BS EN 1592-1-1998 Aluminium and aluminium alloys - HF seam welded tubes - Technical conditions for inspection and delivery《铝和铝合金 HF缝焊管 检验和交付技术状态》.pdf

《BS EN 1592-1-1998 Aluminium and aluminium alloys - HF seam welded tubes - Technical conditions for inspection and delivery《铝和铝合金 HF缝焊管 检验和交付技术状态》.pdf》由会员分享，可在线阅读，更多相关《BS EN 1592-1-1998 Aluminium and aluminium alloys - HF seam welded tubes - Technical conditions for inspection and delivery《铝和铝合金 HF缝焊管 检验和交付技术状态》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS EN 1592-1 : 1998 The E

2、uropean Standard EN 1592-1 : 1997 has the status of a British Standard ICS 77.150.10 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Aluminium and aluminium alloys HF seam welded tubes Part 1. Technical conditions for inspection and deliveryThis British Standard, having been p

3、repared under the direction of the Engineering Sector Board, was published under the authority of the Standards Board and comes into effect on 15 March 1998 BSI 1998 ISBN 0 580 29032 8 BS EN 1592-1 : 1998 Amendments issued since publication Amd. No. Date Text affected National foreword This British

4、Standard is the English language version of EN 1592-1 : 1997 published by the European Committee for Standardization (CEN). Together with BS EN 1592-2 : 1998, BS EN 1592-3 : 1998 and BS EN 1592-4 : 1998 it supersedes BS 4300-1 : 1967 which is withdrawn. The UK participation in its preparation was en

5、trusted by Technical Committee NFE/35, Light metals and their alloys, to Subcommittee NFE/35/5, Wrought aluminium and aluminium alloys, which has the responsibility to: aid enquirers to understand the text; present to the responsible European committee any enquiries on the interpretation, or proposa

6、ls for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement internat

7、ional or European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled International Standards Correspondence Index, or by using the Find facility of the BSI Standards Electronic Catalogue. Compliance with a British Standard does not of its

8、elf confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 8, an inside back cover and a back cover.CEN European Committee for Standardization Comite Europe en de Normalisation Europa isches Komitee fu r No

9、rmung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1997 CEN All rights of exploitation in any form and by any means reserved worldwide to CEN national Members. Ref. No. EN 1592-1 : 1997 E EUROPEAN STANDARD EN 1592-1 NORME EUROPE ENNE EUROPA ISCHE NORM October 1997 ICS 77.150.10 Descripto

10、rs: Aluminium, aluminium alloys, aluminium tubes, welded tubes, orders, delivery, inspection, chemical composition, mechanical properties, defects, dimensional tolerances, tests, packing English version Aluminium and aluminium alloys HF seam welded tubes Part 1: Technical conditions for inspection a

11、nd delivery Aluminium et alliages daluminium Tubes e lectrosoude sH F Partie 1: Conditions techniques de contro le et de livraison Aluminium und Aluminiumlegierungen HF-la ngsnahtgeschweite Rohre Teil 1: Technische Lieferbedingungen This European Standard was approved by CEN on 19 September 1997. CE

12、N members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on app

13、lication to the Central Secretariat or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has

14、 the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom.Page 2 EN 1592-1

15、: 1997 BSI 1998 Foreword This European Standard has been prepared by Technical Committee CEN/TC 132, Aluminium and aluminium alloys, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by en

16、dorsement, at the latest by April 1998, and conflicting national standards shall be withdrawn at the latest by April 1998. Within its programme of work, Technical Committee CEN/TC 132 entrusted CEN/TC 132/WG 12, HF Seam welded tubes, to prepare the following standards: EN 1592-1 Aluminium and alumin

17、ium alloys HF seam welded tubes Part 1: Technical conditions for inspection and delivery This standard is part of a series of four standards. The other standards deal with: EN 1592-2 Aluminium and aluminium alloys HF seam welded tubes Part 2: Mechanical properties EN 1592-3 Aluminium and aluminium a

18、lloys HF seam welded tubes Part 3: Tolerances on dimensions and form for circular tubes EN 1592-4 Aluminium and aluminium alloys HF seam welded tubes Part 4: Tolerances on dimensions and form for square, rectangular and shaped tubes According to the CEN/CENELEC Internal Regulations, the national sta

19、ndards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. Contents

20、Page Foreword 2 Introduction 3 1 Scope 3 2 Normative references 3 3 Definitions 3 4 Orders or tenders 4 5 Requirements 4 5.1 Quality control 4 5.2 Metallurgical condition 4 5.3 Chemical composition 4 5.4 Mechanical properties 4 5.5 Freedom from defects 4 5.6 Dimensional tolerances 5 5.7 Other proper

21、ties 5 6 Test procedure 5 6.1 Sampling 5 6.2 Test methods 6 6.3 Retests 6 7 Inspection documents 6 7.1 General 6 7.2 Documents established on the basis of inspections and tests performed by qualified personnel who are involved in the manufacturing process and/or belong to the quality control departm

22、ent 6 7.3 Documents established on the basis of inspections and tests performed or supervised by qualified personnel organizationally independent from the manufacturing department, according to the requirements specified on the order and carried out on the products for delivery or on the relevant in

23、spection lot 7 8 Packaging, delivery and storage 7 9 Arbitration 7 Annex A (informative) Bibliography 8Page 3 EN 1592-1 : 1997 BSI 1998 Introduction HF seam welded aluminium tubes are made from coils of slit aluminium strip, which are progressively shaped by a series of forming rolls on a mill. At t

24、he point during its passage through the mill that the tube becomes fully formed, it is welded. HF currents are induced into the tube by an induction coil through which the tube passes. The current is confined to the surface of the tube which causes the edges of the strip to reach welding temperature

25、. These edges are forced into contact with each other by pressure rolls and a perfectly formed weld is achieved. No filler wire is used and the resultant weld is perfectly uniform. The external fin from the weld is removed by planing in the next section of mill before the tube passes through a final

26、 series of sizing rolls, which gives its final shape. This continuous operation is carried out at high speed. In this way, the HF seam welded tube benefits from the properties of the initial strip, such as a wide variety of potential alloys and mechanical properties are available. Because of the for

27、ming technique used, the seam welded tube also benefits from specific properties. Thin wall and/or large diameter tubes can be obtained. Different shapes can be produced, from the most frequently used ones to special order shapes. Various finishes can be obtained. Standard tubes are produced with a

28、bright finish. Other finishes available are: mill finish, anodized matt or bright in many colours. Tubes can also be supplied painted. Various patterns are available that can be embossed into the surface of the tubes. Due to the great variety of patterns available, the user is advised to contact the

29、 supplier for further information. The external fin is removed by planing. By special order, the internal fin can also be removed. Due to the great variety of tubes available, the user is advised to consult the supplier with regards to any new application of HF seam welded tubes. 1 Scope This Part o

30、f EN 1592 specifies the technical conditions for inspection and delivery of HF seam welded aluminium tubes. It is applicable to HF seam welded tubes obtained by forming cold-rolled strips. It is applicable to aluminium tubes produced from uncoated aluminium strip, as well as to tubing that is pre-la

31、cquered, pre-painted or pre-anodized prior to forming. 2 Normative references This European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are listed hereafter. F

32、or dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies. EN 515 Aluminium and aluminium alloys Wroug

33、ht products Temper designations EN 573-3 Aluminium and aluminium alloys Chemical composition and form of wrought products Part 3: Chemical composition EN 573-4 Aluminium and aluminium alloys Chemical composition and form of wrought products Part 4: Forms of products EN 1592-2 Aluminium and aluminium

34、 alloys HF seam welded tubes Part 2: Mechanical properties EN 1592-3 Aluminium and aluminium alloys HF seam welded tubes Part 3: Tolerances on dimensions and form for circular tubes EN 1592-4 Aluminium and aluminium alloys HF seam welded tubes Part 4: Tolerances on dimensions and form for square, re

35、ctangular and shaped tubes EN 10002-1 Metallic materials Tensile testing Part 1: Method of test (at ambient temperature) EN 10204 Metallic products Types of inspection documents NOTE. Informative references to documents used in the preparation of this standard, and cited at the appropriate places in

36、 the text, are listed in a bibliography, see annex A. 3 Definitions For the purposes of this standard the following definitions apply: 3.1 HF seam welded aluminium tube Welded tube produced from strip by use of HF current without filler wire. 3.2 round tube Hollow product of circular section, suppli

37、ed in straight lengths.Page 4 EN 1592-1 : 1997 BSI 1998 3.3 square and rectangular tube Hollow product of square or rectangular section, supplied in straight lengths. 3.4 shaped tube Hollow product, of special section, defined by a drawing or pattern, supplied in straight lengths. 3.5 modified surfa

38、ce The surface of the HF seam welded aluminium tube can be modified either by etching, or by a coating of paint, or by anodizing. NOTE. Pre-anodized, pre-painted or pre-lacquered coils can also be used. 3.6 inspection lot Consignment, or part thereof, submitted for inspection, comprising products of

39、 the same grade or alloy, form, temper, thickness or cross-section, and processed in the same manner. 3.7 heat treatment batch or lot A quantity of products of the same grade or alloy, form, thickness or cross section and produced in the same way, heat treated in one furnace load, or such products a

40、s solution-treated and subsequently precipitation-treated in one furnace load. More than one solution-treatment lot can be included in a furnace load. NOTE. For the heat treatment in a continuous furnace, the products heat treated during a time less than 8 h can be considered as belonging to the sam

41、e heat treatment lot. 3.8 sample One or more products taken from an inspection lot. 3.9 specimen One or more pieces taken from each product in the sample, for the purpose of producing test pieces. 3.10 test piece A piece taken from each specimen and suitably prepared for the test. 4 Orders or tender

42、s The order or tender shall define the product required and shall contain the following information: a) the shape and type of the product: round, square, rectangular or shaped HF seam welded aluminium tube; b) description of the material: alloy and metallurgical condition. The latter is shown by the

43、 symbol for the heat and/or mechanical treatment given to the material (see EN 515, EN 573-3 and EN 1592-2); c) the dimensions of the product: diameter or width across flats; wall thickness; length; d) quantity: mass in kilograms or tonnes; number of lengths; e) any requirements for inspection docum

44、ents; f) any special requirements agreed between the producer and purchaser; g) surface finish condition: unless otherwise agreed the tubes shall be supplied in a mill finish condition; other surface finishes can be specified, if applicable, such as painted, lacquered or anodized; h) special packagi

45、ng and delivery requirements (where applicable): ship freight packaging; unit mass of non-standard packages; staggering of delivery intervals; i) in the case of coated HF welded tubes, the coating shall be specified by agreement between producer and purchaser with reference to the relevant standards

46、; j) in the case of etched tubes, the producer and the purchaser shall agree the dimensions and tolerances. 5 Requirements 5.1 Quality control The producer is responsible for the performance of all inspection and tests required by the relevant European Standard and/or the particular specification, p

47、rior to shipment of the product. If the purchaser wishes to inspect the product at the producers works, he shall notify the producer at the time of placing the order. 5.2 Metallurgical condition The metallurgical condition shall be in accordance with EN 1592-2 and EN 515. 5.3 Chemical composition Th

48、e chemical composition of the alloy shall comply with EN 573-3. The aluminium alloys most commonly used for manufacturing the tubes defined in clause 3 are divided in two classes as follows: class A: EN AW-3004, EN AW-3005, EN AW-3103, EN AW-5005, EN AW-5040, EN AW-5049, EN AW-5083, EN AW-5086, EN A

49、W-5251, EN AW-5454, EN AW-5754, EN AW-7075; class B: EN AW-3003, EN AW-3105, EN AW-5052, EN AW-5154B, EN AW-6082, EN AW-7012. Class A and B are defined in EN 573-4. 5.4 Mechanical properties The choice of alloy and condition shall be those made by the purchaser with regard to the intended application. The mechanical properties shall be in conformity with EN 1592-2. Special mechanical properties shall be agreed between producer and purchaser and stated on the orde