《BS 3908-2-1967 Methods for the sampling and analysis of lead and lead alloys - Arsenic in lead and lead alloys (photometric method)《铅和铅合金取样与分析方法 第2部分 砷含量测定(光度测量法)》.pdf》由会员分享，可在线阅读，更多相关《BS 3908-2-1967 Methods for the sampling and analysis of lead and lead alloys - Arsenic in lead and lead alloys (photometric method)《铅和铅合金取样与分析方法 第2部分 砷含量测定(光度测量法)》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS 3908-2: 1967 Method for The determination of arsenic in lead and lead alloys (photometric method)BS3908-2:1967 This British Standard, having been approved by the Non-ferrousMetals Industry Standards Committee and endorsed by the Chairman of theEngineering Divisional Council, was

2、published under theauthority of the General Council on 22 March1967 BSI12-1999 The following BSI references relate to the work on this standard: Committee references NFE/22, NFE/22/6 Draft for commentD65/9009 ISBN 0 580 04441 6 Co-operating organizations The Non-ferrous Metals Industry Standards Com

3、mittee, under whose supervision this British Standard was prepared, consists of representatives from the following Government departments, and scientific and industrial organizations: Aluminium Federation Institution of Mining and Metallurgy Association of Bronze and Brass Founders Institution of Pr

4、oduction Engineers Association of Consulting Engineers Institution of Structural Engineers Board of Trade Lead Development Association* British Bronze and Brass Ingot Manufacturers Light Metal Founders Association Association London Metal Exchange British Electrical and Allied Manufacturers Magnesiu

5、m Industry Council Association Ministry of Defence, Army Department British Lead Manufacturers Association* Ministry of Defence, Navy Department* British Non-ferrous Metals Federation* National Brassfoundry Association British Non-ferrous Metals Research Non-ferrous Metal Stockists Association* Post

6、 Office* Copper Development Association Royal Institute of British Architects Crown Agents for Oversea Governments and Society of British Aerospace Companies Ltd. Administrations Society of Motor Manufacturers and Traders Electric Cable Makers Confederation* Ltd. High Conductivity Copper Association

7、 Tin Research Institute Institute of British Foundrymen Zinc Development Association Institute of Metals Individual manufacturers Institution of Mechanical Engineers (Automobile Division) The Government department and scientific and industrial organizations marked with an asterisk in the above list,

8、 together with the following, were directly represented on the committee entrusted with the preparation of this British Standard: Accumulator Makers Association London Transport Board British Battery Makers Association United Kingdom Atomic Energy Authority Amendments issued since publication Amd. N

9、o. Date CommentsBS3908-2:1967 BSI 12-1999 i Contents Page Co-operating organizations Inside front cover Foreword ii 1 Introduction 1 2 Apparatus 1 3 Solutions required 1 4 Sampling 1 5 Procedure 1 6 Calibration 2 Figure 1 Distillation apparatus 3BS3908-2:1967 ii BSI 12-1999 Foreword This standard ma

10、kes reference to the following British Standards: BS 572, Interchangeable conical ground glass joints. BS 3908, Methods for the sampling and analysis of lead and lead alloys Part1:Sampling of ingot lead, lead alloy ingots, sheet, pipe and cable sheathingalloys. This method for the determination of a

11、rsenic in lead and lead alloys, is the second of a series of methods which will form a complete British Standard under the collective title “Methods for the sampling and analysis of lead and lead alloys”, each method being published as a separate part. The preparation of this series of methods has b

12、een authorized by the Non-ferrous Metals Industry Standards Committee as part of a general programme for the standardization of methods for the sampling and analysis of non-ferrous metals. Other methods in the series are as follows: Part 1: Sampling of ingot lead, lead alloy ingots, sheet, pipe and

13、cable sheathing alloys; Part 3: Determination of bismuth in lead and lead alloys; Part 4: Determination of copper in lead and lead alloys; Part 5: Determination of nickel in lead and lead alloys 1) ; Part 6: Determination of tellurium in lead and lead alloys 1) ; Part 7: Determination of silver in l

14、ead and lead alloys 1) ; Part 8: Determination of cadmium in lead and lead alloys 1) ; Part 9: Determination of sulphur in lead and lead alloys 1) ; Part 10: Determination of antimony in lead and lead alloys; Part 11: Determination of tin in lead and lead alloys 1) ; Part 12: Determination of zinc i

15、n lead and lead alloys 1) . The complete British Standard methods will be found suitable for the grades of metals covered by BS334 “Chemical lead”, BS335 “Regulus metal”, BS602 andBS1085 “Lead pipes for other than chemical purposes”, BS801 “Lead and lead alloy sheaths of electric cable”, BS1178 “Mil

16、led lead sheet and strip for building purposes” and BS3909 “Ingot lead for radiation shielding”. The methods have been found to give reliable and reproducible results, and, while in some instances they may appear to be lengthy, it should be realized that they are put forward as “referee” methods to

17、be used in cases of dispute. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of p

18、ages This document comprises a front cover, an inside front cover, pagesi andii, pages1 to3 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. 1) In course of prepara

19、tionBS3908-2:1967 BSI 12-1999 1 1 Introduction 1.1 Principle. After separation by distillation of the trichloride, arsenic is determined photometrically as the reduced arsenomolybdate complex. 1.2 Range. From0.001% up to0.01% of arsenic. 1.3 Reproducibility. Experiments have been carried out indepen

20、dently by a number of analysts using this method. The degree of reproducibility that can be expected is shown by the following analysis of the results obtained: 2 Apparatus 2.1 Any volumetric glassware used shall be of ClassA accuracy as defined in the appropriate British Standards, or where no Brit

21、ish Standard exists, as described in the National Physical Laboratory Publication “Volumetric Tests on Volumetric glassware”. 2.2 Any instrument suitable for measuring the optical density of the solution at a wavelength of830m4 may be used together with4cm cells. Alternatively, when a filter photome

22、ter of the balanced two-cell type is used the following conditions have been found suitable: Tungsten lamp Ilford609 or equivalent filter 2cm cells. 3 Solutions required All reagents shall be of the highest purity obtainable and distilled or demineralized water shall be used throughout. Solutions sh

23、all be freshly prepared and, where necessary, filtered. Standard arsenic. (1mlN 0.1mg of arsenic). Dissolve0.132g of arsenous oxide in2ml of sodium hydroxide solution(5%w/v). Dilute to approximately50ml and add1ml of hydrochloric acid (sp. gr.1.161.18). Transfer to a1litre volumetric flask, dilute t

24、o the mark and mix. Ammonium molybdate (1%w/v). Dissolve1g of ammonium molybdate (NH 4 ) 6 Mo 7 O 24 .4H 2 O in sulphuric acid(20%v/v), dilute to100ml with sulphuric acid(20%v/v) and mix. Hydrazine sulphate (0.15%w/v). Dissolve0.15g ofhydrazine sulphate in water, dilute to100ml andmix. Ammonium moly

25、bdate hydrazine sulphate. Dilute10ml of ammonium molybdate solution(1%) to90ml, add1ml of hydrazine sulphate solution(0.15%), dilute to100ml and mix. 4 Sampling Recommended methods of obtaining a suitable sample for the analytical procedure given below are described in BS3908-1, “Sampling of ingot l

26、ead, lead alloy ingots, sheet, pipe and cable sheathing alloys”. 5 Procedure 5.1 Weigh2g of sample and transfer to a500ml flat-bottomed flask fitted with a joint of size24/29 (also known as B24) complying with the requirements of BS572 2) . Add20ml of sulphuric acid (sp. gr.1.84) and heat gently unt

27、il the initial reaction is complete, then strongly until the space inside the flask is free from white fumes. 5.2 Cool, add30ml of water and cool again. Addcarefully120ml of hydrochloric acid (sp.gr.1.161.18) and0.2g of hydrazine sulphate. 5.3 Distil the solution in an all-glass apparatus (Figure 1)

28、 collecting the distillate in a250ml beaker cooled in running water and containing50ml of water and5ml of nitric acid (sp. gr.1.42). Continue the distillation until the volume in the flask is reduced to8090ml after3035 minutes then remove the beaker containing the distillate and add10ml of nitric ac

29、id (sp. gr.1.42). 5.4 Evaporate almost to dryness. Place in an ovenat110 C and complete the evaporation (about1020 minutes) but avoid baking. 5.5 Cool and add70ml of the ammonium molybdate-hydrazine sulphate solution, heat in a water bath at100 C for20minutes. Cool, transfer to a100ml volumetric fla

30、sk and dilute to the mark. 5.6 Measure the optical density under the conditions specified under “Apparatus”. 5.7 Carry out simultaneously a blank determination on the reagents, following the same procedure without the sample and using the same quantity of reagents. 5.8 Deduct the blank reading and c

31、alculate the percentage of arsenic in the sample by reference to the appropriate calibration graph. Arsenic content Standard deviation s % 0.010 % 0.001 2) BS572, “Interchangeable conical ground glass joints”.BS3908-2:1967 2 BSI 12-1999 6 Calibration 6.1 Transfer0,0.5,1.0,2.0,3.0 and5.0ml aliquots o

32、f standard arsenic solution(1mlN 0.1mg of arsenic) to a series of250ml beakers, add to each5ml of water,1ml of hydrochloric acid (sp.gr.1.161.18) and1ml of nitric acid (sp.gr.1.42). Continue from paragraph5.4 of the procedure. 6.2 Measure the optical density using the conditions specified under “App

33、aratus” and prepare a calibration graph by plotting the optical density against the weight of arsenic in the various aliquots after deduction of the blank reading. BS 3908-2:1967 BSI 12-1999 3 Figure 1 Distillation apparatusBS 3908-2: 1967 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandards

34、Institution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards

35、should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical comm

36、ittee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI,

37、 international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise r

38、equested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and ser

39、vices. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:020

40、89967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a r

41、etrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade design

42、ations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.