BS 2782-10 Method 1004-1977 Methods of testing plastics Glass reinforced plastics Standard atmospheres for conditioning and testing《塑料试验方法 第10部分 玻璃纤维增强塑料 试验方法1004 调节和试验用标准大气压》.pdf

《BS 2782-10 Method 1004-1977 Methods of testing plastics Glass reinforced plastics Standard atmospheres for conditioning and testing《塑料试验方法 第10部分 玻璃纤维增强塑料 试验方法1004 调节和试验用标准大气压》.pdf》由会员分享，可在线阅读，更多相关《BS 2782-10 Method 1004-1977 Methods of testing plastics Glass reinforced plastics Standard atmospheres for conditioning and testing《塑料试验方法 第10部分 玻璃纤维增强塑料 试验方法1004 调节和试验用标准大气压》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BS 2782 . Part 10 . Method 1004 : 1977 EN 62 UDC (678.5/.8.046.364: 620.171.32/.33: 551.582(4) .! IIqJroduc4ByGLOIIAL J = ENGINEERING DOCUMENTS WIlhTheP_O! BS) Under Royally “-“ British Standard Methods of testing Plastics Part 1 O. G lass reinforced plastics Method 1004. Standard atmospheres for co

2、nditioning and testing Methodes dessai des matieres plastiques Partie 10. Matieres plastiques renforcees au verre textile Methode 1004. Atmospheres normales pour Ie conditionnement et les essais Prufmethoden fUr Kunststoffe T ei I 10. G lasfaserverstarkte Kunststoffe Methode 1004. Normalklima fur Vo

3、rbehandlung und Prufung IMPORTANT NOTE. Before reading this method it is essential to read the foreword, general introduction and instructions to BS 2782, issued separately. Attention is drawn to the information in National appendix A (see inside back cover). This European Standard EN 62 was given,

4、as from 31 August 1977, the status of a British Standard. British Standards Institution Gr3 EUROPEAN STANDARD NORME EUROPEENNE EUROpAISCHE NORM UDC 678.5/8:677.521 :551.51 EN 62 Edition 1 March 1977 Key words: plastics, glass reinforced plastics, tests, testing conditions, test atmospheres, standard

5、 atmospheres, temperature, humidity English version Glass reinforced plastics. Standard atmospheres for conditioning and testing Matieres plastiques renforcees au verre textile. Atmospheres normales pour Ie conditionnement et les essais G lasfaserverstarkte Kunststoffe. Normalklima fUr Vorbehandlung

6、 und PrLifung This European Standard was accepted by CEN on 1977-03-31. The CEN members are bound to adhere to the CEN Internal Regulations which specify under which conditions this European Standard has to be given, without any alteration, the status of a national standard. Up-to-date lists and bib

7、liographical references concerning such national standards may be obtained on application to the CEN Central Secretariat or to any CEN member. This European Standard exists in three versions (English, French, German!. recognized by CEN as equivalent. National versions in other languages rank as tran

8、slations and in case of doubt shall be checked against one of the recognized versions. CEN members are the national standards organizations of Austria, Belgium, Denmark, Finland, France, Germany, Ireland, Italy, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. (EN Europe

9、an Committee for Standardization Comite Europeen de Normalisation Europaisches Komitee fur Normung Central Secretariat: Rue de Brederode, 2, B-1000 Brussels Copyright reserved to all CEN members EN 62 Page 2 Brief history This European Standard was drawn up by CEN Technical Committee 66 Testing of g

10、lass fibre reinforced plastics, the Secretariat of which is held by AFNOR. The contents of.this standard were submitted for ballot to the members of CEN in November 1974 in view of its adoption as a European Standard. This European Standard was adopted by CEN as a result of its acceptance by the fol

11、fowing member countries: Belgium, Denmark, France, Germany, Italy, Portugal, Spain, Sweden, United Kingdom. Glass reinforced plastics. Standard atmospheres for conditioning and testing Foreword Taking into account the climatic conditions existing in Europe, this standard specifies suitable combinati

12、ons of temperature and relative humidity recognized by ISO Recommendation R 291 - 1963, Plastics - Standard atmospheres for conditioning and testing. 1. Scope This standard specifies standard atmospheres for conditioning and testing textile glass reinforced plastics. Special atmospheres applicable t

13、o a particular test or simulating a particular climatic environment are not included. 2. Definition Conditioning, for the purposes of this standard, means exposure of textile glass reinforced plastics to the influence of a prescribed atmosphere for a stipulated period of time. In this sense, the pri

14、ncipal aim of conditioning is to improve the reproducibility of test results. 3. Standard atmosphere The standard test atmosphere is defined below: 3.1 For use when control of temperature and humidity is necessary: 23C, 50 % relative humidity 3.2 For use when only control of temperature is necessary

15、: 23C, ambient humidity 4. Tolerances 4.1 Temperature. The normal tolerance for temperature is 2C. If a closer tolerance is required, it shall be 1C. EN 62 Page 3 4.2 Relative humidity. The normal tolerance for relative humidity is 5 % r.h. If a closer tolerance is required, it shall be 2 % r.h. 5.

16、Conditioning 5.1 When the atmosphere specified in 3.1 is used, the standard time for conditioning is a period of at least 88 hours. 5.2 When the atmosphere specified in 3.2 is used, the standard time for conditioning is a period of 4 hours. 5.3 In the case of particular materials and test specimens

17、which are known to reach temperature and moisture equilibrium rapidly or slowly, and where the times specified in 5.1 or 5.2 are not suitable, a shorter or a longer time may be prescribed in the specifications or test methods concerned. 5.4 The plastics materials should be placed in the conditioning

18、 atmosphere in such a manner that as large a surface as possible of each specimen is exposed. 6. Test atmosphere Unles5 otherwise specified, the specimens shall be tested in the same atmosphere in which they have been conditioned. NOTE. Test specimens conditioned in the atmosphere specified in 3.1 m

19、ay be tested in the corresponding atmosphere specified in 3.2. and those conditioned in the atmosphere specified in 3.2 may be tested in ambient conditions. in cases where the resulting changes of temperature and moisture content are known not to affect the test results. 7. Report The conditioning r

20、eport shall include a reference to this standard and include the following items: 7.1 atmosphere used for conditioning. stating the tolerances applied; 7.2 duration of conditioning; 7.3 atmosphere used for the test. j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j j

21、j j j j National appendix A Origins of work and relationship with other British Standards The United Kingdom participated in the preparation of this and four other similar standards required to enable the principle of reference to standards to be applied in the preparation, by the Commission of the

22、European Communities, of a directive concerning tanks made from reinforced plastics for the transport of dangerous materials. These standards are intended to be used solely for this purpose and they should not be adopted for other applications without full technical consideration of the particular c

23、ircumstances. General considerations relating to the conditioning of plastics are covered in BS 2782, Methods of testing plastics. Foreword, general introduction and instructions. There is no technical incompatibility between the requirements given therein and the present standard. However, the usua

24、l standard atmosphere used in the UK for conditioning plastics is 23 2C, 50 5 % r.h. BS 2782 : Part 10 : Method 1004 : 1977 EN 62 BS 2782 EN62 This British Standard was published under the authority of the Executive Board on 31 August 1977. British Standards Institution, 1977 ISBN: 0 580 09745 5 Cop

25、yright Users of British Standards are reminded that copyright subsists in all BSI publications. No part of this publication may be reproduced in any form without the prior permission in writing of BSI. This does not preclude the free use, in the course of implementing the standard, of necessary deta

26、ils such as symbols and size, type or grade designations. Enquiries should be addressed to the Publications Manager, 101 Pentonville Road, London N1 9ND (Telephone 01-8378801 ; Telex 23218). Cooperating organizations - Part 10 - Method 1004 -1977 Contract requirements Attention is drawn to the fact

27、that this British Standard does not purport to include all the necessary provisions of a contract. Revision of British Standards British Standards are revised, when necessary, by the issue either of amendment slips or of revised editions. It is important that users of British Standards should ascert

28、ain that they are in possession of the latest amendments or editions. The following BSI references relate to the work on this standard: Committee reference PLC/- Draft for comment 74/54599 DC The European Committee for Standardization, undei whOSe direction this European Standard was prepared, compr

29、ises the national standards organizations of the following Western European countries: Austria Belgium Denmark Finland France Germany Ireland Italy Netherlands Norway Portugal Spain Sweden Switzerland United Kingdom Oesterreichisches Normungsinstitut Institut Beige de Normalisation Dansk Standardise

30、ringsraad Suomen Standardisoimisliitto, r.y. Association Franr;:aise de Normalisation DIN Deutsches Institut fur Normung I nstitute for I ndustrial Research and Standards Ente Nazionale Italiano di Unificazione Nederlands Normalisatie-instituut Norges Standardiseringsforbund Repartiao de Normalizaii

31、o I nstituto Nacional de Racionalizaci6n y Normalizaci6n Sveriges Standardiseringskommission Association Suisse de Normalisation British Standards Institution Amendments issued since publication Amd. No. Date of issue Text affected British Standards Institution 2 Park Street London W1A 2BS . Telephone 01-6299000 . Telex 266933 7708