BS 2HC 203-1989 Specification for nickel-chromium-aluminium-molybdenum-niobium alloy castings (Nickel base Cr 13 0 Al 6 0 Mo 4 5 Nb 2 3)《镍-铬-铝-钼-铌合金铸件规范(镍基铬13 0、铝6 0、钼4 5、铌2 3)》.pdf

《BS 2HC 203-1989 Specification for nickel-chromium-aluminium-molybdenum-niobium alloy castings (Nickel base Cr 13 0 Al 6 0 Mo 4 5 Nb 2 3)《镍-铬-铝-钼-铌合金铸件规范(镍基铬13 0、铝6 0、钼4 5、铌2 3)》.pdf》由会员分享，可在线阅读，更多相关《BS 2HC 203-1989 Specification for nickel-chromium-aluminium-molybdenum-niobium alloy castings (Nickel base Cr 13 0 Al 6 0 Mo 4 5 Nb 2 3)《镍-铬-铝-钼-铌合金铸件规范(镍基铬13 0、铝6 0、钼4 5、铌2 3)》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS 2HC 203: 1989 Specification for Nickel-chromium- aluminium- molybdenum-niobium alloy castings (Nickel base Cr 13.0, Al 6.0, Mo 4.5, Nb2.3) UDC 629.7:669.245267128293 14:669.245.018BS2HC203:1989 This British Standard, having been prepared under the directionof the

2、 Aerospace Standards Policy Committee ACE/-, was published under theauthority of the Board of BSIand comes into effect on 31October 1989 BSI 12-1999 First published February 1973 First revision October 1989 The following BSI references relate to the work on this standard: Committee reference ACE/48

3、Draft for comment 88/70331 DC ISBN 0 580 17571 5 Committees responsible for this British Standard The preparation of this British Standard was entrusted by the Aerospace Standards Policy Committee (ACE/-) to Technical Committee ACE/48, upon which the following bodies were represented: British Indust

4、rial Fasteners Federation British Steel Industry Ministry of Defence Seamless Steel Tube Association Society of British Aerospace Companies Limited Amendments issued since publication Amd. No. Date of issue CommentsBS2HC203:1989 BSI 12-1999 i Contents Page Committees responsible Inside front cover F

5、oreword ii 1 Scope 1 2 References 1 3 Material requirements 1 Table 1 Material requirements 2BS2HC203:1989 ii BSI 12-1999 Foreword This revision supersedes BS HC 203:1973, which is withdrawn, and includes trace elements in the chemical composition and is presented in a tabular format. The basic spec

6、ification for the material remains unchanged. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligati

7、ons. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages1 and 2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.BS2

8、HC203:1989 BSI 12-1999 1 1 Scope This British Standard specifies the chemical composition, mechanical properties and inspection and test requirements for a heat resisting precipitation hardening, nickel alloy (Nickel base, Cr 13.0, Al 6.0, Mo 4.5, Nb 2.3) in the form of castings and remelting stock.

9、 2 References This standard makes reference to the following British Standards: BS HC 100, Inspection and testing procedure for iron, nickel, copper, cobalt and refractory metal base alloy castings. BS EN 2500, Aerospace series Guidelines for the preparation and use of standards for metallic materia

10、ls 1) . 3 Material requirements The requirements for the material in the delivery and use of conditions are given inTable 1, the format and nomenclature of which complies with the requirements defined in BS EN2500. 1) In preparation.BS2HC203:1989 2 BSI 12-1999 Table 1 Material requirements 1 Chemica

11、l composition% or (parts per million) Element. C Si Mn S Ag Al As B Bi Cd Co Cr Cu Fe Ga Min. 0.08 5.5 (50) 12.0 Max. 0.20 0.50 0.25 0.015 (5) 6.5 (30) (150) (0.5) (0.2) 1.0 14.0 0.50 2.50 (30) Element. ln Mg Mo Nb + Ta Pb Sb Se Sn Ti Tl V W Zn Zr Ni Min. 3.8 1.8 0.5 0.05 Base Max. (0.2) (50) 5.2 2.

12、8 (5) (3) (5) (30) 1.0 (0.2) 0.1 0.2 (10) 0.15 2 1 2 3 3 Method of melting Vacuum melted and cast 4 Form Remelt stock Castings 5 Acceptance standard BS HC 100, sections 1 and 2 BS HC 100, sections 1 and 3 6 Delivery condition and heat treatment As cast, see note 1. 7 Use condition and heat treatment

13、 As cast, see note 1. 8 Test piece heat treatment sampling Cast None BS HC 100, sections 1 and 2 Separate or integral None, See note 1 See note 2 12 Tensile Temperature C Ambient 13 Proof stress R p 0.2 MPa W 685 14 Strength R m MPa W 755 15 Elongation A % W 2.5 17 Hardness H W 280 HB, or W 290 HV o

14、r W 28.5 HRC 21 Stress rupture Temperature C 980 22 Time t h 23 25 Rupture stress R MPa 150 26 Elongation at rupture A % W 4 27 NOTES 1If required by the order, castings shall be heat treated under vacuum or protective atmosphere for 2 hours at 1170 10 C and cooled to room temperature, followed by p

15、recipitation treatment at 870 10 C, for 2 hours. 2If required, the properties to be obtained on test pieces machined from designated areas of castings shall be agreed between the manufacturer and the purchaser.blankBS 2HC 203: 1989 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitut

16、ion BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should m

17、ake sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee re

18、sponsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, interna

19、tional and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested

20、. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. C

21、ontact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002

22、. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval

23、 system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations.

24、If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.