participation in its preparation was entrusted to TechnicalCommittee ACE/61/-/48, Heat Resisting Alloys for AerospacePurposes.A list of organizations represented on this committee can beobtained on

3、request to its secretary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. BSI 2010ISBN 978 0 580 55076 8ICS 49.025.10Compliance with a British Standard cannot confer immunity fromlegal obligations.This British S

4、tandard was published under the authority of theStandards Policy and Strategy Committee on 30 September 2010.Amendments issued since publicationDate Text affectedBS EN 4700-006:2010EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 4700-006 September 2010 ICS 49.025.10 English Version Aerospace se

5、ries - Steel and heat resisting alloys - Wrought products - Technical specification - Part 006: Pre-production and production forgings Srie arospatiale - Aciers et alliages rsistant chaud - Produits corroys - Spcification technique - Partie 006: Pices types et pices de srie Luft- und Raumfahrt - Sta

6、hl und Hochwarmfesten Legierungen - Umgeformte Erzeugnisse - Technische Lieferbedingungen - Teil 006: Ausfallmuster und Serienschmiedestcke This European Standard was approved by CEN on 9 January 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the cond

7、itions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists in thr

8、ee official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN members are the national standards bodies of

9、Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.

10、EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 4700-006:2010: EBS EN 47

11、00-006:2010EN 4700-006:2010 (E) 2 Contents Page Foreword 3Introduction . 41 Scope 42 Normative references 43 Terms and definitions . 64 Wording of order 65 Health and safety . 66 Technical requirements 66.1 General 66.2 Qualification requirements . 76.3 Re-qualification requirements 76.4 Release req

12、uirements . 76.5 Process control testing (Procedure X) 86.6 Retests 86.7 Special tests . 96.8 Capability clause . 96.9 Statistical process control 96.10 Inspection and test report . 10BS EN 4700-006:2010EN 4700-006:2010 (E) 3 Foreword This document (EN 4700-006:2010) has been prepared by the Aerospa

13、ce and Defence Industries Association of Europe - Standardization (ASD-STAN). After enquiries and votes carried out in accordance with the rules of this Association, this Standard has received the approval of the National Associations and the Official Services of the member countries of ASD, prior t

14、o its presentation to CEN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by March 2011, and conflicting national standards shall be withdrawn at the latest by March 2011. Attention is drawn to the

15、possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countri

16、es are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Sloveni

17、a, Spain, Sweden, Switzerland and the United Kingdom. BS EN 4700-006:2010EN 4700-006:2010 (E) 4 Introduction This European Standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. 1 Scope This Europe

18、an Standard defines the requirements for the ordering, manufacture, testing, inspection and delivery of pre-production and production forgings in steel and heat resisting alloys. 2 Normative references The following referenced documents are indispensable for the application of this document. For dat

19、ed references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN ISO 3651-1, Determination of resistance to intergranular corrosion of stainless steels Part 1: Austenitic and ferritic-austenitic (duplex) stain

20、less steels Corrosion test in nitric acid medium by measurement of loss in mass (Huey test) (ISO 3651-1:1998) EN ISO 3651-2, Determination of resistance to intergranular corrosion of stainless steels Part 2: Ferritic, austenitic and ferritic-austenitic (duplex) stainless steels Corrosion test in med

21、ia containing sulfuric acid (ISO 3651-2:1998) EN ISO 6506-1, Metallic materials Brinell hardness test Part 1: Test method (ISO 6506-1:2005) EN ISO 6507-1, Metallic materials Vickers hardness test Part 1: Test method (ISO 6507-1:2005) EN ISO 6508-1, Metallic materials Rockwell hardness test Part 1: T

22、est method (scales A, B, C, D, E, F, G, H, K, N, T) (ISO 6508-1:2005) EN ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature (ISO 6892-1:2009) prEN ISO 6892-2, Metallic materials Tensile testing Part 2: Method of test at elevated temperature (ISO/DIS 6892-2:2009

23、) EN 2002-001, Aerospace series Metallic materials Test methods Part 001: Tensile testing at ambient temperature EN 2002-002, Aerospace series Metallic materials Test methods Part 002: Tensile testing at elevated temperature EN 2002-005, Aerospace series Test methods for metallic materials Part 005:

24、 Uninterrupted creep and stress-rupture testing EN 2002-16, Aerospace series Metallic materials Test methods Part 16: Non-destructive testing Penetrant testing 1)EN 2003-2, Aerospace series Steels Test methods Part 2: Izod impact test 1)1) Published as ASD-STAN Prestandard at the date of publication

25、 of this standard by Aerospace and Defence Industries Association of Europe-Standardization (ASD-STAN), (www.asd-stan.org). BS EN 4700-006:2010EN 4700-006:2010 (E) 5 EN 2032-1, Aerospace series Metallic materials Part 1: Conventional designation EN 2032-2, Aerospace series Metallic materials Part 2:

26、 Coding of metallurgical condition in delivery condition EN 2078, Aerospace series Metallic materials Manufacturing schedule, inspection schedule, inspection and test report Definition, general principles, preparation and approval EN 2950, Aerospace series Test method Wrought heat resisting alloys S

27、emi-finished products and parts Conditions for macrographic and micrographic examination Atlas of structures and defects EN 2951, Aerospace series Metallic materials Test method Micrographic determination of content of non-metallic inclusions 1)EN 3874, Aerospace series Test methods for metallic mat

28、erials Constant amplitude force-controlled low cycle fatigue testing 1)EN 3987, Aerospace series Test method for metallic materials Constant amplitude force-controlled high cycle fatigue testing 1)EN 3988, Aerospace series Test methods for metallic materials Constant amplitude strain-controlled low

29、cycle fatigue testing 1)EN 4050-1, Aerospace series Test method for metallic materials Ultrasonic inspection of bars, plates, forging stock and forgings Part 1: General requirements 1)EN 4050-4, Aerospace series Test method for metallic materials Ultrasonic inspection of bars, plates, forging stock

30、and forgings Part 4: Acceptance criteria 1)EN 4259, Aerospace series Metallic materials Definition of general terms 1)EN 9100, Quality Management Systems Requirements for Aviation, Space and Defence Organizations EN 9133, Aerospace series Quality management systems Qualification procedure for aerosp

31、ace standard parts EN 10027-1, Designation systems for steels Part 1: Steel names EN 10045-1, Metallic materials Charpy impact test Part 1: Test method EN 10079, Definition of steel products TR 2410, Aerospace series Metallic materials Relationship between dimensional standards and material standard

32、s 2)AMS 2315, Determination of Delta Ferrite Content 3)AMS 2750, Pyrometry 3)2) Published as ASD-STAN Technical Report at the date of publication of this standard by Aerospace and Defence Industries Association of Europe-Standardization (ASD-STAN), (www.asd-stan.org). 3) Published by: SAE National (

33、US) Society of Automotive Engineers http:/www.sae.org/ BS EN 4700-006:2010EN 4700-006:2010 (E) 6 ASTM E709, Standard Guide for Magnetic Particle Testing 4)ASTM E1444, Standard Practice for Magnetic Particle Testing 4)3 Terms and definitions For the purposes of this document, the terms and definition

34、s given in EN 4259 apply. For definitions specific to steel, see EN 10079. 4 Wording of order The order shall clearly indicate: quantities to be supplied; dates of delivery; material standard number; delivery condition and metallurgical code of products; dimensions and tolerances or reference to an

35、appropriate dimensional standard; product designation, when required; forwarding address; nature and type of packing, if required; surface protection, if appropriate; definition and frequency of any special tests and their retest procedures, if required. 5 Health and safety Products in the delivery

36、condition shall fulfil the health and safety laws of the area of the country when and where it is to be delivered. A product safety data sheet shall be available. 6 Technical requirements 6.1 General The product shall satisfy the requirements of the order, drawing inspection schedule or material sta

37、ndard: see Table 2, line 5. The order, drawing or inspection schedule shall specify the tests to be performed upon (i) pre-forgings for qualification and/or requalification (ii) serial production forgings for process control testing (Procedure X: see 6.4) and (iii) batch release when cut-up testing

38、or forgings is required. Unless otherwise specified on the order, drawing or inspection schedule, acceptance criteria for the tests are stated in the material standard, 4) Published by: ASTM National (US) American Society for Testing and Materials http:/www.astm.org/ BS EN 4700-006:2010EN 4700-006:2

39、010 (E) 7 the requirements for each line of which are detailed in Tables 2 and 3 of this technical specification. Table 2 related to lines 1 to 29 (inclusive) of the material standard and Table 3 relates to lines 30 onwards in which the subline format is also used. If a particular test is needed but

40、 not shown in a specific line in Tables 2 and 3, the requirement shall be specified on the order, drawing, inspection schedule or material standard. 6.2 Qualification requirements See line 100 in Table 3 of this technical specification. Qualification shall normally comprise assessment of pre-product

41、ion forgings. See Table 2, section 4.2. 6.3 Re-qualification requirements Re-qualification of serial production forgings may be required, in the following cases: modification of the drawing; use of forging stock from a different source; modifications to the forging stock form and/or manufacturer rou

42、te; modifications to an existing die; use of a new (replacement) die; modifications to the forging manufacturing route; when a significant time interval (usually several years) had elapsed between forging campaigns for a specific part number; when required by the purchaser for any other reason. Re-q

43、ualification testing requirements, especially location of test pieces, shall be identical to those used for the initial qualification of the pre-production forgings unless otherwise specified on the order, drawing or inspection schedule. 6.4 Release requirements Release testing shall be the responsi

44、bility of the manufacturer. The sampling procedure for release testing shall be one of the following, as specified on the order, drawing or inspection schedule. Where no procedure is specified, procedure A shall be used: BS EN 4700-006:2010EN 4700-006:2010 (E) 8 Procedure A: Separate forged test sam

45、ples shall be procedure produced from the same batch of forging stock as that used to make the serial production forgings. Procedure A may be used alone unless denoted AX on the drawing, order or inspection schedule in which case it shall be applied only in conjunction with procedure X (See 6.5). Pr

46、ocedure B: Separate forged heat treatment control test samples shall be prepared which conform to the same material standard as the production forgings, but from a different batch of forging stock. Procedure B shall only be used when full heat treatment of the serial production forgings is carried o

47、ut by the manufacturer and only in conjunction with procedure X (See 6.5). Procedure C: Integral test samples shall be removed from each forgings. The order, drawing of inspection schedule shall specify how many test samples shall be tested per batch. Procedure C may be used alone unless denoted CX

48、on the drawing, order or inspection schedule in which case it shall be applied only in conjunction with procedure X (See 6.5). Procedure D: Test samples shall be machined from forging(s) selected from each production batch and at locations specified on the order, drawing or inspection schedule. When

49、 required, the manufactured shall inform the purchaser of the planned dates for extraction of samples and release testing in order that these operations may be witnessed. 6.5 Process control testing (Procedure X) Procedure X is process control procedure consisting of periodic “cut-up” testing to ensure that the serial produc