ASTM F626-2008(2013) Standard Specification for Fence Fittings《栅栏配件的标准规范》.pdf

《ASTM F626-2008(2013) Standard Specification for Fence Fittings《栅栏配件的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM F626-2008(2013) Standard Specification for Fence Fittings《栅栏配件的标准规范》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F626 08 (Reapproved 2013)Standard Specification forFence Fittings1This standard is issued under the fixed designation F626; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision. A number in parenth

2、eses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the materials, coatingrequirements, and inspection of fence accessories for chain-link fence for the following:1.1.1 Post and

3、line caps,1.1.2 Rail and brace ends,1.1.3 Top rail sleeves,1.1.4 Tie wires, clips, and fasteners,1.1.5 Tension and brace bands,1.1.6 Tension bars,1.1.7 Truss rod assembly,1.1.8 Barbed wire arms,1.1.9 Color coating of fittings, and1.1.10 Fitting size terminology.1.2 The values stated in inch-pound un

4、its are to be regardedas the standard. The SI values given in parentheses are forinformation only.2. Referenced Documents2.1 ASTM Standards:2A641/A641M Specification for ZincCoated (Galvanized)Carbon Steel WireA809 Specification for Aluminum-Coated (Aluminized)Carbon Steel WireA817 Specification for

5、 Metallic-Coated Steel Wire forChain-Link Fence Fabric and Marcelled Tension WireB26/B26M Specification for Aluminum-Alloy Sand Cast-ingsB85 Specification for Aluminum-Alloy Die CastingsB108 Specification for Aluminum-Alloy Permanent MoldCastingsB117 Practice for Operating Salt Spray (Fog) Apparatus

6、B209 Specification for Aluminum and Aluminum-AlloySheet and PlateB209M Specification for Aluminum and Aluminum-AlloySheet and Plate (Metric)B211 Specification for Aluminum and Aluminum-AlloyRolled or Cold Finished Bar, Rod, and WireB211M Specification for Aluminum and Aluminum-AlloyRolled or Cold-Fi

7、nished Bar, Rod, and Wire (Metric)B221 Specification for Aluminum and Aluminum-Alloy Ex-truded Bars, Rods, Wire, Profiles, and TubesB221M Specification for Aluminum and Aluminum-AlloyExtruded Bars, Rods, Wire, Profiles, and Tubes (Metric)B429/B429M Specification for Aluminum-Alloy ExtrudedStructural

8、 Pipe and TubeB800 Specification for 8000 Series Aluminum Alloy Wirefor Electrical PurposesAnnealed and Intermediate Tem-persF552 Terminology Relating to Chain Link FencingF668 Specification for Polyvinyl Chloride (PVC), Polyolefinand Other Polymer-Coated Steel Chain Link Fence FabricF934 Specificat

9、ion for Colors for Polymer-Coated ChainLink Fence Materials2.2 U.S. Government Standard:MIL-R-60346-C Roving, Glass, Fibrous (For Prepreg Tapeand Roving, Filament Winding, and Pultrusion Applica-tions)33. Post and Line Caps3.1 Post and line caps shall be fabricated from pressed steelor cast iron and

10、 hot-dip galvanized with a minimum of 1.2oz/ft2(366 g/m2) of zinc coating of surface area, or fromaluminum alloy 360.0 conforming to die cast SpecificationB85, or sand cast or permanent mold alloy 356.0 or 713.0conforming to Specification B26/B26M or B108.3.2 Post and line caps shall be designed to

11、fit snugly overposts and exclude moisture from inside when tubular posts areused.4. Rail and Brace Ends4.1 Rail and brace ends, when required, shall be fabricatedfrom pressed steel or cast iron, and hot-dip galvanized with aminimum of 1.2 oz/ft2(366 g/m2) of zinc coating of surface1This specificatio

12、n is under the jurisdiction of ASTM Committee F14 on Fencesand is the direct responsibility of Subcommittee F14.40 on Chain Link Fence andWire Accessories.Current edition approved March 1, 2013. Published March 2013. Originallyapproved in 1979. Last previous edition approved in 2008 as F626 - 08. DO

13、I:10.1520/F0626-08R13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Standardization Documen

14、ts Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 191115094, Attn: NPODS.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1area, or from aluminum alloy 360.0 (see Specification B85), oralloy 356.0 or 713.0 (see Specifi

15、cation B26/B26M or Specifi-cation B108).4.2 Rail and brace ends, or other approved means ofconnection, shall be provided when top rail or brace arerequired.5. Top Rail Sleeves5.1 Top rail sleeves shall be fabricated from pressed steel orround steel tubing and hot-dip galvanized with a minimum of1.2

16、oz/ft2(366 g/m2) of zinc coating of surface area, or fromaluminum alloy 6063-T6 (see Specification B221, B221M orSpecification B429/B429M).5.2 Rail sleeve material shall be a minimum of 0.051 in. (1.3mm) in thickness if steel, or a minimum of 0.062 in. (1.8 mm)in thickness if aluminum alloy, and a m

17、inimum of 6 in. (152.4mm) in length.5.3 The rail sleeve must be fabricated to prevent movementalong the rail.6. Tie Wires and Clips6.1 Tie wires or clips, or both, for attaching chain-link fabricto round tubular or rectangular roll-formed horizontal rails andintermediate posts shall be one of the fo

18、llowing systems, asselected by the purchaser:6.1.1 Standard Round Wire Ties with either a preformedhook or pigtail at one end, shall be designed of sufficient lengthto engage one picket of the chain-link fabric at the preformedend of the tie by wrapping it with two 360 degree turns andthen wrapping

19、the body of the tie around the rail or post aminimum of 180 degrees. The opposite end of the tie should besecured to the nearest chain-link fabric picket on this other sideof the post or rail also with two 360 degree wraps. The finalprocess of tightening the tie on the fabric picket wire shoulddraw

20、the fabric and the main body to the tie tightly to the railor post. Care must be taken to ensure that the ends of the tiesor clips do not protrude beyond the vertical plane on either sideof the chain-link fabric to avoid injury to pedestrians in contactwith the fence. Standard round wire ties shall

21、be of one of thefollowing materials, as selected by the purchaser:6.1.1.1 Twelve-gage (0.106 6 0.004-in. (2.69 6 0.10-mm)steel with a tensile strength range from 55 to 65 ksi and withone of the following coatings, as selected by the purchaser:(1) A minimum of 0.80 oz/ft2(230 g/m2) of zinc inaccordan

22、ce with Specification A641 (A641M), Class 3 or Acoating.(2) A minimum of 0.35 oz/ft2(107 g/m2) of aluminum inaccordance with Specification A809.6.1.1.2 Nine-gage (0.148 6 0.005-in. (3.76 6 0.10-mm)steel with a tensile strength range from 55 to 65 ksi and withone of the following coatings, as selecte

23、d by the purchaser:(1) A minimum of 0.90 oz/ft2(270 g/m2) of zinc inaccordance with Specification A641 (A641M), Class 3 or Acoating.(2) A minimum of 0.40 oz/ft2(122 g/m2) of aluminum inaccordance with Specification A809.NOTE 1Heavier zinc coatings than those listed in 6.1.1.1 (1) and6.1.1.2 (1) may

24、be specified if desired, to match the minimum zinc coatingspecified for the fence fabric.6.1.1.3 Nine-gage (0.148 6 0.005-in. (3.76 6 0.125-mm)or (6-gage 0.192 6 0.005-in. (4.88 6 0.125-mm) aluminumAlloy 1350-H19 or approved equal.6.1.2 High-Security Round Wire Ties shall be one of thefollowing, as

25、selected by the purchaser:6.1.2.1 Power-Fastened Round Wire Ties, preformed to theradius of the rail or post and configurated to wrap a full 360around the rail or post and minimum of one complete diamondof the chain-link fabric. The two ends of the tie shall bepreformed in such a manner that they ca

26、n be twisted togetherin a close helix of 112 machine turns, which is equivalent to 3full twists, thereby drawing up tightly around the rail or postand the chain-link fabric. Power-fastened round wire ties shallbe of either 6-gage (0.192 6 0.005-in. (4.88 6 0.125-mm) or9-gage (0.148 6 0.005-in. (3.76

27、 6 0.125-mm) steel asselected by the purchaser, with a tensile strength range from 65to 75 ksi, and with one of the following coatings, as selected bythe purchaser:(1) A minimum of 2.00 oz/ft2(600 g/m2) of zinc for 6-gageor 1.80 oz/ft2(540 g/m2) of zinc for 9-gage in accordance withSpecification A64

28、1 (A641M), Class B coating.(2) A minimum of 0.40 oz/ft2(122 g/m2) of aluminum for6-gage or 9-gage in accordance with Specification A809.6.1.2.2 Manually Fastened Round Wire Ties, of sufficientlength to weave through the fence fabric, wrap around the postor rail a full 360 and be twisted securely wit

29、h three full twists.At the contractors option, these ties may be power twisted.After twisting, the protruding wire ends shall be cut off toprevent untwisting by hand. Manually fastened round wire tiesshall be of either 6-gage (0.192 6 0.005-in. (4.88 6 0.125mm) or 9-gage (0.148 6 0.005-in. (3.76 6 0

30、.125-mm) steelas selected by the purchaser, with a tensile strength range from55 to 65 ksi, and with one of the following coatings, as selectedby the purchaser:(1) A minimum of 1.2 oz/ft2(366 g/m2) of zinc in accor-dance with Specification A817, Type 2, Class 1.(2) A minimum of 0.40 oz/ft2(122 g/m2)

31、 of aluminum inaccordance with Specification A809.6.1.3 Interlocking Flat Wire Ties, preformed to the radius ofthe rail or post and configurated to wrap a full 360 around therail or post and one picket of the chain-link fabric. The ends ofthe tie shall be preformed in such a manner that they willint

32、erlock and flatten down into a double closed loop against therail or post. Interlocking flat wire ties shall be fabricated from0.0625 by 0.375-in. (1.59 by 9.53-mm) flat aluminum Alloy5052-H32 wire with a tolerance of 60.005 in. (61.25 mm).6.1.4 Power-Driven Fasteners, consisting of a knurled pinof

33、carbon steel, heat treated to a hardness of RC 5256 and aminimum tensile strength of 240 000 psi (1655 MPa). Finishshall be zinc electroplating of 0.0003-in. (0.0076-mm) mini-mum thickness, evaluated for corrosion resistance for 72consecutive hours with no signs of rust or corrosion whentested in ac

34、cordance with Practice B117. Cap shall be Type 304stainless steel332 in. (2.38 mm) thick. For 9-gage or 11-gagefabric other than38-in. (9.53-mm) mesh, the pin shall be 1 in.F626 08 (2013)2(25.4 mm) long. For38-in. mesh and 6-gage fabric, the pinshall be 114 in. (31.75 mm) long.6.2 Round wire clips f

35、or attaching chain-link fabric toH-beam posts shall be a minimum of 7-gage (0.177 60.005-in. (4.50 6 0.125-mm) wire, preformed and configu-rated to engage both edges of the fabric side of the flange of theH-beam and one picket of the chain-link fabric. Round wireclips for H-beam posts shall be fabri

36、cated from either steel wirewith a minimum of 0.90 oz/ft2(275 g/m2) of zinc coating inaccordance with Specification A641 (A641M), Class 3 or Acoating, or aluminum Alloy 1350-H19 wire.6.3 Round wire hog rings for attaching chain-link fabric tohorizontal tension wire shall be either 12-gage (0.106 60.

37、005-in. (2.69 6 0.125-mm) steel wire with a minimum of0.80 oz/ft2(230 g/m2) of zinc coating in accordance withSpecification A641 (A641M), Class 3 or A coating, or 9-gage(0.148 6 0.005-in. (3.76 6 0.125-mm) aluminum Alloy1350-H19 wire.6.4 Round metallic-coated steel tie wires, clips, and hogrings sha

38、ll withstand all forming or twisting operations, orboth, without cracking or flaking of the coating to such anextent that any zinc or aluminum can be removed by rubbingwith the bare fingers.NOTE 2Loosening or detachment during forming or twistingoperations, or both, of superficial, small particles o

39、f coating metal formedby mechanical polishing of the surface of the coating wire shall not beconsidered cause for rejection.6.5 Where specified, round metallic-coated tie wires, clips,and hog rings shall be polymer coated to match the color of thechain-link fabric, as selected from Specification F93

40、4. Thecoating process and metallic-coated core wire materials shallbe in accordance with Specification F668. The diameter of themetallic-coated core wire shall be identical to that specified forthe chain-link fabric, but shall not be smaller than 11 gage(0.120 6 0.005 in. (3.05 6 0.125 mm) and not l

41、arger than 9gage (0.148 6 0.005 in. (3.76 6 0.125 mm). The tensilestrength of the core wire constituting the tie wires, clips, andhog rings shall be suitable to accommodate a manual or powerfastening process without causing damage to the metallic orpolymer coatings.NOTE 3Although rust formation on t

42、he cut ends or other unprotectedsurface areas of steel tie wires is primarily an inherent characteristic ofaluminum coated steel wire, rejections of material exhibiting this condi-tion will not be warranted irrespective of the core wire material employedunless it causes significant and noticeable st

43、aining of the tie, the chain-linkfabric, the post surface, or the rail surface.7. Tension and Brace Bands7.1 Tension and brace bands shall be fabricated frompressed steel and hot-dip galvanized with a minimum of 1.2oz/ft2(366 g/m2) of zinc coating of surface area, or fromaluminum alloy 6063-T5, 6063

44、-T6, or 8176H19 (see Speci-fication B211, B211M, B221, B221M,orB800).7.2 Tension bands shall be a minimum of 14 gage (0.074 in.(1.88 mm) in thickness and a minimum of34 in. (19.05 mm)in width.7.3 Brace bands shall be a minimum of 12 gage (0.105 in.(2.66 mm) in thickness and a minimum of34 in. (19.05

45、 mm)in width.8. Tension Bars8.1 Steel tension bars shall be fabricated from merchantquality steel and hot-dip galvanized with a minimum of 1.2oz/ft2(366 g/m2) of zinc coating of surface area.8.2 Fiberglass tension bars shall be manufactured fromunidirectional E-glass fibers in accordance with MIL-R-

46、60346-C and processed to produce the desired shape andmechanical properties. The outer surface shall consist of aminimum average 1.5 mil (0.0015 in. (0.038 mm) thickweather resistant plastic coating.8.3 Aluminum alloy tension bars shall be 6061-T6 or6063-T6 alloy (see Specification B211M or B221M).8

47、.4 Steel or fiberglass tension bars used to connect 134 in.(44.5 mm) and 2 in. (50 mm) mesh fabric to end, gate andcorner posts shall be a minimum of316 in. (4.8 mm) by58 in.(15.9 mm) for fabric heights up to 5 ft (1.52 m) and a minimumof316 in. (4.9 mm) by34 in. (19.1 mm) for fabric heights over5 f

48、t (1.52 m). Steel, fiberglass, or aluminum alloy tension barsused to connect 1 in. (25.4 mm) mesh fabric to end, gate andcorner posts shall be a minimum of14 in. (6.4 mm) by38 in.(9.5 mm).8.5 Aluminum alloy tension bars used to connect 134 in.(44.5 mm) and 2 in. (50 mm) mesh fabric to end, gate andc

49、orner posts shall be a minimum of14 in. (6.4 mm) by34 in.(19.1 mm).8.6 Minimum lengths of tension bar shall be 2 in. (50 mm)less than the full height of the chain link fabric.9. Truss Rod Assembly9.1 Steel truss rods shall be fabricated from516 in. (7.9 mm)merchant quality rod and it and all related devices shall behot-dip galvanized after threading with a minimum of 1.2oz/ft2(366 g/m2) of zinc coating of surface area.9.2 Aluminum alloy truss rods shall be fabricated from38in. (9.5 mm) alloy 6061-T6 (see Specification B211 or B211Mor B221