BS 7874-1998 Method of test for microbiological deterioration of elastomeric seals for joints in pipework and pipelines《管道工程和管线系统连接的弹性密封件微生物损害的试验方法》.pdf

《BS 7874-1998 Method of test for microbiological deterioration of elastomeric seals for joints in pipework and pipelines《管道工程和管线系统连接的弹性密封件微生物损害的试验方法》.pdf》由会员分享，可在线阅读，更多相关《BS 7874-1998 Method of test for microbiological deterioration of elastomeric seals for joints in pipework and pipelines《管道工程和管线系统连接的弹性密封件微生物损害的试验方法》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS 7874 : 1998 ICS 23.040

2、.80 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Method of test for Microbiological deterioration of elastomeric seals for joints in pipework and pipelinesBS 7874 : 1998 This British Standard, having been prepared under the direction of the Sector Board for Materials and Ch

3、emicals, was published under the authority of the Standards Board and comes into effect on 15 March 1998 BSI 1998 The following BSI references relate to the work on this standard: Committee reference PRI/70 Draft announced in Update Standards, February 1998 ISBN 0 580 26299 5 Amendments issued since

4、 publication Amd. No. Date Text affected Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee PRI/70, Elastomeric seals for joints in pipework and pipelines, upon which the following bodies were represented: British Gas plc Br

5、itish Plastics Federation British Precast Concrete Federation Ltd. British Rubber Manufacturers Association Ltd. Chartered Institution of Water and Environmental Management Clay Pipe Development Association Limited Concrete Pipe Association Ductile Iron Producers Association Fibre Cement Manufacture

6、rs Association Limited Malaysian Rubber Producers Research Association RAPRA Technology Ltd. Society of British Water Industries Water Companies Association Water Services Association of England and WalesBS 7874 : 1998 BSI 1998 i Contents Page Committees responsible Inside front cover Foreword ii Me

7、thod 1 Scope 1 2 Informative references 1 3 Principle 1 4 Materials 1 5 Apparatus 1 6 Preparation of test pieces 1 7 Procedure 3 8 Calculation of results 3 9 Test report 4 Figures 1 Typical arrangement of tanks for biodeterioration test 2 2 Test piece dimensions for biodeterioration test 4 List of r

8、eferences Inside back coverii BSI 1998 BS 7874 : 1998 Foreword This British Standard has been prepared by Technical Committee PRI/70. This method was previously contained in annex B of BS 2494 : 1990, from which it has been deleted as a consequence of the publication of BS EN 681-1 : 1996. NOTE. Sea

9、ls of type D, H, S and W, as specified previously in BS 2494 : 1990, conformed to the following requirements: a) the average loss in mass (Z) of the test set of test pieces does not exceed 3.5 %; b) there is no greater release of carbon black or other fillers from the test set than from the control

10、set when the surface of the specimens is lightly rubbed. In the case of composite seals the requirements applied only to those components exposed to the contents of the pipeline or pipework. Within BS EN 681-1 there is no microbiological requirement for elastomeric seals. However, the UK has found t

11、he above requirements and method to be acceptable. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 to 4, an inside back cover and a back cover. BSI 199

12、8 1 BS 7874 : 1998 Method 1 Scope This British Standard details the test method for microbiological deterioration for elastomeric joint seals. The method is applicable to elastomeric components of composite or non-composite rings, seals, jointing gaskets and similar components used to seal aqueous f

13、luids in pipes and fittings. It is applicable to all categories of aqueous fluid, including raw and treated potable water, sewerage and drainage water. 2 Informative references This British Standard refers to other publications that provide information or guidance. Editions of these publications cur

14、rent at the time of issue of this standard are listed on the inside back cover, but reference should be made to the latest editions. 3 Principle Test pieces under tensile strain are exposed to raw river water, inoculated with suitable organisms and maintained at a high dissolved oxygen concentration

15、. Losses in mass are measured at the end of the exposure period and any release of carbon black or other fillers noted. 4 Materials 4.1 A source of raw river water having all the following characteristics: a) an oxygen saturation greater than 60 %; b) a biological oxygen demand (BOD) of # 8.5 mg/l;

16、c) an ammonia content, as ammonium ions, # 0.9 mg/l. 4.2 An inoculum of rubber degrading organisms is provided by introducing into the header tank (5.2)a suspended rubber seal showing active signs of biological deterioration. 5 Apparatus 5.1 Stainless steel frame, containing two stainless steel rods

17、 of 4.7 mm to 4.8 mm diameter, maintained in parallel (110 1) mm apart (see figure 1). NOTE. Spacer plates may be located at intervals as necessary to brace the rods at the specified spacing if the tension exerted by the test pieces would otherwise cause excessive flexure of the rods. 5.2 Header tan

18、k, constructed of non-metallic material and including a cover which permits ventilation. The tank is constructed or enclosed such that light is excluded from the contents of the tank. The tank shall contain water of the type described in 4.1, in which a source of inoculum in accordance with 4.2 is m

19、aintained following an initial residence period of not less than 7 days. The tank shall discharge continuously into the test tank (5.3) via a flow control device which maintains the rate of overflow discharge from the test tank equivalent to (0.4 0.1) volume change/day of the water content of the te

20、st tank. The header tank shall be replenished with water in accordance with 4.1 so that the source of inoculum in the header tank remains submerged. NOTE. The system for replenishment of the header tank will depend upon the rate of discharge used when filling the test tank and when maintaining the r

21、equired rate of overflow discharge from the test tank. 5.3 Test tank, constructed of glass or other inert material, into which the frame can be inserted (see figure 1). The tank shall initially be filled with raw river water conforming to 4.1, or with inoculated water from the header tank, and shall

22、 be provided with an overflow outlet to maintain the level in the test tank by discharging the excess supply of inoculated water from the header tank (5.2), which has been on stream from the header tank for not less than 7 days. Except when access to the samples is required, the tank shall be surrou

23、nded by an enclosure that excludes light. 5.4 Air pump, fitted with a multiple outlet manifold to maintain a visible diffuse air stream throughout the length of the water in the test tank (see figure 1). 5.5 Temperature controls, for maintaining the temperature within the test tank at (23 2)8C. 5.6

24、Balance, capable of weighing to within 0.0005 g. 5.7 Drying oven, maintained at (105 2) 8C. 5.8 Ultrasonic cleaning bath, capable of operation at 45 kHz. NOTE. A power input of 55 W has been found satisfactory for use with an ultrasonic cleaning bath having a capacity of between 1.7 l and 2 l. 6 Pre

25、paration of test pieces Prepare eight test pieces, each measuring approximately 140 mm3 20 mm, from test sheets (2 0.2) mm thick (see figure 2). Punch two holes approximately 3 mm in diameter on the centre line of each strip and (100 1) mm between centres.2 BSI 1998 BS 7874 : 1998 Figure 1. Typical

26、arrangement of tanks for biodeterioration test BSI 1998 3 BS 7874 : 1998 7 Procedure 7.1 Divide the test pieces into a control set of four and a test set of four. Identify each test piece by means of a suitable procedure. Weigh all test pieces to an accuracy of 0.0005 g. Record the individual masses

27、, M 1 , of the control set test pieces and the individual masses, M 2 , of the test set test pieces. Store the control set at (23 2)8C in a sealed opaque envelope or packet. 7.2 Stretch the four test pieces of the test set between the rods, using the punched holes, to give an extension of approximat

28、ely 10 %. Space the test pieces on the frame so that they do not touch one another and record the position of each test piece for identification purposes. If simultaneously testing materials which may give rise to mutual interference, for example by cross-contamination or by the effects on the micro

29、-organisms of a leachable biocide, separate test tanks shall be used which are connected in parallel so that each is flushed at the specified rate (see 4.2). Otherwise, if test pieces of different formulations are to be tested on a common frame, stainless steel separator plates shall be interposed.

30、7.3 Insert the loaded frame into a test tank containing inoculated water in accordance with 4.3 so that the test pieces are completely immersed. Maintain the level of the water by topping up with inoculated water from the header tank and pass air continuously through the water in the test tank. Main

31、tain the temperature within the test tank enclosure at (23 2)8C. 7.4 After 6 months withdraw the frame from the test tank and remove the test pieces of the test set from the frame and the test pieces of the control set from their envelopes maintaining their order and identities. Clean each test piec

32、e for 1 min in the ultrasonic cleaning bath containing clean tap water only, without solvent or detergent. Remove each test piece, rinse for 30 s under running tap water and place in an oven at (105 2)8C for 2 h. 7.5 Remove the test pieces from the oven, allow them to cool to (23 2)8C in a desiccato

33、r for 1 h and weigh them to an accuracy of 0.0005 g. Record the individual masses, M 3 , of the control set test pieces and the individual masses, M 4 , of the test set test pieces. 7.6 After the mass loss measurements have been taken, lightly rub each test piece on one place with a tissue and compa

34、re the carbon black or other filler release of the control test pieces and the exposed test pieces. 8 Calculation of results Calculate the percentage mass loss, M 5 , for each control set test piece as follows: M 5 = 3 100 M 1 2 M 3 M 1 where: M 1 is the initial mass of the test piece (in g); M 3 is

35、 the mass of the test piece after drying (in g). Determine the average mass loss, X, of the control set test pieces. Calculate the percentage mass loss, M 6 , for each test set test piece as follows: M 6 = 3 100 M 2 2 M 4 M 2 where: M 2 is the initial mass of the test piece (in g); M 4 is the mass o

36、f the test piece after testing and drying (in g). Determine the average mass loss, Y, of the test set test pieces. Calculate the difference in average percentage change in mass loss, Z, between the test set pieces and the control set test pieces as follows: Z = Y2 X4 BSI 1998 BS 7874 : 1998 All dime

37、nsions are in millimetres Figure 2. Test piece dimensions for biodeterioration test 9 Test report The test report shall include the following information: a) identification of samples tested; b) test start date; c) test finish date; d) identification of testing laboratory; e) type of water used; f)

38、inoculum used; g) initial values of sample mass; h) final values of sample mass; i) average percentage change in sample mass; j) difference in average percentage mass loss between the test samples and dry control samples, after oven drying; k) removal of carbon black or other filler by the tissue ru

39、b test; l) general observations on the visual appearance of samples after test; m) details of any interruptions or other deviations in the test programme. BSI 1998 BS 7874 : 1998 List of references Informative references BSI standards publications BRITISH STANDARDS INSTITUTION, London BS 2494 : 1990

40、 Specification for elastomeric seals for joints in pipework and pipelines BS EN 681 : Elastomeric seals Materials requirements for pipe joint seals used in water and drainage applications BS EN 681 : Part 1 : 1996 Vulcanized rubberBSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | |

41、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body res

42、ponsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest ame

43、ndments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be

44、found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publi

45、cations should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards

46、BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Cent

47、re. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 70

48、01. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or tran

49、smitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Co