ASTM D5360-2015 Standard Practice for Design and Construction of Bituminous Surface Treatments《处理沥青路面的设计和施工的标准实施规程》.pdf

《ASTM D5360-2015 Standard Practice for Design and Construction of Bituminous Surface Treatments《处理沥青路面的设计和施工的标准实施规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM D5360-2015 Standard Practice for Design and Construction of Bituminous Surface Treatments《处理沥青路面的设计和施工的标准实施规程》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D5360 09D5360 15Standard Practice forDesign and Construction of Bituminous SurfaceTreatments1This standard is issued under the fixed designation D5360; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last r

2、evision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers the design and construction of bituminous surface treatments. It is a guide and should be used as such.

3、End-use specifications should be adopted to conform to job and user requirements.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.

4、3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use. For specific preca

5、utions see Section 9.2. Referenced Documents2.1 ASTM Standards:2D140 Practice for Sampling Bituminous MaterialsD448 Classification for Sizes of Aggregate for Road and Bridge ConstructionD490 Specification for Road TarD946 Specification for Penetration-Graded Asphalt Cement for Use in Pavement Constr

6、uctionD977 Specification for Emulsified AsphaltD1139 Specification for Aggregate for Single or Multiple Bituminous Surface TreatmentsD1369 Practice for Quantities of Materials for Bituminous Surface TreatmentsD2027 Specification for Cutback Asphalt (Medium-Curing Type)D2028 Specification for Cutback

7、 Asphalt (Rapid-Curing Type)D2397 Specification for Cationic Emulsified AsphaltD2399 Practice for Selection of Cutback AsphaltsD2995 Practice for Estimating Application Rate and Residual Application Rate of Bituminous DistributorsD3381 Specification for Viscosity-Graded Asphalt Cement for Use in Pav

8、ement ConstructionD3628 Practice for Selection and Use of Emulsified AsphaltsD5624 Practice for Determining the Transverse-Aggregate Spread Rate for Surface Treatment ApplicationsD6114 Specification for Asphalt-Rubber BinderD6154 Specification for Chemically Modified Asphalt Cement for Use in Paveme

9、nt ConstructionD6373 Specification for Performance Graded Asphalt Binder3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 multiple surface treatmentthe bituminous surface produced by the repeat application of bitumen and aggregate a secondor even a third time, with the aggregate

10、 size usually becoming smaller with each application. Each layer is immediately rolled,preferably with a pneumatic-tired roller.1 This practice is under the jurisdiction of ASTM Committee D04 on Road and Paving Materials and is the direct responsibility of Subcommittee D04.24 onBituminousAsphalt Sur

11、face Treatments.Current edition approved Dec. 1, 2009Dec. 1, 2015. Published January 2010January 2016. Originally approved in 1998. Last previous edition approved in 20052009 asD5360 05.D5360 09. DOI: 10.1520/D5360-09.10.1520/D5360-15.2 For referencedASTM standards, visit theASTM website, www.astm.o

12、rg, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what chang

13、es have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the offici

14、al document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.2 single surface treatmentthe bituminous surface produced by the application of bitumen to a prepared surface followedat once by an aggregate cover. The surface is immedi

15、ately rolled, preferably with a pneumatic-tired roller.3.1.3 surface treatmentan application of bituminous material followed by a layer of mineral aggregate. Multiple applicationsof bituminous material and mineral aggregate may be used.3.1.3.1 DiscussionThe terms “seal coat” and “chip seal” have bee

16、n used interchangeably with the term “surface treatment.”4. Significance and Use4.1 This practice is to be used as a guide and not a specification.5. Ordering Information5.1 Orders for seal coat and surface treatment materials under this guide shall include the following information:5.1.1 Type of bi

17、tumen (asphalt cement,binder, emulsified asphalt, cutback asphalt, road tar) specification designation,5.1.2 Grade of bitumen,5.1.3 Quantity of bitumen required,5.1.4 Type of aggregate (crushed stone, crushed gravel, crushed slag, gravel, slag) specification designation,5.1.5 Size or sizes of aggreg

18、ate to be furnished,5.1.6 Quantity of aggregate required, and5.1.7 Special requirements.6. Aggregate6.1 Cover Aggregate, shall conform to Specification D1139 and Classification D448.6.2 SizeAggregate should be as close to one size as is economically practical, preferably in the range of 12 to 14 in.

19、 (13 to6 mm) for single surface treatments. For multiple surface treatments, aggregate in the range of 1 to 12 in. (25 to 13 mm) is usedfor the bottom layer with each successive layer using aggregate approximately 12 the size of the previous aggregate layer. Largersizes may be used in multiple treat

20、ments.NOTE 1Aggregates larger than 12 in. (13 mm) can cause objectionable tire noise.NOTE 2Aggregates finer than 18 in. (3 mm) are difficult to spread evenly. Also, the finer the aggregate, the smaller is the tolerable range for thebituminous material application rate.6.3 ShapeThe ideal shape is cub

21、ical. Flat or elongated particles are undesirable. Flat particles tend to become aligned on theirflat sides and may be completely covered with bituminous material when enough is used to hold the cubical particles in place.Rounded particles tend to roll and have poor retention, and therefore, are und

22、esirable.6.4 CleanlinessClean aggregate is extremely important. If the coarse aggregate particles are dusty or coated with fine material,the bituminous material may not adhere to the aggregate, resulting in loss of cover aggregate and poor performance. It isrecommended that the fraction passing the

23、No. 200 mesh screen not exceed 1 % by weight.7. Bitumen7.1 When asphalt cementbinder is used, it shall conform to one of the following specifications: D946, D3381, D6114, D6154,or D6373.NOTE 3The grade of asphalt cementbinder to be used depends on climatic conditions and amount and type of traffic.7

24、.2 When cutback asphalt is used, it shall conform to either Specification D2027 or Specification D2028.NOTE 4Selection of cutback type (rapid-cure or medium-cure) and grade depends on the type of construction, climatic conditions, amount and natureof traffic, and cleanliness of aggregate. Refer to P

25、ractice D2399 for selection guide.7.3 When emulsified asphalt is used, it shall conform to either Specification D977 or Specification D2397.NOTE 5The emulsified asphalt type and grade to be used depends on the type of construction, climatic conditions, amount and nature of traffic, andcleanliness of

26、 aggregate. Use Practice D3628 for a selection guide. Other types of emulsified asphalt may be used if experience has shown that satisfactoryperformance will result.7.4 When road tar is used, it shall conform to Specification D490.8. Application Rates8.1 The bituminous material application rate shal

27、l be estimated by using Practice D1369 for guidance.8.2 The bituminous material shall be applied by a bituminous distributor that has been calibrated for had the transverse andlongitudinal application rate rates determined by Practice D2995.D5360 1528.3 The aggregate application rate shall be estima

28、ted by using Practice D1369 as a guide.8.4 The aggregate shall be applied by a self-propelled mechanical spreader or other aggregate spreading device that is capableof uniformly spreading the aggregate at the desired rate and width. The spreader shall be calibrated to apply the quantity of coveraggr

29、egate indicated by the design requirements for a given project. This calibration can be accomplished with several sheets ofcanvas, canvas or other similar material, each being one square yard (square metre), and a suitable scale. This is done in a mannersimilar to Test Method D5624 for bituminous di

30、stributors.9. Precautions9.1 Surface treatment operations should not be carried out during periods of cold or wet weather, or both. The surface shall beclean and dry while performing the work.9.1.1 The air temperature should be at least 50F (10C) in the shade and rising before starting the operation

31、. The operationshould not be permitted when the temperature is 60F (15.6C) or less and falling.9.1.2 The operation should not be carried out in the rain, or when rain is threatening.10. Method of Sampling and Testing10.1 Sample materials in accordance with Practice D140.10.2 Calibrate application eq

32、uipment in accordance with the following standards:10.2.1 Determining Application Rate and Residual Application Rate of Bituminous DistributorsPractice D2995.10.2.2 Determining the Transverse Aggregate Spread Rate for Surface Treatment ApplicationsTest Method D5624.11. Construction Procedure11.1 Pat

33、ch potholes, fill cracks, and repair damaged areas in existing pavement or consolidated base.11.2 The surface to be covered should be cleaned with a rotary broom or other approved means.11.3 Spray bituminous material at the specified rate and proper temperature for type and grade of material. The re

34、commendedviscosity range for spraying is 20120 cSt, kinematic (approximately 1060 SFS). A guide to the range that encompasses thecorrect spraying temperature for various types and grades of material can be found in the appropriate standard for the material (thatis, asphalt cement,binder, cutback asp

35、halt, emulsified asphalt, road tar).NOTE 6The flash point of some grades of bituminous materials is below 250F (121C); therefore, caution must be used when applying heat to thesematerials.11.4 Spread cover aggregate at the specified rate immediately behind the bituminous material spray application t

36、o achievemaximum possible chip wetting and embedment depth. This is essential in the case of asphalt cementbinder and road tar becauseof the rapid increase in viscosity with cooling, and is greatly desirable in the case of emulsified asphalt emulsions and cutbackasphaltsasphalt to maximize the menis

37、cus effect. The cover aggregate should be placed on the bituminous material within 2 minof the bituminous application.11.5 Roll the surface immediately after application of the cover aggregate, aggregate to ensure embedment, preferably with apneumatic-tired roller, to seat chips in the bituminous me

38、mbrane. The speed of the roller should not exceed 5 mph. Depending onenvironment conditions, type and amount of bituminous material, three (3) passes of a 12 to 15-ton pneumatic-tired roller arenormally used. Initial rolling of the aggregate should occur within 5 min of the application of the bitumi

39、nous material, and the finalof the three rolling coverages should be completed within 3015 min.11.6 Control traffic speed until bituminous material has set. It is recommended that traffic speed not exceed 20 mph for a periodof 4 h after placement of the surface treatment.11.7 For multiple surface tr

40、eatments, repeat steps 11.3 11.6. Successive applications should be applied only after the previousbituminous surface treatment has set and cured, usually one day. Remove excess aggregate before applying the second or thirdlayer of surface treatment.D5360 15312. Keywords12.1 chip seal; multiple surf

41、ace treatment; seal coat; single surface treatment; surface treatmentASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of an

42、y such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are in

43、vited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not receive

44、d a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of t

45、his standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 154